CN106118166A - A kind of construction material environmental protection flame retardant acid and alkali-resistance processes coating - Google Patents

A kind of construction material environmental protection flame retardant acid and alkali-resistance processes coating Download PDF

Info

Publication number
CN106118166A
CN106118166A CN201610552796.0A CN201610552796A CN106118166A CN 106118166 A CN106118166 A CN 106118166A CN 201610552796 A CN201610552796 A CN 201610552796A CN 106118166 A CN106118166 A CN 106118166A
Authority
CN
China
Prior art keywords
parts
powder
alkali
acid
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610552796.0A
Other languages
Chinese (zh)
Inventor
余志娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610552796.0A priority Critical patent/CN106118166A/en
Publication of CN106118166A publication Critical patent/CN106118166A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of construction material environmental protection flame retardant acid and alkali-resistance and process coating, composed of the following components: phenyl triethoxysilane, lithium phosphate powder, sodium soap, Oleum Glycines, Bravo, Flos Camelliae Japonicae powder, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene butadiene styrene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, ethylparaben, sym-closene, Mentholum, 5 aminobenzimidazole ketone, tourmaline powder, molybdenum silicide powder, ferric chloride, oxidized paraffin wax, aromatic naphtha, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl phosphate ester.Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.

Description

A kind of construction material environmental protection flame retardant acid and alkali-resistance processes coating
Technical field
The present invention relates to a kind of construction material environmental protection flame retardant acid and alkali-resistance and process coating, belong to building materials technical field of coatings.
Background technology
Building materials are the general designations of material used in civil engineering and architectural engineering, can be divided into structural material, ornament materials and Some proprietary material.Proprietary material refer to for waterproof, moistureproof, anticorrosion, fire prevention, fire-retardant, sound insulation, heat insulation, be incubated, sealing etc..Every Sound material refers to the isolation of noise propagated in air, a kind of material, component or the structure cutting off, separate.Sound insulating material material Requirement be closely knit imporosity or gap；There is bigger weight.Owing to this kind of sound insulating material is closely knit, it is difficult to absorb and pass through acoustic energy And it is strong to reflect energy, so its sound absorbing capabilities is poor.Fire proofing be can suppress or retardation burning and oneself be not easy to combustion The material burnt, is widely used in the fields such as clothing, oil, chemical industry, metallurgy, shipbuilding, fire-fighting, national defence.
Summary of the invention
It is an object of the invention to provide a kind of construction material environmental protection flame retardant acid and alkali-resistance and process coating, in order to be better achieved Construction material environmental protection flame retardant acid and alkali-resistance processes the use function of coating, makes product have fire-retardant, acid and alkali-resistance, anti-mildew antibiotic property Can, improve product serviceability.
To achieve these goals, technical scheme is as follows.
A kind of construction material environmental protection flame retardant acid and alkali-resistance processes coating, is made up of the component of following mass fraction: phenyl three second TMOS 18～22 parts, lithium phosphate powder 16～20 parts, sodium soap 16～20 parts, Oleum Glycines 14～18 parts, Bravo 16 ～20 parts, Flos Camelliae Japonicae powder 16～20 parts, zinc sulfide powder 14～18 parts, jade powder 16～20 parts, flake asbestos 16～20 parts, hydrogenation fourth Nitrile rubber 14～18 parts, double stearic acid aluminium 14～18 parts, sucrose 14～18 parts, styrene butadiene styrene block copolymer (SBS) 16～20 parts, fluorubber 14～18 parts, polyacrylonitrile fibre 12～16 parts, hexahydro phthalic anhydride 16～20 parts, metatitanic acid N-butyl 14～18 parts, ethylparaben 12～16 parts, sym-closene 14～18 parts, Mentholum 12～16 parts, 5-Amino-2-benzimidazolinone 12～16 parts, tourmaline powder 14～18 parts, molybdenum silicide powder 14～18 parts, ferric chloride 14～18 Part, oxidized paraffin wax 14～18 parts, aromatic naphtha 14～18 parts, mandarin oil 14～18 parts, polyacrylate emulsion 14～18 parts, acrylic acid Hydroxyl ethyl ester 14～18 parts, alkyl diphenyl phosphate ester 12～16 parts.
Further, above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 18 parts, 16 parts of lithium phosphate powder, sodium soap 16 parts, Oleum Glycines 14 parts, Bravo 16 parts, Flos Camelliae Japonicae powder 16 parts, zinc sulfide powder 14 parts, jade powder 16 parts, flake asbestos 16 parts, hydrogenated nitrile-butadiene rubber 14 parts, double stearic acid aluminium 14 parts, sugarcane Sugar 14 parts, styrene butadiene styrene block copolymer (SBS) 16 parts, fluorubber 14 parts, polyacrylonitrile fibre 12 parts, hexahydro Phthalic anhydride 16 parts, tetrabutyl titanate 14 parts, ethylparaben 12 parts, sym-closene 14 parts, Mentholum 12 parts, 5-Amino-2-benzimidazolinone 12 parts, tourmaline powder 14 parts, molybdenum silicide powder 14 parts, ferric chloride 14 parts, oxidized paraffin wax 14 parts, aromatic naphtha 14 parts, mandarin oil 14 parts, polyacrylate emulsion 14 parts, 2-(Acryloyloxy)ethanol 14 parts, alkyl diphenyl phosphate ester 12 Part.
Further, above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 20 parts, 18 parts of lithium phosphate powder, sodium soap 18 parts, Oleum Glycines 16 parts, Bravo 18 parts, Flos Camelliae Japonicae powder 18 parts, zinc sulfide powder 16 parts, jade powder 18 parts, flake asbestos 18 parts, hydrogenated nitrile-butadiene rubber 16 parts, double stearic acid aluminium 16 parts, sugarcane Sugar 16 parts, styrene butadiene styrene block copolymer (SBS) 18 parts, fluorubber 16 parts, polyacrylonitrile fibre 14 parts, hexahydro Phthalic anhydride 18 parts, tetrabutyl titanate 16 parts, ethylparaben 14 parts, sym-closene 16 parts, Mentholum 14 parts, 5-Amino-2-benzimidazolinone 14 parts, tourmaline powder 16 parts, molybdenum silicide powder 16 parts, ferric chloride 16 parts, oxidized paraffin wax 16 parts, aromatic naphtha 16 parts, mandarin oil 16 parts, polyacrylate emulsion 16 parts, 2-(Acryloyloxy)ethanol 16 parts, alkyl diphenyl phosphate ester 14 Part.
Further, above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 22 parts, 20 parts of lithium phosphate powder, sodium soap 20 parts, Oleum Glycines 18 parts, Bravo 20 parts, Flos Camelliae Japonicae powder 20 parts, zinc sulfide powder 18 parts, jade powder 20 parts, flake asbestos 20 parts, hydrogenated nitrile-butadiene rubber 18 parts, double stearic acid aluminium 18 parts, sugarcane Sugar 18 parts, styrene butadiene styrene block copolymer (SBS) 20 parts, fluorubber 18 parts, polyacrylonitrile fibre 16 parts, hexahydro Phthalic anhydride 20 parts, tetrabutyl titanate 18 parts, ethylparaben 16 parts, sym-closene 18 parts, Mentholum 16 parts, 5-Amino-2-benzimidazolinone 16 parts, tourmaline powder 18 parts, molybdenum silicide powder 18 parts, ferric chloride 18 parts, oxidized paraffin wax 18 parts, aromatic naphtha 18 parts, mandarin oil 18 parts, polyacrylate emulsion 18 parts, 2-(Acryloyloxy)ethanol 18 parts, alkyl diphenyl phosphate ester 16 Part.
Further, above-mentioned construction material environmental protection flame retardant acid and alkali-resistance process coating production step is as follows:
(1) by the phenyl triethoxysilane of described mass fraction, lithium phosphate powder, sodium soap, Oleum Glycines, hundred bacterium Clearly, Flos Camelliae Japonicae powder, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene-fourth two Alkene-styrene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, to hydroxyl Ethyl benzoate, sym-closene, Mentholum are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, point Dissipating speed 5000～about 5400r/min, jitter time is 30～60min；
(2) add the 5-Amino-2-benzimidazolinone of described mass fraction, tourmaline powder, molybdenum silicide powder, ferric chloride, Oxidized paraffin wax, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, dispersion Time is 30～50min；
(3) aromatic naphtha of described mass fraction, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl are added Phosphate ester, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion 4600～about 4800r/min, during dispersion Between be 20～40min；This product is prepared after mix homogeneously.
This beneficial effect of the invention is: the construction material environmental protection flame retardant acid and alkali-resistance in the present invention processes coating, by following Component forms: phenyl triethoxysilane, lithium phosphate powder, sodium soap, Oleum Glycines, Bravo, Flos Camelliae Japonicae powder, zinc sulphide powder End, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene butadiene styrene block copolymer (SBS), Fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, ethylparaben, trichlorine isocyanide are urinated Acid, Mentholum, 5-Amino-2-benzimidazolinone, tourmaline powder, molybdenum silicide powder, ferric chloride, oxidized paraffin wax, aromatic naphtha, Fructus Citri tangerinae Seed oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl phosphate ester.Product of the present invention has the most superior fire-retardant, resistance to Soda acid, anti-mildew anti-microbial property, improve properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Construction material environmental protection flame retardant acid and alkali-resistance in the present embodiment processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 18 parts, 16 parts of lithium phosphate powder, sodium soap 16 parts, Oleum Glycines 14 parts, Bravo 16 parts, Flos Camelliae Japonicae powder 16 parts, zinc sulfide powder 14 parts, jade powder 16 parts, flake asbestos 16 parts, hydrogenated nitrile-butadiene rubber 14 parts, double stearic acid aluminium 14 parts, sugarcane Sugar 14 parts, styrene butadiene styrene block copolymer (SBS) 16 parts, fluorubber 14 parts, polyacrylonitrile fibre 12 parts, hexahydro Phthalic anhydride 16 parts, tetrabutyl titanate 14 parts, ethylparaben 12 parts, sym-closene 14 parts, Mentholum 12 parts, 5-Amino-2-benzimidazolinone 12 parts, tourmaline powder 14 parts, molybdenum silicide powder 14 parts, ferric chloride 14 parts, oxidized paraffin wax 14 parts, aromatic naphtha 14 parts, mandarin oil 14 parts, polyacrylate emulsion 14 parts, 2-(Acryloyloxy)ethanol 14 parts, alkyl diphenyl phosphate ester 12 Part.
It is as follows that above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating production step:
(1) by the phenyl triethoxysilane of described mass fraction, lithium phosphate powder, sodium soap, Oleum Glycines, hundred bacterium Clearly, Flos Camelliae Japonicae powder, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene-fourth two Alkene-styrene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, to hydroxyl Ethyl benzoate, sym-closene, Mentholum are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, dispersion speed Degree about 5400r/min, jitter time is 60min；
(2) add the 5-Amino-2-benzimidazolinone of described mass fraction, tourmaline powder, molybdenum silicide powder, ferric chloride, Oxidized paraffin wax, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) aromatic naphtha of described mass fraction, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl are added Phosphate ester, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min； This product is prepared after mix homogeneously.
Embodiment 2
Construction material environmental protection flame retardant acid and alkali-resistance in the present embodiment processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 20 parts, 18 parts of lithium phosphate powder, sodium soap 18 parts, Oleum Glycines 16 parts, Bravo 18 parts, Flos Camelliae Japonicae powder 18 parts, zinc sulfide powder 16 parts, jade powder 18 parts, flake asbestos 18 parts, hydrogenated nitrile-butadiene rubber 16 parts, double stearic acid aluminium 16 parts, sugarcane Sugar 16 parts, styrene butadiene styrene block copolymer (SBS) 18 parts, fluorubber 16 parts, polyacrylonitrile fibre 14 parts, hexahydro Phthalic anhydride 18 parts, tetrabutyl titanate 16 parts, ethylparaben 14 parts, sym-closene 16 parts, Mentholum 14 parts, 5-Amino-2-benzimidazolinone 14 parts, tourmaline powder 16 parts, molybdenum silicide powder 16 parts, ferric chloride 16 parts, oxidized paraffin wax 16 parts, aromatic naphtha 16 parts, mandarin oil 16 parts, polyacrylate emulsion 16 parts, 2-(Acryloyloxy)ethanol 16 parts, alkyl diphenyl phosphate ester 14 Part.
It is as follows that above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating production step:
(1) by the phenyl triethoxysilane of described mass fraction, lithium phosphate powder, sodium soap, Oleum Glycines, hundred bacterium Clearly, Flos Camelliae Japonicae powder, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene-fourth two Alkene-styrene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, to hydroxyl Ethyl benzoate, sym-closene, Mentholum are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, dispersion speed Degree about 5200r/min, jitter time is 45min；
(2) add the 5-Amino-2-benzimidazolinone of described mass fraction, tourmaline powder, molybdenum silicide powder, ferric chloride, Oxidized paraffin wax, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) aromatic naphtha of described mass fraction, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl are added Phosphate ester, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min； This product is prepared after mix homogeneously.
Embodiment 3
Construction material environmental protection flame retardant acid and alkali-resistance in the present embodiment processes coating, is made up of the component of following mass fraction: Phenyl triethoxysilane 22 parts, 20 parts of lithium phosphate powder, sodium soap 20 parts, Oleum Glycines 18 parts, Bravo 20 parts, Flos Camelliae Japonicae powder 20 parts, zinc sulfide powder 18 parts, jade powder 20 parts, flake asbestos 20 parts, hydrogenated nitrile-butadiene rubber 18 parts, double stearic acid aluminium 18 parts, sugarcane Sugar 18 parts, styrene butadiene styrene block copolymer (SBS) 20 parts, fluorubber 18 parts, polyacrylonitrile fibre 16 parts, hexahydro Phthalic anhydride 20 parts, tetrabutyl titanate 18 parts, ethylparaben 16 parts, sym-closene 18 parts, Mentholum 16 parts, 5-Amino-2-benzimidazolinone 16 parts, tourmaline powder 18 parts, molybdenum silicide powder 18 parts, ferric chloride 18 parts, oxidized paraffin wax 18 parts, aromatic naphtha 18 parts, mandarin oil 18 parts, polyacrylate emulsion 18 parts, 2-(Acryloyloxy)ethanol 18 parts, alkyl diphenyl phosphate ester 16 Part.
It is as follows that above-mentioned construction material environmental protection flame retardant acid and alkali-resistance processes coating production step:
(1) by the phenyl triethoxysilane of described mass fraction, lithium phosphate powder, sodium soap, Oleum Glycines, hundred bacterium Clearly, Flos Camelliae Japonicae powder, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene-fourth two Alkene-styrene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, to hydroxyl Ethyl benzoate, sym-closene, Mentholum are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, dispersion speed Degree 5000r/min, jitter time is 30min；
(2) add the 5-Amino-2-benzimidazolinone of described mass fraction, tourmaline powder, molybdenum silicide powder, ferric chloride, Oxidized paraffin wax, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) aromatic naphtha of described mass fraction, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl are added Phosphate ester, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min； This product is prepared after mix homogeneously.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as Protection scope of the present invention.

Claims (5)

1. a construction material environmental protection flame retardant acid and alkali-resistance processes coating, it is characterised in that: it is made up of the component of following mass fraction: Phenyl triethoxysilane 18～22 parts, lithium phosphate powder 16～20 parts, sodium soap 16～20 parts, Oleum Glycines 14～18 parts, Bravo 16～20 parts, Flos Camelliae Japonicae powder 16～20 parts, zinc sulfide powder 14～18 parts, jade powder 16～20 parts, flake asbestos 16～20 Part, hydrogenated nitrile-butadiene rubber 14～18 parts, double stearic acid aluminium 14～18 parts, sucrose 14～18 parts, s-B-S Block copolymer 16～20 parts, fluorubber 14～18 parts, polyacrylonitrile fibre 12～16 parts, hexahydro phthalic anhydride 16～ 20 parts, tetrabutyl titanate 14～18 parts, ethylparaben 12～16 parts, sym-closene 14～18 parts, Mentholum 12～16 parts, 5-Amino-2-benzimidazolinone 12～16 parts, tourmaline powder 14～18 parts, molybdenum silicide powder 14～18 parts, trichlorine Change ferrum 14～18 parts, oxidized paraffin wax 14～18 parts, aromatic naphtha 14～18 parts, mandarin oil 14～18 parts, polyacrylate emulsion 14～ 18 parts, 2-(Acryloyloxy)ethanol 14～18 parts, alkyl diphenyl phosphate ester 12～16 parts.
Construction material environmental protection flame retardant acid and alkali-resistance the most according to claim 1 processes coating, it is characterised in that: described Building wood Material environmental protection flame retardant acid and alkali-resistance processes coating and is made up of the component of following mass fraction: phenyl triethoxysilane 18 parts, lithium phosphate 16 parts of powder, sodium soap 16 parts, Oleum Glycines 14 parts, Bravo 16 parts, Flos Camelliae Japonicae powder 16 parts, zinc sulfide powder 14 parts, jade powder 16 parts, flake asbestos 16 parts, hydrogenated nitrile-butadiene rubber 14 parts, double stearic acid aluminium 14 parts, sucrose 14 parts, s-B-S Block copolymer 16 parts, fluorubber 14 parts, polyacrylonitrile fibre 12 parts, hexahydro phthalic anhydride 16 parts, tetrabutyl titanate 14 parts, ethylparaben 12 parts, sym-closene 14 parts, Mentholum 12 parts, 5-Amino-2-benzimidazolinone 12 parts, electricity Gas stone powder 14 parts, molybdenum silicide powder 14 parts, ferric chloride 14 parts, oxidized paraffin wax 14 parts, aromatic naphtha 14 parts, mandarin oil 14 parts, Polyacrylate emulsion 14 parts, 2-(Acryloyloxy)ethanol 14 parts, alkyl diphenyl phosphate ester 12 parts.
3. process coating according to the construction material environmental protection flame retardant acid and alkali-resistance described in claim 1 to 2, it is characterised in that build described in: Build material environment friendly fire-retardant acid and alkali-resistance process coating to be made up of the component of following mass fraction: phenyl triethoxysilane 20 parts, phosphorus Acid lithium powder 18 parts, sodium soap 18 parts, Oleum Glycines 16 parts, Bravo 18 parts, Flos Camelliae Japonicae powder 18 parts, zinc sulfide powder 16 parts, jade Stone powder 18 parts, flake asbestos 18 parts, hydrogenated nitrile-butadiene rubber 16 parts, double stearic acid aluminium 16 parts, sucrose 16 parts, styrene-butadiene-benzene Ethylene block copolymer 18 parts, fluorubber 16 parts, polyacrylonitrile fibre 14 parts, hexahydro phthalic anhydride 18 parts, metatitanic acid are just Butyl ester 16 parts, ethylparaben 14 parts, sym-closene 16 parts, Mentholum 14 parts, 5-Amino-2-benzimidazolinone 14 Part, tourmaline powder 16 parts, molybdenum silicide powder 16 parts, ferric chloride 16 parts, oxidized paraffin wax 16 parts, aromatic naphtha 16 parts, mandarin oil 16 parts, polyacrylate emulsion 16 parts, 2-(Acryloyloxy)ethanol 16 parts, alkyl diphenyl phosphate ester 14 parts.
4. process coating according to the construction material environmental protection flame retardant acid and alkali-resistance described in claims 1 to 3, it is characterised in that build described in: Build material environment friendly fire-retardant acid and alkali-resistance process coating to be made up of the component of following mass fraction: phenyl triethoxysilane 22 parts, phosphorus Acid lithium powder 20 parts, sodium soap 20 parts, Oleum Glycines 18 parts, Bravo 20 parts, Flos Camelliae Japonicae powder 20 parts, zinc sulfide powder 18 parts, jade Stone powder 20 parts, flake asbestos 20 parts, hydrogenated nitrile-butadiene rubber 18 parts, double stearic acid aluminium 18 parts, sucrose 18 parts, styrene-butadiene-benzene Ethylene block copolymer 20 parts, fluorubber 18 parts, polyacrylonitrile fibre 16 parts, hexahydro phthalic anhydride 20 parts, metatitanic acid are just Butyl ester 18 parts, ethylparaben 16 parts, sym-closene 18 parts, Mentholum 16 parts, 5-Amino-2-benzimidazolinone 16 Part, tourmaline powder 18 parts, molybdenum silicide powder 18 parts, ferric chloride 18 parts, oxidized paraffin wax 18 parts, aromatic naphtha 18 parts, mandarin oil 18 parts, polyacrylate emulsion 18 parts, 2-(Acryloyloxy)ethanol 18 parts, alkyl diphenyl phosphate ester 16 parts.
Construction material environmental protection flame retardant acid and alkali-resistance the most according to claim 1 processes coating, it is characterised in that: described Building wood It is as follows that material environmental protection flame retardant acid and alkali-resistance processes coating production step:
(1) by the phenyl triethoxysilane of described mass fraction, lithium phosphate powder, sodium soap, Oleum Glycines, Bravo, tea Pollen, zinc sulfide powder, jade powder, flake asbestos, hydrogenated nitrile-butadiene rubber, double stearic acid aluminium, sucrose, styrene-butadiene-benzene second Alkene block copolymer, fluorubber, polyacrylonitrile fibre, hexahydro phthalic anhydride, tetrabutyl titanate, P-hydroxybenzoic acid second Ester, sym-closene, Mentholum are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, and rate of dispersion is about 5000～5400r/min, jitter time is 30～about 60min；
(2) 5-Amino-2-benzimidazolinone of described mass fraction, tourmaline powder, molybdenum silicide powder, ferric chloride, oxidation are added Paraffin, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, jitter time It is 30～about 50min；
(3) aromatic naphtha of described mass fraction, mandarin oil, polyacrylate emulsion, 2-(Acryloyloxy)ethanol, alkyl diphenyl phosphoric acid are added Ester, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/min, and jitter time is 20～about 40min；This product is prepared after mix homogeneously.
CN201610552796.0A 2016-07-12 2016-07-12 A kind of construction material environmental protection flame retardant acid and alkali-resistance processes coating Pending CN106118166A (en)