CN102351518A - Ceramic blank - Google Patents

Ceramic blank Download PDF

Info

Publication number
CN102351518A
CN102351518A CN2011101671372A CN201110167137A CN102351518A CN 102351518 A CN102351518 A CN 102351518A CN 2011101671372 A CN2011101671372 A CN 2011101671372A CN 201110167137 A CN201110167137 A CN 201110167137A CN 102351518 A CN102351518 A CN 102351518A
Authority
CN
China
Prior art keywords
ceramic blank
ceramic body
ignition
calcination temperature
ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101671372A
Other languages
Chinese (zh)
Inventor
郑泽洽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEHUA SHUNERMEI CRAFTS Co Ltd
Original Assignee
DEHUA SHUNERMEI CRAFTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEHUA SHUNERMEI CRAFTS Co Ltd filed Critical DEHUA SHUNERMEI CRAFTS Co Ltd
Priority to CN2011101671372A priority Critical patent/CN102351518A/en
Publication of CN102351518A publication Critical patent/CN102351518A/en
Pending legal-status Critical Current

Abstract

The invention relates to a ceramic blank. The ceramic blank comprises the following components, by weight, 48-52% of SiO2, 14-17% of Al2O3, 0.3-0.8% of Fe2O3, 0.01-0.03% of TiO2, 6-10% of CaO, 4-8% of MgO, 1-3% of K2O, 0.3-0.6% of Na2O, and the balance loss on ignition, wherein the calcination temperature of the ceramic blank is 1030-1050DEG C. Compared with the prior art, a unique selection of the chemical components of the ceramic blank of the invention, which is carried out in the invention, allows the calcination temperature of the ceramic blank to be low, so the energy consumption for calcinating the ceramic blank is substantially reduced, thereby the ceramic blank has the advantages of accordance of a large trend of energy saving and emission reduction in the modern society, enterprise production cost reduction, and enterprise market competitiveness enhancement.

Description

A kind of ceramic body
Technical field
The present invention relates to a kind of ceramic body.
Background technology
Base substrate is the body material of ceramics component; Pottery of the prior art is no matter be once-firing or twice is burnt till; The firing temperature of its ceramic body is basically all at 1200 and even 1400 ℃, and is very big to the consumption of resource, do not meet overall situation, the megatrend of modern society's energy-saving and emission-reduction.
Summary of the invention
Main purpose of the present invention is to overcome the too high shortcoming of ceramic body firing temperature in the prior art, provides a kind of firing temperature lower ceramic body, thereby reduces energy-output ratio greatly.
The present invention adopts following technical scheme:
A kind of ceramic body, form by following components in weight percentage:
SiO 248-52％
Al 2O 314-17％
Fe 2O 30.3-0.8％
TiO 20.01-0.03％
CaO6-10％
MgO4-8％
K 2O1-3％
Na 2O?0.3-0.6％
The loss on ignition surplus.
The firing temperature of this ceramic body is 1030-1050 ℃.
Can know by the above-mentioned description of this invention; Compared with prior art; A kind of ceramic body of the present invention is owing to carried out unique selection to its chemical ingredients; Make it have lower firing temperature; Thereby reduce ceramic body greatly and burn till consumption the energy; The megatrend that not only meets modern society's energy-saving and emission-reduction has also reduced the production cost of enterprise, strengthens the market competitiveness of enterprise.
Embodiment
Embodiment one
A kind of ceramic body, form by following components in weight percentage:
SiO 249％
Al 2O 315％
Fe 2O 30.45％
TiO 20.02％
CaO?7.85％
MgO?6.02％
K 2O 1.5％
Na 2O 0.38％
The loss on ignition surplus.
The firing temperature of this ceramic body is 1035 ℃.
Embodiment two
A kind of ceramic body, form by following components in weight percentage:
SiO 251％
Al 2O 316.5％
Fe 2O 30.7％
TiO 20.025％
CaO 9％
MgO?7％
K 2O 2.5％
Na 2O 0.55％
The loss on ignition surplus.
The firing temperature of this ceramic body is 1045 ℃.
Embodiment three
A kind of ceramic body, form by following components in weight percentage:
SiO 250.9％
Al 2O 315.7％
Fe 2O 3?0.5％
TiO 20.02％
CaO 8.15％
MgO?5.89％
K 2O 1.69％
Na 2O 0.48％
The loss on ignition surplus.
The firing temperature of this ceramic body is 1040 ℃.
Above-mentioned only is several embodiment of the present invention, but design concept of the present invention is not limited thereto, and allly utilizes this design that the present invention is carried out the change of unsubstantiality, all should belong to the behavior of invading protection domain of the present invention.

Claims (2)

1. ceramic body is characterized in that: be made up of following components in weight percentage:
SiO 248-52％
Al 2O 314-17％
Fe 2O 3?0.3-0.8％
TiO 20.01-0.03％
CaO?6-10％
MgO?4-8％
K 2O 1-3％
Na 2O 0.3-0.6％
The loss on ignition surplus.
2. a kind of ceramic body as claimed in claim 1 is characterized in that: the firing temperature of this ceramic body is 1030-1050 ℃.
CN2011101671372A 2011-06-17 2011-06-17 Ceramic blank Pending CN102351518A (en)