CN102336952A - 一种hdpe垃圾袋复合材料及其制备工艺 - Google Patents
一种hdpe垃圾袋复合材料及其制备工艺 Download PDFInfo
- Publication number
- CN102336952A CN102336952A CN2011102070927A CN201110207092A CN102336952A CN 102336952 A CN102336952 A CN 102336952A CN 2011102070927 A CN2011102070927 A CN 2011102070927A CN 201110207092 A CN201110207092 A CN 201110207092A CN 102336952 A CN102336952 A CN 102336952A
- Authority
- CN
- China
- Prior art keywords
- hdpe
- parts
- mixed
- matrix material
- refuse bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种HDPE垃圾袋复合材料及其制备工艺,其特征在于,它的组分和重量比例份数比例包括:重质碳酸钙85-95份、表面处理剂 1-1.8份、POE3-8份、HDPE55-65份、聚异丁烯1-3份。本发明分散性良好,纵横向拉力保持原有性能,具有良好的推广价值。
Description
技术领域
本发明涉及高密度聚乙烯技术领域,更具体的说是涉及一种HDPE垃圾袋复合材料及其制备工艺。
背景技术
高密度聚乙烯(High Density Polyethylene,简称为“HDPE”),是一种结晶度高、非极性的热塑性树脂,是一种由乙烯共聚生成的热塑性聚烯烃。原态HDPE的外表呈乳白色,在微薄截面呈一定程度的半透明状。PE具有优良的耐大多数生活和工业用化学品的特性。某些种类的化学品会产生化学腐蚀,例如腐蚀性氧化剂(浓硝酸),芳香烃(二甲苯)和卤化烃 (四氯化碳)。该聚合物不吸湿并具有好的防水蒸汽性,可用于包装用途。各种等级HDPE的独有特性是四种基本变量的适当结合:密度、分子量、分子量分布和添加剂。不同的催化剂被用于生产定制特殊性能聚合物。这些变量相结合生产出不同用途的HDPE品级;在性能上达到最佳的平衡。由于高密度乙烯属环保材质,加热达到熔点,即可回收再利用,所以加入适量的添加剂可将其做成HDPE垃圾袋,近年来为使制品轻量化、薄壁化、节约树脂用量、降低成本,需要开发高强度、耐环境应力开裂性能优良的HDPE树脂产品。
发明内容
本发明的目的就是为了解决现有技术之不足而提供的一种不仅分散性良好,纵横向拉力保持原有性能,而且具有环保功能的HDPE垃圾袋复合材料。
本发明的另一目的是提供一种HDPE垃圾袋复合材料的制备工艺。
本发明是采用如下技术解决方案来实现上述目的:一种HDPE垃圾袋复合材料,其特征在于,它的组分和重量比例份数比例包括:
重质碳酸钙 85-95份 (粒径2400-2600目)
表面处理剂 1-1.8份
POE 3-8份
HDPE 55-65份
聚异丁烯 1-3份。
作为上述方案的进一步说明:所述复合材料的组分和重量比例份数优选:
重质碳酸钙 90份
表面处理剂 1.5份
POE 5份
HDPE 60份
聚异丁烯 2份。
所述表面处理剂为端胺基多元醇酯。
一种HDPE垃圾袋复合材料的制备工艺,其特征在于,它包括如下步骤:
a、先将重质碳酸钙加在卧式双螺带混合机,加热中速混合25-35分钟;
b、加表面处理剂,高速混合10-20分钟;
c、加POE和HDPE,高速混合8-12分钟;
d、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐;
e、通过粉体计量喂料机,喂料到连续密炼机;
f、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机;
g、挤出造粒;
e、成品包装。
在所述工艺步骤a过程中,加热中速混合30分钟,混合后的粉料含水量<2%。
在所述工艺步骤b的高速混合过程中,高速混合15分钟,处理剂要完全包覆粉体。
在所述工艺步骤c过程中,高速混合10分钟。
本发明采用上述技术解决方案所能达到的有益效果是:
1、本发明复合材料在传统的吹膜机器上,完全可以正常生产。
2、分散性良好,纵横向拉力保持原有性能。
3、达到环保功能。
具体实施方式
本发明一种HDPE垃圾袋复合材料,其特征在于,它的组分和重量比例份数比例包括:
重质碳酸钙 85-95份 (粒径2500目)
表面处理剂 1-1.8份
POE 3-8份
HDPE 55-65份
聚异丁烯 1-3份。
本实施例优选,重质碳酸钙 90份
表面处理剂 1.5份
POE 5份 (日本三井810)
HDPE 60份(燕山石化5000S)
聚异丁烯 2份 (韩国PB2400)。
HDPE垃圾袋复合材料的制备工艺,它的步骤如下:
1、先将重质碳酸钙加在卧式双螺带混合机,加热中速混合30分钟,达到混合干燥效果,含水量<2%。
2、加表面处理剂,高速混合15分钟, 处理剂完全包覆粉体。
3、加POE和HDPE,高速混合10分钟,各组份分布混合均匀。
4、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐。
5、通过粉体计量喂料机,喂料到连续密炼机。
6、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机。
7、挤出造粒。
8、成品包装。
以上所述的仅是本发明的优选实施方式,应当指出,对于本领域的普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。
Claims (7)
1.一种HDPE垃圾袋复合材料,其特征在于,它的组分和重量比例份数比例包括:
重质碳酸钙 85-95份 、
表面处理剂 1-1.8份、
POE 3-8份、
HDPE 55-65份、
聚异丁烯 1-3份。
2.根据权利要求1所述的一种HDPE垃圾袋复合材料,其特征在于,所述复合材料的组分和重量比例份数优选:
重质碳酸钙 90份、
表面处理剂 1.5份、
POE 5份、
HDPE 60份、
聚异丁烯 2份。
3.根据权利要求1或2所述的一种HDPE垃圾袋复合材料,其特征在于,所述重质碳酸钙粒径2400-2600目,表面处理剂为端胺基多元醇酯。
4.一种HDPE垃圾袋复合材料的制备工艺,其特征在于,它包括如下步骤:
a、先将重质碳酸钙加在卧式双螺带混合机,加热中速混合25-35分钟;
b、加表面处理剂,高速混合10-20分钟;
c、加POE和HDPE,高速混合8-12分钟;
d、通过螺杆上料机,混合好的物料输送到连续密炼机料储料罐;
e、通过粉体计量喂料机,喂料到连续密炼机;
f、将聚异丁烯加到液体计量喂料机,喂料到连续密炼机;
g、挤出造粒;
e、成品包装。
5.根据权利要求4所述的一种HDPE垃圾袋复合材料的制备工艺,其特征在于,在所述工艺步骤a过程中,加热中速混合30分钟,混合后的粉料含水量<2%。
6.根据权利要求4所述的一种HDPE垃圾袋复合材料的制备工艺,其特征在于,在所述工艺步骤b的高速混合过程中,高速混合15分钟,处理剂要完全包覆粉体。
7.根据权利要求4所述的一种HDPE垃圾袋复合材料的制备工艺,其特征在于,在所述工艺步骤c过程中,高速混合10分钟。