CN102453365A - 一种外墙弹性腻子及其加工工艺 - Google Patents
一种外墙弹性腻子及其加工工艺 Download PDFInfo
- Publication number
- CN102453365A CN102453365A CN2010105304749A CN201010530474A CN102453365A CN 102453365 A CN102453365 A CN 102453365A CN 2010105304749 A CN2010105304749 A CN 2010105304749A CN 201010530474 A CN201010530474 A CN 201010530474A CN 102453365 A CN102453365 A CN 102453365A
- Authority
- CN
- China
- Prior art keywords
- exterior walls
- elastic
- ucar
- sanitas
- skimmer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种外墙弹性腻子及其加工工艺。由弹性乳液、分散剂、丙二醇、纤维素、消泡剂、碳酸钙、硅灰石粉、防腐剂、增稠剂和水组成,各成分占总质量的重量百分比例分别为:弹性乳液40-60%、分散剂0.1-0.3%、丙二醇0.2-1%、纤维素0.1-0.3%、消泡剂0.1-0.3%、碳酸钙20-30%、硅灰石粉3-3.5%、防腐剂0.1-0.3%、增稠剂0.3-0.7%、其余为水。本发明产品在常温下具有较强的弹性和超强的粘结力,防水性能优越,是建筑外墙优质批嵌材料,能遮盖墙面的龟裂纹,防止墙面疏松或进一步开裂,保护腔体钢筋免受氧化。本发明工艺操作方便、工作效率高。
Description
技术领域
本发明涉及一种建筑涂料及其加工工艺,尤其涉及一种外墙弹性腻子及其加工工艺。
背景技术
在涂刷过底漆或面漆的墙壁上,由于种种原因会产生龟裂纹和凹凸不平的情况,这样不仅使得墙壁的外形美观受损,还会造成墙壁渗水,防水性能大大降低,不采取弥补措施,墙面会疏松和进一步开裂,造成不可挽回的损失。
发明内容
本发明为了解决以上问题提供了一种弹性好、粘结力好、防水性能优越的外墙弹性腻子及其加工工艺。
本发明产品的技术方案是:由弹性乳液、分散剂、丙二醇、纤维素、消泡剂、碳酸钙、硅灰石粉、防腐剂、增稠剂和水组成,各成分占总质量的重量百分比例分别为:弹性乳液40-60%、分散剂0.1-0.3%、丙二醇0.2-1%、纤维素0.1-0.3%、消泡剂0.1-0.3%、碳酸钙20-30%、硅灰石粉3-3.5%、防腐剂0.1-0.3%、增稠剂0.3-0.7%、其余为水。
本发明工艺的技术方案是:将上述原料按以下步骤进行:
1)、将40%的弹性乳液、1%的消泡剂、0.1%的分散剂、0.2%的丙二醇和36.1%的水投入分散机中;
2)、再将20%的碳酸钙、0.1%的纤维素、3%的硅灰石粉、0.1%的防腐剂投入至分散机中;
3)、最后加入0.3%的增稠剂得到成品。
本发明产品在常温下具有较强的弹性和超强的粘结力,防水性能优越,是建筑外墙优质批嵌材料,能遮盖墙面的龟裂纹,防止墙面疏松或进一步开裂,保护腔体钢筋免受氧化。
本发明工艺操作方便、工作效率高。
具体实施方式
一种外墙弹性腻子,由弹性乳液、分散剂、丙二醇、纤维素、消泡剂、碳酸钙、硅灰石粉、防腐剂、增稠剂和水组成,各成分占总质量的重量百分比例分别为:弹性乳液40-60%、分散剂0.1-0.3%、丙二醇0.2-1%、纤维素0.1-0.3%、消泡剂0.1-0.3%、碳酸钙20-30%、硅灰石粉3-3.5%、防腐剂0.1-0.3%、增稠剂0.3-0.7%、其余为水。
一种外墙弹性腻子的加工工艺,将上述原料按以下步骤进行:
1)、将40%的弹性乳液、1%的消泡剂、0.1%的分散剂、0.2%的丙二醇和36.1%的水投入分散机中;
2)、再将20%的碳酸钙、0.1%的纤维素、3%的硅灰石粉、0.1%的防腐剂投入至分散机中;
3)、最后加入0.3%的增稠剂得到成品。
Claims (2)
1.一种外墙弹性腻子,其特征在于:由弹性乳液、分散剂、丙二醇、纤维素、消泡剂、碳酸钙、硅灰石粉、防腐剂、增稠剂和水组成,各成分占总质量的重量百分比例分别为:弹性乳液40-60%、分散剂0.1-0.3%、丙二醇0.2-1%、纤维素0.1-0.3%、消泡剂0.1-0.3%、碳酸钙20-30%、硅灰石粉3-3.5%、防腐剂0.1-0.3%、增稠剂0.3-0.7%、其余为水。
2.一种外墙弹性腻子的加工工艺,其特征在于:将上述原料按以下步骤进行:
1)、将40%的弹性乳液、1%的消泡剂、0.1%的分散剂、0.2%的丙二醇和36.1%的水投入分散机中;
2)、再将20%的碳酸钙、0.1%的纤维素、3%的硅灰石粉、0.1%的防腐剂投入至分散机中;
3)、最后加入0.3%的增稠剂得到成品。