CN102399408A - Fiberglass reinforced black acrylonitrile-butadiene-styrene modified plastic capable of heat resistance and impact resistance, and its preparation method - Google Patents
Fiberglass reinforced black acrylonitrile-butadiene-styrene modified plastic capable of heat resistance and impact resistance, and its preparation method Download PDFInfo
- Publication number
- CN102399408A CN102399408A CN2010102762463A CN201010276246A CN102399408A CN 102399408 A CN102399408 A CN 102399408A CN 2010102762463 A CN2010102762463 A CN 2010102762463A CN 201010276246 A CN201010276246 A CN 201010276246A CN 102399408 A CN102399408 A CN 102399408A
- Authority
- CN
- China
- Prior art keywords
- styrene
- acrylonitrile
- butadiene
- impact
- abs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fiberglass reinforced black acrylonitrile-butadiene-styrene modified plastic capable of heat resistance and impact resistance, and its preparation method, which solves the problem of poor impact resistance of fiberglass reinforced composite material and simultaneously increases the heat resistance of a composite system. According to the invention, heat resistance and compatibility can be enhanced by adding multiunit random copolymers like heatproof styrene and maleimide, the rigidity can be raised by adding alkali-free staple glass fiber, and the linear expansion coefficient and molding shrinkage of the material can be reduced, simultaneously the impact resistance of a whole system can be improved by adding a silica acrylic acid system impact resistance modifier with small influence on mechanical property and heat resistance. The invention solves the problem that the impact resistance is rapidly decreased when the heat resistance and rigidity are raised. The method of the invention has the advantage of simple and clear technical scheme, and large scale production can be carried out.
Description
Technical field
The present invention relates to a kind of modified plastic material and preparation method thereof, particularly relate to a kind of heat-resisting, anti-impact, the strong black acrylonitrile-butadiene-styrene (ABS) of spun glass (ABS) modified plastics and preparation method thereof.
Background technology
Spun glass strengthens acrylonitrile-butadiene-styrene (ABS) (ABS) matrix material, is to be matrix with the acrylonitrile-butadiene-styrene (ABS), is the matrix material that strongthener is processed with the spun glass, combines the performance of acrylonitrile-butadiene-styrene (ABS) and spun glass.Acrylonitrile-butadiene-styrene (ABS) is broad-spectrum thermoplastic engineering plastic, is applied to fields such as machinery, electronics, electric, instrument, household electrical appliance, military project.But its bending stretch intensity is lower, and thermotolerance is not enough, does not reach the application requiring of acrylonitrile-butadiene-styrene (ABS) aspect automobile.Spun glass strengthens vinyl cyanide-butadiene-vinyl benzene composite material and has good comprehensive performances, and intensity is high, good rigidly, good moldability, dimensional stabilizing.Simultaneously, add the heat-drawn wire that spun glass can suitably improve matrix material, increase substantially tensile property, reduce the coefficient of linear expansion and the molding shrinkage of material.But because the interpolation of spun glass, shock strength obviously descends.
Strengthen the lifting of the overall performance of vinyl cyanide-butadiene-vinyl benzene composite material for spun glass, had a large amount of research carrying out.For promoting the associativity between spun glass and the acrylonitrile-butadiene-styrene resin matrix, some patents have proposed solution.Set forth fiberglass surfacing and be through one or more blend of the vinyl toluene that contains epoxide group or vinyl cyanide and vinylbenzene, nucleocapsid structure, αJia Jibenyixi, TEB 3K and handled.Document is mainly paid close attention to processing characteristics, apparent roughness and aberration, and after so handling, apparent and aberration improves.For example; C1-12 straight-chain dicarboxylic acid tin alkyl with 0.1% to 5% (dibutyl tin maleate, maleic acid dioctyl tin) or C1-12 loop chain di-carboxylic acid organo-tin compound coupling agent; Join graft rubber and vinylbenzene, in the system of vinylbenzene/vinyl toluene/acrylonitrile copolymer.This system still demonstrates good processing characteristics, good anti-impact and resistance toheat when the spun glass that adds 20%.In the case of over-all properties the best, unnotched impact strength (a
n RT) be 22KJ/m
2, notched Izod impact strength (a
k RT) be 9.1KJ/m
2, Vicat B is 108 ℃.Some document descriptions in a kind of acrylonitrile-butadiene-styrene resin, add spun glass and a kind of silicone couplet (β-(3 that contains epoxide group; The 4-epoxy cyclohexane) ethyl trimethoxy silane; The reaction product of alicyclic epoxy and a kind of silane coupling agent), the acrylonitrile-butadiene-styrene (ABS) compound system that makes has higher draw tensile strength and resistance to impact shock.Bibliographical information is in the acrylonitrile-butadiene-styrene resin that the melt blending continuous bulk is produced; Add the compatilizer atactic styrene-maleic anhydride copolymer, processing aid and alkali free glass fibre are prepared resin system excellent in cushion effect, that flexural strength is high.Best case is that heat-drawn wire is 101.5 ℃, and (ASTM D6481.82MPa, 6.4mm), cantilever beam impact strength is 11.5KJ/m under 21.6% the condition at the spun glass addition
2Bibliographical information is changed into the composite of atactic styrene-maleic anhydride copolymer and epoxy resin with compatilizer; The best system that obtains is 30% o'clock at spun glass, has obtained having fine intensity, toughness, resistance toheat, flowing property; Warpage is not floated fine good system.
In sum, no matter be to add various coupling agents, the glass surface treatment still adds compatilizer, all is conceived to increase the bonding force of spun glass and matrix resin.Through increasing bonding force, reach the purpose of improving erosion-resisting characteristics, raising thermotolerance and improving tensile property, this means are very limited after all to the lifting of thermotolerance and erosion-resisting characteristics after all.The present invention is guaranteeing for improving its thermotolerance and erosion-resisting characteristics a suitable method of operating to be provided under processing characteristics and the apparent condition.
Summary of the invention
Technical problem to be solved by this invention is that to overcome common acrylonitrile-butadiene-styrene (ABS) ABS tensile strength lower; The problem that thermotolerance is relatively poor; Adopt spun glass enhancing acrylonitrile-butadiene-styrene (ABS) and heat-proof modifier to improve tensile strength and thermotolerance; Simultaneously, adopt special heat-proof impact-resistant agent to improve the shock resistance of system.Certainly, the resin system of gained also need be considered apparent anchor.
For addressing the above problem, the technical scheme that the present invention adopts is following:
A kind of heat-resisting, anti-impact, glass strengthen black acrylonitrile-butadiene-styrene (ABS) modified plastics, it is characterized in that component is represented mainly to comprise by weight:
Acrylonitrile-butadiene-styrene (ABS) 60-85
Spun glass 2-18
Black agglomerate 1.8-3.0
Compatilizer 4-7
Heat-proof modifier 4-12
Impact modifier 2-10
Oxidation inhibitor 0.2-0.3
High bright dispersion agent 0.09-0.15
Lubricant 0.5-1
Described heat-resisting, anti-impact glass enhancing black acrylonitrile-butadiene-styrene (ABS) modified plastics is characterized in that described glass is the alkali-free short glass fiber, has passed through coupling agent treatment, and length is 3.0-4.5 millimeter filament diameter 13-14 μ m; Described black agglomerate is the acrylonitrile-styrene black masterbatch pellet of 50% carbon black content; Described heat-proof modifier is vinylbenzene, vinyl cyanide, imido random copolymers, and its heat-drawn wire is greater than 120 ℃, and second-order transition temperature is 145-155 ℃; Described impact modifier is the silicon oleic series anti-impact agent of nucleocapsid structure, and rubber constituent is the silicon acrylic rubber, the stone structure of outer grafting SAN resin; Described compatilizer is styrene-grafted copolymer-maleic anhydride; Described oxidation inhibitor is tricresyl phosphite (2, the 4-di-tert-butyl-phenyl) esters (Ciba IRGAFOS 168) and four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters (Ciba IRGANOX 1010); The bright dispersion agent of described height is for being the terminal carboxyl polyester (CH-1A of ShangHai SanZheng polymer Materials Co., Ltd) of anchoring group with amido and alkalimetal ion, and molecular weight is 1000~10000; Described lubricant is pentaerythritol stearate or ethylene bis stearamide.
A kind of heat-resisting, anti-impact glass strengthens the preparation method of black acrylonitrile-butadiene-styrene (ABS) modifying material; It is characterized in that; May further comprise the steps: acrylonitrile-butadiene-styrene (ABS) was dried 3-5 hour under 70-90 ℃ of condition; Spun glass 100-130 ℃ after dry 1-3 hour, spray the silane coupling agent of last 2% (wt%), continued then under 100-130 ℃ of condition dry 3-5 hour.Take by weighing 60-85 part acrylonitrile-butadiene-styrene (ABS), the acrylonitrile-styrene black agglomerate of 1.8-3.0 part, the styrene-grafted copolymer-maleic anhydride of 4-7 part; 4-12 part vinylbenzene, vinyl cyanide, imido random copolymers; The silicon oleic series anti-impact agent of 2-10 part nucleocapsid structure, 0.2-0.3 part tricresyl phosphite (2, the 4-di-tert-butyl-phenyl) esters (Ciba IRGAFOS 168) and four [β-(3; The 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (Ciba IRGANOX1010); 0.09-0.15 part is the high bright dispersion agent of terminal carboxyl polyester of anchoring group with amido and alkalimetal ion, 0.5-1 part pentaerythritol stearate or ethylene bis stearamide lubricant are in high-speed mixer and mixing 3-10 minute discharging; The spun glass that adds 2-18 part then, vibration mixes.Above-mentioned blend composition is added in the twin screw extruder, granulating and forming, processing temperature is 145~230 ℃, the twin screw rotating speed is 180 rev/mins.
A kind of heat-resisting, anti-impact glass strengthens the preparation method of black acrylonitrile-butadiene-styrene (ABS) modifying material; It is characterized in that; May further comprise the steps: acrylonitrile-butadiene-styrene (ABS) was dried 4 hours under 80 ℃ of conditions; Spun glass 100-130 ℃ drying was sprayed the silane coupling agent of last 2% (wt%) after 2 hours, continued then under 120 ℃ of conditions dry 4 hours.Take by weighing 63.43 parts of acrylonitrile-butadiene-styrene (ABS)s, 1.98 parts acrylonitrile-styrene black agglomerate, 6.94 parts styrene-grafted copolymer-maleic anhydride; 9.91 part vinylbenzene, vinyl cyanide, imido random copolymers; 6.94 the silicon oleic series anti-impact agent of part nucleocapsid structure, 0.1 part of tricresyl phosphite (2, the 4-di-tert-butyl-phenyl) ester (Ciba IRGAFOS 168) and 0.2 part of four [β-(3; The 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (Ciba IRGANOX 1010); 0.1 part is the high bright dispersion agent of terminal carboxyl polyester of anchoring group with amido and alkalimetal ion, 0.2 part of pentaerythritol stearate and 0.3 part of ethylene bis stearamide lubricant are in high-speed mixer and mixing discharging in 10 minutes; The spun glass that adds 9.91 parts then, vibration mixes.Above-mentioned blend composition is added in the twin screw extruder, granulating and forming, processing temperature is 145~230 ℃, the twin screw rotating speed is 180 rev/mins.
This heat-resisting, anti-impact of the present invention, glass strengthen black acrylonitrile-butadiene-styrene (ABS) modifying material when keeping higher bending stretch performance, have than conventional glass fiber reinforcement acrylonitrile-butadiene-styrene resin and have the resistance to impact shock of better resistance toheat and Geng Jia.
Test is carried out according to each item standard of table 1.
Each performance test reference standard tabulation of table 1
Project | Standard |
Tensile strength | GB/T 1040-2006, speed 50mm/min |
Tensile modulus | GB/T?1040-2006 |
Flexural strength | GB/T 9341-2000, speed 2mm/min |
Modulus in flexure | GB/T?9341-2000 |
Heat-drawn wire | GB/T 1634.2-2004 keeps flat, load 1.80MPa, 120 ℃/h |
Cantilever beam impact strength | GB/T 1843-2008, the 1J pendulum |
Simple beam impact strength | GB/T 1043.1-2008, the 1J pendulum |
Embodiment
Further specify the present invention through embodiment and Comparative Examples below, do not violating under the aim condition of the present invention, the present invention should be not limited to following experimental example and specifically show content clearly.
(1) embodiment 1-3 and Comparative Examples 2 mainly are that the different glass amounts of assessment add the influence to system.Embodiment 1, and embodiment 2, Comparative Examples 2, and embodiment 3 glass ratios are respectively 2%, 5%, 10%, 15% of main body component (except processing aid and the oxidation inhibitor).Comparative Examples 3 is for to be replaced with impact modifier 2 with impact modifier 1, and impact modifier 1 is the agent of silicon acrylic acid series anti-impact, and impact modifier 2 is the anti-impact agent of polymethylmethacrylate-butadiene-styrene nucleocapsid structure.Each raw-material weight is as shown in table 1.Oven dry is advanced the twin screw extruder granulation after mixing, and processing temperature is 145~230 ℃, and the twin screw rotating speed is 180 rev/mins.
Table 2 embodiment 1-3 prescription and performance table
Can find out from above embodiment; Add spun glass and can significantly improve tensile property and bending property, thermal denaturation temperature is also had positive influence, but can reduce shock strength; But impact modifier 1 is compared with impact modifier 2; Impact-resistant modified effect is more obvious, and is simultaneously, also less to stable on heating influence.
(2) embodiment 4-5 and Comparative Examples 2 mainly are the influences of assessment impact modifier 1 different add-ons to system; Embodiment 6 is after impact modifier 1 is replaced with impact modifier 3; Contrast situation with Comparative Examples 2; Impact modifier 1 and 3 is all the agent of silicon acrylic acid series anti-impact, but the particle diameter of anti-impact agent 1 is bigger, and the particle diameter of anti-impact agent 3 is less.Embodiment 4, and embodiment 5, and Comparative Examples 2 impact modifiers 1 ratio is respectively 2%, 4%, 7% of main body component (except processing aid and the oxidation inhibitor).Each raw-material weight is as shown in table 1.Oven dry is advanced the twin screw extruder granulation after mixing, and processing temperature is 145~230 ℃, and the twin screw rotating speed is 180 rev/mins.
Table 3 embodiment 4-6 prescription and performance table
Can find out that from above embodiment impact modifier 1 is compared with impact modifier 3, impact-resistant modified effect is obvious, big than impact modifier 3 to the negative impact of mechanical property, but less to stable on heating influence not as impact modifier 3.
(3) embodiment 7-9 mainly is the influences of the different add-ons of assessment heat-proof modifier to system.Embodiment 7, and embodiment 8, and the ratio of embodiment 9 heat-proof modifiers is respectively 7%, 10%, 12% of main body component (except processing aid and the oxidation inhibitor).Each raw-material weight is as shown in table 1.Oven dry is advanced the twin screw extruder granulation after mixing, and processing temperature is 145~230 ℃, and the twin screw rotating speed is 180 rev/mins.
Table 4 embodiment 7-9 prescription and performance table
Can find out that from above embodiment heat-proof modifier promotes the system mechanical property, impacts decline.Heat-drawn wire has a more substantial increase.
Heat-resisting, anti-impact glass of the present invention strengthens black acrylonitrile-butadiene-styrene (ABS) modifying material owing to adopted heat-proof modifier and novel impact modifier; In the higher mechanical property of maintenance, have than conventional glass fiber reinforcement acrylonitrile-butadiene-styrene resin and have the resistance to impact shock of better resistance toheat and Geng Jia.
Claims (4)
1. heat-resisting, an anti-impact glass strengthens black acrylonitrile-butadiene-styrene (ABS) modified plastics, it is characterized in that component is represented mainly to comprise by weight:
Acrylonitrile-butadiene-styrene (ABS) 60-85
Spun glass 2-18
Black agglomerate 1.8-3.0
Compatilizer 4-7
Heat-proof modifier 4-12
Impact modifier 2-10
Oxidation inhibitor 0.2-0.3
High bright dispersion agent 0.09-0.15
Lubricant 0.5-1
2. heat-resisting, anti-impact glass enhancing black acrylonitrile-butadiene-styrene (ABS) modified plastics according to claim 1; It is characterized in that; Described glass is the alkali-free short glass fiber, has passed through coupling agent treatment, and length is 3.0-4.5 millimeter filament diameter 13-14 μ m; Described black agglomerate is the acrylonitrile-styrene black masterbatch pellet of 50% carbon black content; Described heat-proof modifier is vinylbenzene, vinyl cyanide, imido random copolymers, and its heat-drawn wire is greater than 120 ℃, and second-order transition temperature is 145-155 ℃; Described impact modifier is the silicon oleic series anti-impact agent of nucleocapsid structure, and rubber constituent is the silicon acrylic rubber, the stone structure of outer grafting SAN resin; Described compatilizer is styrene-grafted copolymer-maleic anhydride (SMA); Described oxidation inhibitor is tricresyl phosphite (2 ,-di-tert-butyl-phenyl) ester (Ciba IRGAFOS 168) and four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (Ciba IRGANOX 1010); The bright dispersion agent of described height is for being the terminal carboxyl polyester of anchoring group with amido and alkalimetal ion, and molecular weight is 1000~10000; Described lubricant is pentaerythritol stearate (PETS) or ethylene bis stearamide (EBS).
3. a kind of heat-resisting, anti-impact glass according to claim 1 and 2 strengthens the preparation method of black acrylonitrile-butadiene-styrene (ABS) modified plastics; It is characterized in that; May further comprise the steps: acrylonitrile-butadiene-styrene (ABS) was dried 3-5 hour under 70-90 ℃ of condition; Spun glass 100-130 ℃ after dry 1-3 hour, spray the silane coupling agent of last 2% (wt%), continued then under 100-130 ℃ of condition dry 3-5 hour.Take by weighing 60-85 part acrylonitrile-butadiene-styrene (ABS), the acrylonitrile-styrene black agglomerate of 1.8-3.0 part, the styrene-grafted copolymer-maleic anhydride of 4-7 part; 4-12 part vinylbenzene, vinyl cyanide, imido random copolymers; The silicon oleic series anti-impact agent of 2-10 part nucleocapsid structure, 0.2-0.3 part tricresyl phosphite (2, the 4-di-tert-butyl-phenyl) esters (Ciba IRGAFOS 168) and four [β-(3; The 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (Ciba IRGANOX 1010); 0.09-0.15 part is the high bright dispersion agent of terminal carboxyl polyester of anchoring group with amido and alkalimetal ion, 0.5-1 part pentaerythritol stearate or ethylene bis stearamide lubricant are in high-speed mixer and mixing 3-10 minute discharging; The spun glass that adds 2-18 part then, vibration mixes.Above-mentioned blend composition is added in the twin screw extruder, granulating and forming, processing temperature is 145~230 ℃, the twin screw rotating speed is 180 rev/mins.
4. a kind of heat-resisting, anti-impact glass according to claim 3 strengthens the preparation method of black acrylonitrile-butadiene-styrene (ABS) modified plastics; It is characterized in that; May further comprise the steps: acrylonitrile-butadiene-styrene (ABS) was dried 4 hours under 80 ℃ of conditions; Spun glass 100-130 ℃ drying was sprayed the silane coupling agent of last 2% (wt%) after 2 hours, continued then under 120 ℃ of conditions dry 4 hours.Take by weighing 63.43 parts of acrylonitrile-butadiene-styrene (ABS)s, 1.98 parts acrylonitrile-styrene black agglomerate, 6.94 parts styrene-grafted copolymer-maleic anhydride; 9.91 part vinylbenzene, vinyl cyanide, imido random copolymers; 6.94 the silicon oleic series anti-impact agent of part nucleocapsid structure, 0.1 part of tricresyl phosphite (2, the 4-di-tert-butyl-phenyl) ester (Ciba IRGAFOS 168) and 0.2 part of four [β-(3; The 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (Ciba IRGANOX 1010); 0.1 part is the high bright dispersion agent of terminal carboxyl polyester of anchoring group with amido and alkalimetal ion, 0.2 part of pentaerythritol stearate and 0.3 part of ethylene bis stearamide lubricant are in high-speed mixer and mixing discharging in 10 minutes; The spun glass that adds 9.91 parts then, vibration mixes.Above-mentioned blend composition is added in the twin screw extruder, granulating and forming, processing temperature is 145~230 ℃, the twin screw rotating speed is 180 rev/mins.