CN102329531B - 一种仿天空蓝色防腐、分解有机污染物的纳米涂料 - Google Patents
一种仿天空蓝色防腐、分解有机污染物的纳米涂料 Download PDFInfo
- Publication number
- CN102329531B CN102329531B CN201110140856.5A CN201110140856A CN102329531B CN 102329531 B CN102329531 B CN 102329531B CN 201110140856 A CN201110140856 A CN 201110140856A CN 102329531 B CN102329531 B CN 102329531B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- anticorrosion
- paint
- organic pollutant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种仿天空蓝色防腐、分解有机污染物的纳米涂料。由以下成分构成：薄片状铝粉1，酞青蓝2，锐钛型纳米二氧化钛14，粒径90nm的半透明球状蓝颜料40，粒径100nm的大白粉2，用20％的矿物油凝胶的聚酰胺改性的烷基树脂30，溶剂10，抗结皮剂0.15，25％固含量的环烷酸钴干燥剂0.85。给人以视觉放松，同时达到防腐和分解有机污染物的功效。
Description
技术领域
本发明涉及一种涂料，特别是仿天空蓝色防腐、分解有机污染物的纳米涂料。
背景技术
随着国民经济与高科技的发展，对涂料的要求除通用型外，对特种涂料的需求日益迫切。防腐涂料中，过氧乙烯涂料、环氧树脂涂料、氧磺化聚乙烯涂料等都兼或存在着，但各有不足。过氧乙烯涂料在70年代初问世，这种涂料具有一定防腐作用，但由于较大的分子量，流平性不理想，固含量低，一般只有14～18％，漆膜密度差，粘度也很低，只有20～50秒，其附着力也不好，漆膜易脱落。
环氧树脂涂料从60年代初开始被应用，至今在很大范围内被应用着，但其存在脆性大，双组份使用不方便，对硫酸、硝酸及草酸的防腐性能不理想等缺点。氧磺化聚乙烯涂料是80年代初新研究开发的防腐涂料，也存在着双组份，使用不方便，贮存稳定性差，耐酸、耐碱性差等缺点。现急待新一代防腐涂料的出现。
在紫外(UV)和近UV辐射的作用下电子从价带跃迁到导带，使得半导体材料二氧化钛具有光催化性能。产生的反应性的电子-空穴对迁移到二氧化钛颗粒的表面，在那里所述空穴氧化所吸附的水而产生反应性的羟基自由基且所述电子还原所吸附的氧而产生超氧自由基，所述两者都能够降解在空气中的NOx和挥发性有机化合物(VOC)。鉴于这些性能，已经在涂料等中使用光催化二氧化钛等以从空气中除去污染物。这种涂料还具有自清洁的优势，因为也在表面上对污物(油脂、霉、霉菌、藻类等)进行氧化。
同时，尽管现有的光催化二氧化钛涂料具有优势，但是在本领域中存在改进的空间。特别地，已经观察到，常规光催化二氧化钛涂料的初始活性差，除非所述涂料已经被预活化例如通过用水洗涤而被预活化。尽管不期望受限于任何理论，但是认为，需要活化步骤以从催化剂表面上将涂料组合物中存在的有机成分除去、或者可能需要活化步骤以在二氧化钛颗粒上提供水合表面，由此生成反应性自由基物种。然而，这种附加步骤使得光催化二氧化钛涂料的应用有点不方便，因为它耗时且增加了应用过程的额外成本。期望提供光催化二氧化钛涂料，尤其是以油漆的形式提供，其不需要预活化(例如洗涤步骤或与某些元素接触)就能实现高的初始活性水平。
还难以提供具有高光催化剂含量的涂料，因为催化剂易于氧化且分解涂料的聚合物漆基。当涂料暴露于源自日光直射的强UV辐射时，这种问题加剧，外墙油漆的情况就是如此。通常利用无机漆基或用在相对低的催化剂浓度下抵抗光催化氧化的有机聚合物来配制这种涂料。然而，在低光照条件下，涂料的去污性能低于最佳水平。期望提供用于低光照环境(例如室内)中的涂料，所述涂料掺有高含量的光催化剂以使去污能力最优选且所述涂料可抵抗降解，另外期望在室内光照条件下提供高催化活性。
发明内容
针对现有技术的不足，本发明的目的之一是提供涂料组合物，其包含能够从空气中除去污染物的二氧化钛光催化剂，该光催化剂不需要预活化就具有高的初始活性。本发明的进一步的目的是提供具有高含量的光催化二氧化钛的耐久性涂料，所述涂料在低光照环境中，尤其是在可见光的存在下，具有去污活性；
第二目的在于：含有具有能够使人或动物愉悦的色彩，特别是仿天空蓝色的涂料，惊奇的发现通过该颜色，人的心情更加舒畅或动物的生活更加温顺，特别是动物园里的动物。
第三目的在于：同时达到一种具有防腐的目的，能够用于广阔的户外各种结构，特别是金属结构。
根据前述目的和其它内容，已经惊奇地发现，包含晶粒尺寸为约10-45nm、更优选约20nm～约30nm的二氧化钛的涂料不需要预活化(例如通过用水洗涤)即可在光的存在下获得高初始水平的光催化活性。本发明的涂料在可见光存在下显示了显著的光催化活性，这使得它们在低光照环境中(包括室内中)可理想地用作去污涂料。
同时发现了最佳的合适的蓝色系配比及合适的功能性填料达到上述效果，具体涂料重量份组成如下：
薄片状铝粉 1
酞青蓝 2
粒径10-45nm的锐钛型纳米二氧化钛 14
粒径90nm的半透明球状蓝颜料 40
粒径100nm的大白粉 2
用20%的矿物油凝胶的聚酰胺改性的烷基树脂 30
溶剂 10
抗结皮剂 0.15
25%固含量的环烷酸钴干燥剂 0.85。
具体实施方式
实施例1
涂料的重量份组成如下：
薄片状铝粉 1
酞青蓝 2
粒径30nm的锐钛型纳米二氧化钛 14
粒径90nm的半透明球状蓝颜料 40
粒径100nm的大白粉 2
用20%的矿物油凝胶的聚酰胺改性的烷基树脂 30
溶剂 10
抗结皮剂 0.15
25%固含量的环烷酸钴干燥剂 0.85。
经与常规涂料相比，本发明实施例的技术效果如下：
本发明的涂料，具有突出的防腐性能，同时还具有生态环境友好的颜色，及分解有机污染物的功能，多组分达到了协同作用，比单独任何一种成分起到的作用更大，有更加实际应用的广大空间。
申请人声明，本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (1)
1.一种仿天空蓝色防腐、分解有机污染物的纳米涂料组合物，由下述重量份组分构成：