CN102398297A - Steel mesh sandwich ceramic product and manufacturing method thereof - Google Patents
Steel mesh sandwich ceramic product and manufacturing method thereof Download PDFInfo
- Publication number
- CN102398297A CN102398297A CN2011100417181A CN201110041718A CN102398297A CN 102398297 A CN102398297 A CN 102398297A CN 2011100417181 A CN2011100417181 A CN 2011100417181A CN 201110041718 A CN201110041718 A CN 201110041718A CN 102398297 A CN102398297 A CN 102398297A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- internal mold
- bake
- kiln
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a steel mesh sandwich ceramic product and a manufacturing method thereof and relates to a ceramic product and a manufacturing method thereof. The invention discloses the ceramic product and the manufacturing method thereof. A steel mesh sandwich is added into the ceramic product to fulfill the aims of improving the strength of the ceramic product and reducing breakage. The manufacturing method comprises the following steps of: applying cut mud blanks and steel mesh outside an inflated inner die layer by layer, wherein for the circular product, a synchronous three-roll rolling roller can be used to tightly attach the mud blanks, the steel mesh and the inner die, and for the non-circular product, a beating plate can be used to tightly beat the mud blanks, the steel mesh and the inner die; when the mud blanks are dried to the degree of meeting the requirement, extracting the air in the inner die to ensure the inner die to be shrunk, so that the inner die can be separated from blank bodies; and carrying out the subsequent processing programs which are the same with those of the common ceramic product.
Description
[technical field]
The present invention relates to a kind of ceramic and preparation method, especially steel wire sandwich ceramic and preparation method.
[background technology]
Existing ceramic all is pure ceramic body, and its resisting breakage ability is low, is prone to fragmentation, is difficult for long preservation.
[summary of the invention]
The purpose of this invention is to provide a kind of new ceramic and preparation method.It is in the ceramic porcelain body, to add the steel wire sandwich, improves the intensity of ceramic body with this, reduces breakage rate, reach can long preservation purpose.
For realizing above-mentioned purpose, steel wire sandwich ceramic of the present invention and preparation method are outside completely charged internal mold; Successively applying ointment or plaster and go up to cut out good moulded pottery not yet put in a kiln to bake and steel wire, is moulded pottery not yet put in a kiln to bake near the ground floor of internal mold, then is that steel wire is alternate and deposited with moulded pottery not yet put in a kiln to bake; But number of plies one deck, but also multilayer.For round goods, available synchronous three roller rolling rollings are real, and the outer contour of rolling roller coincide with the outer contour of inflation internal mold each other, like Fig. 1, Fig. 2, Fig. 3, Fig. 4, so just make the closely knit applying of moulded pottery not yet put in a kiln to bake, steel wire and internal mold, and thickness is even; For non-circular goods, available beating plate is patted closely knit getting final product.When treating that moulded pottery not yet put in a kiln to bake is dried to satisfactory degree, extract the air in the internal mold out, make its contraction, just can internal mold be separated with base substrate.Thereafter procedure is identical with common ceramic.
So-called synchronous three roller rolling rollers roll the driven rotation with the rotation of blank simultaneously be exactly 2, three the rolling rollers of coding among Fig. 3, Fig. 4 can squeeze to round blank center synchronously.
[description of drawings]
Below in conjunction with the accompanying drawing and the specific embodiment the present invention is done further detailed explanation.Wherein:
Fig. 1 is the inflation internal mold sketch map among the present invention.
Fig. 2 is the sketch map that moulded pottery not yet put in a kiln to bake and the steel wire among the present invention stacks.
Elevational schematic view when Fig. 3 is the synchronous three roller rolling rollers work among the present invention.
Floor map when Fig. 4 is the synchronous three roller rolling rollers work among the present invention.
The pairing parts of each digital marking are:
1-inflates internal mold;
2-rolling roller;
The 3-moulded pottery not yet put in a kiln to bake;
The 4-steel wire.
[specific embodiment]
Earlier roll into the moulded pottery not yet put in a kiln to bake 3 that thickness adheres to specification to raw mud on the mud machine rolling; Again steel wire 4 and moulded pottery not yet put in a kiln to bake 3 are cut into required shape on request; And overlay them on the placenta in certain sequence; Be placed on completely charged internal mold 1 on the steel wire 4 and moulded pottery not yet put in a kiln to bake 3 that stacks afterwards, moulded pottery not yet put in a kiln to bake 3 and steel wire 4 are successively applied ointment or plaster on internal mold 1.If circular goods, stick finish after, make the placenta rotation, synchronous three roller rolling rollers 2 are squeezed to the placenta center roll, the 2 passive rotations of rolling roller make moulded pottery not yet put in a kiln to bake 3, steel wire 4 and internal mold 1 closely knit applying; If be non-circular goods, available beating plate is patted closely knit getting final product.When treating that moulded pottery not yet put in a kiln to bake is dried to satisfactory degree, extract the air in the internal mold 1 out, make its contraction, just can internal mold 1 be separated with base substrate.Thereafter procedure is identical with common ceramic.
Claims (6)
1. steel wire sandwich ceramic and preparation method.Its goods are characterised in that: in the ceramic porcelain body, add steel wire sandwich (4), improve ceramic intensity to reach, reduce damaged purpose.Its method for production is characterised in that: outside completely charged internal mold (1), successively apply ointment or plaster to go up and cut out good moulded pottery not yet put in a kiln to bake (3) and steel wire (4), for round goods, available synchronous three roller rolling rollers (2) make moulded pottery not yet put in a kiln to bake (3), steel wire (4) and the closely knit applying of internal mold (1); For non-circular goods, available beating plate is patted closely knit getting final product.When treating that moulded pottery not yet put in a kiln to bake is dried to satisfactory degree, extract the air in the internal mold (1) out, make its contraction, just can internal mold (1) be separated with base substrate.Thereafter procedure is identical with common ceramic.
2. steel wire sandwich ceramic according to claim 1 is characterized in that: in the ceramic porcelain body, add one or more layers and cut out good steel wire sandwich (4) in advance.
3. the preparation method of steel wire sandwich ceramic according to claim 1 is characterized in that: use inflation internal mold (1) in the greenwave carcass, and when treating that moulded pottery not yet put in a kiln to bake is dried to satisfactory degree, the negative pressure of the bleeding demoulding.
4. the preparation method of steel wire sandwich ceramic according to claim 1 is characterized in that: for round goods, with synchronous three roller rolling rollers (2), make moulded pottery not yet put in a kiln to bake (3), steel wire (4) and the closely knit applying of internal mold (1).
5. the preparation method of steel wire sandwich ceramic according to claim 1; It is characterized in that: the outer contour of rolling roller (2) coincide mutually with the outer contour of inflation inner membrance (1); So just make moulded pottery not yet put in a kiln to bake (3), steel wire (4) and the closely knit applying of internal mold (1), and thickness is even.
6. the preparation method of steel wire sandwich ceramic according to claim 1 is characterized in that: the rolling direction of three rolling rollers (2) is all pointed to goods placenta center, and can advance and retreat synchronously.