CN102424733B - Putty for wooden furniture - Google Patents
Putty for wooden furniture Download PDFInfo
- Publication number
- CN102424733B CN102424733B CN201110366723.XA CN201110366723A CN102424733B CN 102424733 B CN102424733 B CN 102424733B CN 201110366723 A CN201110366723 A CN 201110366723A CN 102424733 B CN102424733 B CN 102424733B
- Authority
- CN
- China
- Prior art keywords
- parts
- gas phase
- following component
- phase sio
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a putty for wooden furniture. The putty mainly comprises a main agent and a curing agent, wherein the main agent consists of the following components in part by weight: 64 to 66 parts of unsaturated polyester resin, 8 t o12 parts of styrene, 2 to 4 parts of phosphoric acid triallyl ester, 3 to 5 parts of bentonite, 3 to 5 parts of white corundum, 2 to 3 parts of gas-phase SiO2, 3 to 5 parts of attapulgite, 0.1 to 0.3 part of hydroquinone, 0.2 to 0.4 part of copper naphthenate, 0.2 to 0.4 part of dimethylaniline, 3 to 8 parts of titanium white and 1 to 2 parts of cobalt naphthenate; and the curing agent consists of the following components in part by weight: 10 to 14 parts of cyclohexanone peroxide, 2 to 3 parts of gas-phase SiO2, 3 to 5 parts of titanium white and 0.2 to 0.5 part of polyvinylpyrrolidone.
Description
Technical field
The present invention relates to chemistry painting industry field, particularly a kind of polyputty used for wood furniture.
Background technology
Atomized ash is a kind of polymerization putty take unsaturated polyester as main body, and commodity are called atomized ash.It is mainly used in filleting before application of metal, non-metal material surface, fills and leads up, and smooth, smooth in the hope of ground before application facilitates coating decoration.Along with the development of domestic furniture application and decoration industry, the requirement of the surface effect to furniture application and Indoor Wooden finishing, decoration is also more and more higher.Product appearance quality causes that all the more human consumer pays close attention to, and high-quality application proposes more and more higher requirement to the processing of ground indirectly.At the competition of within the trade, under the realities such as inflation pressure at home, wood furniture factory and interior decoration and decoration industry be urgent to be found and has wooden ground easy construction and novel material efficiently.At present existing in wooden application FAQs be, because of the variation of wooden ground water content, timber product is deformed, before and after the application of especially large-scale wood furniture goods, in substrate treatment process, the distortion of ground, shrink and make decorative coveringn breakage.Existing atomized ash complicated construction technique, must repeatedly be coated with mill.Not specialized application is not at the atomized ash of wood furniture production and decoration and decoration industry on the market, and the while also lacks easy construction, atomic ash special product efficiently.Simplify construction technology so develop a new generation, the special atomized ash goods of wooden ground have become extremely urgent market demands.Can fill up the blank that current wood furniture production and home decoration are short of specialized atomized ash.
Summary of the invention
For the deficiencies in the prior art, one of object of the present invention is to provide a kind of polyputty used for wood furniture, and this atomized ash and various wooden sticking power are good; Application property is good, easy to use; There is good snappiness and anti-contracility, overcome and cause the damaged situation of decorative coveringn because of distortion, contraction and the cracking of woodenware ground; Rate of drying is fast; Can fill up larger hole or crackle; Can support the use with the wood lacquer of main flow on the market.
For achieving the above object, the technical solution used in the present invention is as follows:
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: unsaturated polyester resin 64-66 part, vinylbenzene 8-12 part, triallyl phosphate 2-4 part, wilkinite 3-5 part, white fused alumina 3-5 part, gas phase SiO
22-3 part, protruding Attapulgite 3-5 part, Resorcinol 0.1-0.3 part, copper naphthenate 0.2-0.4 part, xylidine 0.2-0.4 part, titanium dioxide 3-8 part, cobalt naphthenate 1-2 part, wherein said solidifying agent is made up of following component in weight part: cyclohexanone peroxide 10-14 part, gas phase SiO
22-3 part, titanium dioxide 3-5 part, polyvinylpyrrolidone 0.2-0.5 part.
Preferably, wherein said host is made up of following component in weight part: unsaturated polyester resin 64.5-65.5 part, vinylbenzene 9-11 part, triallyl phosphate 2.5-3.5 part, wilkinite 3.5-4.5 part, white fused alumina 3.5-4.5 part, gas phase SiO
22.2-2.8 part, protruding Attapulgite 3.5-4.5 part, Resorcinol 0.15-0.25 part, copper naphthenate 0.25-0.35 part, xylidine 0.25-0.35 part, titanium dioxide 4-6 part, cobalt naphthenate 1.2-1.8 part, wherein said solidifying agent is made up of following component in weight part: cyclohexanone peroxide 11-13 part, gas phase SiO
22.2-2.8 part, titanium dioxide 3.5-4.5 part, polyvinylpyrrolidone 0.3-0.4 part.
Most preferably, wherein said host is made up of following component in weight part: 65 parts of unsaturated polyester resins, 10 parts of vinylbenzene, 3 parts of triallyl phosphates, 4 parts of wilkinites, 4 parts of white fused aluminas, gas phase SiO
22.5 parts, 4.0 parts of protruding Attapulgites, 0.20 part of Resorcinol, 0.30 part of copper naphthenate, 0.30 part of xylidine, 5 parts of titanium dioxides, 1.5 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 12 parts of cyclohexanone peroxides, gas phase SiO
22.5 parts, 4 parts of titanium dioxides, 0.35 part of polyvinylpyrrolidone.
The beneficial effect of the inventive method is:
The present invention has determined above-mentioned component and content on the basis of great many of experiments, makes to reach collaborative between each component, thereby reaches following technique effect:
1) application property is good, easy to use, easily preparation, and blade coating smoothness, reduces to be repeatedly coated with mill number of times; Rate of drying is fast, 15 minutes inner dryings of normal temperature.
2) putty membrane exquisiteness, smooth, smooth, can improve the quality of paint film; Can fill up larger hole or crackle, the wooden ground compared with rough grain is had to good filling effect, can reduce woodenware priming paint usage quantity.
3) this putty has good snappiness and anti-contracility, guarantees ground planeness; And with various wooden strong adhesions.
4) can be with the wood paint of various main flows on the market as supported the use with vinylformic acid, nitro, polyester, urethane etc.
Embodiment
Embodiment mono-
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: 64 parts of unsaturated polyester resins, 12 parts of vinylbenzene, 2 parts of triallyl phosphates, 5 parts of wilkinites, 3 parts of white fused aluminas, gas phase SiO
23 parts, 3 parts of protruding Attapulgites, 0.3 part of Resorcinol, 0.2 part of copper naphthenate, 0.4 part of xylidine, 3 parts of titanium dioxides, 2 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 10 parts of cyclohexanone peroxides, gas phase SiO
23 parts, 3 parts of titanium dioxides, 0.5 part of polyvinylpyrrolidone.
Embodiment bis-
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: 66 parts of unsaturated polyester resins, 8 parts of vinylbenzene, 4 parts of triallyl phosphates, 3 parts of wilkinites, 5 parts of white fused aluminas, gas phase SiO
22 parts, 5 parts of protruding Attapulgites, 0.1 part of Resorcinol, 0.4 part of copper naphthenate, 0.2 part of xylidine, 8 parts of titanium dioxides, 1 part of cobalt naphthenate, wherein said solidifying agent is made up of following component in weight part: 14 parts of cyclohexanone peroxides, gas phase SiO
22 parts, 5 parts of titanium dioxides, 0.2 part of polyvinylpyrrolidone.
Embodiment tri-
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: 64.5 parts of unsaturated polyester resins, 11 parts of vinylbenzene, 2.5 parts of triallyl phosphates, 4.5 parts of wilkinites, 3.5 parts of white fused aluminas, gas phase SiO
22.8 parts, 3.5 parts of protruding Attapulgites, 0.25 part of Resorcinol, 0.25 part of copper naphthenate, 0.35 part of xylidine, 4 parts of titanium dioxides, 1.8 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 11 parts of cyclohexanone peroxides, gas phase SiO
22.8 parts, 3.5 parts of titanium dioxides, 0.4 part of polyvinylpyrrolidone.
Embodiment tetra-
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: 65.5 parts of unsaturated polyester resins, 9 parts of vinylbenzene, 3.5 parts of triallyl phosphates, 3.5 parts of wilkinites, 4.5 parts of white fused aluminas, gas phase SiO
22.2 parts, 4.5 parts of protruding Attapulgites, 0.15 part of Resorcinol, 0.35 part of copper naphthenate, 0.25 part of xylidine, 6 parts of titanium dioxides, 1.2 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 13 parts of cyclohexanone peroxides, gas phase SiO
22.2 parts, 4.5 parts of titanium dioxides, 0.3 part of polyvinylpyrrolidone.
Embodiment five
A kind of polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, and wherein said host is made up of following component in weight part: 65 parts of unsaturated polyester resins, 10 parts of vinylbenzene, 3 parts of triallyl phosphates, 4 parts of wilkinites, 4 parts of white fused aluminas, gas phase SiO
22.5 parts, 4 parts of protruding Attapulgites, 0.2 part of Resorcinol, 0.3 part of copper naphthenate, 0.3 part of xylidine, 5 parts of titanium dioxides, 1.5 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 12 parts of cyclohexanone peroxides, gas phase SiO
22.5 parts, 4 parts of titanium dioxides, 0.3 part of polyvinylpyrrolidone.
Applicant's statement, the present invention illustrates detailed process equipment and process flow process of the present invention by above-described embodiment, but the present invention is not limited to above-mentioned detailed process equipment and process flow process, do not mean that the present invention must rely on above-mentioned detailed process equipment and process flow process and could implement.Person of ordinary skill in the field should understand, any improvement in the present invention, and the selections of the equivalence replacement to the each raw material of product of the present invention and the interpolation of ancillary component, concrete mode etc., within all dropping on protection scope of the present invention and open scope.
Claims (3)
1. a polyputty used for wood furniture, this atomized ash is made up of host and solidifying agent, it is characterized in that, wherein said host is made up of following component in weight part: unsaturated polyester resin 64-66 part, vinylbenzene 8-12 part, triallyl phosphate 2-4 part, wilkinite 3-5 part, white fused alumina 3-5 part, gas phase SiO
22-3 part, protruding Attapulgite 3-5 part, Resorcinol 0.1-0.3 part, copper naphthenate 0.2-0.4 part, xylidine 0.2-0.4 part, titanium dioxide 3-8 part, cobalt naphthenate 1-2 part, wherein said solidifying agent is made up of following component in weight part: cyclohexanone peroxide 10-14 part, gas phase SiO
22-3 part, titanium dioxide 3-5 part, polyvinylpyrrolidone 0.2-0.5 part.
2. a kind of polyputty used for wood furniture as claimed in claim 1, wherein said host is made up of following component in weight part: unsaturated polyester resin 64.5-65.5 part, vinylbenzene 9-11 part, triallyl phosphate 2.5-3.5 part, wilkinite 3.5-4.5 part, white fused alumina 3.5-4.5 part, gas phase SiO
22.2-2.8 part, protruding Attapulgite 3.5-4.5 part, Resorcinol 0.15-0.25 part, copper naphthenate 0.25-0.35 part, xylidine 0.25-0.35 part, titanium dioxide 4-6 part, cobalt naphthenate 1.2-1.8 part, wherein said solidifying agent is made up of following component in weight part: cyclohexanone peroxide 11-13 part, gas phase SiO
22.2-2.8 part, titanium dioxide 3.5-4.5 part, polyvinylpyrrolidone 0.3-0.4 part.
3. a kind of polyputty used for wood furniture as claimed in claim 2, wherein said host is made up of following component in weight part: 65 parts of unsaturated polyester resins, 10 parts of vinylbenzene, 3 parts of triallyl phosphates, 4 parts of wilkinites, 4 parts of white fused aluminas, gas phase SiO
22.5 parts, 4.0 parts of protruding Attapulgites, 0.20 part of Resorcinol, 0.30 part of copper naphthenate, 0.30 part of xylidine, 5 parts of titanium dioxides, 1.5 parts of cobalt naphthenates, wherein said solidifying agent is made up of following component in weight part: 12 parts of cyclohexanone peroxides, gas phase SiO
22.5 parts, 4 parts of titanium dioxides, 0.35 part of polyvinylpyrrolidone.