CN102354473A - High-brightness long-afterglow luminescent indicator plate and preparation method thereof - Google Patents
High-brightness long-afterglow luminescent indicator plate and preparation method thereof Download PDFInfo
- Publication number
- CN102354473A CN102354473A CN2011103345823A CN201110334582A CN102354473A CN 102354473 A CN102354473 A CN 102354473A CN 2011103345823 A CN2011103345823 A CN 2011103345823A CN 201110334582 A CN201110334582 A CN 201110334582A CN 102354473 A CN102354473 A CN 102354473A
- Authority
- CN
- China
- Prior art keywords
- preparation
- substrate
- reflective membrane
- luminous
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-brightness long-afterglow luminescent indicator plate and a preparation method thereof. The preparation method comprises the following steps: pasting a reflective film on the front face of a substrate; spray-printing a luminous coating on the reflective film so as to form a graphical silkscreen; coating a diphenylethene-biphenyl sodium disulfonate fluorescent layer on the silkscreen; and coating a radiation-proof UV (ultraviolet) gloss oil protective layer on the reflective film which is not covered with graphs as well as the fluorescent layer. The preparation method of the luminous coating comprises the following steps: firstly pouring one third of a cristobalite transparent filler into a mixing tank, adding special light-transmitting resin, PE (polyethylene) resin and dioctyl phthalate (DOP), and then evenly stirring; and sequentially adding pigment, a nano rare-earth luminescent material, glass microspheres and the residual cristobalite transparent filler while stirring, and then evenly stirring for use. For the high-brightness long-afterglow luminescent indicator plate obtained by the preparation method, the brightness can reach 19,800mcd/m<2>, luminescence time can reach 10-14 hours in the case of single light absorption for 30 minutes, the minimum retro-reflection coefficient is cd.1*x<-1>m<-2> for various colors, the observation angle is 0.2 degree, and the incident angle is -4 degree. The high-brightness long-afterglow luminescent indicator plate has the advantages of endless cyclic energy storage, aging resistance, corrosion resistance, flame retardance, no toxicity, no harm, no radiation and energy conservation and is environmentally-friendly.
Description
Technical field
The present invention relates to a kind of energy-accumulating luminous label, be specifically related to a kind of high brightness, long-persistence luminous label, the invention still further relates to the preparation method of this luminescence scutcheon.
Background technology
Label relates to the important media in personal safety as well as the property safety field as safety, traffic, caution, prompting, fire-fighting etc., in productive life, is playing the part of indispensable role.From the angle of caution, prompting, label requires to have eye-catching understandable, long-lived characteristics usually.Present most sign manufacturing adopts common reflective membrane technology, and display effect is general, and display effect is poorer under dark environment such as night and misty rain weather, needs just can distinguish under the strong illumination.Because manufacture craft is coarse, use material poor, a lot of labels come into operation promptly begin soon to fade, get rusty, image comes off.Aging rapidly under solar radiation, wind and weather condition; Until corrosion damage; Thoroughly lose caution, suggesting effect, both brought great dangerous hidden danger, increase maintenance cost again to lives and properties; Therefore press for and employ new technology, guarantee that label can play the effect of caution, prompting really under various environment.
Energy-accumulating luminous label can improve the visual not enough shortcoming of common label; Make people rain, mist, dark, night visual isopter resolving ability difference environment descend without light-illuminating and just can clearly recognize label; Especially mountain area, township road lack lighting installation night; Common Scutcheon coating does not have the light-illuminating can not be reflective, makes pedestrian and bicycle end user can't see the sign label, causes dangerous the generation; Bring hidden danger to traffic safety, so be necessary to develop the label of suitable luminescent materials.The energy-storing self-luminescent label can active illuminating on the basis of satisfying the reflective requirement of label, has initiatively identifiability.Its visuality is superior to common label greatly under no light source, dark environment, lets the people can clear identification.Energy-storing self-luminescent label dispense with outer connecting power, but infinite loop is luminous, is energy-conserving and environment-protective product of new generation, is the developing direction that the national policy emphasis is supported.
Chinese patent CN1108413 discloses a kind of luminescence scutcheon and preparation method thereof, adopts electrostatic painting process to process protective layer on the card in one's hand surface, is becoming hide chromatograph and luminescent layer with silk screen process dry powder through high-temperature firing at character code pattern position again.The present invention adopts white resin dry powder to be fired into the screening chromatograph.Adopt luminescent material to become luminescent layer, utilize light shield layer to hide the dark brown protective layer with the transparent resin mixed sintering, bringing into play incandescnet particle effect in the luminescent layer to greatest extent, and keep incandescnet particle not with outside air contact with moisture, enhancing luminescence scutcheon luminous intensity.But still there is the problem that luminous intensity is low, fluorescent lifetime is short.
Summary of the invention
Technical matters to be solved by this invention provides a kind of energy-storing self-luminescent, long-lived high-brightness long persistence luminescence scutcheon.
For solving the problems of the technologies described above; The technical scheme that high-brightness long persistence luminescence scutcheon of the present invention is adopted is: it comprises substrate; The front of said substrate is provided with reflective membrane; Reflective membrane is provided with figure silk-screen layer, establishes talan biphenyl sodium disulfonate fluorescence coating on the silk-screen layer again, and figure does not reach and scribbled radiation proof UV gloss oil protective layer on the reflective membrane of figure covering and the fluorescence coating; Said silk-screen layer is a kind of luminous paint, and this luminous paint comprises following material by weight percentage:
Printing opacity is resin dedicated: 15~20;
PE resin: 0.8~1.2;
Dioctyl phthalate: 0.8~1.2;
Cristobalite transparent filler: 40~45;
The glass microballoon of granularity<150 μ m: 18~20;
EVA: 0.6~1.1;
Nano rare earth luminescent material: 14~20.
The present invention also provides the preparation method of above-mentioned high-brightness long persistence luminescence scutcheon, the steps include:
A) luminous paint preparation: at first pour 1/3rd cristobalite transparent filler into mixing kettle, add then that printing opacity is resin dedicated, PE resin, dioctyl phthalate, stir; Under stirring condition, add successively after pigment, nano rare earth luminescent material, glass microballoon and remaining cristobalite transparent filler stir, it is subsequent use to go out the still pack again;
B) luminescence scutcheon preparation: the geomery by regulation cuts substrate, the polishing burr; Reflective membrane is cut into size of substrate, is flattened on substrate front side; With the web plate centrally aligned substrate center of having carved figure; The luminous paint that has prepared is imprinted on the reflective membrane through the even spraying of web plate; Form luminous pattern silk-screen layer through the polymerization deposition reaction, on the silk-screen layer, evenly spray talan biphenyl sodium disulfonate again and form fluorescence coating; Figure reaches and is evenly sprayed the formation of one deck radiation proof UV gloss oil protective layer, desiccant dehumidification, check, packing again on the reflective membrane of figure covering and the fluorescence coating.
Label of the present invention adopts substrate, reflective membrane, silk-screen layer, fluorescence coating and protective layer; The silk-screen layer is printed as figure by luminous paint; And contain the nano rare earth luminescent material in the luminous paint, therefore, label of the present invention has the self luminous characteristic of high-brightness long persistence; And it is anti-aging, fire-retardant, anticorrosive, anti-oxidant, durable in use.Do not have radiation such as ultraviolet ray, infrared ray in the label autoluminescence spectrum, dazzle is little; Not containing any radioelement and heavy metal, do not pollute the environment, can not damage health, is new generation of green environment-friendly and energy-efficient product.Label of the present invention can be widely used in safe, caution, the prompting in fields such as traffic, fire-fighting, electric power, municipal administration, factories and miness, dwelling house, sight spot, military affairs, can play the effect of instant floor light in electric power supply inconvenience or the zone that often has a power failure.
The preparation method of label of the present invention is simple, practical, and use occasion that can be different according to label adopts different substrate materials to make, like various sheet metals, flame-proof PVC plate, plastic base, rubber, pottery, acrylic board, tempered glass, film etc.Adopt nano rare earth luminescent material and macromolecule resin to adopt in-situ inserted technology, implement link aggregation (HSL) and polymerization deposition (HSCVD), produce the energy-accumulating luminous label of high brightness, long afterglow.The luminosity of label is up to 19800mcd/ ㎡, and fluorescent lifetime reaches 10-14 hours under 30 minutes prerequisites of single extinction.Each color minimal reverse reflection coefficient cd1x 1m 2,0.2 ° of observation angle, incident angle-4 °.The infinite loop accumulation of energy, anti-aging, corrosion-resistant, fire-retardant, nontoxic, radiationless, energy-conserving and environment-protective.
Description of drawings
Fig. 1 is the exploded perspective view of luminescence scutcheon of the present invention;
Fig. 2 is the assembling synoptic diagram of luminescence scutcheon of the present invention;
Fig. 3 is the hole transfer mechanism figure of luminous paint among the present invention;
Fig. 4 is the spectral distribution graph of luminous paint among the present invention.
Embodiment
Share the track road signs with craspedodrome and right-hand rotation is example explanation the present invention.Visible by Fig. 1 and Fig. 2; High-brightness long persistence luminescence scutcheon of the present invention comprises substrate 1; The front of substrate 1 is provided with reflective membrane 2; Reflective membrane 2 is provided with figure silk-screen layer 3, establishes talan biphenyl sodium disulfonate fluorescence coating 4 on the silk-screen layer 3 again, and remaining reflective membrane 2 is provided with radiation proof UV gloss oil protective layer 5 with fluorescence coating 4.
Label of the present invention is made according to the geomery and the Graphics Design of national relevant industries standard-required.Said figure is word, figure or its combination.Concrete preparation method is:
A) luminous paint preparation: the cristobalite transparent filler that at first takes by weighing 2.8 ㎏ is poured mixing kettle into, then adds resin dedicated 1.8 ㎏ of printing opacity and PE resin 0.1 ㎏, dioctyl phthalate 0.1 ㎏, stirs; Under stirring condition, add successively after pigment, nano rare earth luminescent material 1.8 ㎏, glass microballoon 1.8 ㎏ and 1.4 ㎏ cristobalite transparent fillers stir, it is subsequent use to go out the still pack again;
B) luminescence scutcheon preparation: the geomery by regulation cuts substrate 1, the polishing burr; Reflective membrane 2 is cut into substrate 1 size, is flattened on substrate 1 front; With web plate centrally aligned substrate 1 center of having carved figure; The luminous paint that has prepared is imprinted on the reflective membrane 2 through the even spraying of web plate; Form luminous pattern silk-screen layer 3 through the polymerization deposition reaction, going up evenly at silk-screen layer 3 (only luminous pattern zone) again, spraying talan biphenyl sodium disulfonate forms fluorescence coating 4; Evenly do not sprayed one deck radiation proof UV gloss oil on the reflective membrane 2 of figure covering and the fluorescence coating 4 and form protective layer 5, desiccant dehumidification is checked appearance graphic, geomery, function (darkroom check) again, packs.
Raw material among the present invention is the commercially available prod; Wherein: the high-purity silicon dioxide product that the cristobalite transparent filler extract for the cristobalite ore deposit; EVA is a vinyl-vinyl acetate copolymer; The nano rare earth luminescent material is a novel rare-earth element aluminum Barbiturates material, and Science and Technology Ltd. produces by credit Dexing, Shenzhen.
The luminous paint that the present invention uses is to adopt the nano rare earth luminescent material formulated, and luminosity is up to 19800mcd/ ㎡, and fluorescent lifetime reaches 10-14 hours under 30 minutes prerequisites of single extinction.The nano rare earth raw material is mainly the light-accumulating luminous material of rear-earth-doped aluminate, has extremely strong extinction-hold light-luminous power, extremely long serviceable life (>=15 years); Can absorb repeatedly-store-visible emitting, (200-450nm), excitation source is easy to get excitation wavelength range; Sunshine or common daylight lamp get final product; Through absorbing ultraviolet or visible light, after being transformed, luminous energy is stored in the lattice, and can be luminous energy and luminous with Conversion of energy again in the dark.With Eu
2+The MAl2O4:Eu that activates
2+, RE
3+(M=alkali earth metal, RE=REE) for the hole transfer mechanism of the new type long-persistence luminescent material of representative referring to Fig. 3.
Visible by Fig. 3, because Eu
2+And RE
3+Introducing, in crystal lattice, produce defective, the different local level of the depth has just been arranged.At first, when luminophor receives ultraviolet light or solar light irradiation, luminescent center Eu
2+Ground state 4f7 (8S) Electron absorption photon to excited state 4f65d1 transition (1), on the 4f track, just produced an electron vacancy (being the hole), get back to ground state when combining when electronics jumps again with the hole, just produced luminous (2).The electronics that is in the valence band can obtain energy and fill up the hole on the 4f track from environment, on valence band, produce new hole simultaneously, and this process is equivalent to the hole and transfers to valence band and cause Eu
2+Become Eu
+(3).Move in valence band in hole in the valence band, then by RE
3+Defective can be with to capture and make RE
3+Change RE into
4+(4).Along with prolongation and the thermal perturbation of time, by RE
3+The hole of capturing obtains enough energy and comes back to valence band (5) from environment.Migration is continued in the hole of getting back in the valence band, when near Eu
+Local energy level the time again can be by Eu
+Capture and discharge photon and form twilight sunset (6) with the electron recombination of 4f65d1 configuration.The hole metastasis model is thought, RE
3+Effect be exactly the hole of capturing in the valence band, change the quantity and the concentration in hole, the hole is emitted in time prolongation and thermal perturbation then, makes luminescent center trapped hole again, and is luminous with electron recombination, thereby prolongs after time and reinforcement afterglow intensity.This novel nano rare earth luminescent material is compared with traditional zinc sulphide series luminescent powder, and it is stable to have chemical property, and light-accumulated luminous conversion efficiency is high, and is nontoxic, harmless, "dead", and production run also unharmful substance produces.
The product quality inspection center is detected through Anhui Province, and luminous paint meets GB/T 13306-2011 national standard.Visible light is the appreciable part of human eye in the electromagnetic wave spectrum, and visible spectrum does not have accurate scope; The appreciable electromagnetic wavelength of common people's eyes is between 400~700 nm, and the human eye of twenty-twenty vision is the most responsive to the electromagnetic wave that wavelength is about between 500~560 nm.Referring to the spectral distribution graph of Fig. 4, its luminescent light wave peak value is: 524nm, luminous radiance: 9.08 * i 0-6 (W/SR/M' ').Its luminous light wave just human eye to the most responsive wavelength coverage of light wave in.
This luminous paint is a kind of environmental protection, nontoxic, radiationless, pollution-free product.Inspection center of technical quality surveillance authority is detected through Anhui Province, meets GB/T 6566-2001 standard, reaches the category-A finishing material, and detected value is lower 50 times than standard value.There is not harm for human body, directly contacting skin.
The parameters of label of the present invention is:
1, product composition: base material, nano rare earth luminescent material;
2, luminosity: 19800mcd/ ㎡;
3, fluorescent lifetime: single extinction 30 minutes, can be at the dark place luminous 10-14 hours;
4, glow color: gold-tinted, blue light etc.;
5, material hardness: soft or hard all can;
6, reflective parameter: each color minimal reverse reflection coefficient cd1x 1m 2,0.2 ° of observation angle, incident angle-4 °;
7, properties of product: infinite loop accumulation of energy, anti-aging, corrosion-resistant, fire-retardant, nontoxic, radiationless, energy-conserving and environment-protective;
8, installation method: inserted, riveted type, suspension type, paste formula etc.
Claims (2)
1. high-brightness long persistence luminescence scutcheon; Comprise substrate; It is characterized in that: the front of said substrate (1) is provided with reflective membrane (2); Reflective membrane (2) is provided with figure silk-screen layer (3), establishes talan biphenyl sodium disulfonate fluorescence coating (4) on the silk-screen layer (3) again, and figure and the reflective membrane (2) and the fluorescence coating (4) that are not hidden by figure are provided with radiation proof UV gloss oil protective layer (5); Said silk-screen layer is a kind of luminous paint, and this luminous paint comprises following material by weight percentage:
Printing opacity is resin dedicated: 15~20;
PE resin: 0.8~1.2;
Dioctyl phthalate: 0.8~1.2;
Cristobalite transparent filler: 40~45;
The glass microballoon of granularity<150 μ m: 18~20;
EVA: 0.6~1.1;
Nano rare earth luminescent material: 14~20.
2. the preparation method of a high-brightness long persistence luminescence scutcheon as claimed in claim 1 the steps include:
A) luminous paint preparation: at first pour 1/3rd cristobalite transparent filler into mixing kettle, add then that printing opacity is resin dedicated, PE resin, dioctyl phthalate, stir; Under stirring condition, add successively after pigment, nano rare earth luminescent material, glass microballoon and remaining cristobalite transparent filler stir, it is subsequent use to go out the still pack again;
B) luminescence scutcheon preparation: the geomery by regulation cuts substrate (1), the polishing burr; Reflective membrane (2) is cut into substrate (1) size, is flattened on the positive formation of substrate (1); With web plate centrally aligned substrate (1) center of having carved figure; The luminous paint that has prepared is imprinted on the reflective membrane (2) through the even spraying of web plate; Form luminous pattern silk-screen layer (3) through the polymerization deposition reaction, going up evenly at silk-screen layer (3) again, spraying talan biphenyl sodium disulfonate forms fluorescence coating (4); Figure and the reflective membrane (2) and the upward even spraying one deck of fluorescence coating (4) radiation proof UV gloss oil that are not hidden by figure form protective layer (5), desiccant dehumidification, check, packing again.