CN102396813B - Burr pulling method for anti-slip gloves - Google Patents

Burr pulling method for anti-slip gloves Download PDF

Info

Publication number
CN102396813B
CN102396813B CN 201010285736 CN201010285736A CN102396813B CN 102396813 B CN102396813 B CN 102396813B CN 201010285736 CN201010285736 CN 201010285736 CN 201010285736 A CN201010285736 A CN 201010285736A CN 102396813 B CN102396813 B CN 102396813B
Authority
CN
China
Prior art keywords
pull
solution
burrs
burr
glove
Prior art date
Application number
CN 201010285736
Other languages
Chinese (zh)
Other versions
CN102396813A (en
Inventor
王昶
顾群
Original Assignee
王昶
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王昶 filed Critical 王昶
Priority to CN 201010285736 priority Critical patent/CN102396813B/en
Publication of CN102396813A publication Critical patent/CN102396813A/en
Application granted granted Critical
Publication of CN102396813B publication Critical patent/CN102396813B/en

Abstract

本发明涉及一种防滑手套的拉毛刺方法,包括以下步骤:(1)将棉胆浸渍在凝固剂溶液中,使棉胆上带有凝固剂溶液;(2)将处理后的棉胆浸渍到乳胶溶液中,使棉胆外表面形成一层乳胶膜,然后对其定型预干燥;(3)在加工槽内填充拉毛刺胶溶液,加工槽的搅拌板对拉毛刺胶溶液进行搅拌;(4)将棉胆上乳胶成膜的手套半成品浸渍到装有拉毛刺胶溶液的加工槽内,将手套取出后进一步硫化干燥处理,即为成品。 The present invention relates to a method of non-slip gloves pull burr, comprising the steps of: (1) impregnating the biliary cotton coagulation solution, the coagulation solution with cotton so bile; (2) bile processed cotton immersed latex solution, the outer surface of the cotton of the latex film layer bladder is formed, and then shaped to its pre-dried; (3) pull-filled gum solution in the processing tank burrs, processed groove was stirred for pulling plate gum solution was stirred burr; (4 ) glove latex film forming semifinished bladder cotton immersed with pull burrs gum solution processing tank, the glove is further removed after vulcanization drying treatment is finished. 本发明是一种设计合理、操作简单、实用性强、适合工业化生产时使用的防滑手套的拉毛刺方法,采用本方法生产出的防滑手套防滑效果好、使用安全可靠、表面毛刺分布均匀、花纹整齐美观、拉毛刺和未拉毛刺的分界线明显整齐、经久耐用,易于配对。 The present invention has reasonable design, simple, practical, burrs pull method used for anti-slip glove suitable for industrial production, the present process for producing a non-slip gloves slip effective, safe and reliable, uniform surface distribution of the burrs, the pattern neat appearance, pulling burrs and the burr unstretched clear boundary neat, durable and easy to match.

Description

防滑手套的拉毛刺方法 Pull method glitch slip gloves

技术领域 FIELD

[0001] 本发明涉及手套领域,尤其是防滑手套的拉毛刺方法。 [0001] The present invention relates to the field of a glove, in particular glove slip pull method burrs.

背景技术 Background technique

[0002] 在日常生活以及加工生产过程中人们经常使用手套,现有的手套表面通常比较光滑,人们戴着这种手套搬抬物品或作业时,物品容易从手上滑脱掉到地上被摔坏,这样既造成物品损坏,又容易砸伤搬运物品的人;此外,在作业时由于手套不具有防滑性能、摩擦力小,因此使用工具时容易产生不稳定,吃不上力气,影响作业效率。 [0002] When used often in everyday life and working gloves production process, the conventional glove surface is generally smoother, people wearing the glove in lifting operations or an article, the article is easy to fall to the ground from the hands slip was cast bad, then it will cause property damage, and easy to carry items of injured people; in addition, the glove does not have a job due to the slip resistance, friction is small, and therefore prone to instability when using a tool, could not get the strength, influence operational efficiency. 为了克服以上缺陷,防止物品掉落,保证作业时便捷稳定,目前已经出现了一种防滑的手套,这种手套的手指、掌心以及手背处均制出防滑毛刺,毛刺增加了手套的摩擦力,在一定程度上可以防止物品在搬运过程中掉落以及提高作业工具的使用效率。 To overcome these shortcomings, to prevent items from falling, to ensure convenient and stable job, now there is a non-slip gloves, the glove fingers, palm and back of the hand are made out of non-slip burr burr increases the friction gloves, to a certain extent can prevent the article from falling and improving the efficiency of the work tool during handling. 不过受加工工艺的限制,现有的这种防滑手套表面所制出的毛刺分布不均匀,虽然可以起到一定的防滑作用,但是效果并不特别明显。 However, the process is limited, a conventional non-slip surface of the glove produced an uneven distribution of the burrs, although can play a role in anti-skid, but the effect is not particularly significant. 此外,手套表面所拉出的毛刺没有花纹,不但影响美观,而且还很难找到两个外形相近的拉毛刺手套进行配对使用或者出售。 Further, the glove surface without burrs drawn pattern, not only affects the appearance, but also difficult to find the two pull burr shape similar gloves paired or sold.

发明内容 SUMMARY

[0003] 本发明的目的在于克服现有技术的不足,提供一种操作简单、设计合理的拉毛刺方法,采用本方法所制得的防滑手套表面毛刺分布均匀、花纹整齐美观、适合配对出售且防滑效果好。 [0003] The object of the present invention is to overcome the disadvantages of the prior art, there is provided a simple, rational design methods pull burrs, prepared by this method the surface of non-slip gloves burr distribution, neat appearance pattern, and adapted to mate with the sale non-slip effect.

[0004] 本发明解决其技术问题是通过以下技术方案实现的: [0004] The present invention to solve the technical problem is achieved by the following technical solution:

[0005] 一种防滑手套的拉毛刺方法,其特征在于:包括以下步骤: [0005] A method for pulling burrs slip glove, characterized by: comprising the steps of:

[0006] (I)将手套棉胆套装在模具上,将棉胆浸溃在凝固剂溶液中,使棉胆带有凝固剂溶液; [0006] (I) The cotton glove on the mold set gall, gall cotton impregnated in the coagulant solution, so that the coagulation solution with a cotton bladder;

[0007] (2)将浸溃了凝固剂的棉胆浸溃到乳胶溶液中,使棉胆外表面形成一层乳胶膜,然后对手套半成品进行预干燥定型处理直至其表面的乳胶膜处于半干状态; [0007] (2) The cotton impregnated a bile coagulant dipping into the latex solution, the outer surface of the latex film layer bladder is formed of cotton, and then pre-dried semi-finished glove routine processing until an emulsion surface of the film in a semi- dry state;

[0008] (3)在加工槽内填充拉毛刺胶溶液,加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行均匀搅拌; [0008] (3) in the processing solution tank filled gum pull burrs, stirred tank process implementing forward and backward through the plate back to pull the burr gum solution was uniformly stirred;

[0009] (4)将乳胶成膜的手套半成品浸溃到装有拉毛刺胶溶液的加工槽内,然后将表面涂覆了拉毛刺胶溶液的手套半成品取出后,进一步进行干燥和硫化处理,即为成品。 [0009] (4) The film formation of the latex glove impregnated semifinished product to pull burrs with a gum solution processing tank, and then the coated surface of the gum solution pull burrs removed semifinished glove, further dried and vulcanized, It is finished.

[0010] 而且,所述步骤(I)中的凝固剂通常为氯化钙或者硝酸钙或者其他盐类凝固剂,其溶剂为甲醇。 [0010] Further, the step (I) is generally the coagulant is calcium chloride or calcium nitrate or other salts coagulant, which solvent is methanol.

[0011] 而且,步骤(2)中的乳胶溶液是天然乳胶溶液或者丁腈乳胶溶液。 [0011] Further, a latex solution of step (2) is a solution of natural latex or nitrile latex solution.

[0012] 而且,所述步骤(3)中的拉毛刺胶溶液可以是天然乳胶拉毛刺胶,其胶粒粒径为40〜60mesh,浓度为13%〜16% ;拉毛刺胶溶液也可以是丁腈乳胶拉毛刺胶,其胶粒粒径为50〜80mesh,浓度为14%〜17%。 [0012] Further, the step of pulling the gum solution burrs (3) may be a natural latex rubber pull burrs, which rubber particle diameter 40~60mesh, concentration of 13% ~ 16%; pull gum solution may be a glitch nitrile rubber latex pull burrs, which rubber particle diameter 50~80mesh, concentration of 14% ~ 17%.

[0013] 而且,所述步骤(3)中加工槽的槽体上端的两侧分别安装一导轨,该两个导轨之间导向滑动安装一横梁,该横梁的中部安装在一液压缸的柱塞杆上,该横梁下端制出一位于槽体内的搅拌板。 [0013] Further, the step (3) on both sides of the upper end of the groove processing are attached to a guide groove, a beam guide is slidably mounted between the two rails, the middle of the cross member is mounted in a piston cylinder rod, the lower end of the cross plate is made out of a stirred tank body.

[0014] 而且,所述搅拌板的上部制出一组并排设置的矩形通孔,每个矩形通孔的高度均为搅拌板高度的一半,每个矩形通孔的宽度均为2cm,相邻两个矩形通孔之间的间距为4cm;搅拌板的下部制出一矩形回流孔,该矩形回流孔的最上端与矩形通孔的最下端之间的间距为2cm,矩形回流孔与搅拌板左右两侧边的间距均为2cm,矩形回流孔与搅拌板底边的间距为1cm。 [0014] Further, an upper portion of the stirring plate is made out of a set of juxtaposed rectangular through hole, the height of each rectangular through hole are stirred for half of the height of the plate, the width of each rectangular through-holes are 2cm, adjacent the distance between the two rectangular through hole is 4cm; lower stirring plate made out of a rectangular return hole, the spacing between the uppermost and lowermost rectangular through hole of the rectangular hole is refluxed 2cm, rectangular hole was stirred at reflux for plate left and right side edges of the spacing are 2cm, return hole pitch rectangular base plate with stirring for 1cm.

[0015] 而且,所述的搅拌板正向水平推行速度为20cm/s〜25cm/s ;搅拌板的反向水平拉回速度为10cm/s〜15cm/s。 [0015] Further, the stirring board level implementation of the forward speed of 20cm / s~25cm / s; stirring speed reverse level back plate is 10cm / s~15cm / s.

[0016] 而且,所述步骤(4)中加工槽上升使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升时间为1.5s,手套半成品在拉毛刺胶溶液中浸溃时间为0.5〜5s,然后加工槽下降,下降时间为0.5s。 [0016] Further, the step (4) in the working tank rises glove impregnated semifinished burr pull the gum solution in the processing tank, the groove machining rise time 1.5s, semi-finished glove was immersed in crushed gum pulling time glitches It is 0.5~5s, and then processed groove fall, fall time of 0.5s.

[0017] 而且,所述步骤(4)中手套半成品的硫化处理在105〜110°C的硫化干燥炉中进行,硫化干燥时间为40〜50min。 [0017] Further, the step (4) of semi-finished glove vulcanization process carried out at 105~110 ° C curing oven drying, the drying time of the vulcanization 40~50min.

[0018] 本发明的优点和有益效果为: [0018] The advantages and benefits of the present invention are:

[0019] 1、本拉毛刺方法中的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,搅拌后的拉毛刺胶溶液胶粒均匀,无漩涡,因此加工出的手套表面的毛刺花纹分布均匀,从而保证了本手套防滑效果明显,可以避免手上握持的东西掉落,防止物品摔坏以及砸伤使用者,提高作业工具的使用效率。 [0019] 1, the present method was stirred pull burr plate by implementing forward and backward to pull back the burr gum solution was stirred, uniform pulling burrs gum rubber stirred solution, no swirl, thus machined surface of the glove burrs distribution pattern, thus ensuring the present anti-slip glove obvious effect, to avoid falling hand grip things, prevent the article broke and injured by the user, to improve the efficiency of the work tool.

[0020] 2、采用本拉毛刺方法搅拌后的拉毛刺胶溶液无气泡、波动小,手套浸溃后从溶液中提拉的速度快,因此加工出的手套表面无花沟,拉毛刺与未拉毛刺的分界线明显整齐。 [0020] 2, using the method of the present pull pull burr after burr gum solution was stirred for bubble-free, small fluctuation, fast Gloves impregnated pulled from the solution velocity, thus machined without Huagou glove surface, and not pull burr pull clear dividing line glitches neat.

[0021] 3、采用本拉毛刺方法所制得的手套表面外形美观、毛刺分布均匀、一致性好,便于配对出售。 [0021] 3, the present method pull burrs resulting glove surface appearance, uniformity of distribution of the burrs, consistency, easy to sell pairs.

[0022] 4、本发明是一种设计合理、操作简单、实用性强、适合工业化生产时使用的防滑手套的拉毛刺方法,采用本方法生产出的防滑手套防滑效果好、使用安全可靠、能提高作业工具的使用效率。 [0022] 4, the present invention is a reasonable design, burrs pull method using a non-slip gloves is simple, practical, suitable for industrial production, the use of the present method produce good non-slip gloves anti-slip effect, safe and reliable, can improve the efficiency of the work tool. 此外,手套表面毛刺分布均匀、花纹整齐美观、质量好、经久耐用且适合配对出售。 Furthermore, the surface of the glove burr uniform distribution pattern neat appearance, good quality, durable and adapted to mate with the sale.

附图说明 BRIEF DESCRIPTION

[0023] 图1是防滑手套的主视图; [0023] FIG. 1 is a front view of a non-slip gloves;

[0024] 图2是加工槽的示意图; [0024] FIG. 2 is a schematic diagram of the processing tank;

[0025] 图3是图2中搅拌板和横梁的放大示意图。 [0025] FIG. 3 is an enlarged schematic view of the cross member and the plate of FIG. 2 with stirring.

具体实施方式 Detailed ways

[0026] 下面通过具体实施例对本发明作进一步详述,以下实施例只是描述性的,不是限定性的,不能以此限定本发明的保护范围。 [0026] The following specific embodiments of the present invention will be further described in detail, the following embodiments are merely illustrative, and not limiting, in order not to limit the scope of the present invention.

[0027] —种防滑手套的拉毛刺方法,其特征在于:包括以下步骤: [0027] - Pull Method burrs species slip glove, characterized by: comprising the steps of:

[0028] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂通常为氯化钙或者硝酸钙或者其他盐类凝固剂,其溶剂为甲醇。 [0028] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton gall coagulant solution, or the coagulant is calcium chloride is generally coagulant calcium nitrate or other salts, which solvent is methanol.

[0029] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液可以是天然乳胶溶液,也可以是丁腈乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0029] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, the solution may be a natural latex latex solution, the solution may be a nitrile latex, the outer surface of the bladder to form a layer having a certain cotton latex film thickness, and then pre-dried semi-finished glove routine processing of the film surface to which the latex is semi-dry state.

[0030] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液可以是天然乳胶拉毛刺胶,其胶粒粒径为40〜60mesh,浓度为13%〜16% ;拉毛刺胶溶液也可以是丁腈乳胶拉毛刺胶,其胶粒粒径为50〜80mesh,浓度为14%〜17%。 [0030] (3) in the processing solution tank filled gum pull burr, the burr pull gum solution may be natural rubber latex pull burrs, which rubber particle diameter 40~60mesh, concentration of 13% ~ 16%; pull glitch gum The solution may be a nitrile rubber latex pull burrs, which rubber particle diameter 50~80mesh, concentration of 14% ~ 17%.

[0031] 根据棉胆表面所形成的乳胶膜的不同,需要选取不同的拉毛刺胶溶液,如乳胶膜为天然乳胶膜时采用天然乳胶拉毛刺胶,乳胶膜为丁腈乳胶膜时,则采用丁腈乳胶拉毛刺胶。 When [0031] Depending on the latex film formed on the surface of the bladder cotton, need to select a different burr pull the gum solution, the latex film is employed as natural latex rubber burrs when pulling a film of natural latex, nitrile latex film is a film of latex, it is used nitrile rubber latex pull burrs.

[0032] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为20cm/s〜25cm/s,速度较快是为了促使沉淀在溶液下部的胶粒快速悬浮;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为lOcm/s〜15cm/s,速度较慢是为了抑制过快引起的漩涡以及气泡,溶液表面稳定;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0032] The board processed groove was stirred by forward and reverse implementation of the pull-back of burrs gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 20cm / s~25cm / s, faster in order to induce rapid precipitation of colloidal particles suspended in the lower portion of the solution; and then stirred for inverse horizontal back panel, which back is relatively slow, generally lOcm / s~15cm / s, in order to suppress excessive slow due to swirl and bubbles, stabilize the solution surface; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred.

[0033] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃0.5〜5s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s,快速下降有利于拉毛刺的表面形成花纹,均匀美观,拉毛刺和未拉毛刺的分界线明显整齐。 [0033] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 0.5~5s, then machining tank drops, which drops faster fall time of about 0.5s, the surface is conducive to the rapid decline of the pull-burr formation patterns, uniform appearance, pulling burrs and the burr unstretched clear boundary neat.

[0034] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入105〜110°C的硫化干燥炉中处理,硫化干燥40〜50min,最后将成型的手套从模具上取下即为手套成品I。 [0034] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed 105~110 ° C drying oven vulcanization process, the vulcanization dried 40~ 50min, and finally removing the molded glove is the finished glove from the mold I.

[0035] 以下对步骤(3)中所使用的加工槽结构进行详细描述,本说明书中每一实施例中所使用的加工槽均为此结构:加工槽包括一个矩形的槽体2,在槽体上端的两侧分别安装一导轨3,该两个导轨之间导向滑动安装一横梁4,该横梁的中部安装在一液压缸6的柱塞杆5上,该液压缸为油缸,横梁下端制出一位于槽体内的竖直的搅拌板7。 [0035] Hereinafter, the step of machining groove structure (3) used in the detailed description, examples machining tank used in the present specification, each structure of this embodiment are: a processing tank comprises a rectangular tank 2, the groove are attached to the both sides of the upper end of a rail 3, between the two guide rails 4 slidably mounted on a beam, the central beam is mounted on a cylinder of the plunger rod 56, the hydraulic cylinder is a cylinder, the lower end of beam system a body located in a groove 7 of a vertical stirring plate.

[0036] 在搅拌板上制作一套矩形孔,其保证了含有胶粒的拉毛刺在搅拌过程中胶粒分布均匀,搅拌过程不产生过多的涡流和气泡,使表面的防滑胶粒均匀,花纹美丽,该套矩形孔具体要求如下:搅拌板的上部制出一组并排设置的矩形通孔8,每个矩形通孔的高度均为搅拌板高度的一半,每个矩形通孔的宽度A均为2cm,相邻两个矩形通孔之间的间距B为4cm,矩形通孔的数量根据槽体的宽度进行设定。 [0036] Production of a rectangular hole in the stir plate, which ensures glitch pull micelles containing colloidal particles uniformly distributed in the mixing process, the mixing process does not produce too many bubbles and vortices, anti-slip rubber surface uniformly, beautiful patterns, the set of rectangular apertures requirements are as follows: the upper plate of the stirring produced a set of juxtaposed rectangular through hole 8, the height of each rectangular through hole are stirred for half the plate height, the width a of each rectangular through-hole are 2cm, the spacing B between two adjacent rectangular through hole is 4cm, the number of rectangular through hole is set according to the width of the tank body.

[0037] 搅拌板的下部制出一矩形回流孔9,该矩形回流孔的最上端与矩形通孔的最下端之间的间距C为2cm,矩形回流孔与搅拌板左右两侧边的间距D均为2cm,矩形回流孔与搅拌板底边的间距E为Icm,该矩形回流孔通常为一个。 A lower [0037] stirred a rectangular plate made of a return hole 9, the return hole of the rectangular clearance C between the uppermost end and the lowermost end of the through hole is rectangular 2cm, rectangular holes stirred at reflux for plate spacing around both sides of the D are 2cm, rectangular bottom plate was stirred at reflux for hole spacing E is Icm, which is generally a rectangular return hole.

[0038] 实施例1 [0038] Example 1

[0039] 一种防滑手套的拉毛刺方法,包括以下步骤: [0039] A method for pulling burrs slip glove, comprising the steps of:

[0040] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为氯化钙凝固剂,其溶剂为甲醇。 [0040] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium chloride coagulant , which solvent is methanol.

[0041] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是天然乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0041] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of natural latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the semi-finished glove pre-drying the latex styling treatment to the film surface thereof is in semi-dry state.

[0042] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是天然乳胶拉毛刺胶,其胶粒粒径为40mesh〜50mesh,浓度为16%。 [0042] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull natural latex rubber, which rubber particle diameter 40mesh~50mesh, concentration of 16%.

[0043] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为25cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为15cm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0043] Processing was stirred tank plate by implementing forward and reverse back to pull the burr gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 25cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, typically 15cm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0044] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃5s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0044] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 5s, and then machining tank drops, which drops faster fall time is approximately 0.5s.

[0045] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入105°C的硫化干燥炉中处理,硫化干燥50min,最后将成型的手套从模具上取下即为成品。 [0045] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in a 105 ° C drying oven vulcanization process, the vulcanization dried 50min, and finally molding is finished glove is removed from the mold.

[0046] 实施例2 [0046] Example 2

[0047] 一种防滑手套的拉毛刺方法,包括以下步骤: [0047] A method for pulling burrs slip glove, comprising the steps of:

[0048] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为氯化钙凝固剂,其溶剂为甲醇。 [0048] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium chloride coagulant , which solvent is methanol.

[0049] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是天然乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0049] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of natural latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the semi-finished glove pre-drying the latex styling treatment to the film surface thereof is in semi-dry state.

[0050] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是天然乳胶拉毛刺胶,其胶粒粒径为50〜60mesh,浓度为14%。 [0050] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull natural latex rubber, which rubber particle diameter 50~60mesh, concentration of 14%.

[0051] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为22cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为12cm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0051] The board processed groove was stirred by forward and reverse implementation of the pull-back of burrs gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 22cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, typically 12cm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0052] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃2s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0052] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 2s, then machining tank drops, which drops faster fall time is approximately 0.5s.

[0053] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入108°C的硫化干燥炉中处理,硫化干燥45min,最后将成型的手套从模具上取下即为成品。 [0053] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in a 108 ° C drying oven vulcanization process, the vulcanization dried for 45 min, and finally molding is finished glove is removed from the mold.

[0054] 实施例3 [0054] Example 3

[0055] 一种防滑手套的拉毛刺方法,包括以下步骤: [0055] A method for pulling burrs slip glove, comprising the steps of:

[0056] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为硝酸钙凝固剂,其溶剂为甲醇。 [0056] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium nitrate coagulant, The solvent which is methanol.

[0057] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是天然乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0057] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of natural latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the semi-finished glove pre-drying the latex styling treatment to the film surface thereof is in semi-dry state.

[0058] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是天然乳胶拉毛刺胶,其胶粒粒径为40mesh〜60mesh,浓度为13%。 [0058] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull natural latex rubber, which rubber particle diameter 40mesh~60mesh, concentration of 13%.

[0059] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为20cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为lOcm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0059] Processing was stirred tank plate by implementing forward and reverse back to pull the burr gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 20cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, generally lOcm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0060] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃0.5s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0060] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 0.5s, and then machining tank drops, which drops faster fall time is approximately 0.5s.

[0061] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入110°c的硫化干燥炉中处理,硫化干燥40min,最后将成型的手套从模具上取下即为成品。 [0061] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in 110 ° c drying oven vulcanization process, the vulcanization dried 40min, and finally molding is finished glove is removed from the mold.

[0062] 实施例4 [0062] Example 4

[0063] 一种防滑手套的拉毛刺方法,包括以下步骤: [0063] A method for pulling burrs slip glove, comprising the steps of:

[0064] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为氯化钙凝固剂,其溶剂为甲醇。 [0064] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium chloride coagulant , which solvent is methanol.

[0065] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是丁腈乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0065] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of nitrile latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the glove routine processing semi-finished pre-dried to an emulsion surface of the film in semi-dry state.

[0066] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是丁腈乳胶拉毛刺胶,其胶粒粒径为50mesh〜60mesh,浓度为16%。 [0066] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull nitrile rubber latex, rubber particle size which is 50mesh~60mesh, concentration of 16%.

[0067] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为20cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为lOcm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0067] Processing was stirred tank plate by implementing forward and reverse back to pull the burr gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 20cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, generally lOcm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0068] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃0.5s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0068] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 0.5s, and then machining tank drops, which drops faster fall time is approximately 0.5s.

[0069] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入105°C的硫化干燥炉中处理,硫化干燥50min,最后将成型的手套从模具上取下即为成品。 [0069] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in a 105 ° C drying oven vulcanization process, the vulcanization dried 50min, and finally molding is finished glove is removed from the mold.

[0070] 实施例5 [0070] Example 5

[0071] 一种防滑手套的拉毛刺方法,包括以下步骤: [0071] A method for pulling burrs slip glove, comprising the steps of:

[0072] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为硝酸钙凝固剂,其溶剂为甲醇。 [0072] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium nitrate coagulant, The solvent which is methanol.

[0073] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是丁腈乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0073] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of nitrile latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the glove routine processing semi-finished pre-dried to an emulsion surface of the film in semi-dry state. [0074] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是丁腈乳胶拉毛刺胶,其胶粒粒径为60mesh〜70mesh,浓度为14%。 [0074] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull nitrile rubber latex, rubber particle size which is 60mesh~70mesh, concentration of 14%.

[0075] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为23cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为13cm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0075] Processing was stirred tank plate by implementing forward and reverse back to pull the burr gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 23cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, typically 13cm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0076] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃3s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0076] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 3s, then machining tank drops, which drops faster fall time is approximately 0.5s.

[0077] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入105°C的硫化干燥炉中处理,硫化干燥50min,最后将成型的手套从模具上取下即为成品。 [0077] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in a 105 ° C drying oven vulcanization process, the vulcanization dried 50min, and finally molding is finished glove is removed from the mold.

[0078] 实施例6 [0078] Example 6

[0079] 一种防滑手套的拉毛刺方法,包括以下步骤: [0079] A method for pulling burrs slip glove, comprising the steps of:

[0080] (I)将手套棉胆套装在模具上,将套装在模具上的棉胆浸溃在凝固剂溶液中,使棉胆浸溃上凝固剂溶液,该凝固剂为氯化钙凝固剂,其溶剂为甲醇。 [0080] (I) The cotton glove bladder set on the mold in the mold to suit bile cotton impregnated in the coagulant solution, so that the impregnated cotton bile coagulation solution, the coagulant is calcium chloride coagulant , which solvent is methanol.

[0081] (2)将浸溃了凝固剂溶液的棉胆浸溃到乳胶溶液中,该乳胶溶液是丁腈乳胶溶液,使棉胆外表面形成一层具有一定厚度的乳胶膜,然后对手套半成品进行预干燥定型处理至其表面的乳胶膜处于半干状态。 [0081] (2) The impregnated cotton gall coagulant solution to the latex dipping solution, and the latex solution is a solution of nitrile latex, the outer surface of the bladder is formed of cotton of the latex film layer having a certain thickness, then the glove routine processing semi-finished pre-dried to an emulsion surface of the film in semi-dry state.

[0082] (3)在加工槽内填充拉毛刺胶溶液,该拉毛刺胶溶液是丁腈乳胶拉毛刺胶,其胶粒粒径为60mesh〜80mesh,浓度为17%。 [0082] (3) filled in the processing tank burr pull the gum solution, the gum solution is a pull burr burr pull nitrile rubber latex, rubber particle size which is 60mesh~80mesh, concentration of 17%.

[0083] 加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行搅拌,加工槽的搅拌板先从加工槽的一侧向另一侧正向水平推行,其推行速度相对较快,通常为25cm/s ;然后搅拌板反方向水平拉回,其拉回速度相对较慢,通常为15cm/s ;搅拌板的水平往复移动可将加工槽内的拉毛刺胶溶液搅拌均匀。 [0083] Processing was stirred tank plate by implementing forward and reverse pull-back of the burrs gum solution was stirred, a stirred tank process starting at one side plate of the machining tank implement forward horizontally to the other side, which relative speed implementation faster, typically 25cm / s; and then stirred for inverse horizontal back panel, which back is relatively slow, typically 15cm / s; horizontal reciprocating plate agitation pull burr processing tank the gum solution can be uniformly stirred .

[0084] (4)加工槽上升,使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升速度较慢,其上升时间大约为1.5s,将手套半成品在拉毛刺胶溶液中浸溃5s,然后加工槽下降,其下降速度较快,下降时间大约为0.5s。 [0084] (4) working tank rises, semi-finished glove impregnated burr pulling the gum solution in the processing tank, the processing tank rises slower rise time of about 1.5s, semi-finished glove pull glitch in the gum solution dipping 5s, and then machining tank drops, which drops faster fall time is approximately 0.5s.

[0085] 将表面涂覆了拉毛刺胶溶液的手套半成品进一步进行预干燥处理,直至其表面的拉毛刺胶基本固化,然后放入110°C的硫化干燥炉中处理,硫化干燥50min,最后将成型的手套从模具上取下即为成品。 [0085] The surface-coated gloves semi pull burrs gum solution further pre-drying process, until the pull burrs substantially cured rubber surface, and then placed in a 110 ° C drying oven vulcanization process, the vulcanization dried 50min, and finally molding is finished glove is removed from the mold.

Claims (8)

1.一种防滑手套的拉毛刺方法,其特征在于:包括以下步骤: (1)将手套棉胆套装在模具上,将棉胆浸溃在凝固剂溶液中,使棉胆带有凝固剂溶液; (2)将浸溃了凝固剂的棉胆浸溃到乳胶溶液中,使棉胆外表面形成一层乳胶膜,然后对手套半成品进行预干燥定型处理直至其表面的乳胶膜处于半干状态; (3)在加工槽内填充拉毛刺胶溶液,加工槽的搅拌板通过正向推行和反向拉回对拉毛刺胶溶液进行均匀搅拌,搅拌板的上部制出一组并排设置的矩形通孔,每个矩形通孔的高度均为搅拌板高度的一半,每个矩形通孔的宽度均为2cm,相邻两个矩形通孔之间的间距为4cm;搅拌板的下部制出一矩形回流孔,该矩形回流孔的最上端与矩形通孔的最下端之间的间距为2cm,矩形回流孔与搅拌板左右两侧边的间距均为2cm,矩形回流孔与搅拌板底边的间距为Icm ; (4)将乳胶成膜的 1. A method of pulling burrs slip glove, characterized by: comprising the steps of: (1) The cotton glove on the mold set bladder, gall cotton impregnated in the coagulant solution, so that the coagulation solution with cotton gall ; (2) the impregnated cotton bladder coagulant dipping into the latex solution, the outer surface of the latex film layer bladder is formed of cotton, and then pre-dried semi-finished glove routine processing until an emulsion surface of the film in dry state ; (3) in the processing solution tank filled gum pull burrs, stirred tank process implementing forward and backward through the plate back to pull the burr gum solution was uniformly stirred, stirring upper plate made out of a set of juxtaposed rectangular through hole, the height of each rectangular through hole are stirred for half of the height of the plate, the width of each rectangular through-holes are 2cm, the spacing between adjacent rectangular through hole of two 4cm; lower stirring system out of a rectangular plate return hole, the spacing between the uppermost and lowermost rectangular through hole of the rectangular hole is refluxed 2cm, rectangular holes reflux with stirring plate are both right and left side of the pitch 2cm, hole spacing and stirred at reflux rectangular bottom plate of is Icm; (4) forming the latex 手套半成品浸溃到装有拉毛刺胶溶液的加工槽内,然后将表面涂覆了拉毛刺胶溶液的手套半成品取出后,进一步进行干燥和硫化处理,即为成品。 Gloves impregnated semifinished product to pull burrs with a gum solution processing tank, and then the coated surface of the gum solution pull burrs removed semi glove, drying and further vulcanization treatment is finished.
2.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(I)中的凝固剂通常为氯化钙或者硝酸钙或者其他盐类凝固剂,其溶剂为甲醇。 The pull-slip gloves burr method according to claim 1, wherein: said step (I) is generally the coagulant is calcium chloride or calcium nitrate or other salts coagulant, which solvent is methanol.
3.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(2)中的乳胶溶液是天然乳胶溶液或者丁腈乳胶溶液。 The method according to pull burrs slip gloves according to claim 1, wherein: said step of latex solution (2) is a solution of natural latex or nitrile latex solution.
4.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(3)中的拉毛刺胶溶液可以是天然乳胶拉毛刺胶,其胶粒粒径为40〜60mesh,浓度为13%〜16% ;拉毛刺胶溶液也可以是丁腈乳胶拉毛刺胶,其胶粒粒径为50〜80mesh,浓度为14%〜17%。 The pull-slip gloves burr method according to claim 1, wherein: said step of pulling the gum solution burrs (3) may be a natural latex rubber pull burrs, which rubber particle diameter 40~60mesh, concentration of 13% ~ 16%; pull burrs gum solution may be pulled burr nitrile rubber latex, rubber particle size which is 50~80mesh, concentration of 14% ~ 17%.
5.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(3)中加工槽的槽体上端的两侧分别安装一导轨,该两个导轨之间导向滑动安装一横梁,该横梁的中部安装在一液压缸的柱塞杆上,该横梁下端制出一位于槽体内的搅拌板。 The pull-slip gloves burr method according to claim 1, wherein: said step (3) on both sides of the upper end of the groove processing are attached to a guide groove, guide rail slidably mounted between the two a beam, the central beam is mounted on the plunger rod of a hydraulic cylinder, the lower end of the cross plate is made out of a stirred tank body.
6.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述的搅拌板正向水平推行速度为20cm/s〜25cm/s ;搅拌板的反向水平拉回速度为10cm/s〜15cm/s。 The pull-slip gloves burr method according to claim 1, wherein: said plate forward horizontally stirring speed was introduced 20cm / s~25cm / s; stirring speed reverse level back plate is 10cm / s~15cm / s.
7.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(4)中加工槽上升使手套半成品浸溃在加工槽内的拉毛刺胶溶液中,加工槽上升时间为1.5s,手套半成品在拉毛刺胶溶液中浸溃时间为0.5〜5s,然后加工槽下降,下降时间为0.5s。 7. The method of claim 1 pull burr slip gloves claim, wherein: said step (4) in the working tank rises glove impregnated semifinished burr pull the gum solution in the processing tank, the processing tank rise time is 1.5s, semi-finished glove was immersed in the gum solution crushing burrs pull time 0.5~5s, and then processed groove fall, fall time of 0.5s.
8.根据权利要求1所述的防滑手套的拉毛刺方法,其特征在于:所述步骤(4)中手套半成品的硫化处理在105〜110°C的硫化干燥炉中进行,硫化干燥时间为40〜50min。 8. The method of slip gloves pull burr according to claim 1, wherein: said step (4) in the vulcanization process carried out in the glove semifinished 105~110 ° C curing oven drying, the drying time of curing 40 ~50min.
CN 201010285736 2010-09-19 2010-09-19 Burr pulling method for anti-slip gloves CN102396813B (en)