CN102372957A - High pollution-resistant styreneacrylic latex paint - Google Patents
High pollution-resistant styreneacrylic latex paint Download PDFInfo
- Publication number
- CN102372957A CN102372957A CN2010102543606A CN201010254360A CN102372957A CN 102372957 A CN102372957 A CN 102372957A CN 2010102543606 A CN2010102543606 A CN 2010102543606A CN 201010254360 A CN201010254360 A CN 201010254360A CN 102372957 A CN102372957 A CN 102372957A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- styreneacrylic
- resistant
- latex paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high pollution-resistant styreneacrylic latex paint, which is mainly prepared by mixing the following raw materials according to the weight proportion: 157 parts of styreneacrylic, 13 parts of dispersing agent, 80 parts of deionized water, 15 parts of oxalic acid adipic dihydrazide, 2 parts of dispersing agent, 4 parts of defoamer, 11 parts of mildew preventive, 23 parts of kaolin, 15 parts of titanium white, 15 parts of heavy calcium powder, 15 parts of texanol and 12 parts of polyethers thickening agent. The invention has the following advantages that: a coating is fine and smooth, and has an elegant mercerizing effect; and the high pollution-resistant styreneacrylic latex paint has good crack resistance, can make up the fine and small cracks of a base layer, has preeminent water resistance, alkali resistance, pollution resistance, weather resistance, and excellent light and color protection performance, can make wall bodies be new for a long time, and has mould resistance, antibiosis and ultraviolet radiation resistance.
Description
Technical field
The present invention relates to a kind of high resistant styrene-acrylic latex coating.
Technical background
Rubber-emulsion paint is to be that base-material adds pigment, filler and one type of formulated water-borne coatings of various auxiliary agent with the acrylate copolymer emulsion, and the decorating inner and external walls that is mainly used in buildings uses.Have good weathering resistance and chemical resistance mostly after the rubber-emulsion paint normal temperature film forming by conventional acrylate copolymer emulsion preparation, but resistance to soiling is poor, thereby has had a strong impact on the result of use of rubber-emulsion paint.Cause the relatively poor major cause of rubber-emulsion paint resistance to soiling to be because rubber-emulsion paint paint film second-order transition temperature (Tg) is low high with water-absorbent: Tg is low excessively; After the rubber-emulsion paint film forming, when envrionment temperature is high slightly, paint film will after-tack; Pollutent is easy to stick to coating surface and pollutes, and is difficult to simultaneously remove; In addition, when rubber-emulsion paint paint film water-absorbent was too high, the dust (be dissolved in water or be scattered in the dust in the water) that sticks to coating surface through the paint film suction was just many, thereby caused paint film to show dirty easily.
Summary of the invention
The present invention seeks in order to overcome the deficiency of prior art, a kind of high resistant styrene-acrylic latex coating of high resistance to soiling is provided.
For addressing the above problem, previous technical scheme of the present invention is: a kind of high resistant styrene-acrylic latex coating stirs according to weight proportion by following raw material and processes: 157 parts of benzene emulsions, 13 parts of dispersion agents, 80 parts of deionized waters; 15 parts of ethylene acid hydrazides, 2 parts of dispersion agents, 4 parts of skimmers; 11 parts of mould inhibitors, 23 parts of kaolin, 15 parts of white titanium pigments; 15 parts of dicalcium powders, 15 parts of film coalescence aid, 12 parts of polyethers thickening materials.
Beneficial effect of the present invention:
1, the moist mercerization effect of coating with elegance.Splitting resistance is good, the fine cracks sharp, basic unit of covering;
2, preeminent water-fast, alkaline-resisting, contamination resistance and weathering resistance;
3, guarantor's light, the tint retention of excellence can make body of wall permanent as new;
4, antimildew and antibacterial, ultraviolet radiation preventing.
Embodiment
Instance of the present invention is can not limit the present invention to explanation of the present invention, in implication suitable with the present invention and any change and the adjustment in the scope, all should think within the scope of the invention.
Embodiment 1
A kind of high resistant styrene-acrylic latex coating stirs through the stirrer high speed dispersion according to weight proportion by following raw material and processes: 157 parts of benzene emulsions, 13 parts of dispersion agents, 80 parts of deionized waters; 15 parts of ethylene acid hydrazides, 2 parts of dispersion agents, 4 parts of skimmers; 11 parts of mould inhibitors, 23 parts of kaolin, 15 parts of white titanium pigments; 15 parts of dicalcium powders, 15 parts of film coalescence aid, 12 parts of polyethers thickening materials.
Table 1, basic mechanical design feature of the present invention
Alkali resistance (h) | Contrast ratio | Abrasion resistance (inferior) | Anti-contamination % | Water tolerance (h) | Artificial ageing resistance |
>48 | >0.93 | >8000 | <15 | >96 | >600 |
Claims (1)
1. one kind high resistant styrene-acrylic latex coating is characterized in that it mainly is to be stirred according to weight proportion by following raw materials according to process: 157 parts of benzene emulsions, 13 parts of dispersion agents, 80 parts of deionized waters; 15 parts of ethylene acid hydrazides, 2 parts of dispersion agents, 4 parts of skimmers; 11 parts of mould inhibitors, 23 parts of kaolin, 15 parts of white titanium pigments; 15 parts of dicalcium powders, 15 parts of film coalescence aid, 12 parts of polyethers thickening materials.