CN102367342B - A kind of Multifunctional environmental protection paint - Google Patents
A kind of Multifunctional environmental protection paint Download PDFInfo
- Publication number
- CN102367342B CN102367342B CN201110307651.1A CN201110307651A CN102367342B CN 102367342 B CN102367342 B CN 102367342B CN 201110307651 A CN201110307651 A CN 201110307651A CN 102367342 B CN102367342 B CN 102367342B
- Authority
- CN
- China
- Prior art keywords
- parts
- less
- microns
- coating
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 15 25 parts；30 50 nano titanium oxides 35 parts, 30 50 nano silicons 13 parts, 200 300 mesh zinc oxide 23 parts, white carbon 46 parts, 2 methyl 4 isothiazoline 3 ketone 12 parts, carbamate 12 parts, less than 100 microns dicalcium powders 58 parts, less than 100 microns light calcium carbonate powders 35 parts, 37 parts of kieselguhr, styrene-acrylic emulsion 10 20 parts, hydroxyethyl cellulose 12 parts, white glue with vinyl 35 parts, polyurethane 23 parts, 12 parts of magnesium sulfate, industrial table salt 12 parts, sucrose 12 parts.
Description
Technical field
The present invention relates to constructional ornamental material field, particularly to a kind of Multifunctional environmental protection paint.
Background technology
Along with the quickening of people's rhythm of life and the raising to life taste, health problem becomes people and extraordinarily closes
The problem of note.In modern society, the health of the indoor pollution serious threat mankind.Indoor pollution is primarily referred to as
From building and ornament materials produce formaldehyde, benzene, ammonia, radon；Indoor household electrical equipment electromagnetic wave and radiation；
The burning of coal, liquefied gas, natural gas etc.；Decoct the smog produced in the high-temperature cooking courses of processing such as frying baking；
Family dote on virus, the pollutant such as antibacterial destroy family daily life environment, affect health of people.Except
Outside indoor pollution, mosquito, fly, Mantidis, Cimex bedbug, Aranea, the class pest of Formica fusca, family, factory,
The ground such as warehouse, office, hospital, school, hotel, are seen everywhere, all-pervasive.These insecticides are not only
A lot of worry is brought to the life of people, it is often more important that, they cause pathophoresis and the serious harm mankind
Healthy.The diseases such as hepatitis, dysentery, malaria, sleeping sickness, dengue fever, pneumonia are exactly to be passed by them
Broadcast.So, eradicate insect, change living environment, become the significant problem that the mankind pay close attention to already.
Interior wall coating is the finishing material that indoor usable floor area is maximum, along with people's concern to health problem,
People develop except several functions interior wall coating, and these functional interior wall coatings are except own low toxicity, nontoxic
Outward, generally it is made to possess specific function in a certain respect, such as existing skill by the component that adds that interpolation is special
Art have a large amount of except methanal paint, fungus and mildew resistance coating and parasite killing insect-repelling paint etc..But this kind of coating leads to
Often function singleness, and as described above, and the indoor that people live are more than being perplexed by a kind of problem.As
Really coating only possesses a kind of function, even if the effect of this function is the best, it also can only solve in a certain respect
Problem.And interior wall coating once applies, the 8-10 year to be continued.During this period, other problem
The method that can only lean on other solves.Therefore, needing exploitation one badly can adsorption-decomposition function formaldehyde, moreover it is possible to remove
Other harmful gass, again possess fungus and mildew resistance function, even can the multifunctional coating of parasite killing.
Summary of the invention
For the deficiencies in the prior art, an object of the present invention is to provide a kind of Multifunctional environmental protection paint,
To solve the problem of functional paint function singleness in prior art.
For reaching above-mentioned purpose, the technical solution used in the present invention is as follows:
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 15-25
Part；30-50 nano titanium oxide 3-5 part, 30-50 nano silicon 1-3 part, 200-300 mesh aoxidizes
Zinc 2-3 part, white carbon 4-6 part, MIT 1-2 part, carbamate 1-2
Part, less than 100 microns dicalcium powder 5-8 parts, less than 100 microns light calcium carbonate powder 3-5 parts, kieselguhr 3-7 part,
Styrene-acrylic emulsion 10-20 part, hydroxyethyl cellulose 1-2 part, white glue with vinyl 3-5 part, polyurethane 2-3 part, sulfur
Acid magnesium 1-2 part, industrial table salt 1-2 part, sucrose 1-2 part.
Having the beneficial effect that of coating prepared by the present invention
The present invention, by reasonably selecting reasonably combined with consumption of active princlple, achieves unexpected skill
Art effect, although single effective ingredient consumption is little, but due to the synergism with other component, achieves
The technique effect not worse than prior art simple function coating.Such as, the active princlple removing formaldehyde is nanometer
Titanium dioxide, its amount ratio is of the prior art low, but the removing effect of formaldehyde of coating of the present invention is than existing skill
Art is excellent, and the clearance rate of 8 hours formaldehyde reaches more than 97%.The performance of the coating of the present invention is as shown in the table:
As can be seen from the above table, the coating of the present invention can remove the various dusty gass of indoor, and possesses
Fungus and mildew resistance performance and resistance to scrub, but also common insect can be murdered.These indexs above-mentioned can meet commonly
Family's requirement to coating property.And the environmental protection of coating own, do not cause secondary pollution.
Detailed description of the invention
Embodiment one
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 15 parts；
30-50 nano titanium oxide 3 parts, 30-50 nano silicon 1 part, 200-300 mesh zinc oxide 2 parts,
White carbon 4 parts, MIT 1 part, carbamate 1 part, less than 100 microns
Dicalcium powder 5 parts, less than 100 microns light calcium carbonate powders 3 parts, 3 parts of kieselguhr, styrene-acrylic emulsion 10 parts, ethoxy
Cellulose 1 part, white glue with vinyl 3 parts, polyurethane 2 parts, 1 part of magnesium sulfate, industrial table salt 1 part, sucrose 1
Part.
Embodiment two
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 25 parts；
30-50 nano titanium oxide 5 parts, 30-50 nano silicon 3 parts, 200-300 mesh zinc oxide 3 parts,
White carbon 6 parts, MIT 2 parts, carbamate 2 parts, less than 100 microns
Dicalcium powder 8 parts, less than 100 microns light calcium carbonate powders 5 parts, 7 parts of kieselguhr, styrene-acrylic emulsion 20 parts, ethoxy
Cellulose 2 parts, white glue with vinyl 5 parts, polyurethane 3 parts, 2 parts of magnesium sulfate, industrial table salt 2 parts, sucrose 2
Part.
Embodiment three
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 20 parts；
30-50 nano titanium oxide 4 parts, 30-50 nano silicon 2 parts, 200-300 mesh zinc oxide 2.5 parts,
White carbon 5 parts, MIT 1.5 parts, carbamate 1.5 parts, 100 microns
Following dicalcium powder 7 parts, less than 100 microns light calcium carbonate powders 4 parts, 5 parts of kieselguhr, styrene-acrylic emulsion 15 parts, hydroxyl
Ethyl cellulose 1.5 parts, white glue with vinyl 4 parts, polyurethane 2.5 parts, 1.5 parts of magnesium sulfate, industrial table salt 1.5
Part, sucrose 1.5 parts.
Embodiment four
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 18 parts；
30-50 nano titanium oxide 4 parts, 30-50 nano silicon 3 parts, 200-300 mesh zinc oxide 2 parts,
White carbon 4 parts, MIT 2 parts, carbamate 1 part, less than 100 microns
Dicalcium powder 8 parts, less than 100 microns light calcium carbonate powders 3 parts, 3 parts of kieselguhr, styrene-acrylic emulsion 20 parts, ethoxy
Cellulose 1.5 parts, white glue with vinyl 4 parts, polyurethane 2.5 parts, 1.5 parts of magnesium sulfate, industrial table salt 1.5 parts,
Sucrose 1.5 parts.
Embodiment five
A kind of Multifunctional environmental protection paint, this coating is made up of following material in parts by weight: pure water 22 parts；
30-50 nano titanium oxide 3 parts, 30-50 nano silicon 3 parts, 200-300 mesh zinc oxide 2 parts,
White carbon 4 parts, MIT 1 part, carbamate 2 parts, less than 100 microns
Dicalcium powder 7 parts, less than 100 microns light calcium carbonate powders 4 parts, 6 parts of kieselguhr, styrene-acrylic emulsion 18 parts, ethoxy
Cellulose 1.5 parts, white glue with vinyl 4 parts, polyurethane 2.5 parts, 1.5 parts of magnesium sulfate, industrial table salt 1.5 parts,
Sucrose 1.5 parts.
Applicant states, above-described embodiment only for technology design and the feature of the present invention are described, its object is to
Allow person skilled in the art will appreciate that present disclosure and to implement according to this, can not be limited this with this
The protection domain of invention.Person of ordinary skill in the field it will be clearly understood that any improvement in the present invention,
The equivalence of raw material each to product of the present invention is replaced and the interpolation of auxiliary element, concrete way choice etc., all falls
Within the scope of protection scope of the present invention and disclosure.
Claims (2)
1. a Multifunctional environmental protection paint, it is characterised in that this coating is made up of following material in parts by weight:
Pure water 15-25 part；30-50 nano titanium oxide 3-5 part, 30-50 nano silicon 1-3 part,
200-300 mesh zinc oxide 2-3 part, white carbon 4-6 part, MIT 1-2 part,
Carbamate 1-2 part, less than 100 microns dicalcium powder 5-8 parts, less than 100 microns light calcium carbonate powder 3-5 parts,
Kieselguhr 3-7 part, styrene-acrylic emulsion 10-20 part, hydroxyethyl cellulose 1-2 part, white glue with vinyl 3-5 part is poly-
Urethane 2-3 part, magnesium sulfate 1-2 part, industrial table salt 1-2 part, sucrose 1-2 part.
2. Multifunctional environmental protection paint as claimed in claim 1, it is characterised in that this coating is in parts by weight
It is made up of following material: pure water 20 parts；30-50 nano titanium oxide 4 parts, 30-50 nanometer titanium dioxide
Silicon 2 parts, 200-300 mesh zinc oxide 2.5 parts, white carbon 5 parts, MIT 1.5
Part, carbamate 1.5 parts, less than 100 microns dicalcium powders 7 parts, less than 100 microns light calcium carbonate powders 4 parts,
5 parts of kieselguhr, styrene-acrylic emulsion 15 parts, hydroxyethyl cellulose 1.5 parts, white glue with vinyl 4 parts, polyurethane 2.5
Part, 1.5 parts of magnesium sulfate, industrial table salt 1.5 parts, sucrose 1.5 parts.