CN108947470A - 调湿净化材料及制备方法、应用和应用调湿净化材料制备得到的产品 - Google Patents
调湿净化材料及制备方法、应用和应用调湿净化材料制备得到的产品 Download PDFInfo
- Publication number
- CN108947470A CN108947470A CN201810984402.8A CN201810984402A CN108947470A CN 108947470 A CN108947470 A CN 108947470A CN 201810984402 A CN201810984402 A CN 201810984402A CN 108947470 A CN108947470 A CN 108947470A
- Authority
- CN
- China
- Prior art keywords
- parts
- damping
- scavenging material
- scavenging
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种调湿净化材料及制备方法、应用和应用调湿净化材料制备得到的产品,涉及环境材料技术领域,本发明提供的调湿净化材料,包括特定配比的硅藻土、蛭石粉、珍珠岩粉、乙烯脲、植物纤维和负离子粉。通过各特定组分和配比之间的协同配合,使得本发明提供的调湿净化材料具有良好的调湿作用,容湿量大,调湿迅速。并且,能够有效吸附并分解甲醛,能够去除空气中的异味,净化空气。本发明提供的上述调湿净化材料的制备方法,工艺简单,操作方便,有效提高生产效率。本发明提供的应用调湿净化材料制备得到的产品,可根据使用者的需求制备成建筑材料或装饰品,在具有与上述调湿净化材料相同的有益效果的基础上,使用寿命长,可达5‑10年。
Description
技术领域
本发明涉及环境材料技术领域,尤其是涉及一种调湿净化材料及制备方法、应用和应用调湿净化材料制备得到的产品。
背景技术
调湿材料是具有可根据环境湿度变化控制水蒸气吸附的功能材料。在湿度较高时,材料能够吸附环境中的水蒸气;当湿度降低时,能够排放出自身吸附的水蒸气。空气相对湿度是衡量室内环境的一项重要参数,合适的湿度对人体健康、工农业生产都具有十分重要的作用。我国南方潮湿地区年平均相对湿度为70%~80%,有时高达95%~100%,而北方地区干燥时期的相对湿度最低达到10%以下,湿度调节非常必要。
另外,室内环境污染对现代人类健康的影响具有严重的危害性,特别是夏季,随着室温的升高,各种建筑材料和家具中的有害气体如甲醛,苯系物等挥发性有机物的释放量也随之增加。这些有害气体表现出毒性、刺激性,能引起机体免疫水平失调,影响中枢神经系统功能,出现头晕、头痛、嗜睡、无力、胸闷等症状。
现有的材料通常单纯负责调湿或单纯负责净化,缺少调湿净化一体的材料。
有鉴于此,特提出本发明。
发明内容
本发明的第一个目的在于提供一种调湿净化材料,以缓解现有技术中存在的环保材料难以兼具调湿和净化功能的技术问题。
本发明的第二个目的在于提供上述调湿净化材料的制备方法,该方法工艺简单,操作方便,能够节约大量的人力和物力,有效提高生产效率,且制备得到的调湿净化材料兼具调湿和净化的功能。
本发明的第三个目的在于提供上述调湿净化材料在制备建筑材料或装饰品中的应用。
本发明的第四个目的在于提供应用上述调湿净化材料制备得到的产品。
本发明提供了一种调湿净化材料,所述调湿净化材料包括如下重量份的原料:
硅藻土200-250份、蛭石粉50-100份、珍珠岩粉50-100份、乙烯脲30-60份、植物纤维20-40份、易溶盐20-40份和负离子粉15-25份。
进一步地,所述调湿净化材料包括如下重量份的原料:
硅藻土210-240份、蛭石粉60-90份、珍珠岩粉60-90份、乙烯脲35-55份、植物纤维25-35份、易溶盐25-35份和负离子粉17-23份。
优选地,所述调湿净化材料包括如下重量份的原料:
硅藻土220-230份、蛭石粉70-80份、珍珠岩粉70-80份、乙烯脲40-50份、植物纤维28-32份、易溶盐28-32份和负离子粉19-21份。
进一步地,所述调湿净化材料还包括抗菌剂1-5份,优选为1-4份,更优选为1-3份;
优选地,所述抗菌剂为无机抗菌剂;
优选地,所述抗菌剂包括纳米银离子、氧化锌、氧化铜、磷酸二氢铵或碳酸锂中的一种或多种。
进一步地,所述调湿净化材料还包括硅烷偶联剂5-10份,优选为6-8份;
优选地,所述硅烷偶联剂包括乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷或乙烯基三(β-甲氧乙氧基)硅烷中的一种或多种。
进一步地,所述调湿净化材料还包括胶凝材料500-550份,优选为510-540份,更优选为520-530份;
优选地,所述胶凝材料为无机胶凝材料;
优选地,所述无机胶凝材料包括石灰、石膏或水泥中的一种或多种。
进一步地,所述调湿材料还包括负离子激发剂10-30份,优选15-25份,更优选18-22份;
优选地,所述负离子激发剂为发光材料;
优选地,所述发光材料包括荧光粉或过度金属氧化物。
本发明还提供了上述的调湿净化材料的制备方法,所述制备方法包括:
将配方量的各组分混合均匀,活化后,调整堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
进一步地,当堆积密度小于0.5g/cm3时,采用胶凝材料或重钙粉进行调整,当堆积密度大于1.0g/cm3时,采用珍珠岩粉进行调整;
优选地,所述制备方法包括如下步骤:
(a)向配方重量份的硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入硅烷偶联剂混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入配方量的乙烯脲、植物纤维和抗菌剂,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入配方量的负离子粉和负离子激发剂,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
本发明还提供了上述的调湿净化材料或应用上述的制备方法制备得到的调湿净化材料在制备建筑材料或装饰品中的应用。
另外,本发明还提供了应用上述的调湿净化材料或应用上述的制备方法制备得到的调湿净化材料制备得到的产品
本发明提供的调湿净化材料,包括特定配比的硅藻土、蛭石粉、珍珠岩粉、乙烯脲、植物纤维和负离子粉。其中,硅藻土具有松散、质轻、多孔、吸水性和渗透性强的特性,选择硅藻土作为原料,保证调湿净化材料具有强吸附能力,能够有效去除空气中的有害物质和异味,同时,在被动调湿的基础上,其多孔结构还能够加大吸湿容量,并且具有随环境湿度改变而快速调湿的优点;蛭石质轻、透气性好、隔热、吸声、吸水力强,选择蛭石粉作为原料,使得该调湿净化材料可循环利用,节约成本,也保证了调湿净化材料的稳定性,不易因温度变化而影响其调湿或净化的功能;乙烯脲会和甲醛进行不可逆反应,吸收后直接分解部分甲醛,选择乙烯脲作为原料,能够达到短期快速而大量除掉室内的高浓度甲醛等有害气体的目的,防止二次污染;植物纤维有吸湿的功能,且其透气性良好,选择植物纤维作为原料,能够起到辅助吸湿除潮的作用;负离子粉具有产生负氧离子、去除游离空气中的有害气体及异味、抗菌抑菌的作用,在原料中加入负离子粉,能够使调湿净化材料释放大量的对人体有益的负氧离子,保健人体的同时净化空气。上述各组分相容性良好,通过各特定组分和配比之间的协同配合,使得本发明提供的调湿净化材料具有良好的调湿作用,容湿量大,调湿迅速。在湿度大时能够有效吸湿,在环境干燥时,能够利用自身储存的水分加湿,解决南潮北燥的苦恼,无能耗,无噪音,可循环利用,节约成本。并且,能够有效吸附并分解甲醛,克服传统的物理吸附除甲醛达饱和之后会释放甲醛的问题。利用其强大的吸附能力,能够去除空气中的异味,净化空气,解决室内、车内空间异味大的烦恼。本发明提供的调湿净化材料适用于各种需要调节空气质量及湿度的环境。
本发明提供的上述调湿净化材料的制备方法,工艺简单,操作方便,能够节约大量的人力和物力,有效提高生产效率,且制备得到的调湿净化材料兼具调湿和净化的功能。
本发明提供的应用上述调湿净化材料制备得到的产品,可根据使用者的需求制备成建筑材料或装饰品,在具有与上述调湿净化材料相同的有益效果的基础上,使用寿命长,可达5-10年。
具体实施方式
下面将结合实施例对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
本发明提供了一种调湿净化材料,所述调湿净化材料包括如下重量份的原料:
硅藻土200-250份、蛭石粉50-100份、珍珠岩粉50-100份、乙烯脲30-60份、植物纤维20-40份、易溶盐20-40份和负离子粉15-25份。
其中,硅藻土是一种硅质岩石,是一种生物成因的硅质沉积岩,主要由古代硅藻的遗骸所组成。其化学成分以SiO2为主,可用SiO2·nH2O表示,矿物成分为蛋白石及其变种。硅藻土的密度1.9-2.3g/cm3,比表面积40-65m2/g,孔体积0.45-0.98m3/g,吸水率是自身体积的2-4倍,有细腻、松散、质轻、多孔、吸水性和渗透性强的性质。本发明选择硅藻土作为原料,保证本发明提供的调湿净化材料具有强吸附能力,能够有效去除空气中的有害物质(如甲醛等)和异味,同时,在被动调湿的基础上,其多孔结构还能够加大吸湿容量,并且具有随环境湿度改变而快速调湿的优点。其含量例如可以为,但不限于200份、210份、220份、230份、240份或250份。
蛭石是一种天然、无机,无毒的矿物质,在高温作用下会膨胀,属于硅酸盐。其质轻、透气性好、隔热、吸声、吸水力强。典型但非限制性的蛭石粉的细度可以为200-400目,例如可以为,但不限于200目、220目、250目、280目、300目、320目、350目、380目或400目。密度可以为2.4~2.7g/cm3,例如2.4g/cm3、2.5g/cm3、2.6g/cm3或2.7g/cm3。膨胀后的蛭石平均容重为100~200kg/m3,例如可以为,但不限于100kg/m3、120kg/m3、150kg/m3、180kg/m3或200kg/m3。本发明选择蛭石粉作为原料,一方面保证了调湿净化材料在高湿度时具有良好的吸湿作用,在干燥时能够利用自身储存的水分加湿,可循环利用,节约成本。另一方面,也保证了调湿净化材料的稳定性,不易因温度变化而影响其调湿或净化的功能。其含量例如可以为,但不限于50份、60份、70份、80份、90份或100份。
珍珠岩是一种火山喷发的酸性熔岩,经急剧冷却而成的玻璃质岩石,主要化学成分为SiO2 70%±,H2O 4-6%,Fe2O3,膨胀珍珠岩微粉是珍珠岩矿砂经预热,瞬时高温焙烧膨胀后在接料仓上方形成的一种悬浮白色粉状固体。其原理为:珍珠岩矿石经破碎形成一定粒度的矿砂,经预热焙烧,急速加热(1000℃以上),矿砂中水分汽化,在软化的含有玻璃质的矿砂内部膨胀的微细粉体的非金属矿产品。其具有洁白、质轻特征和乳化、润滑作用。典型但非限制性的珍珠岩粉可以为密度2.2-2.4g/cm3,堆积密度在50-100Kg/m3。本发明选择膨胀珍珠岩粉作为原料,一方面是利用其质轻调节产品的密度,提高吸湿体积容湿量,降低成本。另一方面自身具有去污、过滤、净化功效,辅助提高产品的净化功能。其含量例如可以为,但不限于50份、60份、70份、80份、90份或100份。
乙烯脲分子式是C3H6N2O,具有甲醛捕捉的作用。现有的净化材料多选择吸附材料,如活性炭对甲醛等有害物质进行物理吸附,但吸附饱和之后或在温度升高时会再释放已吸附的甲醛,造成二次污染。而乙烯脲会和甲醛进行不可逆反应,吸收后直接分解部分甲醛。本发明选择乙烯脲作为原料,能够达到短期快速而大量除掉室内的高浓度甲醛等有害气体的目的,防止二次污染,并且,乙烯脲在弱光条件下即可完成甲醛等有害物质的去除,无需紫外线等特殊条件。其含量例如可以为,但不限于30份、40份、50份或60份。
植物纤维可分为种子纤维、韧皮纤维、叶纤维或果实纤维。其中种子纤维是指一些植物种子表皮细胞生长成的单细胞纤维,如棉、木棉。韧皮纤维是从一些植物韧皮部取得的单纤维或工艺纤维,如:亚麻、苎麻、黄麻、竹纤维。叶纤维是从一些植物的叶子或叶鞘取得的工艺纤维,如:剑麻、蕉麻。果实纤维是从一些植物的果实取得的纤维,如:椰子纤维。植物纤维有吸湿的功能,且其透气性良好。本发明选择植物纤维作为原料,能够起到辅助吸湿除潮的作用。此外,通过植物纤维还能够提高调湿净化材料所制成的产品的韧性和抗冲击性。其含量例如可以为,但不限于20份、30份或40份。
易溶盐为能在1-10mL溶剂中溶解至少1g的盐类。典型但非限制性的易溶盐为钾盐,钠盐,铵盐,硝酸盐等。在本发明提供的调湿净化材料中加入易溶盐,并通过工艺制备,使得易溶盐均匀的吸附在多孔材料的孔道中,能够与多孔材料协同配合,从而增加本品与周围空气中水分或有害气味的浓度差,提高吸附力度和速度,达到更好的调湿效果。其含量例如可以为,但不限于20份、30份或40份。
负离子粉是人类利用自然界产生负离子的原理,人工合成或者配比的一种复合矿物,具有产生负氧离子的作用,负氧离子还具有其他的作用,如去除游离空气中的有害气体及异味、抗菌抑菌等。若在原料中加入负离子粉,能够使调湿净化材料释放大量的对人体有益的负氧离子,保健人体的同时,依靠负离子的电离分解作用,进行长期分解甲醛。净化空气。负离子粉包括电气石粉、神山麦饭石粉、桂阳石粉、火山岩粉、奇冰石粉、六环石粉、盐石粉、镭石粉、砭石粉、海鸥石粉、蛋白石粉、角闪石粉、微斜长石粉或水溶性负离子粉中的一种或多种。其含量例如可以为,但不限于15份、20份或25份。
在一些优选的实施方式中,所述调湿净化材料包括如下重量份的原料:
硅藻土210-240份、蛭石粉60-90份、珍珠岩粉60-90份、乙烯脲35-55份、植物纤维25-35份、易溶盐25-35份和负离子粉17-23份。
优选地,所述调湿净化材料包括如下重量份的原料:
硅藻土220-230份、蛭石粉70-80份、珍珠岩粉70-80份、乙烯脲40-50份、植物纤维28-32份、易溶盐28-32份和负离子粉19-21份。
通过对各组分的配比进行进一步的调整和优化,使得本发明提供的调湿净化材料具有更好的调湿和净化空气的功能。
在一些优选的实施方式中,所述调湿净化材料还包括抗菌剂1-5份,例如可以为,但不限于1份、2份、3份、4份或5份,优选为1-4份,更优选为1-3份。
本发明使用的抗菌剂对病原微生物有杀死作用或抑制生长作用,但又不妨碍人类正常生活。在调湿净化材料中加入抗菌剂,能够使该材料在净化空气的基础上,抗菌抑菌,避免空气中的病原菌对人体造成伤害,保证人体健康。
优选地,所述抗菌剂为无机抗菌剂。
无机抗菌剂是通过物理吸附离子交换等方法达到抗菌杀菌目的的,无毒副作用,安全、健康。
优选地,所述抗菌剂包括纳米银离子、氧化锌、氧化铜、磷酸二氢铵或碳酸锂中的一种或多种。
在一些优选的实施方式中,所述调湿净化材料还包括硅烷偶联剂5-10份,例如可以为,但不限于5份、6份、7份、8份、9份或10份,优选为6-8份。
硅烷偶联剂的分子结构式一般为:Y-R-Si(OR)3(式中Y一有机官能基,SiOR一硅烷氧基)。硅烷氧基对无机物具有反应性,有机官能基对有机物具有反应性或相容性。因此,当硅烷偶联剂介于无机和有机界面之间,可形成有机基体-硅烷偶联剂-无机基体的结合层。在调湿净化材料中加入硅烷偶联剂,能够增加乙烯脲与其他组分之间的结合性,提高产品的稳定性。
优选地,所述硅烷偶联剂包括乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷或乙烯基三(β-甲氧乙氧基)硅烷中的一种或多种。
在一些优选的实施方式中,所述调湿净化材料还包括胶凝材料500-550份,例如可以为,但不限于500份、510份、520份、530份、540份或550份,优选为510-540份,更优选为520-530份。
胶凝材料又称胶结料,是指通过自身的物理化学作用,由可塑性浆体变为坚硬石状体的过程中,能将散粒或块状材料粘结成为整体的材料,亦称为胶结材料。在调湿净化材料中加入胶凝材料,能够增强该材料的可塑性,使其能够根据使用者的需求制备为建筑材料或固定形状的装饰品等。
优选地,所述胶凝材料为无机胶凝材料;
无机胶凝材料在具备将散粒或块状材料粘结成为整体的材料的性能的基础上,无毒副作用,安全、健康。
优选地,所述无机胶凝材料包括石灰、石膏或水泥中的一种或多种。
在一些优选的实施方式中,所述调湿材料还包括负离子激发剂10-30份,例如可以为,但不限于10份、15份、20份、25份或30份,优选15-25份,更优选18-22份。
负离子激发剂能够使本发明提供的调湿净化材料中的负离子粉更大限度地释放负氧离子,达到去除游离空气中的有害气体及异味、抗菌抑菌的目的,同时大量的负氧离子还能够保证使用者的身体健康。
优选地,所述负离子激发剂为发光材料。
利用具有低放射性的发光材料类物质,使得分子外层电子脱离原子核的束缚,越出轨道。此时,气体分子变成了正离子,所越出的电子便与其它中性分子结合形成负离子,从而起到激发负离子的作用。
优选地,所述发光材料包括荧光粉或过度金属氧化物。
在一个优选的实施方式中,金属氧化物优选为镧系氧化物,例如可以为,但不限于如氧化钐、氧化镥或氧化镧。
本发明还提供了上述的调湿净化材料的制备方法,包括:
将配方量的各组分混合均匀,活化后,调整堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
该方法工艺简单,操作方便,能够节约大量的人力和物力,有效提高生产效率,且制备得到的调湿净化材料兼具调湿和净化的功能。
其中,堆积密度例如可以为,但不限于0.5g/cm3、0.6g/cm3、0.7g/cm3、0.8g/cm3、0.9g/cm3或1.0g/cm3。
在一些优选的实施方式中,当堆积密度小于0.5g/cm3时,采用胶凝材料或重钙粉进行调整,当堆积密度大于1.0g/cm3时,采用珍珠岩粉进行调整。
胶凝材料和重钙粉的密度均大于调湿净化材料的终密度,选择胶凝材料和重钙粉调整密度,可以避免引入能够与其他原料产生反应的活性物质,保证调湿净化材料的原本性能。
珍珠岩粉的密度小于调湿净化材料的终密度,选择珍珠岩粉调整密度,因其本身为调湿净化材料的原料,可以避免引入能够与其他原料产生反应的活性物质,保证调湿净化材料的原本性能。
优选地,所述制备方法包括如下步骤:
(a)向配方重量份的硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入硅烷偶联剂混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入配方量的乙烯脲、植物纤维和抗菌剂,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入配方量的负离子粉和负离子激发剂,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
本发明还提供了上述的调湿净化材料或应用上述的制备方法制备得到的调湿净化材料在制备建筑材料或装饰品中的应用。
另外,本发明还提供了应用上述的调湿净化材料或应用上述的制备方法制备得到的调湿净化材料制备得到的产品。
该产品可根据需要做成桌面、柜板、装饰墙等;或做成吊顶板大面积使用;或直接使用本发明提供的调湿净化材料进行现场搅拌,刮抹于需要调控室内环境的基层上;或在当前业内所推崇的绿色建筑、被动式或装配式房屋所使用复合墙板将本品复合于其内表面,起到调湿净化效果;或可以成型为约(15-25)cm*(10-15)cm*(2-4)cm大小的调湿净化砖或异形摆件,用于调节密闭的小空间内的环境质量,如汽车、抽屉、柜子、冰箱、图书室、环境舱、文物保护箱、小吸烟室、小厕所等小空间使用,随心摆放;或可以成型为任意大小的装饰型调湿净化板,干挂或粘贴于室内墙面,其表面可以布置一层透气的壁布或布画或涂刷一层透气涂料(如无机涂料),在美化环境的同时,又极大改善密闭空间的环境质量;或可以制作成标准的吊顶板或装饰线用于室内吊顶和装饰处理;或可以做成浮雕板画,并根据自己喜好装裱,像美妙的书画一样安放在墙上任何地方,体现书香门第的氛围同时,又能时刻调湿和净化环境;或可以与其他机械设备进行组合,做成无能耗、无噪音的调湿净化器/箱等;或可以单独或复合做成隔板或者照壁等。总之,用途广泛,花样繁多,任由选择。
下面结合具体实施例和对比例,对本发明作进一步说明。
实施例1
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土200份、蛭石粉100份、珍珠岩粉50份、乙烯脲60份、竹纤维20份、KCl 40份和负离子粉15份。
实施例2
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土250份、蛭石粉50份、珍珠岩粉100份、乙烯脲30份、棉纤维40份、KNO3 20份和负离子粉25份。
实施例3
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份和负离子粉20份。
实施例4
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份、负离子粉20份、纳米银离子1份、乙烯基三乙氧基硅烷10份、石膏500份和荧光粉30份。
实施例5
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份、负离子粉20份、纳米银离子5份、乙烯基三甲氧基硅烷5份、石灰550份和荧光粉10份。
实施例6
本实施例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份、负离子粉20份、纳米银离子3份、乙烯基三(β-甲氧乙氧基)硅烷8份、水泥525份和荧光粉20份。
实施例7
本实施例提供了一种调湿净化材料,主要由如下方法制备得到:
(a)取实施例6提供的配方量的各组分,向硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入乙烯基三(β-甲氧乙氧基)硅烷混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入乙烯脲、植物纤维和纳米银离子,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入负离子粉和荧光粉,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为0.5g/cm3,得到所述调湿净化材料。
实施例8
本实施例提供了一种调湿净化材料,主要由如下方法制备得到:
(a)取实施例6提供的配方量的各组分,向硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入乙烯基三(β-甲氧乙氧基)硅烷混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入乙烯脲、植物纤维和纳米银离子,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入负离子粉和荧光粉,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为1.0g/cm3,得到所述调湿净化材料。
实施例9
本实施例提供了一种调湿净化材料,主要由如下方法制备得到:
(a)取实施例6提供的配方量的各组分,向硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入乙烯基三(β-甲氧乙氧基)硅烷混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入乙烯脲、植物纤维和纳米银离子,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入负离子粉和荧光粉,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为0.6-0.7g/cm3,得到所述调湿净化材料。
对比例1
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份和负离子粉20份。
对比例2
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份、NaCl30份和负离子粉20份。
对比例3
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、乙烯脲45份、椰子纤维30份、NaCl 30份和负离子粉20份。
对比例4
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、椰子纤维30份、NaCl30份和负离子粉20份。
对比例5
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、NaCl 30份和负离子粉20份。
对比例6
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份和负离子粉20份。
对比例7
本对比例提供了一种调湿净化材料,主要由如下重量份的原料制成:
硅藻土225份、蛭石粉75份、珍珠岩粉75份、乙烯脲45份、椰子纤维30份和NaCl 30份。
为了对本发明提供的调湿净化材料行进一步的说明,进行如下实验:
实验例1粉状材料指标
一、依据WW/T0068-2015《馆藏文物保存环境控制调湿材料》对本发明实施例1-9及对比例1-7提供的调湿净化材料进行检测,其检测标准如表1所示,检测结果如表2所示。
表1馆藏文物保存环境控制调湿材料检测标准
项目 | 标准要求 |
单位吸湿能力(g) | ≥10 |
单位放湿能力(g) | ≥4 |
单位目标湿容量(g) | >2 |
单位吸湿速度(g) | >4 |
单位放湿速度(g) | >1.2 |
表2调湿净化材料检测结果
从上述结果中可以看出,本发明实施例1-9提供的调湿净化材料,通过各特定组分和配比之间的协同配合,使得本发明提供的调湿净化材料具有良好的调湿作用,在湿度大时能够有效吸湿,在环境干燥时,能够利用自身储存的水分加湿,且容湿量大,调湿迅速。而对比例1-7提供的调湿净化材料,无论在调湿效果、调湿速度或容湿量的方面,其效果均不及本发明实施例的水平。
其中,实施例1-3提供的调湿净化材料,其原料组分完全相同,仅配比不同。但实施例3提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均优于实施例1和2的水平。说明通过对各组分的配比进行进一步的调整和优化,使得本发明提供的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
实施例3与实施例6提供的调湿净化材料,其相同组分的配比相同,但实施例6中添加了抗菌剂、硅烷偶联剂、胶凝材料和负离子激发剂作为助剂。但实施例6提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均优于实施例3的水平。说明通过添加合适的助剂,与原料进行进一步的协同作用,使得本发明提供的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
实施例4-6提供的调湿净化材料,其原料组分和配比完全相同,助剂的组分也相同,仅助剂仅配比不同。但实施例6提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均优于实施例4和5的水平。说明通过对各助剂的配比进行进一步的调整和优化,使得本发明提供的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
实施例6与实施例9,分别采用了相同的原料,但实施例9应用本发明提供的制备方法对调湿净化材料进行制备,实施例9提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均分别优于实施例6的水平。说明在原料相同的条件下,应用本发明提供的制备方法制备得到的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
实施例7、实施例8以及实施例9,均分别采用了相同的原料和相同的制备方法进行制备,仅制备的条件参数不同。但实施例9提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均分别优于实施例7和8的水平。说明在原料和方法相同的条件下,应用本发明提供的优选制备方法制备得到的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
实施例3与对比例1-7提供的调湿净化材料,其相同组分的配比相同,但对比例1中缺少硅藻土、对比例2中缺少蛭石粉、对比例3中缺少珍珠岩粉、对比例4中缺少乙烯脲、对比例5中缺少植物纤维、对比例6中缺少易溶盐、对比例7中缺少负离子粉。实施例3提供的调湿净化材料无论在调湿效果、调湿速度或容湿量的方面均优于对比例1-7的水平。说明在相同原料组分的配比相同的情况下,只有通过各原料特定组分之间的协同配合,才能使得本发明提供的调湿净化材料具有更好的调湿作用,容湿量更大,调湿更迅速。
二、依据JC/T1074-2008《室内空气净化功能涂覆材料净化性能》对本发明实施例1-10及对比例1-7提供的调湿净化材料进行检测。涂抹量:1.5kg/m2或者涂抹厚度约为2mm其检测标准如表3所示,检测结果如表4所示。
表3室内空气净化功能涂覆材料净化性能检测标准
表4调湿净化材料检测结果
从上述结果中可以看出,本发明实施例1-9提供的调湿净化材料,通过各特定组分和配比之间的协同配合,使得本发明提供的调湿净化材料能够有效吸附并分解甲醛,克服传统的物理吸附除甲醛达饱和之后会释放甲醛的问题。利用其强大的吸附能力,能够去除空气中的异味,净化空气,解决室内、车内空间异味大的烦恼。而对比例1-7提供的调湿净化材料,在空气净化效率或持久性的方面,其效果均不及本发明实施例的水平。
其中,实施例1-3提供的调湿净化材料,其原料组分完全相同,仅配比不同。但实施例3提供的调湿净化材料无论在去除有害物质或净化空气的方面均优于实施例1和2的水平。说明通过对各组分的配比进行进一步的调整和优化,使得本发明提供的调湿净化材料使得本发明提供的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实施例3与实施例6提供的调湿净化材料,其相同组分的配比相同,但实施例6中添加了抗菌剂、硅烷偶联剂、胶凝材料和负离子激发剂作为助剂。但实施例6提供的调湿净化材料无论在去除有害物质或净化空气的方面均优于实施例3的水平。说明通过添加合适的助剂,与原料进行进一步的协同作用,使得本发明提供的调湿净化材料使得本发明提供的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实施例4-6提供的调湿净化材料,其原料组分和配比完全相同,助剂的组分也相同,仅助剂仅配比不同。但实施例6提供的调湿净化材料无论在去除有害物质或净化空气的方面均优于实施例4和5的水平。说明通过对各助剂的配比进行进一步的调整和优化,使得本发明提供的调湿净化材料使得本发明提供的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实施例6与实施例9,均分别采用了相同的原料,但实施例9应用本发明提供的制备方法对调湿净化材料进行制备,实施例9提供的调湿净化材料无论在去除有害物质或净化空气的方面均分别优于实施例6的水平。说明在原料相同的条件下,应用本发明提供的制备方法制备得到的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实施例7、实施例8以及实施例9,均分别采用了相同的原料和相同的制备方法进行制备,仅制备的条件参数不同。但实施例9提供的调湿净化材料无论在去除有害物质或净化空气的方面均分别优于实施例7和8的水平。说明在原料和方法相同的条件下,应用本发明提供的制备方法制备得到的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实施例3与对比例1-7提供的调湿净化材料,其相同组分的配比相同,但对比例1中缺少硅藻土、对比例2中缺少蛭石粉、对比例3中缺少珍珠岩粉、对比例4中缺少乙烯脲、对比例5中缺少植物纤维、对比例6中缺少易溶盐、对比例7中缺少负离子粉。实施例3提供的调湿净化材料无论在去除有害物质或净化空气的方面均优于对比例1-7的水平。说明在相同原料组分的配比相同的情况下,只有通过各原料特定组分之间的协同配合,才能使得本发明提供的调湿净化材料能够更有效吸附并分解甲醛,去除空气中的异味,净化空气。
实验例2板状材料指标
根据实验例1的结果可知,本发明实施例9提供的调湿净化材料在调湿和净化方面的效果均略高于其他组。因此,为节约实验成本,本实验例应用实施例9提供的调湿净化材料制备成尺寸规格为1500*900mm的板型产品,并依据JC/T2082-2011《调湿功能室内建筑装饰材料》Ⅲ类和JC/T2188-2013《室内空气净化吸附材料净化性能》对该板型产品进行检测,检测标准和检测结果如表5所示。
表5检测标准及结果
从上述检测结果中可以看出,应用本发明实施例9提供的调湿净化材料制备得到的版型材料,同样具有良好的调湿作用,容湿量大,调湿迅速。在湿度大时能够有效吸湿,在环境干燥时,能够利用自身储存的水分加湿。并且,能够有效吸附并分解甲醛,克服传统的物理吸附除甲醛达饱和之后会释放甲醛的问题。利用其强大的吸附能力,能够去除空气中的异味,净化空气,解决室内、车内空间异味大的烦恼。本发明提供的调湿净化材料适用于各种需要调节空气质量及湿度的环境。
最后应说明的是:以上各实施例仅用以说明本发明的技术方案,而非对其限制;尽管参照前述各实施例对本发明进行了详细的说明,本领域的普通技术人员应当理解:其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分或者全部技术特征进行等同替换;而这些修改或者替换,并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
1.一种调湿净化材料,其特征在于,所述调湿净化材料包括如下重量份的原料:
硅藻土200-250份、蛭石粉50-100份、珍珠岩粉50-100份、乙烯脲30-60份、植物纤维20-40份、易溶盐20-40份和负离子粉15-25份。
2.根据权利要求1所述的调湿净化材料,其特征在于,所述调湿净化材料包括如下重量份的原料:
硅藻土210-240份、蛭石粉60-90份、珍珠岩粉60-90份、乙烯脲35-55份、植物纤维25-35份、易溶盐25-35份和负离子粉17-23份;
优选地,所述调湿净化材料包括如下重量份的原料:
硅藻土220-230份、蛭石粉70-80份、珍珠岩粉70-80份、乙烯脲40-50份、植物纤维28-32份、易溶盐28-32份和负离子粉19-21份。
3.根据权利要求1或2所述的调湿净化材料,其特征在于,所述调湿净化材料还包括抗菌剂1-5份,优选为1-4份,更优选为1-3份;
优选地,所述抗菌剂为无机抗菌剂;
优选地,所述抗菌剂包括纳米银离子、氧化锌、氧化铜、磷酸二氢铵或碳酸锂中的一种或多种。
4.根据权利要求1或2所述的调湿净化材料,其特征在于,所述调湿净化材料还包括硅烷偶联剂5-10份,优选为6-8份;
优选地,所述硅烷偶联剂包括乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷或乙烯基三(β-甲氧乙氧基)硅烷中的一种或多种。
5.根据权利要求1或2所述的调湿净化材料,其特征在于,所述调湿净化材料还包括胶凝材料500-550份,优选为510-540份,更优选为520-530份;
优选地,所述胶凝材料为无机胶凝材料;
优选地,所述无机胶凝材料包括石灰、石膏或水泥中的一种或多种。
6.根据权利要求1或2所述的调湿净化材料,其特征在于,所述调湿材料还包括负离子激发剂10-30份,优选15-25份,更优选18-22份;
优选地,所述负离子激发剂为发光材料;
优选地,所述发光材料包括荧光粉或过度金属氧化物。
7.如权利要求1-6任一项所述的调湿净化材料的制备方法,其特征在于,所述制备方法包括:
将配方量的各组分混合均匀,活化后,调整堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
8.根据权利要求7所述的制备方法,其特征在于,当堆积密度小于0.5g/cm3时,采用胶凝材料或重钙粉进行调整,当堆积密度大于1.0g/cm3时,采用珍珠岩粉进行调整;
优选地,所述制备方法包括如下步骤:
(a)向配方重量份的硅藻土、蛭石粉、珍珠岩粉和易溶盐中加入硅烷偶联剂混合均匀,得到活化吸附载体粉;
(b)向所述活化吸附载体粉中加入配方量的乙烯脲、植物纤维和抗菌剂,混合均匀得到复合载体粉;
(c)向所述复合载体粉中加入配方量的负离子粉和负离子激发剂,混合均匀得到复合调湿净化粉;
(d)调整所述复合调湿净化粉的堆积密度为0.5-1.0g/cm3,得到所述调湿净化材料。
9.如权利要求1-6任一项所述的调湿净化材料或应用权利要求7或8所述的制备方法制备得到的调湿净化材料在制备建筑材料或装饰品中的应用。
10.应用权利要求1-6任一项所述的调湿净化材料或应用权利要求7或8所述的制备方法制备得到的调湿净化材料制备得到的产品。