CN102372938A - Silicon acrylic sterilization emulsion paint - Google Patents
Silicon acrylic sterilization emulsion paint Download PDFInfo
- Publication number
- CN102372938A CN102372938A CN2010102543964A CN201010254396A CN102372938A CN 102372938 A CN102372938 A CN 102372938A CN 2010102543964 A CN2010102543964 A CN 2010102543964A CN 201010254396 A CN201010254396 A CN 201010254396A CN 102372938 A CN102372938 A CN 102372938A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- silicon
- silicon acrylic
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a silicon acrylic sterilization emulsion paint, which is prepared from the following raw materials according to the weight proportion: 170 parts of silicon acrylic emulsion, 35 parts of cellulose ether, 30 parts of wood fiber, 18 parts of vinyl acetate, 10 parts of polyethylene glycol, 10 parts of lauryl sodium sulfate, 75 parts of water, 15 parts of zinc oxide, 22 parts of white powder, 25 parts of polyvinyl alcohol, 12 parts of hydroxyethyl cellulose, 1 part of mildew preventive, 5 parts of texanol, 5 parts of titanium white, 5 parts of kaolin and 1 part of thickening agent. The product disclosed by the invention has the advantages of effectively removing mould, bearing scouring, shielding wall cracks, facilitating constructions and the like.
Description
Technical field
The present invention relates to a kind of silicon third sterilization rubber-emulsion paint.
Technical background
Rubber-emulsion paint is being commonly called as of latex coating, is present popular interior outer wall building coating.Coating is meant and is applied to body surface and forms solid-state filming to have a class I liquid I of protection, decoration or property or the general name of solid material.Early stage coating is main raw material with the vegetables oil mostly, so the title of " paint " is arranged.The wide range of coating, varnish, wood lacquer, insullac, automobile finish etc. all belong to the scope of coating.Along with the rise of home decoration trend, trade sales coating is as one that grows stronger day by day in the coating family, and consumer relations is close day by day.At present, the security of inner wall of building rubber-emulsion paint, health more and more cause people's attention, the indoor paint product of market demand superior performance, function uniqueness, health environment-friendly.The high molecular polymer Film Forming Mechanism of Latex Coatings is that particle is piled up gathering, film have ventilation property, water-permeable, and restricted the raising of rubber-emulsion paint glossiness.At present, the decoration of construction wall generally uses traditional rubber-emulsion paint, uses above-mentioned rubber-emulsion paint back wall surface to be easy to the mildew bacterium, both human body is worked the mischief, and has destroyed the attractive in appearance of body of wall again.
Summary of the invention
The present invention seeks in order to overcome the deficiency of prior art, a kind of silicon third sterilization rubber-emulsion paint that can effectively dispel mould is provided.
For addressing the above problem, previous technical scheme of the present invention is: a kind of silicon third sterilization rubber-emulsion paint stirs according to weight proportion by following raw material and processes: 170 parts of silicon third latexes, 35 parts of ether of cellulose, 30 parts of wood fibres, 18 parts of vinyl acetates; 10 parts of polyoxyethylene glycol, 10 parts of sodium lauryl sulphate, 75 parts of water, 15 parts of zinc oxide; 22 parts of chalk powders, 25 parts of Z 150PH, 12 parts of Natvosols, 1 part of mould inhibitor; 5 parts of film coalescence aid, 5 parts of white titanium pigments, 5 parts of kaolin, 1 part of thickening material.Beneficial effect of the present invention:
1, effectively dispels mould.
2, seepage force, strong adhesion;
3, block the body of wall crackle.
Embodiment
Instance of the present invention is can not limit the present invention to explanation of the present invention, in implication suitable with the present invention and any change and the adjustment in the scope, all should think within the scope of the invention.
Embodiment 1
A kind of silicon third sterilization rubber-emulsion paint stirs through the stirrer high speed dispersion according to weight proportion by following raw material and processes: 170 parts of silicon third latexes, 35 parts of ether of cellulose, 30 parts of wood fibres, 18 parts of vinyl acetates; 10 parts of polyoxyethylene glycol, 10 parts of sodium lauryl sulphate, 75 parts of water, 15 parts of zinc oxide; 22 parts of chalk powders, 25 parts of Z 150PH, 12 parts of Natvosols, 1 part of mould inhibitor; 5 parts of film coalescence aid, 5 parts of white titanium pigments, 5 parts of kaolin, 1 part of thickening material.
The basic mechanical design feature such as the following table 1 of the product of the present invention's preparation.
Table 1, basic mechanical design feature of the present invention
| Alkali resistance | Contrast ratio | Abrasion resistance (inferior) | Anti-contamination % | Water tolerance | Artificial ageing resistance |
| 48h is no abnormal | ＞0.87 | ＞500 | ＜20 | 96h is no abnormal | ＞250 |
Claims (1)
1. silicon third a sterilization rubber-emulsion paint is characterized in that it mainly is to be stirred according to weight proportion by following raw materials according to process: 170 parts of silicon third latexes, 35 parts of ether of cellulose, 30 parts of wood fibres, 18 parts of vinyl acetates; 10 parts of polyoxyethylene glycol, 10 parts of sodium lauryl sulphate, 75 parts of water, 15 parts of zinc oxide; 22 parts of chalk powders, 25 parts of Z 150PH, 12 parts of Natvosols, 1 part of mould inhibitor; 5 parts of film coalescence aid, 5 parts of white titanium pigments, 5 parts of kaolin, 1 part of thickening material.