CN102390955B - 一种陶粒保温砌块 - Google Patents

一种陶粒保温砌块 Download PDF

Info

Publication number
CN102390955B
CN102390955B CN 201110206968 CN201110206968A CN102390955B CN 102390955 B CN102390955 B CN 102390955B CN 201110206968 CN201110206968 CN 201110206968 CN 201110206968 A CN201110206968 A CN 201110206968A CN 102390955 B CN102390955 B CN 102390955B
Authority
CN
China
Prior art keywords
weight
haydite
fine sand
ceramsite
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110206968
Other languages
English (en)
Other versions
CN102390955A (zh
Inventor
吴杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Huaxu Self-Insulation Wall Materials Co Ltd
Original Assignee
Ningbo Huaxu Self-Insulation Wall Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Huaxu Self-Insulation Wall Materials Co Ltd filed Critical Ningbo Huaxu Self-Insulation Wall Materials Co Ltd
Priority to CN 201110206968 priority Critical patent/CN102390955B/zh
Publication of CN102390955A publication Critical patent/CN102390955A/zh
Application granted granted Critical
Publication of CN102390955B publication Critical patent/CN102390955B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种陶粒保温砌块，特点是它以水泥、粉煤灰、陶粒和细砂为原料，水泥的重量百分比为20-40，粉煤灰的重量百分比为20-40，陶粒的重量百分比为30-55，细砂的重量百分比为5-20，陶粒的表观密度为450-650kg/m3，粒径为5mm-50mm，细砂粒径小于1mm，还包括与原料总重量相比重量百分比为0.05-0.5的引气剂，优点在于以经高温烧结的陶粒做为粗轻骨料加上直径小于1mm的细砂做为细骨料来控制砌块的干燥收缩率，以水泥和粉煤灰做为胶凝材料来浇注制模，以空气来降低重量提高保温性能，本发明不需要使用减水剂和减缩剂，因此在保证砌块的保温性能的同时，相应地能够进一步降低产品的制造成本。

Description

一种陶粒保温砌块
技术领域
本发明涉及一种保温砌块，尤其是涉及一种陶粒保温砌块。
背景技术
随着建筑节能要求的进一步提高和建筑高层化趋势的进一步发展，人们对建筑墙体的保温要求越来越高。传统的墙体保温措施主要是在外墙外设置各种保温材料，但是这种传统的保温方法越来越表现出不足之处，尤其是北京的央视大楼火灾和上海11.15大火发生之后，其在安全性，可靠性和防火性上所存在的缺陷已引起各方面的高度关注。有鉴于此，陶粒保温砌块作为一种具有保温性能的轻质墙体材料受到了越来越多的重视。
如2009年8月19日公告授权的200510061387.2号中国发明专利公开了一种高强轻质混凝土砌块及其制造方法，它含有水泥、粉煤灰、引气剂和轻粗骨料、减水剂、减缩剂，所述水泥的重量百分含量为10％-30％，所述引气剂的重量百分含量为0.1％-0.5％，所述减水剂为水泥重量的0.25％-1.5％，所述减缩剂为水泥重量的0.25％-1.5％，所述轻粗骨料的重量百分含量为30％-70％，其余为粉煤灰，所述轻粗骨料是粒径大于5mm、颗粒表观密度不大于800kg/m3的轻质骨料。该发明的砌块降低了重量，导热系数更低，砌块尺寸精度高、强度高，生产成本较低。但是该发明的砌块在采用基本原料的基础上，还要使用一定数量的减水剂和减缩剂，因此相应地会提高产品的制造成本。
发明内容
本发明所要解决的技术问题是提供一种不需要使用减水剂和减缩剂，因此相应地能够进一步降低产品的制造成本的一种陶粒保温砌块。
本发明解决上述技术问题所采用的技术方案为：一种陶粒保温砌块，它以水泥、粉煤灰、陶粒和细砂为原料，所述的水泥的重量百分比为20-40，所述的粉煤灰的重量百分比为20-40，所述的陶粒的重量百分比为30-55，所述的细砂的重量百分比为5-20，所述的陶粒的表观密度为450-650kg/m3，粒径为5mm-50mm，所述的细砂粒径小于1mm，还包括与原料总重量相比重量百分比为0.05-0.5的引气剂。
所述的细砂为含泥量小于5%的河砂或石砂。
所述的陶粒为粘土陶粒或页岩陶粒或污泥陶粒。
与现有技术相比，本发明的优点在于以经高温烧结的陶粒做为粗轻骨料加上直径小于1mm的细砂做为细骨料来控制砌块的干燥收缩率，以水泥和粉煤灰做为胶凝材料来浇注制模，以空气来降低重量提高保温性能。本发明不需要使用减水剂和减缩剂，因此在保证砌块的保温性能的同时，相应地能够进一步降低产品的制造成本。
本发明的成品具有以下性能指标：
1、砌块的抗压强度符合表1的规定。
表1抗压强度单位为兆帕
Figure GDA00002922879500021
2、不同干密度的砌块对应的强度级别符合表2的规定。
表2砌块的强度级别
Figure GDA00002922879500022
3、砌块的干密度符合表3的规定。
表3砌块的干密度单位为每千克每立方米
Figure GDA00002922879500023
4、砌块的干燥收缩、抗冻性和导热系数（干态）符合表4的规定。
表4干燥收缩值、绝对干燥收缩值、抗冻性和导热系数
Figure GDA00002922879500031
5、砌块的放射性水平符合GB6566－2001国家标准的规定。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
实施例一：一种陶粒保温砌块，它以水泥、粉煤灰、陶粒和细砂为原料，水泥为42.5普通硅酸盐水泥，水泥的重量百分比为38；粉煤灰为Ⅲ级灰，粉煤灰的重量百分比为20；陶粒为粘土陶粒，陶粒的表观密度为450kg/m3，粒径为50mm，陶粒的重量百分比为37；细砂为含泥量为4%的河砂，细砂粒径为0.8mm，细砂的重量百分比为5；并按上述原料重量的0.2%加入引气剂。产品技术指标为B06、A3.5。
实施例二：一种陶粒保温砌块，它以水泥、粉煤灰、陶粒和细砂为原料，水泥为42.5普通硅酸盐水泥，水泥的重量百分比为26；粉煤灰为Ⅱ级灰，粉煤灰的重量百分比为26；陶粒为页岩陶粒，陶粒的表观密度为550kg/m3，粒径为25mm，陶粒的重量百分比为40；细砂为含泥量为3%的石砂，细砂粒径为0.6mm，细砂的重量百分比为8；并按上述原料重量的0.15%加入引气剂。产品技术指标为B07、A5.0。
实施例三：一种陶粒保温砌块，它以水泥、粉煤灰、陶粒和细砂为原料，水泥为42.5普通硅酸盐水泥，水泥的重量百分比为25；粉煤灰为Ⅲ级灰，粉煤灰的重量百分比为18；陶粒为污泥陶粒，陶粒的表观密度为650kg/m3，粒径为5mm，陶粒的重量百分比为47；细砂为含泥量为4%的石砂，细砂粒径为0.8mm，细砂的重量百分比为10；并按上述原料重量的0.14%加入引气剂。产品技术指标为B07、A5.0。

Claims (2)

1.一种陶粒保温砌块，其特征在于它以水泥、粉煤灰、经高温烧结的陶粒和细砂为原料，以经高温烧结的陶粒做为粗轻骨料加上细砂做为细骨料来控制砌块的干燥收缩率，以水泥和粉煤灰做为胶凝材料来浇注制模，以空气来降低重量提高保温性能，所述的水泥的重量百分比为20-40，所述的粉煤灰的重量百分比为20-40，所述的陶粒的重量百分比为30-55，所述的细砂的重量百分比为5-20，所述的陶粒的表观密度为450-650kg/m3，粒径为5mm-50mm，所述的细砂粒径小于1mm，还包括与原料总重量相比重量百分比为0.05-0.5的引气剂;
其中，所述的陶粒为粘土陶粒或页岩陶粒或污泥陶粒；所述砌块的干态导热系数小于等于0.18W/（m·k）。
2.如权利要求1所述的一种陶粒保温砌块，其特征在于所述的细砂为含泥量小于5%的河砂或石砂。
CN 201110206968 2011-07-22 2011-07-22 一种陶粒保温砌块 Expired - Fee Related CN102390955B (zh)