CN102408830A - 一种多功能环保建筑涂料及其制备方法 - Google Patents
一种多功能环保建筑涂料及其制备方法 Download PDFInfo
- Publication number
- CN102408830A CN102408830A CN2011103134061A CN201110313406A CN102408830A CN 102408830 A CN102408830 A CN 102408830A CN 2011103134061 A CN2011103134061 A CN 2011103134061A CN 201110313406 A CN201110313406 A CN 201110313406A CN 102408830 A CN102408830 A CN 102408830A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- filler
- thickening material
- skimmer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种多功能环保建筑涂料,由以下组分按重量比组成:填料25-60份;净味乳液30-60份;负离子粉1-5份;阻燃剂5-10份;水20-35份,助剂2-5份;其中,所述填料包括木质纤维(80-200目)0.5~2份,硅藻土(80-180目)10~20份,开孔膨胀珍珠岩(10-180目)5~15份。本发明具有以下优点和效果:吸音效果好;净化空气,调节湿度,涂膜中含有的大量的孔隙,内表面积大,可以吸附空气中的有毒有害气体,同时可以调节室内空气湿度;干膜密度低,具有良好的节能保温性能;施工简便:施工时,可直接在合格基材上喷涂成整体美观的涂层。
Description
技术领域
本发明涉及一种建筑涂料及其制备方法,具体涉及一种具有节能保温、湿度调节、空气净化、吸音等综合性能的新型功能建筑涂料。
背景技术
涂料因其色彩丰富,装饰性好,生产施工简单,逐渐成为建筑工程中最重要的装饰材料之一。在日益追求高品质生活环境的今天,人们对于室内环境的噪声、湿度、空气质量、保温等方面都有明确的要求,尤其是在一些娱乐场所其封闭的环境特性对噪声、空气质量、节能保温的要求尤为严格,迫切需要研发人员能够开发一种功能多样的新型建筑涂料。
发明内容
针对现有技术存在的不足,本发明所要解决的技术问题是,提供一种多功能环保建筑涂料及其制备方法,具有节能保温、湿度调节、空气净化、吸音等综合性能。
为解决上述的技术问题,本发明所采用的技术方案是,一种多功能环保建筑涂料,由以下组分按重量比组成:填料25-60份;净味乳液30-60份;负离子粉1-5份;阻燃剂5-10份;水20-35份,助剂2-5份;
其中,所述填料包括木质纤维(80-200目)0.5~2份,硅藻土(80-180目)10~20份,开孔膨胀珍珠岩(10-180目)5~15份。所述填料既可增加涂膜厚度和物理机械性能,使涂膜耐久,提高涂料遮盖力,改善涂料流动性,还可以降低成本。木质纤维和硅藻土在涂层中形成大量的相互连通的孔隙,一方面,在提高吸音效果的同时净化室内异味、调节室内空气湿度,另一方面可以降低涂膜密度使涂料变为一种轻质涂料,而且添加硅藻土还具有调节粘度的作用;负离子粉能够吸收空气中的有害气体如甲醛、二氧化硫等,释放出对人体有意的负离子,同时由于本涂料具有多孔结构,增大了表面积,更有助于负离子的释放。
开孔形态的膨胀珍珠岩具有密度小,导热系数低,化学性稳定,使用温度范围宽,吸湿能力小,无毒无味,不腐蚀,不燃烧,吸音等特点。添加开孔膨胀珍珠岩使涂料所形成的涂膜含有大量相互贯通的微孔。膨胀珍珠岩颗粒粒级越高,颗粒越细,粘结剂优良越大,漆膜越容易开裂;颗粒粒级越低,颗粒越大,则孔隙太大,吸声效果变差。目数在14-28目之间,即粒径在0.6-1.2mm之间的膨胀珍珠岩对高频吸声效果较好;目数在28目以上,即粒径小于0.6mm的膨胀珍珠岩,对低频吸声效果较好。本发明优选目数在10-180目之间的开孔膨胀珍珠岩,既保持漆膜装饰外观的厚重质感,又能针对不同的噪声频率提供更好的吸声效果。木质纤维的填加在起到增加保温效果的同时,更能提高涂膜强度,防止漆膜开裂。
上述的一种多功能环保建筑涂料,其净味乳液的平均粒径为0.15-0.5μm。选择上述中等粒径的净味乳液,在干燥过程中不产生任何有毒气体,又避免了乳液粒径太细,渗入到开孔膨胀珍珠岩的微孔中,阻塞孔洞,影响吸声效果。
上述的一种多功能环保建筑涂料,其助剂包括:增稠剂0.3-0.5份;润湿剂0.1-0.3份;分散剂0.3-0.5份;防霉剂0.1-0.2份;防腐剂0.1-0.2份;消泡剂0.3-0.4份;成膜助剂1.0-2.0份;丙二醇0.2-0.5份;其中,所述增稠剂为羟乙基纤维素或蒙脱石粘土增稠剂。加入增稠剂能达到理想的罐内防沉效果和厚涂抗流挂效果,并提高涂料的保水性,使厚涂的漆膜不开裂。一般在制漆预混合阶段添加增稠剂,使增稠剂在水中充分分散,直至液体变成胶状能更好的发挥其优越的增稠流变性能。
制备本发明的多功能环保建筑涂料的方法依次由以下步骤组成:
(1)预混合:
按照上述配方量将负离子粉、阻燃剂、助剂中的增稠剂、润湿剂、分散剂、防霉剂、防腐剂和1/2的消泡剂加入分散缸中,与1/2的水相混合,以300-500转/分的速率低速搅拌20-30分钟,形成胶状溶液;
(2)分散调漆:
按照上述配方量将净味乳液、成膜助剂和丙二醇加入到胶状溶液中,搅拌均匀;然后,将填料按照上述配方量混合均匀并等分为2-3份,当浆料以300-500转/分的速率低速搅拌均匀后,加入1份填料,分2-3批依次加入;最后将余下的1/2消泡剂和1/2水加入浆料中,搅拌均匀。
生产步骤中的消泡剂分两次添加,是为了分别在预混和阶段与分散调漆阶段抑制泡沫的产生,以取得更好的消泡效果。
本发明制备的新型环保功能建筑涂料具有以下优点和效果:
1、吸音效果好:填料选用粗粒径的开孔膨胀珍珠岩、空心玻璃微珠、硅藻土和木质纤维,使漆膜中含有大量互相贯通的微孔,漆膜孔隙率的增大,使得吸声效果提高,平均吸声系数大于0.5;
2、净化空气,调节湿度:涂膜中含有的大量的孔隙,内表面积大,可以吸附空气中的有毒有害气体,同时可以调节室内空气湿度。其中的负离子粉可以不断吸收有害气体,释放负离子。当空气湿度较大时,孔隙壁尤其是木质纤维可以吸附一定水分,当湿度较低时其含有的水分又可以缓慢释放,增加空气湿度;
3、干膜密度低具有良好的节能保温性能;
4、施工简便:施工时,可直接在合格基材上喷涂成整体美观的涂层。
具体实施方式
下面通过实施例对本发明做进一步说明。在对以下实施例的主要性能指标的测试中,吸声系数的检测依据GBJ47-83《混响室法吸声系数测量规范》检测;负离子个数采用AIC-2负离子浓度仪测定;导热系数参照GB/T 17371-1998进行测试。
实施例1
本实施例的多功能环保建筑涂料,由以下组分按重量比组成:填料36份;净味乳液60份;负离子粉1份;助剂5份;阻燃剂(东莞市尔道化工有限公司,Doher-601)5份;水20份。其中,填料包括木质纤维(80目)1份,硅藻土(80目)20份,开孔膨胀珍珠岩(10目)15份。助剂包括:增稠剂(美国罗门哈斯公司,TT-935)0.4份;润湿剂(上海向岚化工有限公司,Triton CF-10)0.2份;分散剂(德国科宁公司,SN5040)0.4份;防霉剂(福州邦联化工有限公司,MB-11)0.2份;防腐剂(福州邦联化工有限公司,MB-16)0.2份;消泡剂(德国毕克化学公司,BYK-052)0.3份;成膜助剂(美国伊士曼化工公司,TAXANOL)1.5份;丙二醇0.5份。
制备本实施例的多功能环保建筑涂料的方法依次由以下步骤组成:
(1)预混合:
按照上述配方量将负离子粉、阻燃剂、助剂中的增稠剂、润湿剂、分散剂、防霉剂、防腐剂和1/2的消泡剂加入分散缸中,与1/2的水相混合,以300-500转/分的速率低速搅拌20-30分钟,形成胶状溶液;
(2)分散调漆:
按照上述配方量将净味乳液、成膜助剂和丙二醇加入到胶状溶液中,搅拌均匀;然后,将填料按照上述配方量混合均匀并等分为2-3份,当浆料以300-500转/分的速率低速搅拌均匀后,加入1份填料,分2-3批依次加入;最后将余下的1/2消泡剂和1/2水加入浆料中,搅拌均匀。
净味乳液为巴斯夫提供,该乳液固含量为54~56%,平均粒径0.3~0.5μm,最低成膜温度24℃。
实施例2
本实施例的多功能环保建筑涂料,由以下组分按重量比组成:填料25份;净味乳液30份;负离子粉5份;助剂3份;阻燃剂(东莞市尔道化工有限公司,Doher-6200)6份;水35份。其中,填料包括木质纤维(200目)0.5份,硅藻土(130目)10份,开孔膨胀珍珠岩(180目)5份。助剂包括:增稠剂(美国罗门哈斯公司,DR-72)0.3份;润湿剂(上海助剂厂有限公司,OP-10)0.1份;分散剂(德国科宁公司,SN5040)0.3份;防霉剂(福州邦联化工有限公司,MB-11)0.1份;防腐剂(福州邦联化工有限公司,MB-16)0.1份;消泡剂(德国毕克化学公司,BYK-055)0.35份;成膜助剂(美国伊士曼化工公司,TAXANOL)2份;丙二醇0.3份。
制备本实施例的多功能环保建筑涂料的方法依次由以下步骤组成:
(1)预混合:
按照上述配方量将负离子粉、阻燃剂、助剂中的增稠剂、润湿剂、分散剂、防霉剂、防腐剂和1/2的消泡剂加入分散缸中,与1/2的水相混合,以300-500转/分的速率低速搅拌20-30分钟,形成胶状溶液;
(2)分散调漆:
按照上述配方量将净味乳液、成膜助剂和丙二醇加入到胶状溶液中,搅拌均匀;然后,将填料按照上述配方量混合均匀并等分为2-3份,当浆料以300-500转/分的速率低速搅拌均匀后,加入1份填料,分2-3批依次加入;最后将余下的1/2消泡剂和1/2水加入浆料中,搅拌均匀。
净味乳液为美国陶氏化学上海联碳胶乳有限公司提供,该乳液固含量为49~51%,平均粒径0.3μm,最低成膜温度20℃。
实施例3
本实施例的多功能环保建筑涂料,由以下组分按重量比组成:填料60份;净味乳液40份;负离子粉2.5份;助剂2份;阻燃剂(东莞市尔道化工有限公司,Doher-6200)10份;水30份。其中,填料包括木质纤维(100目)2份,硅藻土(180目)15份,开孔膨胀珍珠岩(120目)12份。助剂包括:增稠剂(美国罗门哈斯公司,DR-73)0.5份;润湿剂(上海向岚化工有限公司,Triton CF-10)0.3份;分散剂(德国毕克化学公司,Disperbyk 154)0.5份;防霉剂(北京金源恒泰精细化工有限公司,华科-108)0.15份;防腐剂(北京金源恒泰精细化工有限公司,华科-088)0.15份;消泡剂(德国毕克化学公司,BYK-052)0.4份;成膜助剂(美国伊士曼化工公司,TAXANOL)1份;丙二醇0.2份。
制备本实施例的多功能环保建筑涂料的方法依次由以下步骤组成:
(1)预混合:
按照上述配方量将负离子粉、阻燃剂、助剂中的增稠剂、润湿剂、分散剂、防霉剂、防腐剂和1/2的消泡剂加入分散缸中,与1/2的水相混合,以300-500转/分的速率低速搅拌20-30分钟,形成胶状溶液;
(2)分散调漆:
按照上述配方量将净味乳液、成膜助剂和丙二醇加入到胶状溶液中,搅拌均匀;然后,将填料按照上述配方量混合均匀并等分为2-3份,当浆料以300-500转/分的速率低速搅拌均匀后,加入1份填料,分2-3批依次加入;最后将余下的1/2消泡剂和1/2水加入浆料中,搅拌均匀。
净味乳液为美国陶氏化学上海联碳胶乳有限公司提供,该乳液固含量为49~51%,平均粒径0.3μm,最低成膜温度20℃。
将以上三个实施例的涂料涂覆在石棉水泥板上制备1mm厚的漆膜,主要性能的车市结果如下:
以上所述,仅是本发明的较佳实施例而已,并非是对本发明作其它形式的限制,任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型,仍属于本发明技术方案的保护范围。
Claims (4)
1.一种多功能环保建筑涂料,由以下组分按重量比组成:
填料25-60份;净味乳液30-60份;负离子粉1-5份;阻燃剂5-10份;水20-35份,助剂2-5份;
其中,所述填料包括木质纤维(80-200目)0.5~2份,硅藻土(80-180目)10~20份,开孔膨胀珍珠岩(10-180目)5~15份。
2.根据权利要求1所述的多功能环保建筑涂料,所述净味乳液的平均粒径为0.15-0.5μm。
3.根据权利要求1所述的多功能环保建筑涂料,所述助剂包括:增稠剂0.3-0.5份;润湿剂0.1-0.3份;分散剂0.3-0.5份;防霉剂0.1-0.2份;防腐剂0.1-0.2份;消泡剂0.3-0.4份;成膜助剂1.0-2.0份;丙二醇0.2-0.5份;其中,所述增稠剂为羟乙基纤维素或蒙脱石粘土增稠剂。
4.制备权利要求1中的多功能环保建筑涂料的方法依次由以下步骤组成:
(1)预混合:
按照上述配方量将负离子粉、阻燃剂、助剂中的增稠剂、润湿剂、分散剂、防霉剂、防腐剂和1/2的消泡剂加入分散缸中,与1/2的水相混合,以300-500转/分的速率低速搅拌20-30分钟,形成胶状溶液;
(2)分散调漆:
按照上述配方量将净味乳液、成膜助剂和丙二醇加入到胶状溶液中,搅拌均匀;然后,将填料按照上述配方量混合均匀并等分为2-3份,当浆料以300-500转/分的速率低速搅拌均匀后,加入1份填料,分2-3批依次加入;最后将余下的1/2消泡剂和1/2水加入浆料中,搅拌均匀。