CN102424892A - 一种洁净钢生产用纯钙丝制备方法 - Google Patents
一种洁净钢生产用纯钙丝制备方法 Download PDFInfo
- Publication number
- CN102424892A CN102424892A CN2011103833969A CN201110383396A CN102424892A CN 102424892 A CN102424892 A CN 102424892A CN 2011103833969 A CN2011103833969 A CN 2011103833969A CN 201110383396 A CN201110383396 A CN 201110383396A CN 102424892 A CN102424892 A CN 102424892A
- Authority
- CN
- China
- Prior art keywords
- calcium
- steel
- molten steel
- preparation
- filaments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种洁净钢生产用纯钙丝制备方法,所述方法为:将钙锭加热后经挤压机挤压成钙丝,再经包裹机用钢带将钙丝包裹成型,经缠盘机包装成钙丝线。用本发明制备方法生产的纯钙丝能加入到钢包的临界点(一般在钢包的2/3处)以下,钙与钢液的接触时间长,并且稳定,增加了钙丝与钢水的反应时间,钙收得率达到35%以上。而且减少氩气用量,避免了钢液的喷溅现象。
Description
技术领域
本发明涉及一种洁净钢生产用纯钙丝制备方法。
背景技术
钙处理是上个世纪20世纪70年代发展起来的一种钢水精炼手段。其主要目的包括:1、深度降低钢中O、S等有害元素含量;2、改变夹杂物组成形态,避免浇铸中发生水口堵塞并改善钢材力学性能。
历史上,钙处理曾经有向钢包内直接加入钙合金、向钢液内喷吹钙合金等方法,但由于处理效果不稳定或成本过高等原因已渐被淘汰。
现在钙处理方法应用的是钢包喂钙线方法。它是将钙合金(Ca、Ca-Si、Ca-Fe等)用钢皮包裹制成包芯线,通过喂丝机的导引管将其以很高的速度插入钢液。喂丝过程中同时伴随惰性气体搅拌,以增加Ca蒸汽泡在钢液中的停留时间和良好的混合。这种方法在全世界的钢铁企业中得到了广泛应用并取得了极大成功。
上述几种包芯线已经能够满足大部分钢种精炼的技术要求,但相对来讲还存在好多问题,钢水中会增加S、P、C、Si等杂质,影响洁净钢的纯度,同时由于以上几种包芯线在使用过程中经常出现反应剧烈、钢液飞溅现象,钙的收得率较低仅有12%左右,大量的钙都无谓地浪费了。
发明内容
本发明需要解决的技术问题就在于克服现有包芯线存在的不足、使钢水钙处理稳定,提供一种洁净钢生产用纯钙丝制备方法,用本发明制备方法生产的纯钙丝能加入到钢包的临界点(一般在钢包的2/3处)以下,钙与钢液的接触时间长,并且稳定,增加了钙丝与钢水的反应时间,钙收得率达到35%以上。而且减少氩气用量,避免了钢液的喷溅现象。
为解决上述问题,本发明采用如下技术方案:
本发明提供了一种洁净钢生产用纯钙丝制备方法,所述方法为:将钙锭加热后经挤压机挤压成钙丝,再经包裹机用钢带将钙丝包裹成型,经缠盘机包装成钙丝线。
本发明制备的钙丝,是由外皮包裹钙丝组成,钙丝杂质总和不高于0.15wt%;所述的外皮为A3钢。所述的钙丝直径为7.0±5mm。
本发明所述的钙丝的制备方法优点为:
1.钙丝是外皮钢壳、芯部为钙丝的结构,其穿透能力极强,使得钙丝能够加入到钢水的临界点(钢包2/3处)以下,在钢液中钙丝与钢水中氧、硫等反应,达到脱出氧、硫和其它夹杂物等,提高钢水的纯净度,同时提高了钙收得率;
2、钙丝的生产过程的关键部位采用惰性气体处理,防止与空气中的氧接触发生钙的氧化反应;
因而,本发明制备的钙丝的优势有:
1、快速脱氧、脱硫。
2、减少钢水中夹杂物含量。
3、提高钢水纯净度。
4、提高钢水流动性,提高钢坯连铸效率。
具体实施方式
本发明提供了一种洁净钢生产用纯钙丝制备方法,所述方法为:将钙锭加热后经挤压机挤压成钙丝,再经包裹机用钢带将钙丝包裹成型,经缠盘机包装成钙丝线。
本实施例制备的钙丝线的规格参数如下:
1.线直径:9.6mm。
2.包芯线成分(质量%):钢壳78;钙丝22。
3.每米重量(克/米):钢壳310;实芯钙58。
4.实芯钙的化学成份(%)
Ca | Fe Ni Cu Mg Al Si |
≥ | ≤ |
98.5 | 0.015 0.004 0.0025 0.65 0.6 0.012 |
喂入方式:在LF炉处理末期喂入,在钢种:10MnCrMoV、65Mn等精炼中,喂线后Ca的收得率稳定,平均收得率为38%,平均脱硫率30%,最高脱硫率36%,最低硫含量0.004%,平均脱氧率25%,最低氧含量0.0007%,喂线后钢水浇注正常,铸坯质量良好,表明此钙丝还可以促进夹杂物变性,净化钢水和改善钢水浇注性能,并且可以消除中包水口结瘤现象。
本发明是一种洁净钢(超低氧、硫、夹杂物)生产用纯钙丝,它能够使钢水钙处理稳定。它能加入到钢包的临界点(一般在钢包的2/3处)以下,增加钙丝与钢水的反应时间,减少氩气用量,避免了钢液的喷溅现象。钙与钢液的接触时间长,并且稳定,钙收得率达到35%以上。
本发明的钙丝,是由外皮包裹钙丝组成,钙丝杂质总和不高于0.15wt%;所述的外皮为A3钢。所述的钙丝直径为7.0±5mm。
本发明所述的钙丝的优点有:
1.钙丝是外皮为钢壳、芯部为钙丝的结构,穿透能力极强,使得钙丝能够加入到钢水的临界点(钢包2/3处)以下,在钢液中钙丝与钢水中氧、硫等反应,达到脱出氧、硫和其它夹杂物等,提高钢水的纯净度,同时提高了钙收得率。
2、钙丝的生产过程的关键部位采用惰性气体处理,防止与空气中的氧接触发生钙的氧化反应。
因而,本发明的优势有:
1、快速脱氧、脱硫。
2、减少钢水中夹杂物含量。
3、提高钢水纯净度。
4、提高钢水流动性,提高钢坯连铸效率。
最后应说明的是:显然,上述实施例仅仅是为清楚地说明本发明所作的举例,而并非对实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明的保护范围之中。
Claims (1)
1.一种洁净钢生产用纯钙丝制备方法,其特征在于,所述方法为:将钙锭加热后经挤压机挤压成钙丝,再经包裹机用钢带将钙丝包裹成型,经缠盘机包装成钙丝线。