CN102321438A - 一种阻燃胶添加剂、阻燃胶及其应用方法 - Google Patents
一种阻燃胶添加剂、阻燃胶及其应用方法 Download PDFInfo
- Publication number
- CN102321438A CN102321438A CN 201110222266 CN201110222266A CN102321438A CN 102321438 A CN102321438 A CN 102321438A CN 201110222266 CN201110222266 CN 201110222266 CN 201110222266 A CN201110222266 A CN 201110222266A CN 102321438 A CN102321438 A CN 102321438A
- Authority
- CN
- China
- Prior art keywords
- cigarette
- glue
- fire retardant
- retardant
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种阻燃胶添加剂、阻燃胶及其应用方法。采用一种或多种属食品添加剂类无机原料，与适当的助剂和增稠剂组成阻燃胶添加剂，按一定比例与普通高速卷烟接嘴胶均匀混合即构成新型阻燃接嘴胶。该新型阻燃接嘴胶具有制备简单、无毒无害、不破坏普通接嘴胶性状、稳定可靠，用其卷制的香烟无异味，能保持卷烟原有的抽吸品质，未熄灭的香烟燃烧到有接装纸的部位时，1-2分钟内烟蒂自行全部熄灭，自熄率为100％，因此能有效预防和减少因未熄灭烟蒂所引起的火灾。
Description
技术领域
本发明涉及卷烟技术领域，具体来说是一种阻燃胶添加剂、阻燃胶及其应用方法。
背景技术
我国是世界上最大的香烟生产国，也是世界上最大的烟草消费国。随着烟草科技的发展，“吸烟与健康”、“吸烟与安全”已逐渐成为烟草行业发展的主流趋势。这主要从两个方面来考虑：一是烟支燃烧产生的烟气对人体及周围环境产生的损害和污染，二是指由吸烟引起的火灾。
燃着的烟头表面温度为200℃～300℃，中心温度为700℃～800℃，明显高于其他可燃物品的燃点。如纸张为130℃，棉被、麻绒为150度，松木为250℃。一支香烟延烧时间为4～15分钟，吸剩的烟头一般能继续燃着1～4分钟，在这个时间内，许多易燃性物品均能被点燃。有时烟头扔在棉被、刨花、木屑或草丛中，要阴燃几十分钟，不容易被人注意，危险性更大。
根据统计，日本家庭火灾中吸烟引起的占26％，美国家庭火灾中吸烟引起的占29.1％。这些国家每年都有不少人由于粗心大意死于吸烟或乱扔烟头而引起的火灾中。在我国一些城市中烟头引起的火灾约占火灾总数的七分之一，由乱扔烟头引发的房屋或森林火灾导致人员和财产损失的新闻报道时有发生。
如何最大限度地降低吸剩的烟头引发火灾的风险，减少火灾造成的人员和财产损失，设计和生产一种可使吸剩的烟头及时自动熄灭的香烟是本发明的出发点。
发明内容
本发明的目的是提供一种新型环保阻燃胶添加剂、阻燃胶及其应用方法，用其卷制的香烟具备烟蒂自熄功能，即当该类香烟烟支燃烧到有接装纸的部位时，烟蒂会自行全部熄灭。
本发明的阻燃胶添加剂，是由以下质量百分比组分组成：10-25％阻燃剂、70-85％助剂和1-5％增稠剂组成，所述的阻燃剂包括磷酸二氢铵、磷酸氢二铵、磷酸铵、磷酸二氢钠、磷酸氢二钠、水溶性聚磷酸铵中的一种或多种。
所述的助剂包括水或1-5％的稀磷酸水溶液，所述的增稠剂包括羟丙基甲基纤维素、淀粉磷酸酯钠、海藻酸钠、黄原胶、甲壳素、罗望子多糖胶、钛白粉中的一种或多种。
本发明的阻燃胶，是将上述的阻燃胶添加剂与普通高速卷烟接嘴胶混合得到的阻燃胶。具体是将上述的阻燃胶添加剂与普通高速卷烟接嘴胶按照质量比例1∶5-6混合得到的阻燃胶。所述的普通高速卷烟接嘴胶由聚乙酸乙烯酯、乙酸乙烯共聚物、聚乙烯醇中的一种或几种组成。
上述的阻燃胶用于胶粘和阻燃；具体是用于卷烟接嘴的胶粘和阻燃。
本发明所用原材料均属食品添加剂类，无毒无害，安全环保。
阻燃胶添加剂基本上不破坏普通接嘴胶性状，如颜色、气味、酸碱性、粘度、稳定性、保质期等。
该新型阻燃接嘴胶在上机卷制烟支时，其卷制速度、粘接力度和质量与普通高速卷烟接嘴胶基本无差别。所卷制的香烟能保持卷烟原有的抽吸品质和口味，烟气化学指标基本无变化。
新型阻燃接嘴胶所卷制的香烟当燃烧到有接装纸的部位时，1-2分钟内烟蒂会自行全部熄灭，自熄率为100％。因此能有效预防和减少因未熄灭烟蒂所引起的火灾。
本发明与已有技术相比具有显著优点：
A.本发明所用阻燃剂安全环保，完全符合食品添加剂的要求；
B.新型阻燃接嘴胶可由阻燃胶添加剂与目前市售任何一种普通高速卷烟接嘴胶混合制得，且制备工艺简单，无须对卷烟设备作任何改动，可应用于所有卷烟接装纸；
C.由新型阻燃接嘴胶卷制的香烟能保持卷烟原有的抽吸品质和口味，烟气化学指标基本无变化；
D.所卷制的香烟当燃烧到有接装纸的部位时，1-2分钟内烟蒂会自行全部熄灭，自熄率为100％，因此能有效预防和减少因未熄灭烟蒂所引起的火灾。。
具体实施方式
现结合实施例进一步说明，而不会对本发明形成限制：
实施例1
阻燃胶添加剂和新型阻燃接嘴胶制备：
在118克水中加入2克羟丙基甲基纤维素，搅拌溶解至澄清透明溶液，再加入30克磷酸二氢铵，搅拌至完全溶解。再称取850克普通高速卷烟接嘴胶于搅拌器中，边搅拌边缓慢加入阻燃胶添加剂至完全混合均匀为止即可。
分别采用上述新型阻燃接嘴胶和普通高速卷烟接嘴胶、相同烟丝和其它辅料，按常规生产方法卷接成两种卷烟样品。由专业评吸师对两种卷烟样品品质(香气、和谐、杂气、刺激性、余味等)进行评价。同时按标准方法对两种卷烟样品主流烟气常规化学指标进行分析检测。
卷烟样品品质评价结果表明，由新型阻燃接嘴胶卷制的香烟能保持卷烟原有的抽吸品质和口味。
卷烟样品主流烟气常规化学指标分析检测结果表明两者基本无差异，具体见下表1：
表1
烟蒂自熄试验：
E.两种卷烟样品分为两组，各取20支点燃后水平放置，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表2。
F.两种卷烟样品分为两组，各取20支点燃后竖直放置(燃头朝上)，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表2。
表2
| 点燃支数 | 自熄支数 | 自熄率 | |
| 普通高速卷烟接嘴胶 | 40 | 6 | 15％ |
| 本发明新型阻燃接嘴胶 | 40 | 40 | 100％ |
实施例2
阻燃胶添加剂和新型阻燃接嘴胶制备：
在118克水中加入2克羟丙基甲基纤维素，搅拌溶解至澄清透明溶液，再加入20克磷酸二氢铵和20克磷酸氢二铵，搅拌至完全溶解。再称取850克普通高速卷烟接嘴胶于搅拌器中，边搅拌边缓慢加入阻燃胶添加剂至完全混合均匀为止即可。
分别采用上述新型阻燃接嘴胶和普通高速卷烟接嘴胶、相同烟丝和其它辅料，按常规生产方法卷接成两种卷烟样品。由专业评吸师对两种卷烟样品品质(香气、和谐、杂气、刺激性、余味等)进行评价。同时按标准方法对两种卷烟样品主流烟气常规化学指标进行分析检测。
卷烟样品品质评价结果表明，由新型阻燃接嘴胶卷制的香烟能保持卷烟原有的抽吸品质和口味。
卷烟样品主流烟气常规化学指标分析检测结果表明两者基本无差异，具体见下表3：
表3
烟蒂自熄试验：
G.两种卷烟样品分为两组，各取20支点燃后水平放置，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表4。
H.两种卷烟样品分为两组，各取20支点燃后竖直放置(燃头朝上)，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表4。
表4
| 点燃支数 | 自熄支数 | 自熄率 | |
| 普通高速卷烟接嘴胶 | 40 | 4 | 10％ |
| 本发明新型阻燃接嘴胶 | 40 | 40 | 100％ |
实施例3
阻燃胶添加剂和新型阻燃接嘴胶制备：
在118克水中加入5克黄原胶，搅拌溶解至澄清透明溶液；然后加入40克磷酸二氢铵，搅拌至完全溶解；最后加入3克食品级钛白粉，搅拌至均匀悬浊液。再称取850克普通高速卷烟接嘴胶于搅拌器中，边搅拌边缓慢加入上述阻燃胶添加剂水溶液至完全混合均匀为止即可。
分别采用上述新型阻燃接嘴胶和普通高速卷烟接嘴胶、相同烟丝和其它辅料，按常规生产方法卷接成两种卷烟样品。由专业评吸师对两种卷烟样品品质(香气、和谐、杂气、刺激性、余味等)进行评价。同时按标准方法对两种卷烟样品主流烟气常规化学指标进行分析检测。
卷烟样品品质评价结果表明，由新型阻燃接嘴胶卷制的香烟能保持卷烟原有的抽吸品质和口味。
卷烟样品主流烟气常规化学指标分析检测结果表明两者基本无差异，具体见下表5：
表5
烟蒂自熄试验：
I.两种卷烟样品分为两组，各取20支点燃后水平放置，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表6。
J.两种卷烟样品分为两组，各取20支点燃后竖直放置(燃头朝上)，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表6。
表6
| 点燃支数 | 自熄支数 | 自熄率 | |
| 普通高速卷烟接嘴胶 | 40 | 0 | 0％ |
| 本发明新型阻燃接嘴胶 | 40 | 40 | 100％ |
实施例4
阻燃胶添加剂和新型阻燃接嘴胶制备：
在118克水中加入5克黄原胶，搅拌溶解至澄清透明溶液，再加入30克磷酸二氢钠和10克磷酸氢二钠，搅拌至完全溶解。再称取850克普通高速卷烟接嘴胶于搅拌器中，边搅拌边缓慢加入阻燃胶添加剂至完全混合均匀为止即可。
分别采用上述新型阻燃接嘴胶和普通高速卷烟接嘴胶、相同烟丝和其它辅料，按常规生产方法卷接成两种卷烟样品。由专业评吸师对两种卷烟样品品质(香气、和谐、杂气、刺激性、余味等)进行评价。同时按标准方法对两种卷烟样品主流烟气常规化学指标进行分析检测。
卷烟样品品质评价结果表明，由新型阻燃接嘴胶卷制的香烟能保持卷烟原有的抽吸品质和口味。
卷烟样品主流烟气常规化学指标分析检测结果表明两者基本无差异，具体见下表7：
表7
烟蒂自熄试验：
K.两种卷烟样品分为两组，各取20支点燃后水平放置，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表8。
L.两种卷烟样品分为两组，各取20支点燃后竖直放置(燃头朝上)，自行燃烧，当燃至接装纸的部位时，观察其自熄率。结果见下表8。
表8
| 点燃支数 | 自熄支数 | 自熄率 | |
| 普通高速卷烟接嘴胶 | 40 | 2 | 5％ |
| 本发明新型阻燃接嘴胶 | 40 | 40 | 100％ |
Claims (7)
1.一种阻燃胶添加剂，其特征在于，是由以下质量百分比组分组成：10-25％阻燃剂、70-85％助剂和1-5％增稠剂组成，所述的阻燃剂包括磷酸二氢铵、磷酸氢二铵、磷酸铵、磷酸二氢钠、磷酸氢二钠、水溶性聚磷酸铵中的一种或多种。
2.根据权利要求1所述的添加剂，其特征在于，所述的助剂包括水或1-5％的稀磷酸水溶液，所述的增稠剂包括羟丙基甲基纤维素、淀粉磷酸酯钠、海藻酸钠、黄原胶、甲壳素、罗望子多糖胶、钛白粉中的一种或多种。
3.一种阻燃胶，其特征在于，是将权利要求1所述的阻燃胶添加剂与普通高速卷烟接嘴胶混合得到的阻燃胶。
4.根据权利要求3所述的普通高速卷烟接嘴胶由聚乙酸乙烯酯、乙酸乙烯共聚物、聚乙烯醇中的一种或几种组成。
5.根据权利要求3所述的阻燃胶，其特征在于，是将权利要求1所述的阻燃胶添加剂与普通高速卷烟接嘴胶按照质量比例1∶5-6混合得到的阻燃胶。
6.一种阻燃胶的应用方法，其特征在于，用于胶粘和阻燃。
7.一种阻燃胶的应用方法，其特征在于，用于卷烟接嘴的胶粘和阻燃。