CN102344732A - 一种涂料及其制备方法 - Google Patents
一种涂料及其制备方法 Download PDFInfo
- Publication number
- CN102344732A CN102344732A CN2011102498747A CN201110249874A CN102344732A CN 102344732 A CN102344732 A CN 102344732A CN 2011102498747 A CN2011102498747 A CN 2011102498747A CN 201110249874 A CN201110249874 A CN 201110249874A CN 102344732 A CN102344732 A CN 102344732A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- paint
- agent
- rotating speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种涂料及其制备方法，按照重量分数计原料中包含以下组分：聚苯乙烯空心微球100-200份，硅酸铝30-125份，高岭土30-135份，增稠剂2-5份，消泡剂1-10份，分散剂1-10份，乙二醇8-38份，润湿剂3-10份，乳胶漆乳液180-550份，水100-350份。本发明涂料是由一些悬浮于惰性乳胶中的聚苯乙烯空心微球构成，该微球的微观结构有利于对红外线的反射和散射，另外本发明的微球为密闭空心球体，导热系数很低，添加进涂料中可形成很多微观的独立绝热腔体，从而大大提高涂膜的隔热性。
Description
技术领域
本发明属于涂料领域，尤其涉及一种用于建筑表面的隔热涂料及其制备方法。
背景技术
目前，我国现有的建筑物墙体保温涂料通常是以提高气相空隙率、降低导热系数和传导传热为主，例如纤维类保温材料和型材类保温材料。型材类无机保温材料需要拼装施工，存在接缝多、影响美观、防水性差、使用寿命短等缺点，纤维类保温材料是通过提高对流传热和辐射传热实现保温隔热，需要有较厚的涂层，且隔热效果不好。
发明内容
本发明设计了一种涂料及其制备方法，其目的是提供一种具有高效隔热功能且环保无污染的涂料。
为了实现上述目的，本发明采用了以下方案：
一种涂料，其特征在于：按照重量分数计原料中包含以下组分：
聚苯乙烯空心微球100-200份，
硅酸铝30-125份，
高岭土30-135份，
增稠剂2-5份，
消泡剂1-10份，
分散剂1-10份，
乙二醇8-38份，
润湿剂3-10份，
乳胶漆乳液180-550份，
水100-350份。
所述涂料的组分中还含有三乙胺pH调节剂3-10份。
所述涂料的组分中还含有防腐剂2-3份。
所述的润湿剂为聚异氰酸酯类物质。
所述的聚苯乙烯微球的直径为30-115微米。
一种涂料的制备方法，其特征在于：
(1)按比例称取各原料;
(2)将水和助剂加入搅拌机中，1000-3000 rpm转速下搅拌至均匀;
(3)加入乳胶漆乳液，1000-3000rpm转速下搅拌至均匀;
(4)加入填料，600-900rpm转速下搅拌至均匀;
(5)经150-180目筛过筛。
所述的涂料在建筑物、油罐或集装箱墙体的应用，其特征在于：将所述反射隔热、保温涂层材料涂敷或喷涂于所述墙体的内侧或外侧，涂层厚度为小于1.5mm。
该涂料及其制备方法具有以下有益效果：
（1）本发明涂料是由一些悬浮于惰性乳胶中的聚苯乙烯空心微球构成，该微球的粒径属于红外线波长范围，因此涂层表面的微观结构有利于对红外线的反射和散射，从而能够反射太阳热。
（2）本发明涂料微球为密闭空心球体，导热系数很低，添加进涂料中可形成很多微观的独立绝热腔体，从而大大提高涂膜的隔热性。
（3）本发明涂料制备方法科学，流程简单，适于规模化生产加工。
具体实施方式
下面结合实施例，对本发明做进一步说明：
实施例1
涂料的生产方法：
按照重量分数计称取以下组分：聚苯乙烯空心微球180份，硅酸铝90份，高岭土125份，增稠剂5份，消泡剂2份，分散剂5份，乙二醇35份，聚氧化丙烯类润湿剂4份，纯丙乳液500份，水120份。涂料的组分中还含有三乙胺pH调节剂5份，防腐剂2份。将水和增稠剂，消泡剂，分散剂，乙二醇，氢氧化钠pH调节剂和防腐剂加入搅拌机中，1500rpm转速下搅拌至均匀;加入纯丙乳液，1800rpm转速下搅拌至均匀;加入聚苯乙烯空心微球、硅酸铝和高岭土，800rpm转速下搅拌至均匀;经165目筛过筛。
经测试，其拉伸强度大于1MPa，太阳反射比大于0.8，导热系数大于0.04。
上面结合具体实施例对本发明进行了示例性的描述，显然本发明的实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的各种改进，或未经改进将本发明的构思和技术方案直接应用于其它场合的，均在本发明的保护范围内。
Claims (7)
1.一种涂料，其特征在于：按照重量分数计原料中包含以下组分：
聚苯乙烯空心微球100-200份，
硅酸铝30-125份，
高岭土30-135份，
增稠剂2-5份，
消泡剂1-10份，
分散剂1-10份，
乙二醇8-38份，
润湿剂3-10份，
乳胶漆乳液180-550份，
水100-350份。
2.根据权利要求1所述涂料，其特征在于：所述涂料的组分中还含有三乙胺pH调节剂3-10份。
3.根据权利要求1或2所述涂料，其特征在于：所述涂料的组分中还含有防腐剂2-3份。
4.根据权利要求1所述涂料，其特征在于：所述的润湿剂为聚异氰酸酯类物质。
5.根据权利要求1或4所述涂料，其特征在于：所述的聚苯乙烯微球的直径为30-115微米。
6.一种根据权利要求1-5所述涂料的制备方法，其特征在于：
(1)按比例称取各原料;
(2)将水和助剂加入搅拌机中，1000-3000 rpm转速下搅拌至均匀;
(3)加入乳胶漆乳液，1000-3000rpm转速下搅拌至均匀;
(4)加入填料，600-900rpm转速下搅拌至均匀;
(5)经150-180目筛过筛。
7.根据权利要求1-5所述的涂料在建筑物、油罐或集装箱墙体的应用，其特征在于：将所述反射隔热、保温涂层材料涂敷或喷涂于所述墙体的内侧或外侧，涂层厚度为小于1.5mm。