CN102361359A - 一种耐腐蚀的电机用钕铁硼永磁 - Google Patents
一种耐腐蚀的电机用钕铁硼永磁 Download PDFInfo
- Publication number
- CN102361359A CN102361359A CN2011103466870A CN201110346687A CN102361359A CN 102361359 A CN102361359 A CN 102361359A CN 2011103466870 A CN2011103466870 A CN 2011103466870A CN 201110346687 A CN201110346687 A CN 201110346687A CN 102361359 A CN102361359 A CN 102361359A
- Authority
- CN
- China
- Prior art keywords
- percent
- equal
- motor
- corrosion
- neodymium iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α-β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu;N为添加元素,包括选自Ti、V、Cr、Mn、Ni、Zr、Nb、Mo和Bi的一种或一种以上元素;α、β、x、y为各元素原子百分比含量;其中,20%≤α≤25%,5%≤β≤12%,3%≤x≤7%,5%≤y≤10%。
Description
技术领域
本发明涉及电机用永磁领域,特别涉及一种耐腐蚀的电机用钕铁硼永磁。
背景技术
R-Fe-B系钕铁硼稀土永磁体,以其优良的磁性能得到越来越多的应用,被广泛用于医疗的核磁共振成像,计算机硬盘驱动器,手机的振动电机,混合动力汽车的电机,风力发电机等。目前,R-Fe-B系钕铁硼稀土永磁体采用的制造方法通常为:
a、合金熔炼步骤:即将稀土R(R为Nd、Pr、Dy、Tb稀土类元素的一种或两种以上)、铁、硼铁及金属M(M为Al、Cu、Co、Ag等金属元素的一种或两种以上),在真空状态及惰性气体保护下熔炼成合金,并浇铸到水冷模具中冷却或通过真空速凝炉,在水冷铜辊的快速冷却下,将熔炼的合金铸成合金薄片;
b、氢碎步骤:将熔炼后的合金薄片装入容器内,并向容器内通入H2使合金发生吸H2反应,然后再对容器加热和抽真空,以实现合金脱H2,这时合金就会沿晶界产生裂痕;
c、制粉步骤:在N2气氛下,用气流磨将氢碎后的合金磨成平均粒度在2~10μm的合金粉;
d、压制步骤:在磁场取向压机中,将平均粒度在2~10μm的合金粉压制成磁块,当压机压力低时可通过等静压进行二次加压;
e、烧结步骤:将压制好的磁块在真空烧结炉中进行烧结,其烧结温度为1000~1200℃;
g、时效步骤:将烧结后的磁块在真空时效炉中进行时效处理,一般真空时效炉的温度为500~600℃;
h、加工步骤:对磁体进行机械加工或涂层;
通过上述方法制造的R-Fe-B稀土永磁体,虽然达到了磁性能的要求,但其耐腐蚀性及热稳定性较差,该缺点正在影响其在电机类等领域的应用。
发明内容
针对现有技术的不足,本发明的目的之一在于提供一种耐腐蚀的电机用钕铁硼永磁,该方法可实现在保持磁性能的条件下,改善钕铁硼的耐腐蚀性和热稳定性。
为了实现上述的目的,本发明采用的技术方案如下:
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu;N为添加元素,包括选自Ti、V、Cr、Mn、Ni、Zr、Nb、Mo和Bi的一种或一种以上元素;α、β、x、y为各元素原子百分比含量;其中,20%≤α≤25%,5%≤β≤12%,3%≤x≤7%,5%≤y≤10%。
优选,Co和Cu各占50%。
优选,N为Ti、Mn、Cr和V中的一种或两种。
优选,22%≤α≤24%,7%≤β≤10%,4%≤x≤6%,6%≤y≤8%。
最优选,α为23%,β为9%,x为5%,y为7%。
本发明可用常规的钕铁硼制备工艺生产。
本发明的优点和效果:
本发明通过对稀土元素Nd、Dy和Ho的选用和配比,以及添加元素的选用,使得在磁体的晶界相(富Nd、富B相)增加了金属的含量,有效地避免了这些金属进入R2Fe14B的主相中,从而有效地提高了稀土永磁体的耐腐蚀性和热稳定性。
具体实施方式
实施例一
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu,二者各占50%;N为添加元素,选自Ti;α、β、x、y为各元素原子百分比含量;其中,α为20%,β为12%,x为3%,y为10%。
实施例二
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu,二者各占50%;N为添加元素,包括选自Ti、V,其中Ti占70%,V占30%;α、β、x、y为各元素原子百分比含量;其中,α为25%,β为5%,x为7%,y为5%。
实施例三
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu,二者各占50%;N为添加元素,选自Mn;α、β、x、y为各元素原子百分比含量;其中,α为23%,β为7%,x为5%,y为8%。
实施例四
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu,二者各占50%;N为添加元素,选自Cr;α、β、x、y为各元素原子百分比含量;其中,α为23%,β为9%,x为5%,y为7%。
实施例五
一种耐腐蚀的电机用钕铁硼永磁,所述钕铁硼材料的组成为ReαBβMxNyFe1-α -β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu,二者各占50%;N为添加元素,包括选自Cr、Mn,其中Cr占60%,Mn占40%;α、β、x、y为各元素原子百分比含量;其中,α为23%,β为9%,x为5%,y为7%。
申请人声明,本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程,但本发明并不局限于上述详细工艺设备和工艺流程,即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (5)
1.一种耐腐蚀的电机用钕铁硼永磁,其特征在于,所述钕铁硼材料的组成为ReαBβMxNyFe1-α-β-x-y,其中:Re为稀土元素,为Nd、Dy与Ho的混合物,其中按重量百分比计,Nd为50%,Dy和Ho各占25%;M为添加元素,包括Co和Cu;N为添加元素,包括选自Ti、V、Cr、Mn、Ni、Zr、Nb、Mo和Bi的一种或一种以上元素;α、β、x、y为各元素原子百分比含量;其中,20%≤α≤25%,5%≤β≤12%,3%≤x≤7%,5%≤y≤10%。
2.如权利要求1所述的耐腐蚀的电机用钕铁硼永磁,其中Co和Cu各占50%。
3.如权利要求1所述的耐腐蚀的电机用钕铁硼永磁,其中N为Ti、Mn、Cr和V中的一种或两种。
4.如权利要求1所述的耐腐蚀的电机用钕铁硼永磁,其中22%≤α≤24%,7%≤β≤10%,4%≤x≤6%,6%≤y≤8%。
5.如权利要求4所述的耐腐蚀的电机用钕铁硼永磁,其中α为23%,β为9%,x为5%,y为7%。