CN102372454A - 一种水泥助磨剂 - Google Patents

一种水泥助磨剂 Download PDF

Info

Publication number
CN102372454A
CN102372454A CN2010102547861A CN201010254786A CN102372454A CN 102372454 A CN102372454 A CN 102372454A CN 2010102547861 A CN2010102547861 A CN 2010102547861A CN 201010254786 A CN201010254786 A CN 201010254786A CN 102372454 A CN102372454 A CN 102372454A
Authority
CN
China
Prior art keywords
grinding aid
cement
cement grinding
water
isopropanolamine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010102547861A
Other languages
English (en)
Other versions
CN102372454B (zh
Inventor
胡鉴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Jiye Changqing New Materials Co ltd
Original Assignee
Guangzhou Built To Last Chemical Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Built To Last Chemical Co ltd filed Critical Guangzhou Built To Last Chemical Co ltd
Priority to CN2010102547861A priority Critical patent/CN102372454B/zh
Publication of CN102372454A publication Critical patent/CN102372454A/zh
Application granted granted Critical
Publication of CN102372454B publication Critical patent/CN102372454B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水泥助磨剂，包括以下组份：多元醇胺，多元醇，木质磺酸盐，水。所述组份的重量百分比分别为：多元醇胺20～40％，多元醇5～10％，木质磺酸盐10～30％，水20～65％。本发明不会增加水泥的吸水量，助磨效果较好。

Description

一种水泥助磨剂
技术领域
本发明涉及一种水泥助磨剂。
背景技术
在水泥的制作过程中，当各种物料喂入磨机后粉磨，此时物料与物料、物料与研磨体之间会发生剧烈、频繁的摩擦和撞击，使得物料产生静电，这些带有电荷的物料会吸附在钢球及研磨体的表面，使得水泥磨机出现严重的包球包锻现象；当喂入的附加材料的湿度大于5％时，还会在磨机中大量水蒸气，增加了研磨料的湿度，也会产生上述的包球包锻现象。为了解决静电问题，大多数厂家采用加入水泥助磨剂的方法。目前，水泥助磨剂有粉体和液体两大类，液体助磨剂使用比较方便，因此应用比较普遍。大多数液体助磨剂配方存在一定的缺陷：水泥的吸水量会增大，影响了水泥的质量。
发明内容
本发明的目的提供一种水泥助磨剂，不会增加水泥的吸水量，助磨效果较好。
本发明的目的是这样实现的：
一种水泥助磨剂，包括以下组份：多元醇胺，多元醇，木质磺酸盐，水。
优选地，本发明所述组份的重量百分比分别为：多元醇胺20～40％，多元醇5～10％，木质磺酸盐10～30％，水20～65％。
优选地，本发明所述的多元醇胺为三乙醇胺、三异丙醇胺的其中一种或几种，所述三乙醇胺、三异丙醇胺的重量百分比分别为15～25％、5～15％；所述的多元醇为二乙二醇；所述的木质磺酸盐为改性木质素磺酸钠。
其中，三乙醇胺分子中有N原子，有一对未共用电子，很容易与金属离子形成共价键发生络合，与金属离子形成比较稳定的络合物，这些络合物在溶液中形成许多可溶区，从而提高水化产物的扩散塑料，提高水泥的早期强度；此外三乙醇胺还可提高比表面积，降低细度，加快流速。
三异丙醇胺可通过与难水化的矿物C4AF发生络合反应，促进其持续水化，提高水泥的后期强度，同时三异丙醇胺还具有良好的分散作用，有利于磨机产量的提高。
二乙二醇可起到助磨快、消除静电，以及防冻便于冬季施工的作用。
改性木质素磺酸钠是一种阴离子表面活性剂，其含有不饱和键，能产生较大的吸附力，对水泥颗粒具有明显的分散作用，在水泥粉磨过程中能提高物料的流动速度，还可适当引气显著降低水泥标准稠度用水量，不会增加水泥的吸水量。
由上可见，与现有技术相比，本发明有如下有益效果：
本发明可降低水泥标准稠度用水量，不会增加水泥的吸水量；提高台产量15％～25％；水泥28天强度可以增加3～6Mpa；可以很好地跟水泥中的其他添加剂相适应；还可充当水泥工业节能减排上的好助手，在水泥粉磨过程中产生节能降耗、减排利废、提质增效的效果。
具体实施方式
下面将结合具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例一
水泥助磨剂，包括以下重量百分比的组份：
三乙醇胺15％，三异丙醇胺10％，二乙二醇8％，改性木质素磺酸钠20％，水47％。
实施例二
水泥助磨剂，包括以下重量百分比的组份：
三乙醇胺25％，三异丙醇胺5％，二乙二醇5％，改性木质素磺酸钠10％，水55％。
实施例三
水泥助磨剂，包括以下重量百分比的组份：
三乙醇胺20％，三异丙醇胺15％，二乙二醇10％，改性木质素磺酸钠30％，水25％。
实施例四
水泥助磨剂，包括以下重量百分比的组份：
三乙醇胺24％，三异丙醇胺14％，二乙二醇8％，改性木质素磺酸钠25％，水29％。
实施例五
水泥助磨剂，包括以下重量百分比的组份：
三乙醇胺16％，三异丙醇胺12％，二乙二醇6％，改性木质素磺酸钠25％，水51％。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (6)

1.一种水泥助磨剂，其特征在于包括以下组份：
多元醇胺，多元醇，木质磺酸盐，水。
2.根据权利要求1所述的水泥助磨剂，其特征是：所述组份的重量百分比分别为：多元醇胺20～40％，多元醇5～10％，木质磺酸盐10～30％，水20～65％。
3.根据权利要求1所述的水泥助磨剂，其特征是：所述的多元醇胺为三乙醇胺、三异丙醇胺的其中一种或几种。
4.根据权利要求3所述的水泥助磨剂，其特征是：所述三乙醇胺、三异丙醇胺的重量百分比分别为15～25％、5～15％。
5.根据权利要求1所述的水泥助磨剂，其特征是：所述的多元醇为二乙二醇。
6.根据权利要求1所述的水泥助磨剂，其特征是：所述的木质磺酸盐为改性木质素磺酸钠。
CN2010102547861A 2010-08-16 2010-08-16 一种水泥助磨剂 Active CN102372454B (zh)