CN102369854B - Pe/eva复合多功能棚膜 - Google Patents
Pe/eva复合多功能棚膜 Download PDFInfo
- Publication number
- CN102369854B CN102369854B CN2011102466939A CN201110246693A CN102369854B CN 102369854 B CN102369854 B CN 102369854B CN 2011102466939 A CN2011102466939 A CN 2011102466939A CN 201110246693 A CN201110246693 A CN 201110246693A CN 102369854 B CN102369854 B CN 102369854B
- Authority
- CN
- China
- Prior art keywords
- film
- eva
- greenhouse film
- eva resin
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种农用棚膜及其制备方法，具体涉及一种PE/EVA复合多功能棚膜，其特征在于由内层、中层和外层三层薄膜复合而成，其中内层和中层添加大量的EVA树脂。本发明的优点在于：通过科学合理的配方设计达到既满足棚膜使用的各种功能性要求，又无需额外增加生产设备，以期降低生产成本。由于复合多功能棚膜中含有较高量EVA树脂，相比EVA树脂含量低或不含EVA树脂的聚烯烃树脂棚膜，具有良好的透光性和透明度，更显著的保温性能，优异的耐低温性能，寿命更长，物理力学性能及相容性更优异，流滴和消雾持效期显著延长。
Description
技术领域
本发明涉及一种农用棚膜及其制备方法，具体涉及一种高性能PE/EVA复合多功能棚膜。
背景技术
我国是世界上农用塑料薄膜使用量最多的国家，塑料薄膜在农田的应用上所取得的保温保湿增产的效果，已得到农业生产的公认。生产农用棚膜的原料主要是聚烯烃树脂，棚膜多在我国北方的冬、春季使用。因为气候寒冷，大棚内外温度、湿度相差都较大，导致棚膜内壁上附有大量的雾滴。雾滴使光线发生折射，使薄膜的透光性大为降低；雾滴落至作物上会使其枯烂，降低了作物的产量和质量；雾滴滴落时极易传播病菌，使棚室内的湿度增加，增加病虫害；棚内温度将随着雾珠蒸发而降低，减弱了大棚的保温效果。因此要求棚膜既无滴又防雾，将棚的雾气、水汽形成水滴，沿棚膜壁流下，提高透明度；同时还要使棚膜具有抗光、热、氧老化等功能，使用期更长；并且随着科技的发展和棚膜在园艺等领域的推广应用，对棚膜的要求越来越高，特别是对棚膜的耐老化性能、耐低温性能、保温性能、流滴和消雾的持续性等有更高的要求。
发明内容
本发明的目的是提供一种高性能PE/EVA复合多功能棚膜，能够具有寿命长、耐低温、保温好、流滴期和消雾期持久的优点。
本发明所述的PE/EVA复合多功能棚膜，由内层、中层和外层三层薄膜复合而成，其中，内层、中层和外层薄膜分别由以下重量份数的原料制成：
其中，EVA的VA质量含量≥3%。
本发明中EVA（乙烯-醋酸乙烯共聚物）、LLDPE（线形低密度聚乙烯）、LDPE（低密度聚乙烯）和mLLDPE（茂金属线型低密度聚乙烯）均为聚烯烃类树脂，光稳定剂、抗氧剂、流滴剂、消雾剂和水滑石均起到助剂的作用。
所述的三层薄膜中的光稳定剂均优选用光稳定剂783，三层薄膜中的抗氧剂优均选用抗氧剂B215。
本发明所使用的流滴剂和消雾剂均选用添加型，市售的流滴剂和消雾剂均可使用。
目前主要的聚烯烃树脂棚膜的制备方法有两种，外涂敷法和内添加法。本发明属内添加法中的母料法，原有设备、工艺工序保持不变，按照配方中各层的组分配比单独混合，首先将少量的聚烯烃类树脂粉料和各种助剂混合均匀，经螺杆挤出机制得各种功能性母料，该功能性母料为粒料，然后功能性母料再与剩余的聚烯烃类树脂混合均匀，剩余的聚烯烃类树脂选用粒料，最后经三层共挤吹塑薄膜机组按照厚度1:1:1挤出而成。
本发明的优点在于：通过科学合理的配方设计达到既满足棚膜使用的各种高功能性要求，又无需额外增加生产设备，以期降低生产成本。由于复合多功能棚膜中含有较高量EVA树脂，相比EVA树脂含量低或不含EVA树脂的聚烯烃树脂棚膜，具有更好的透光性，更高的透明度，更显著的保温性能，优异的耐低温性能，寿命更长，物理力学性能及相容性更优异，流滴和消雾持效期显著延长。
具体实施方式
以下结合实施例对本发明做进一步说明。
实施例1：
本发明所述的复合多功能棚膜，由内层、中层和外层三层薄膜经吹塑工艺复合而成，其中，内层、中层和外层薄膜分别由以下重量份数的原料制成：
本例产品主要性能指标：
拉伸强度（MPa）：28.8（纵向）、28.3（横向）；断裂伸长率（%）：603（纵向）、761（横向）；直角撕裂强度（KN/m）：113.1（纵向）、122.1（横向）；透光率（%）：89.5；雾度（%）：18.72；初滴时间（s）：165；流滴失效时间（d）：10。
实施例2：
本发明所述的复合多功能棚膜，由内层、中层和外层三层薄膜吹塑工艺复合而成，其中，内层、中层和外层薄膜分别由以下重量份数的原料制成：
本例产品主要性能指标：
拉伸强度（MPa）：29.5（纵向）、28.7（横向）；断裂伸长率（%）：620.1（纵向）、751.3（横向）；直角撕裂强度（KN/m）：103.1（纵向）、114.0（横向）；透光率（%）：90.0；雾度（%）：14.01；初滴时间（s）：181；流滴失效时间（d）：15。
实施例3：
本发明所述的复合多功能棚膜，由内层、中层和外层三层薄膜吹塑工艺复合而成，其中，内层、中层和外层薄膜分别由以下重量份数的原料制成：
本例产品主要性能指标：
拉伸强度（MPa）：30.0（纵向）、27.4（横向）；断裂伸长率（%）：650.1（纵向）、760.2（横向）；直角撕裂强度（KN/m）：101.0（纵向）、119.0（横向）；透光率（%）：90.0；雾度（%）：14.02；初滴时间（s）：153；流滴失效时间（d）：15。
Claims (3)
1.一种PE/EVA复合多功能棚膜，其特征在于由内层、中层和外层三层薄膜复合而成，其中，内层、中层和外层薄膜分别由以下重量份数的原料制成：
其中，EVA的VA质量含量≥3%。
2.根据权利要求1所述的PE/EVA复合多功能棚膜，其特征在于三层薄膜中的光稳定剂均选用光稳定剂783。
3.根据权利要求1所述的PE/EVA复合多功能棚膜，其特征在于三层薄膜中的抗氧剂均选用抗氧剂B215。