CN102444252A - Composite hexahedral aluminium-wood decorative plate and process thereof - Google Patents
Composite hexahedral aluminium-wood decorative plate and process thereof Download PDFInfo
- Publication number
- CN102444252A CN102444252A CN2011102503196A CN201110250319A CN102444252A CN 102444252 A CN102444252 A CN 102444252A CN 2011102503196 A CN2011102503196 A CN 2011102503196A CN 201110250319 A CN201110250319 A CN 201110250319A CN 102444252 A CN102444252 A CN 102444252A
- Authority
- CN
- China
- Prior art keywords
- substrate
- aluminium
- aluminium foil
- wood composite
- composite decorating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite hexahedral aluminium-wood decorative plate, which comprises a substrate. The six surfaces of the substrate are provided with aluminium foil layers. A polymeric film is arranged between the substrate and the aluminium foil layer. The substrate and the aluminium foil layer are stuck together through the polymeric film. In the event of constructing, the front of the composite aluminium-wood decorative plate is outward; a fire source, a water source or mould and the like are prevented from being contacted with the substrate by utilizing the characteristics of the aluminium foil layers and the isolation action; thus, the purposes of preventing fire, water and mould are achieved; furthermore, harmful gases, such as free formaldehyde and the like in the substrate, are also prevented from being released indoors; the substrate is completely wrapped through the aluminium foil layers; harmful gases, such as free formaldehyde and the like in the substrate, are prevented from being released; simultaneously, the composite hexahedral aluminium-wood decorative plate can effectively resist fire, water and mould; furthermore, the composite hexahedral aluminium-wood decorative plate disclosed by the invention also has the advantages of being firm for sticking the aluminium foil layers to the substrate, abundant in substrate material selection, low in cost, good in decorative effect and the like.
Description
Technical field
The present invention relates to a kind of aluminium wood composite decorating board, particularly a kind of six aluminium wood composite decorating board and processing technology thereof.
Background technology
Along with human development of science and technology, the progress of society, people's material and culture level is improving constantly, and luxurious dwelling environment becomes the target that people constantly pursue, and decoration industry is developed as the industry of modern civilization rapidly thereupon.Yet in the decoration industry development, human also being faced with fitted up the variety of issue that brings, as: the scarcity day by day of disaster hidden-trouble, environment pollution, famous and precious timber, rock material resource etc.Developing a kind of novel fire prevention, environmental protection, substitute the finishing material of famous and precious timber, stone material, can satisfy people's finishing requirement, economize on resources, make things convenient for decoration construction again simultaneously, is the cardinal task of pendulum in face of ours.
Aluminium foil surface has good transfer printing property, can stamp various natural famous and precious wood grains, bag etc.Existing aluminium wood complex technique is just simply at the one or both sides applying aluminium foil or the aluminium skin of substrate, and such simple composite though played decoration function, has but been brought various worries to the user:
Fire hazardous, because substrate layer has only two faces to be provided with aluminium foil, the side of substrate layer all is exposed in the air, is easy to cause fire.
The moisture-sensitive distortion, because the substrate layer multiselect is used timber, in long-term the use, the side of substrate layer can absorb airborne moisture and deform, and has a strong impact on attractive in appearance.
Influence healthyly, existing aluminium-wood composite board adopts glue that aluminium sheet and substrate layer are bonded together more, and free pernicious gases such as formaldehyde can be discharged in the air in long-term the use, influence people's health.
Can't form the piece of nature,, therefore in engineering construction, during close assembly, can not form the piece of nature, influence decorative effect because the side of conventional aluminum wood composite board does not have the aluminium foil decorative layer.
Summary of the invention
The objective of the invention is to; A kind of six aluminium wood composite decorating board and processing technology thereof are provided; It not only can adopt hot transfer technique to substitute natural wood grain, bag plate, has same decoration function, also has the advantage of fire prevention, protection against the tide, anti-deformation, antistatic, anti-pernicious gas release.
Technical scheme of the present invention: a kind of six aluminium wood composite decorating board, comprise substrate, be equipped with aluminium foil layer on six faces of substrate, be provided with polymeric membrane between substrate and the aluminium foil layer, substrate and aluminium foil layer bond together through polymeric membrane.Polymeric membrane is set between substrate and aluminium foil layer can makes aluminium foil layer and firm the bonding together of substrate, can effectively prevent the long-time phenomenon of using back aluminium foil generation bulge.
In aforesaid six aluminium wood composite decorating board, the thickness of said substrate is 3mm～35mm.
In aforesaid six aluminium wood composite decorating board, said substrate adopts fire-retardant high density fiberboard, burning-resistant medium density fibreboard, solid wood plate, silicate and plank composite plate, pure silicon hydrochlorate plate, plastic plate, aluminum honeycomb panel or aluminum veneer.Therefore the characteristic that these materials all have difficult combustion or do not fire adopts these materials to do the flameproof effect that substrate can increase product.
In aforesaid six aluminium wood composite decorating board, the thickness of aluminium foil layer is 0.07mm～0.35mm.
In aforesaid six aluminium wood composite decorating board, the aluminium foil layer of four sides of substrate and the aluminium foil layer of substrate front side are for being wholely set.The purpose that employing is wholely set is when plate and plate splicing, can form the nature piece by nature for flanging is seemed, solves the factitious shortcoming of conventional aluminum wood composite board piece.
A kind of processing technology of aforementioned six aluminium wood composite decorating board may further comprise the steps:
Step 1, cutting back of the body aluminium: with crop tool aluminium foil is carried out cutting, make the size of aluminium foil identical with the bottom surface size of substrate;
Step 4, hot transfer printing: will cut out good heat transfer film and overlay on the face aluminium, and be placed on together and carry out hot transfer printing on the hot press, and make face aluminium surface form required pattern, the pressure of hot press is 40kgf/m
2～60kgf/m
2, temperature is 160 ℃～190 ℃, hot pressing time is 10s～30s;
Step 5 is cut out polymeric membrane: cut out the polymeric membrane measure-alike with substrate surface with crop tool;
Step 6, the overlaying of the back side: earlier substrate surface is cleaned out, will cut out then get well, clean polymeric membrane covers on the substrate; Polymeric membrane is alignd with substrate; To carry on the back aluminium then and cover on the polymeric membrane, and be put on the hot press together with substrate and overlay, controlled pressure is 40kgf/m
2～60kgf/m
2, temperature is 120 ℃～150 ℃, hot pressing time is 80s～100s;
Step 7, positive overlays: will post one of back of the body aluminium and face down, and polymeric membrane overlayed on the substrate again; And the face aluminium that transfer printing is good overlays on the polymeric membrane; The length that makes each limit of face aluminium stretch out substrate is equal to the thickness of substrate, is placed on the hot press then to overlay, and controlled pressure is 40kgf/m
2～60kgf/m
2, 120 ℃～140 ℃ of temperature, hot pressing time 80s～100s;
Step 8, edge sealing: the decorative panel that will post face aluminium is put into and carries out edge sealing on the edge banding machine, and temperature is 70 ℃～100 ℃, time 15s～50s; Two long sides of envelope seal two short sides more earlier;
Step 9, pasting protective film: the decorative panel that will overlay aluminium foil layer places on the laminator, with the press mold machine diaphragm is overlayed the front at decorative panel.
In the processing technology of aforesaid six aluminium wood composite decorating board, in the said step 4, the pressure of hot press is 50kgf/m
2, temperature is 180 ℃, hot pressing time is 15s.
In the processing technology of aforesaid six aluminium wood composite decorating board, in said step 6 and the step 7, the pressure of hot press is 50kgf/m
2, temperature is 130 ℃, hot pressing time is 90s.
In the processing technology of aforesaid six aluminium wood composite decorating board, in the said step 8, the temperature of edge banding machine is 80 ℃, and the edge sealing time is 40s.
In the processing technology of aforesaid six aluminium wood composite decorating board; After the process that overlays at the described back side of step 6 finishes and the said edge sealing end of step 8 back is carried out deburring to six aluminium wood composite decorating boards and is handled; That is: the aluminium foil that will extend beyond the substrate is pruned, and the aluminium foil edge is alignd with substrate edges; Finishing the back at the said pad pasting of step 9 packs six aluminium wood composite decorating boards; That is: use the international standard pallet to make collet; On collet, fill up the transfer film that one deck was used before the packing earlier, and then six aluminium wood composite decorating boards are piled up neatly according to one positive one anti-order, decorative panel pile height is controlled at 1～1.2 meter; Press a veneer at uppermost aluminium wood composite decorating board loam cake then, pack with iron strap and special-purpose packing pincers.
Compared with prior art, the present invention wraps up substrate through using aluminium foil fully, makes substrate and air isolated, has played effective fire prevention, waterproof effect, because airborne moisture can't enter in the substrate, substrate in use is difficult for deforming.Because substrate is wrapped up by aluminium foil fully, pernicious gases such as formaldehyde free in the substrate are difficult for being discharged in the air, help health, environmental protection., play same decoration function because but therefore the various patterns of surface transfer printing, the pattern of aluminium sheet can replace famous and precious timber.Because six faces of composite decorating board of the present invention are equipped with aluminium foil layer, therefore efficiently solve the problem that the conventional aluminum wood composite board can't form the nature piece.
Description of drawings
Fig. 1 is a cross-sectional view of the present invention.
Being labeled as in the accompanying drawing: 1-substrate, 2-aluminium foil layer, 3-polymeric membrane.
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is further described.
Embodiments of the invention 1: as shown in Figure 1; A kind of six aluminium wood composite decorating board comprises substrate 1, is equipped with aluminium foil layer 2 on six faces of substrate 1; Be provided with polymeric membrane 3 between substrate 1 and the aluminium foil layer 2, substrate 1 bonds together through polymeric membrane 3 with aluminium foil layer 2.The thickness of substrate 1 is 18mm.Substrate 1 adopts fire-retardant high density fiberboard.The thickness of aluminium foil layer 2 is 0.2mm.The aluminium foil layer 2 in the aluminium foil layer 2 of 1 four sides of substrate and substrate 1 front is for being wholely set.
A kind of processing technology of aforementioned six aluminium wood composite decorating board may further comprise the steps:
Step 1, cutting back of the body aluminium: with crop tool aluminium foil is carried out cutting, make the size of aluminium foil identical with the bottom surface size of substrate;
Step 4, hot transfer printing: will cut out good heat transfer film and overlay on the face aluminium, and be placed on together and carry out hot transfer printing on the hot press, and make face aluminium surface form required pattern, the pressure of hot press is 50kgf/m
2, temperature is 180 ℃, hot pressing time is 15s;
Step 5 is cut out polymeric membrane: cut out the polymeric membrane measure-alike with substrate surface with crop tool;
Step 6, the overlaying of the back side: earlier substrate surface is cleaned out, will cut out then get well, clean polymeric membrane covers on the substrate; Polymeric membrane is alignd with substrate; To carry on the back aluminium then and cover on the polymeric membrane, and be put on the hot press together with substrate and overlay, controlled pressure is 50kgf/m
2, temperature is 130 ℃, hot pressing time is 90s;
Step 7, positive overlays: will post one of back of the body aluminium and face down, and polymeric membrane overlayed on the substrate again; And the face aluminium that transfer printing is good overlays on the polymeric membrane; The length that makes each limit of face aluminium stretch out substrate is equal to the thickness of substrate, is placed on the hot press then to overlay, and controlled pressure is 50kgf/m
2, 130 ℃ of temperature, hot pressing time 90s;
Step 8, edge sealing: the decorative panel that will post face aluminium is put into and carries out edge sealing on the edge banding machine, and temperature is 80 ℃, time 40s; Two long sides of envelope seal two short sides more earlier;
Step 9, pasting protective film: the decorative panel that will overlay aluminium foil layer places on the laminator, with the press mold machine diaphragm is overlayed the front at decorative panel.
Overlay at the described back side of step 6 and after process end back and the said edge sealing of step 8 finish the wooden composite decorating boards of six aluminium are carried out the deburring processing, that is: the aluminium foil that will extend beyond the substrate is pruned, and the aluminium foil edge is alignd with substrate edges; Finishing the back at the said pad pasting of step 9 packs six aluminium wood composite decorating boards; That is: use the international standard pallet to make collet; On collet, fill up the transfer film that one deck was used before the packing earlier, and then six aluminium wood composite decorating boards are piled up neatly according to one positive one anti-order, decorative panel pile height is controlled at 1.1 meters; Press a veneer at uppermost aluminium wood composite decorating board loam cake then, pack with iron strap and special-purpose packing pincers.
Embodiments of the invention 2: as shown in Figure 1; A kind of six aluminium wood composite decorating board comprises substrate 1, is equipped with aluminium foil layer 2 on six faces of substrate 1; Be provided with polymeric membrane 3 between substrate 1 and the aluminium foil layer 2, substrate 1 bonds together through polymeric membrane 3 with aluminium foil layer 2.The thickness of substrate 1 is 3mm.Substrate 1 adopts burning-resistant medium density fibreboard.The thickness of aluminium foil layer 2 is 0.07mm.The aluminium foil layer 2 in the aluminium foil layer 2 of 1 four sides of substrate and substrate 1 front is for being wholely set.
A kind of processing technology of aforementioned six aluminium wood composite decorating board may further comprise the steps:
Step 1, cutting back of the body aluminium: with crop tool aluminium foil is carried out cutting, make the size of aluminium foil identical with the bottom surface size of substrate;
Step 4, hot transfer printing: will cut out good heat transfer film and overlay on the face aluminium, and be placed on together and carry out hot transfer printing on the hot press, and make face aluminium surface form required pattern, the pressure of hot press is 40kgf/m
2, temperature is 160 ℃, hot pressing time is 10s;
Step 5 is cut out polymeric membrane: cut out the polymeric membrane measure-alike with substrate surface with crop tool;
Step 6, the overlaying of the back side: earlier substrate surface is cleaned out, will cut out then get well, clean polymeric membrane covers on the substrate; Polymeric membrane is alignd with substrate; To carry on the back aluminium then and cover on the polymeric membrane, and be put on the hot press together with substrate and overlay, controlled pressure is 40kgf/m
2, temperature is 120 ℃, hot pressing time is 80s;
Step 7, positive overlays: will post one of back of the body aluminium and face down, and polymeric membrane overlayed on the substrate again; And the face aluminium that transfer printing is good overlays on the polymeric membrane; The length that makes each limit of face aluminium stretch out substrate is equal to the thickness of substrate, is placed on the hot press then to overlay, and controlled pressure is 40kgf/m
2, 120 ℃ of temperature, hot pressing time 80s;
Step 8, edge sealing: the decorative panel that will post face aluminium is put into and carries out edge sealing on the edge banding machine, and temperature is 70 ℃, time 15s; Two long sides of envelope seal two short sides more earlier;
Step 9, pasting protective film: the decorative panel that will overlay aluminium foil layer places on the laminator, with the press mold machine diaphragm is overlayed the front at decorative panel.
Overlay at the described back side of step 6 and after process end back and the said edge sealing of step 8 finish the wooden composite decorating boards of six aluminium are carried out the deburring processing, that is: the aluminium foil that will extend beyond the substrate is pruned, and the aluminium foil edge is alignd with substrate edges; Finishing the back at the said pad pasting of step 9 packs six aluminium wood composite decorating boards; That is: use the international standard pallet to make collet; On collet, fill up the transfer film that one deck was used before the packing earlier, and then six aluminium wood composite decorating boards are piled up neatly according to one positive one anti-order, decorative panel pile height is controlled at 1 meter; Press a veneer at uppermost aluminium wood composite decorating board loam cake then, pack with iron strap and special-purpose packing pincers.
Embodiments of the invention 3: as shown in Figure 1; A kind of six aluminium wood composite decorating board comprises substrate 1, is equipped with aluminium foil layer 2 on six faces of substrate 1; Be provided with polymeric membrane 3 between substrate 1 and the aluminium foil layer 2, substrate 1 bonds together through polymeric membrane 3 with aluminium foil layer 2.The thickness of said substrate 1 is 35mm.Said substrate 1 adopts the solid wood plate.The thickness of aluminium foil layer 2 is 0.35mm.The aluminium foil layer 2 in the aluminium foil layer 2 of 1 four sides of substrate and substrate 1 front is for being wholely set.
A kind of processing technology of aforementioned six aluminium wood composite decorating board may further comprise the steps:
Step 1, cutting back of the body aluminium: with crop tool aluminium foil is carried out cutting, make the size of aluminium foil identical with the bottom surface size of substrate;
Step 4, hot transfer printing: will cut out good heat transfer film and overlay on the face aluminium, and be placed on together and carry out hot transfer printing on the hot press, and make face aluminium surface form required pattern, the pressure of hot press is 60kgf/m
2, temperature is 190 ℃, hot pressing time is 30s;
Step 5 is cut out polymeric membrane: cut out the polymeric membrane measure-alike with substrate surface with crop tool;
Step 6, the overlaying of the back side: earlier substrate surface is cleaned out, will cut out then get well, clean polymeric membrane covers on the substrate; Polymeric membrane is alignd with substrate; To carry on the back aluminium then and cover on the polymeric membrane, and be put on the hot press together with substrate and overlay, controlled pressure is 60kgf/m
2, temperature is 150 ℃, hot pressing time is 100s;
Step 7, positive overlays: will post one of back of the body aluminium and face down, and polymeric membrane overlayed on the substrate again; And the face aluminium that transfer printing is good overlays on the polymeric membrane; The length that makes each limit of face aluminium stretch out substrate is equal to the thickness of substrate, is placed on the hot press then to overlay, and controlled pressure is 60kgf/m
2, 140 ℃ of temperature, hot pressing time 100s;
Step 8, edge sealing: the decorative panel that will post face aluminium is put into and carries out edge sealing on the edge banding machine, and temperature is 100 ℃, time 50s; Two long sides of envelope seal two short sides more earlier;
Step 9, pasting protective film: the decorative panel that will overlay aluminium foil layer places on the laminator, with the press mold machine diaphragm is overlayed the front at decorative panel.
Overlay at the described back side of step 6 and after process end back and the said edge sealing of step 8 finish the wooden composite decorating boards of six aluminium are carried out the deburring processing, that is: the aluminium foil that will extend beyond the substrate is pruned, and the aluminium foil edge is alignd with substrate edges; Finishing the back at the said pad pasting of step 9 packs six aluminium wood composite decorating boards; That is: use the international standard pallet to make collet; On collet, fill up the transfer film that one deck was used before the packing earlier, and then six aluminium wood composite decorating boards are piled up neatly according to one positive one anti-order, decorative panel pile height is controlled at 1～1.2 meter; Press a veneer at uppermost aluminium wood composite decorating board loam cake then, pack with iron strap and special-purpose packing pincers.
In addition, substrate 1 can also be silicate and plank composite plate, pure silicon hydrochlorate plate, plastic plate, any one in aluminum honeycomb panel or the aluminum veneer among each embodiment.
Method for using: during construction; With the front of aluminium wood composite decorating board outwardly; Utilize aluminium foil layer 2 self characteristics and buffer action to avoid contact substrates 1 such as burning things which may cause a fire disaster, water source or mould; Thereby reach fire prevention, waterproof and mildew-resistant purpose, the pernicious gases of also having stopped in addition in the substrate 1 such as free formaldehyde are discharged into indoor situation.
Claims (10)
1. six aluminium wood composite decorating board; Comprise substrate (1); It is characterized in that: be equipped with aluminium foil layer (2) on six faces of substrate (1), be provided with polymeric membrane (3) between substrate (1) and the aluminium foil layer (2), substrate (1) bonds together through polymeric membrane (3) with aluminium foil layer (2).
2. a kind of six aluminium wood composite decorating board according to claim 1, it is characterized in that: the thickness of said substrate (1) is 3mm～35mm.
3. a kind of six aluminium wood composite decorating board according to claim 2, it is characterized in that: said substrate (1) adopts fire-retardant high density fiberboard, burning-resistant medium density fibreboard, solid wood plate, silicate and plank composite plate, pure silicon hydrochlorate plate, plastic plate, aluminum honeycomb panel or aluminum veneer.
4. a kind of six aluminium wood composite decorating board according to claim 3, it is characterized in that: the thickness of aluminium foil layer (2) is 0.07mm～0.35mm.
5. a kind of six aluminium wood composite decorating board according to claim 4, it is characterized in that: the aluminium foil layer (2) in the aluminium foil layer (2) of (1) four side of substrate and substrate (1) front is for being wholely set.
6. the processing technology of any one said six aluminium wood of a claim 1～5 composite decorating board is characterized in that, may further comprise the steps:
Step 1, cutting back of the body aluminium: with crop tool aluminium foil is carried out cutting, make the size of aluminium foil identical with the bottom surface size of substrate;
Step 2, cutting face aluminium: with crop tool aluminium foil is carried out cutting, thickness * 2 of the end face length+substrate of the length=substrate of aluminium foil, thickness * 2 of the end face width+substrate of the width=substrate of aluminium foil;
Step 3 is cut out transfer film: choose a kind of heat transfer film that has pattern, it is carried out cutting, make the size of heat transfer film identical with face aluminium size;
Step 4, hot transfer printing: will cut out good heat transfer film and overlay on the face aluminium, and be placed on together and carry out hot transfer printing on the hot press, and make face aluminium surface form required pattern, the pressure of hot press is 40kgf/m
2～60kgf/m
2, temperature is 160 ℃～190 ℃, hot pressing time is 10s～30s;
Step 5 is cut out polymeric membrane: cut out the polymeric membrane measure-alike with substrate surface with crop tool;
Step 6, the overlaying of the back side: earlier substrate surface is cleaned out, will cut out then get well, clean polymeric membrane covers on the substrate; Polymeric membrane is alignd with substrate; To carry on the back aluminium then and cover on the polymeric membrane, and be put on the hot press together with substrate and overlay, controlled pressure is 40kgf/m
2～60kgf/m
2, temperature is 120 ℃～150 ℃, hot pressing time is 80s～100s;
Step 7, positive overlays: will post one of back of the body aluminium and face down, and polymeric membrane overlayed on the substrate again; And the face aluminium that transfer printing is good overlays on the polymeric membrane; The length that makes each limit of face aluminium stretch out substrate is equal to the thickness of substrate, is placed on the hot press then to overlay, and controlled pressure is 40kgf/m
2～60kgf/m
2, 120 ℃～140 ℃ of temperature, hot pressing time 80s～100s;
Step 8, edge sealing: the decorative panel that will post face aluminium is put into and carries out edge sealing on the edge banding machine, and temperature is 70 ℃～100 ℃, time 15s～50s; Two long sides of envelope seal two short sides more earlier;
Step 9, pasting protective film: the decorative panel that will overlay aluminium foil layer places on the laminator, with the press mold machine diaphragm is overlayed the front at decorative panel.
7. the processing technology of six aluminium wood composite decorating board according to claim 6, it is characterized in that: in the said step 4, the pressure of hot press is 50kgf/m
2, temperature is 180 ℃, hot pressing time is 15s.
8. the processing technology of six aluminium wood composite decorating board according to claim 6, it is characterized in that: in said step 6 and the step 7, the pressure of hot press is 50kgf/m
2, temperature is 130 ℃, hot pressing time is 90s.
9. the processing technology of six aluminium wood composite decorating board according to claim 6, it is characterized in that: in the said step 8, the temperature of edge banding machine is 80 ℃, and the edge sealing time is 40s.
10. the processing technology of six aluminium wood composite decorating board according to claim 6; It is characterized in that: after the process that overlays at the described back side of step 6 finishes and the said edge sealing end of step 8 back is carried out deburring to six aluminium wood composite decorating boards and is handled; That is: the aluminium foil that will extend beyond the substrate is pruned, and the aluminium foil edge is alignd with substrate edges; Finishing the back at the said pad pasting of step 9 packs six aluminium wood composite decorating boards; That is: use the international standard pallet to make collet; On collet, fill up the transfer film that one deck was used before the packing earlier, and then six aluminium wood composite decorating boards are piled up neatly according to one positive one anti-order, decorative panel pile height is controlled at 1～1.2 meter; Press a veneer at uppermost aluminium wood composite decorating board loam cake then, pack with iron strap and special-purpose packing pincers.