CN102433742A - Method for processing anti-static flame retardant liquid chemical-proof acrylic cotton fabric - Google Patents
Method for processing anti-static flame retardant liquid chemical-proof acrylic cotton fabric Download PDFInfo
- Publication number
- CN102433742A CN102433742A CN2011103081276A CN201110308127A CN102433742A CN 102433742 A CN102433742 A CN 102433742A CN 2011103081276 A CN2011103081276 A CN 2011103081276A CN 201110308127 A CN201110308127 A CN 201110308127A CN 102433742 A CN102433742 A CN 102433742A
- Authority
- CN
- China
- Prior art keywords
- liquid chemical
- vinyon
- percentage
- flame retardant
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for processing an anti-static flame retardant liquid chemical-proof acrylic cotton fabric, comprising the steps of greige cloth waving, pretreatment dyeing, flame retardant treatment, ecological treatment and finished product inspection, wherein Teflon finishing is further performed after the flame retardant and ecological treatment; the greige cloth is woven from the blended yarns of modacrylic fibersand cotton fibers; and conductive carbon fibers are arranged in the warp direction and the weft direction at intervals of 3-9 mm. The anti-static flame retardant liquid chemical-proof acrylic cotton property of the anti-static flame retardant liquid chemical-proof acrylic cotton fabric provided in the invention reaches EN368, while the anti-static property thereof reaches EN1149; and simultaneously, the fabric has dressing properties such as softness, comfort, abrasive resistance and the like.
Description
Technical field
The present invention relates to the processing method of the anti-liquid chemical nitrile COTTON FABRIC of a kind of anti-static inflaming-retarding.
Background technology
At present both at home and abroad seldom about the product of the anti-liquid chemical nitrile COTTON FABRIC aspect of anti-static inflaming-retarding; The anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding has characteristics such as powerful height, good hand touch, free from extraneous odour, good flame resistance than the cotton flame-retardant textile, have better effect for protecting human body.A lot of now national collieries, petrochemical industry, enterprises such as smelting all begin the protective clothing that the anti-liquid chemical nitrile COTTON FABRIC of requirement assembling anti-static inflaming-retarding is made.The requirements of making of the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding is very high, requires can reach EN368 and EN1149 standard simultaneously.
Summary of the invention
The object of the present invention is to provide a kind of rational in infrastructure, the processing method of antistatic, the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding that anti-fire-retardant performance is good.
Technical solution of the present invention is:
The processing method of the anti-liquid chemical nitrile COTTON FABRIC of a kind of anti-static inflaming-retarding comprises that grey cloth is weaved, pre-treatment dyeing, flame treatment, ecological arrangement, finished product inspection step, it is characterized in that: after fire-retardant ecological arrangement, also carry out the teflon arrangement; Said grey cloth is weaved by the blended yarn of Vinyon N and cotton fiber and is formed, and is being provided with conductive carbon fibre through the every interval 3～9mm of broadwise, and the percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 50～55%
Cotton fiber 42～47%
Conductive carbon fibre 1～3%;
The treatment fluid of flame treatment is made up of following component in percentage by weight:
The dressing liquid of ecological arrangement is made up of following component in percentage by weight:
Sulphite 2～4%
Formaldehyde catching agent (dimethyl-1,3-acetone-dihydroxy hydrochlorate) 3～12%
The deionized water surplus;
The dressing liquid of teflon arrangement is made up of following component in percentage by weight:
Said Vinyon N is the modification Vinyon N.
The grammes per square metre of fabric is 180～300g/m
2
Characteristics of the present invention are: the anti-liquid chemical nitrile COTTON FABRIC of (1) anti-static inflaming-retarding has adopted modification Vinyon N and cotton fiber blending; Add a spot of conductive carbon fibre by a certain percentage; Through the teflon arrangement, prevent multiple functions such as liquid chemical nitrile cotton again thereby make lining have the fire-resistant antistatic anti-static inflaming-retarding simultaneously.
(2) adopt vinyl phosphate and O, O dimethyl-N-methylol third rare amide groups phosphate carries out flame-proof treatment processing to the cotton fiber of lining, has improved the fire resistance of lining.
(3) the Vinyon N ratio of the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding is about 50～60%, and conductive carbon fibre occupies ratio 1%～3%, and cotton ratio is about 40～50%, and fabric weight is at 180～300g/m
2Between do not wait.
(4) square inweaves the organic conductive carbon fiber between the anti-liquid chemical nitrile COTTON FABRIC employing of anti-static inflaming-retarding etc., inweaves method through gridding, is evenly distributed among the lining, has excellent conducting performance, conductive filament spacing (3～9mm, latticed).
Each item technical performance index table 1 of product
Can see that from table 1 the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding has multiple functions such as fire-retardant, antistatic; Performances such as the COLOR FASTNESS of fabric, brute force, feel are all fine simultaneously; Each item data target has all reached the relevant standard index of home or overseas; Each item performance indications of product reach EN11612 through the fire resistance that SGS detects the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding, and antistatic performance reaches the requirement of EN1149.Compare some domestic functional fabrics and have tangible technical advantage, this product is to belong to the higher flame retardant products of class, is applicable to the application of petrochemical industry; With respect to external similar products; Not only quality is secure, and price is also relatively cheap, so market potential is very big.
Below in conjunction with embodiment the present invention is described further.
The specific embodiment
Embodiment 1:
The processing method of the anti-liquid chemical nitrile COTTON FABRIC of a kind of anti-static inflaming-retarding comprises that grey cloth is weaved, pre-treatment dyeing, flame treatment, ecological arrangement, finished product inspection step, after fire-retardant ecological arrangement, also carries out the teflon arrangement; Said grey cloth is weaved by the blended yarn of Vinyon N and cotton fiber and is formed, and is being provided with conductive carbon fibre through the every interval 3～9mm of broadwise (routine 3mm, 6mm, 9mm), and the percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 50%
Cotton fiber 47%
Conductive carbon fibre 3%;
The treatment fluid of flame treatment is made up of following component in percentage by weight:
The dressing liquid of ecological arrangement is made up of following component in percentage by weight:
Sulphite 2%
Formaldehyde catching agent (dimethyl-1,3-acetone-dihydroxy hydrochlorate) 12%
The deionized water surplus;
The dressing liquid of teflon arrangement is made up of following component in percentage by weight:
The grammes per square metre of fabric is 180～300g/m
2(routine 180g/m
2, 250g/m
2, 300g/m
2)
Embodiment 2:
The percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 52%
Cotton fiber 46%
Conductive carbon fibre 2%;
The treatment fluid of flame treatment is made up of following component in percentage by weight:
The dressing liquid of ecological arrangement is made up of following component in percentage by weight:
Sulphite 3%
Formaldehyde catching agent (dimethyl-1,3-acetone-dihydroxy hydrochlorate) 7%
The deionized water surplus;
The dressing liquid of teflon arrangement is made up of following component in percentage by weight:
All the other are with embodiment 1.
Embodiment 3:
The percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 55%
Cotton fiber 44%
Conductive carbon fibre 1%;
The treatment fluid of flame treatment is made up of following component in percentage by weight:
The dressing liquid of ecological arrangement is made up of following component in percentage by weight:
Sulphite 4%
Formaldehyde catching agent (dimethyl-1,3-acetone-dihydroxy hydrochlorate) 3%
The deionized water surplus;
The dressing liquid of teflon arrangement is made up of following component in percentage by weight:
All the other are with embodiment 1.
Embodiment 4:
The percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 55%
Cotton fiber 42%
Conductive carbon fibre 3%;
All the other are with embodiment 1.
Certainly, the present invention can also have other suitable embodiment, and the Vinyon N in the routine grey cloth raw material of the present invention can adopt the modification Vinyon N.
Claims (3)
1. the processing method of the anti-liquid chemical nitrile COTTON FABRIC of an anti-static inflaming-retarding comprises that grey cloth is weaved, pre-treatment dyeing, flame treatment, ecological arrangement, finished product inspection step, it is characterized in that: after fire-retardant ecological arrangement, also carry out the teflon arrangement; Said grey cloth is weaved by the blended yarn of Vinyon N and cotton fiber and is formed, and is being provided with conductive carbon fibre through the every interval 3 ~ 9mm of broadwise, and the percentage by weight of Vinyon N, cotton fiber, conductive carbon fibre is in the grey cloth:
Vinyon N 50 ~ 55%
Cotton fiber 42 ~ 47%
Conductive carbon fibre 1 ~ 3%;
The treatment fluid of flame treatment is made up of following component in percentage by weight:
O, O dimethyl-N-methylol third rare amide groups phosphate 10 ~ 25%
High etherificate hexamethylol melamine resin 4 ~ 10%
Polyvinyl resin 1 ~ 5%
Phosphatase 11 ~ 4%
Penetrating agent JFC 1%
The deionized water surplus;
The dressing liquid of ecological arrangement is made up of following component in percentage by weight:
Sulphite 2 ~ 4%
Formaldehyde catching agent (dimethyl-1,3-acetone-dihydroxy hydrochlorate) 3 ~ 12%
The deionized water surplus;
The dressing liquid of teflon arrangement is made up of following component in percentage by weight:
Teflon 7 ~ 10%
Six D resins 2 ~ 4%
Ester acid zinc 1 ~ 2%
The deionized water surplus.
2. the processing method of the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding according to claim 1, it is characterized in that: said acrylic fibers are Vinyon N.
3. the processing method of the anti-liquid chemical nitrile COTTON FABRIC of anti-static inflaming-retarding according to claim 1 and 2, it is characterized in that: the grammes per square metre of fabric is 180 ~ 300g/m
2