CN102321981A - Printing and dyeing method for multicolor jacquard cotton cloth - Google Patents
Printing and dyeing method for multicolor jacquard cotton cloth Download PDFInfo
- Publication number
- CN102321981A CN102321981A CN 201110260221 CN201110260221A CN102321981A CN 102321981 A CN102321981 A CN 102321981A CN 201110260221 CN201110260221 CN 201110260221 CN 201110260221 A CN201110260221 A CN 201110260221A CN 102321981 A CN102321981 A CN 102321981A
- Authority
- CN
- China
- Prior art keywords
- water
- jacquard weave
- weave cotton
- ratio
- grams per
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention designs a printing and dyeing method for multicolor jacquard cotton cloth. The method comprises: the first step, liquid alkali preshrinking; the second step, reduction and dyeing; the third step, dehydration; the fourth step, sizing and shaping; the fifth step, calendaring, thus obtaining the multicolor jacquard cotton cloth. According to the printing and dyeing method for multicolor jacquard cotton cloth, liquid alkali preshrinking is adopted before reduction and dyeing so as to make white jacquard cotton cloth shrunk, and the density of the jacquard part is further increased while the density of the jacquard-free part is further reduced, so that a multicolor state can be presented after dyeing, boundaries among different colors are distinct, and the color within one area unit is consistent. In this way, the color of the jacquard part can be made prominent effectively so as to endow the jacquard with a sense of concave-convex. After finishing liquid alkali preshrinking, the jacquard cotton cloth is cleaned with clear water, and the using amount of the reduction dye can be effectively reduced during reduction and dyeing. In addition, the jacquard cotton cloth treated with the printing and dyeing method of the invention can has a consistent color in a same area unit of different positions, thus effectively improving the quality of the jacquard cotton cloth.
Description
Technical field
The present invention relates to the lining field of printing and dyeing, especially a kind of dyeing method of polychrome jacquard weave cotton.
Background technology
In dyeing; Traditional dyeing method to the jacquard weave cotton is comparative maturity; But the jacquard weave cotton through existing method printing and dyeing can produce following shortcoming: 1. the color of the jacquard weave cotton after the printing and dyeing is more single, and jacquard weave and non-jacquard weave place color are approaching, can't realize that jacquard weave place produces concave-convex sense; 2. inconsistent for the color of the same area unit of the diverse location of jacquard weave cotton.Because above-mentioned shortcoming, the added value of product of existing jacquard weave cotton is low, and kind is low, is difficult to make high light jacquard weave cotton to get into high-end market.
Summary of the invention
The objective of the invention is provides a kind of jacquard weave cotton that can make to produce multiple color for the deficiency that solves above-mentioned technology, and the dyeing method of the polychrome jacquard weave cotton of the solid colour in the same area unit of diverse location.
In order to achieve the above object, the dyeing method of the polychrome jacquard weave cotton that the present invention designed: the first step, liquid caustic soda are collected in advance and are contracted, and the jacquard weave cotton is soaked to put in liquid caustic soda solution shrink; In second step, reduction stain uses reducing dye dyeing with the jacquard weave cotton after the first step is handled, and pH value is regulated in oxidizer reduction more at last; In the 3rd step, dehydration will dehydrate through the jacquard weave cotton after second step handled; Above-mentioned three steps are carried out the starching typing after accomplishing again: dried jacquard weave cotton is carried out starching, again through the setting machine typing; The calender press polish is handled then, promptly obtains polychrome jacquard weave cotton.This method collects the jacquard weave cotton in advance through liquid caustic soda to contract, and it is bigger to reach jacquard weave place density, the littler effect of non-jacquard weave place density; Cause to present multicolour after the dyeing; And the solid colour of the same area unit of diverse location, the printing and dyeing effect is better, improves the quality and the quality of jacquard weave cotton.
Said jacquard weave cotton adopts the high grade yarn jacquard weave cotton that comprises that 60 yarns are above, uses the jacquard weave cotton of high-quality, can improve the quality of products, and improves its added value.
As optimization, liquid caustic soda is collected in advance in the compression process, and the concentration of the liquid caustic soda solution of employing is 10-30%, soaks that to put temperature be normal temperature to 90 degree centigrade, and soaking the time of putting is 1-60 minute.
Reduction stain at first soaks the jacquard weave cotton and puts in water, and the mass ratio of cloth and water is 1: 30; Add simultaneously to soak behind the dye leveller and put 8-12 minute; Add the alkali resistance reducing dye again, heat up, when temperature reaches 45 degrees centigrade, begin to add reductant and rise to 65 degrees centigrade adding before in temperature; Insulation is 25-35 minute when rising to 65 degrees centigrade, with clear water the jacquard weave cotton is cleaned up again; The jacquard weave cotton soaked placing water, add oxidant, is 35-45 degree centigrade in temperature, keeps 25-35 minute, cleans up with clear water again; The jacquard weave cotton being soaked places water to add acid adjusting pH value to 8-10 again.In the epoxy dyeing course,, with the oxidant reduction, make color more true to nature again, regulate pH value at last, make the jacquard weave cotton can not cause damage human body skin through reducing dye dyeing.
When adopting levelling agent to be paregal O (alkyl polyoxyethylene ether) in the reduction stain process, paregal O (alkyl polyoxyethylene ether) is the 0.8-1.2 grams per liter with the ratio of water, and the adding reductant is the powder that at first takes a policy; Then add glucose; Add sodium hydrosulfite or reductant GR300 again, the amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the first time, and the amount of glucose and the ratio of water are the 0.8-1.2 grams per liter; The amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the second time; The amount of reductant GR300 and the ratio of water are the 0.8-1.2 grams per liter, and the oxidant of employing is a hydrogen peroxide solution, and the ratio of hydrogen peroxide solution and water is the 4-6 grams per liter.
The starching typing, auxiliary agent is adopted in starching: 7 parts of polyvinyl alcohol (PVA), 3 parts of starch, cured 3 parts, 2 parts of greases, 100 parts in water, above umber are mass fraction; The slurry preparation adds polyvinyl alcohol and starch in the entry at normal temperatures, heats to 80 degrees centigrade after waiting to dissolve, and adds cured and grease again, continues to be warming up to boiling point, heat preservation for standby use; During typing, setting machine pads, and adopting setting temperature is 170-190 degree centigrade, shaping time be 20-40 rice/minute.
Liquid caustic soda is collected in advance in the compression process, and the concentration of the liquid caustic soda solution of employing is put temperature, soaked the time of putting and be inversely proportional to soaking, and soaks to put with clear water cloth to be cleaned up after accomplishing.Rinse the liquid caustic soda on the jacquard weave cotton well through clear water, can save the use amount of the dyestuff in the follow-up reduction stain process.
The dyeing method of the resulting polychrome jacquard weave of the present invention cotton before reduction stain, adopts liquid caustic soda to collect in advance and contracts; White jacquard weave cotton is shunk, and the density of jacquard weave place further increases, and non-jacquard weave place density further reduces; So that the state that presents polychrome after the dyeing, and the boundary between the different colours is clear, and the solid colour in the same area unit; Can effectively protrude the color of jacquard weave place, make jacquard weave have concave-convex sense.Simultaneously accomplish liquid caustic soda collect in advance contract after, adopt clear water that the jacquard weave cotton is cleaned up, can effectively reduce the use amount of reducing dye in the reduction stain process, reduce production costs.Jacquard weave cotton through the printing and dyeing of this method in addition, the solid colour of the same area unit of its diverse location can effectively improve the quality and the quality of jacquard weave cotton.
The specific embodiment
Through embodiment the present invention is done further description below.
Embodiment 1:
The dyeing method of the polychrome jacquard weave cotton that present embodiment is described: the first step, liquid caustic soda are collected in advance and are contracted, and the jacquard weave cotton is soaked to put in liquid caustic soda solution shrink; In second step, reduction stain uses reducing dye dyeing with the jacquard weave cotton after the first step is handled, and pH value is regulated in oxidizer reduction more at last; In the 3rd step, dehydration will dehydrate through the jacquard weave cotton after second step handled; Above-mentioned three steps are carried out the starching typing after accomplishing again: dried jacquard weave cotton is carried out starching, again through the setting machine typing; The calender press polish is handled then, promptly obtains polychrome jacquard weave cotton.
Said jacquard weave cotton adopts the high grade yarn jacquard weave cotton that comprises that 60 yarns are above.
Reduction stain at first soaks the jacquard weave cotton and puts in water, and the mass ratio of cloth and water is 1: 30; Add simultaneously to soak behind the dye leveller and put 8-12 minute; Add the alkali resistance reducing dye again, heat up, when temperature reaches 45 degrees centigrade, begin to add reductant and rise to 65 degrees centigrade adding before in temperature; Insulation is 25-35 minute when rising to 65 degrees centigrade, with clear water the jacquard weave cotton is cleaned up again; The jacquard weave cotton soaked placing water, add oxidant, is 35-45 degree centigrade in temperature, keeps 25-35 minute, cleans up with clear water again; The jacquard weave cotton being soaked places water to add acid adjusting pH value to 8-10 again.
Liquid caustic soda is collected in advance and is contracted, and the concentration of the liquid caustic soda solution of employing is put temperature, soaked the time of putting and be inversely proportional to soaking, and soaks to put with clear water cloth to be cleaned up after accomplishing.
Embodiment 2:
The dyeing method of the polychrome jacquard weave cotton that present embodiment is described, the first step, liquid caustic soda is collected in advance and is contracted, and the concentration of the liquid caustic soda solution of employing is 10%, soaks that to put temperature be 90 degrees centigrade, and soaking the time of putting is 60 minutes, soaks to put with clear water cloth to be cleaned up after accomplishing.
In second step, reduction stain at first soaks the jacquard weave cotton and puts in water; The mass ratio of cloth and water is 1: 30, adds paregal O (alkyl polyoxyethylene ether) simultaneously, and paregal O (alkyl polyoxyethylene ether) is 0.8 grams per liter with the ratio of water; Soak and put 12 minutes, add the alkali resistance reducing dye again, heat up; Powder (amount of sodium hydrosulfite and the ratio of water are 4 grams per liters) begins to take a policy when temperature reaches 45 degrees centigrade; Then add glucose (amount of glucose and the ratio of water are 0.8 grams per liter), powder that takes a policy again (amount of sodium hydrosulfite and the ratio of water are 4 grams per liters) or reductant GR300 (amount of reductant GR300 and the ratio of water are 0.8 grams per liter), and before temperature rises to 65 degrees centigrade, add; Insulation is 25 minutes when rising to 65 degrees centigrade, with clear water the jacquard weave cotton is rinsed well again; The jacquard weave cotton soaked placing water, add hydrogen peroxide solution (ratio of hydrogen peroxide solution and water is 4 grams per liters), is 35 degrees centigrade in temperature, keeps 25 minutes, cleans up with clear water again; The jacquard weave cotton being soaked places water to add acid adjusting pH value to 8 again.
The 3rd step, dehydration, the jacquard weave cotton that second step was handled dehydrates processing.
The 4th step, the starching typing, sizing agent: 7 parts of polyvinyl alcohol (PVA), 3 parts of starch, cured 3 parts, 2 parts of greases, 100 parts in water, above umber are mass fraction; The slurry preparation adds polyvinyl alcohol and starch in the entry at normal temperatures, heats to 80 degrees centigrade after waiting to dissolve, and adds cured and grease again, continues to be warming up to boiling point, heat preservation for standby use; During typing, setting machine pads, and adopting setting temperature is 170 degrees centigrade, and shaping time is 20 meters/minute.
In the 5th step, press polish is handled the jacquard weave cotton after the processing of the 4th step through the calender press polish.
Can obtain polychrome jacquard weave cotton.
Embodiment 3:
The dyeing method of the polychrome jacquard weave cotton that present embodiment is described, the first step, liquid caustic soda is collected in advance and is contracted, and the concentration of the liquid caustic soda solution of employing is 30%, soaks that to put temperature be normal temperature, and soaking the time of putting is 1 minute, soaks to put with clear water cloth to be cleaned up after accomplishing.
In second step, reduction stain at first soaks the jacquard weave cotton and puts in water; The mass ratio of cloth and water is 1: 30, adds paregal O (alkyl polyoxyethylene ether) simultaneously, and paregal O (alkyl polyoxyethylene ether) is 1.2 grams per liters with the ratio of water; Soak and put 8 minutes, add the alkali resistance reducing dye again, heat up; Powder (amount of sodium hydrosulfite and the ratio of water are 6 grams per liters) begins to take a policy when temperature reaches 45 degrees centigrade; Then add glucose (amount of glucose and the ratio of water are 1.2 grams per liters), powder that takes a policy again (amount of sodium hydrosulfite and the ratio of water are 6 grams per liters) or reductant GR300 (amount of reductant GR300 and the ratio of water are 1.2 grams per liters), and before temperature rises to 65 degrees centigrade, add; Insulation is 35 minutes when rising to 65 degrees centigrade, with clear water the jacquard weave cotton is cleaned up again; The jacquard weave cotton soaked placing water, add hydrogen peroxide solution (ratio of hydrogen peroxide solution and water is 6 grams per liters), is 45 degrees centigrade in temperature, keeps 35 minutes, cleans up with clear water again; The jacquard weave cotton being soaked places water to add acid adjusting pH value to 10 again.
The 3rd step, dehydration, the jacquard weave cotton that second step was handled dehydrates processing.
The 4th step, the starching typing, sizing agent: 7 parts of polyvinyl alcohol (PVA), 3 parts of starch, cured 3 parts, 2 parts of greases, 100 parts in water, above umber are mass fraction; The slurry preparation adds polyvinyl alcohol and starch in the entry at normal temperatures, heats to 80 degrees centigrade after waiting to dissolve, and adds cured and grease again, continues to be warming up to boiling point, heat preservation for standby use; During typing, setting machine pads, and adopting setting temperature is 190 degrees centigrade, and shaping time is 40 meters/minute.
In the 5th step, press polish is handled the jacquard weave cotton after the processing of the 4th step through the calender press polish.
Can obtain polychrome jacquard weave cotton.
Claims (9)
1. the dyeing method of a polychrome jacquard weave cotton, it is characterized in that: the first step, liquid caustic soda are collected in advance and are contracted, and the jacquard weave cotton is soaked to put in liquid caustic soda solution, to collect in advance contract; In second step, reduction stain will use reducing dye dyeing through the jacquard weave cotton that the first step is collected in advance after contracting, and pH value is regulated in oxidizer reduction more at last; In the 3rd step, dehydration will dehydrate through the jacquard weave cotton after the dyeing of second step.
2. the dyeing method of polychrome jacquard weave cotton according to claim 1 is characterized in that carrying out the starching typing again after the above-mentioned three steps completion: dried jacquard weave cotton is carried out starching, again through the setting machine typing; The calender press polish is handled then, promptly obtains polychrome jacquard weave cotton.
3. the dyeing method of polychrome jacquard weave cotton according to claim 1 and 2 is characterized in that said jacquard weave cotton adopts the high grade yarn jacquard weave cotton that comprises that 60 yarns are above.
4. the dyeing method of polychrome jacquard weave cotton according to claim 1 and 2, it is characterized in that described liquid caustic soda is collected in advance contracts, and the concentration of the liquid caustic soda solution of employing is 10%-30%, soaks that to put temperature be normal temperature to 90 degree centigrade, and soaking the time of putting is 1 minute-60 minutes.
5. the dyeing method of polychrome jacquard weave cotton according to claim 1 and 2 is characterized in that reduction stain, at first the jacquard weave cotton is soaked and puts in water; The mass ratio of cloth and water is 1: 30, adds simultaneously to soak behind the levelling agent to put 8-12 minute, adds the alkali resistance reducing dye again; Heat up; When temperature reaches 45 degrees centigrade, begin to add reductant and rise to 65 degrees centigrade in temperature adding before, insulation is 25-35 minute when rising to 65 degrees centigrade, with clear water the jacquard weave cotton is cleaned up again; The jacquard weave cotton soaked placing water, add oxidant, is 35-45 degree centigrade in temperature, keeps 25-35 minute, cleans up with clear water again; The jacquard weave cotton being soaked places water to add acid adjusting pH value to 8-10 again.
6. the dyeing method of polychrome jacquard weave cotton according to claim 1 and 2, when it is characterized in that adopting in the reduction stain process levelling agent to be paregal O, the ratio of paregal O and water is the 0.8-1.2 grams per liter; The adding reductant is the powder that at first takes a policy, and then adds glucose, adds sodium hydrosulfite or reductant GR300 again; The amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the first time; The amount of glucose and the ratio of water are the 0.8-1.2 grams per liter, and the amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the second time, and the amount of reductant GR300 and the ratio of water are the 0.8-1.2 grams per liter; The oxidant that adopts is a hydrogen peroxide solution, and the ratio of hydrogen peroxide solution and water is the 4-6 grams per liter.
7. the dyeing method of polychrome jacquard weave cotton according to claim 4, when it is characterized in that adopting in the reduction stain process levelling agent to be paregal O, the ratio of paregal O and water is the 0.8-1.2 grams per liter; The adding reductant is the powder that at first takes a policy, and then adds glucose, adds sodium hydrosulfite or reductant GR300 again; The amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the first time; The amount of glucose and the ratio of water are the 0.8-1.2 grams per liter, and the amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the second time, and the amount of reductant GR300 and the ratio of water are the 0.8-1.2 grams per liter; The oxidant that adopts is a hydrogen peroxide solution, and the ratio of hydrogen peroxide solution and water is the 4-6 grams per liter.
8. the dyeing method of polychrome jacquard weave cotton according to claim 5, when it is characterized in that adopting in the reduction stain process levelling agent to be paregal O, the ratio of paregal O and water is the 0.8-1.2 grams per liter; The adding reductant is the powder that at first takes a policy, and then adds glucose, adds sodium hydrosulfite or reductant GR300 again; The amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the first time; The amount of glucose and the ratio of water are the 0.8-1.2 grams per liter, and the amount of sodium hydrosulfite and the ratio of water are the 4-6 grams per liter for the second time, and the amount of reductant GR300 and the ratio of water are the 0.8-1.2 grams per liter; The oxidant that adopts is a hydrogen peroxide solution, and the ratio of hydrogen peroxide solution and water is the 4-6 grams per liter.
9. the dyeing method of polychrome jacquard weave cotton according to claim 2 is characterized in that described starching typing, and auxiliary agent is adopted in starching: 7 parts of polyvinyl alcohol (PVA), and 3 parts of starch, cured 3 parts, 2 parts of greases, 100 parts in water, above umber are mass fraction; The slurry preparation adds polyvinyl alcohol and starch in the entry at normal temperatures, heats to 80 degrees centigrade after waiting to dissolve, and adds cured and grease again, continues to be warming up to boiling point, heat preservation for standby use; During typing, setting machine pads, and adopting setting temperature is 170-190 degree centigrade, shaping time be 20-40 rice/minute.