CN102344707A - Fire resisting paint - Google Patents
Fire resisting paint Download PDFInfo
- Publication number
- CN102344707A CN102344707A CN2010102451252A CN201010245125A CN102344707A CN 102344707 A CN102344707 A CN 102344707A CN 2010102451252 A CN2010102451252 A CN 2010102451252A CN 201010245125 A CN201010245125 A CN 201010245125A CN 102344707 A CN102344707 A CN 102344707A
- Authority
- CN
- China
- Prior art keywords
- paint
- gram
- mixture additive
- pitch
- borax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fire resistant paint, comprising a mixture additive and an anion ecological paint, wherein, the mixture additive comprises 30-55 wt% of asphalt, 15-30 wt% of mineral spirit, 5-15 wt% of vermiculite, 5-15 wt% of fine asbestos, 2-3 wt% of borax, and 5-10 wt% of mica powder. The fire resistant paint is mainly applied on utensils and furniture, and can resist flame when a fire starts.
Description
Technical field
The present invention relates to a kind of paint, be specifically related to a kind of retardant paint with fire-proof function.
Background technology
Common paint does not have the fp function, can cause the loss that is difficult to remedy in case run into fire etc.And common paint contains toxic substances such as benzene, and life-time service is harmful to HUMAN HEALTH.
Summary of the invention
Goal of the invention: the objective of the invention is provides a kind of fire line strong retardant paint for solving the deficiency of prior art.
The technical scheme that the present invention adopts: a kind of retardant paint, component that retardant paint comprised and weight percent thereof are:
Pitch 30~55%
Mineral turpentine 15~30%
Vermiculite 5~15%
Thin smart asbestos 5~15%
Borax 2~3%
Mica powder 5~10%
Pitch, mineral turpentine, vermiculite, thin smart asbestos, borax, mica powder are mixed, and the mixture additive in the retardant paint accounts for 0.5~2% of paint total amount.
Beneficial effect: the present invention joins in the paint after chemical substances such as pitch, mineral turpentine, vermiculite, thin smart asbestos, borax, mica powder are mixed; This paint is coated on implements and the furniture; Paint is kept out fire and flare through the power of the burning generation recoil of self; Big fire can not the degree of depth be burnt, and then reach the fp purpose.
Embodiment:
Elaborate in the face of embodiments of the invention down.
Embodiment 1
450 gram pitch, 200 gram mineral turpentine, 150 gram vermiculites, the thin smart asbestos of 100 grams, 20 gram boraxs, 80 gram mica powders are mixed, 20 gram mixture additives are joined 1000 gram anion ecological paint, stir, grind again, increase its viscosity.
Embodiment 2
500 gram pitch, 250 gram mineral turpentine, 100 gram vermiculites, the thin smart asbestos of 100 grams, 20 gram boraxs, 80 gram mica powders are mixed, 20 gram mixture additives are joined 1000 gram anion ecological paint, stir, grind again, increase its viscosity.
Embodiment 1
400 gram pitch, 250 gram mineral turpentine, 100 gram vermiculites, the thin smart asbestos of 150 grams, 20 gram boraxs, 80 gram mica powders are mixed, 20 gram mixture additives are joined 1000 gram anion ecological paint, stir, grind again, increase its viscosity.
Claims (3)
1. a retardant paint comprises mixture additive and anion ecological paint, and it is characterized in that: described mixture additive is mixed and made into by pitch, mineral turpentine, vermiculite, thin smart asbestos, borax, mica powder.
2. retardant paint according to claim 1, it is characterized in that: component that described mixture additive comprised and weight percent thereof are:
Pitch 30~55%
Mineral turpentine 15~30%
Vermiculite 5~15%
Thin smart asbestos 5~15%
Borax 2~3%
Mica powder 5~10%
3. retardant paint according to claim 1 is characterized in that: the mixture additive in the retardant paint accounts for 0.5~2% of paint total amount.