CN102409541A - 一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法 - Google Patents
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法 Download PDFInfo
- Publication number
- CN102409541A CN102409541A CN2011102378961A CN201110237896A CN102409541A CN 102409541 A CN102409541 A CN 102409541A CN 2011102378961 A CN2011102378961 A CN 2011102378961A CN 201110237896 A CN201110237896 A CN 201110237896A CN 102409541 A CN102409541 A CN 102409541A
- Authority
- CN
- China
- Prior art keywords
- rust
- container
- parts
- preparation
- percentage concentration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于:A)取浓度为0.1%的渗透剂T1份,浓度为1%的氨基硅油0.5~1.5份,加入到第一容器中,搅拌均匀,然后再加入浓度为0.5%的十二烷基苯磺酸钠溶液0.5~1.5份,搅拌至混合均匀;B)取浓度为2%的草酸4份,浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为6~7,得到所需要的丝织品揭展剂。与现有技术比较,本发明的优点是:1)对丝织品的原有结构、性能不会造成破坏作用;2)对于固结有铁锈、铜锈、土锈的丝织品具有很好的揭展效果;3)对于糟朽的丝织品,揭展后其断裂强力会有所提高。
Description
技术领域
本发明涉及的是一种丝绸文物保护方法,特别涉及一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法。
背景技术
中国是丝绸文明古国,在漫长的历史长河中,勤劳智慧的中国人民对自己祖先能够给人类创造如此绚丽多彩的丝绸,一直像史诗般的加以赞颂。但是对于古代出土的丝织品,由于其本身独特的有机材质,再加上受埋藏环境的影响,使得丝织品遭受了巨大的破坏和损失。
整摞放置及包裹在一起的丝织品,长期被深埋于地下,受到地震、墙体等压力及泥土的挤压,温湿度、土壤盐碱度、霉菌和微生物的侵蚀等各种条件的影响,随着时间的流逝,这些丝织品可能黏连、固结在一起,考古专家形容其像一个个“牛粪堆”,为了使这些宝贵文物面世,就必须先将其揭展开来。国内外关于揭展剂的研究还很少,国外在这方面是一片空白;国内有几家博物馆在这方面做过研究,但由于出土丝织品的黏结、固结情况、污染物不同,因此揭展剂的研究具有很强的针对性。
发明内容
本发明的目的在于提供一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,采用具有很好渗透、润湿性能的表面活性剂以及低分子量有机酸,能将固结在一起的丝织品很好的揭展开来,并且对丝织品的各种原有性能几乎没有什么不良影响。
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于采用如下步骤:
A)按照质量份数取质量百分浓度为0.1%的渗透剂T1份,质量百分浓度为1%的氨基硅油0.5~1.5份,加入到第一容器中,搅拌均匀,然后再加入质量百分浓度为0.5%的十二烷基苯磺酸钠溶液0.5~1.5份,搅拌至混合均匀;所述的氨基硅油是亲水性的环氧聚醚改性硅油;
B)按照与步骤A)相同的质量份数计量取质量百分浓度为2%的草酸4份,质量百分浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;
C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为6~7,得到所需要的丝织品揭展剂。
与现有技术比较,本发明的优点是:1)对丝织品的原有结构、性能不会造成破坏作用;2)对于固结有铁锈、铜锈、土锈的丝织品具有很好的揭展效果;3)对于糟朽的丝织品,揭展后其断裂强力会有所提高,从而有利于丝织品的保存。
具体实施方式
实施例1:
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于采用如下步骤:
A)按照质量份数取质量百分浓度为0.1%的渗透剂T1份,质量百分浓度为1%的氨基硅油0.5份,加入到第一容器中,搅拌均匀,然后再加入质量百分浓度为0.5%的十二烷基苯磺酸钠溶液1.5份,搅拌至混合均匀;所述的氨基硅油是亲水性的环氧聚醚改性硅油;
B)按照与步骤A)相同的质量份数计量取质量百分浓度为2%的草酸4份,质量百分浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;
C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为6,得到所需要的丝织品揭展剂。
实施例2:
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于采用如下步骤:
A)按照质量份数取质量百分浓度为0.1%的渗透剂T1份,质量百分浓度为1%的氨基硅油1.5份,加入到第一容器中,搅拌均匀,然后再加入质量百分浓度为0.5%的十二烷基苯磺酸钠溶液0.5份,搅拌至混合均匀;所述的氨基硅油是亲水性的环氧聚醚改性硅油;
B)按照与步骤A)相同的质量份数计量取质量百分浓度为2%的草酸4份,质量百分浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;
C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为7,得到所需要的丝织品揭展剂。
实施例3:
一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于采用如下步骤:
A)按照质量份数取质量百分浓度为0.1%的渗透剂T1份,质量百分浓度为1%的氨基硅油1份,加入到第一容器中,搅拌均匀,然后再加入质量百分浓度为0.5%的十二烷基苯磺酸钠溶液1份,搅拌至混合均匀;所述的氨基硅油是亲水性的环氧聚醚改性硅油;
B)按照与步骤A)相同的质量份数计量取质量百分浓度为2%的草酸4份,质量百分浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;
C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为6.5,得到所需要的丝织品揭展剂。
Claims (1)
1.一种固结有铁锈、铜锈、土锈的丝织品揭展剂的制备方法,其特征在于采用如下步骤:
A)按照质量份数取质量百分浓度为01%的渗透剂T1份,质量百分浓度为1%的氨基硅油0.5~1.5份,加入到第一容器中,搅拌均匀,然后再加入质量百分浓度为0.5%的十二烷基苯磺酸钠溶液0.5~1.5份,搅拌至混合均匀;所述的氨基硅油是亲水性的环氧聚醚改性硅油;
B)按照与步骤A)相同的质量份数计量取质量百分浓度为2%的草酸4份,质量百分浓度为1%的乙二胺四乙酸4份,加入到第二容器中,搅拌至混合均匀;
C)将第一容器和第二容器中的溶液混合,加入去离子水调节混合溶液的pH值为6~7,得到所需要的丝织品揭展剂。