CN102320790A - 东川河砂混凝土 - Google Patents
东川河砂混凝土 Download PDFInfo
- Publication number
- CN102320790A CN102320790A CN 201110267564 CN201110267564A CN102320790A CN 102320790 A CN102320790 A CN 102320790A CN 201110267564 CN201110267564 CN 201110267564 CN 201110267564 A CN201110267564 A CN 201110267564A CN 102320790 A CN102320790 A CN 102320790A
- Authority
- CN
- China
- Prior art keywords
- dongchuan
- river
- river sand
- sand
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
东川河砂混凝土,采用以下方法制得:按质量百分数采用24.4%~36.2%的东川河砂、44.8%~45.8%的碎石,5.4%~16.9%的水泥,3.0%~4.8%的粉煤灰,1.0%~2.3%的矿渣,6.8%~8.3%的水,加入0.1%~0.6%的外加剂,经搅拌得到;所述东川河砂是云南省昆明市东川区及周边地区小江流域,山体表层岩石风化后被雨水冲刷形成的泥石流淤积在河道里所形成的河砂。本发明大量利用东川河砂,环保、安全而且采选成本低。其配方合理,制作方法简单,不仅制得的东川河砂混凝土性能优良,强度高,耐久性能好,施工性能好,还为东川河沙的开发利用提供了广阔的应用空间。
Description
技术领域
本发明涉建筑材料技术领域,主要是混凝土技术领域。
背景技术
当前,由于建筑业的高速发展,对配制混凝土的沙石等原料的需求量也急速增长,导致人们大量开采石灰石矿山和石英砂矿山,带来日益严重的环境破坏问题,因此,在建筑材料特别是混凝土及相关材料的使用与使用过程中,如何寻找新的替代材料以减少对资源环境的破坏更加备受关注。
在云南省昆明市东川区及周边地区小江流域,由于山体表层岩石风化后被雨水冲刷,每年都会形成严重的泥石流,泥石流淤积在河道里所产生的河砂(公称粒径小于5mm),称为东川泥石流河沙,简称东川河砂。长期以来,泥石流都是小江流域,特别是东川地区最突出的自然灾害,给当地城镇建设,居民生活,工矿交通和农田水利造成极为严重的危害,是当地建设中急待解决的大祸患。众多的泥石流沟群向山坡蚕食、向河谷淤积,导致区域环境恶化、山坡荒芜,河滩地“砂石化”现象日趋严重,人们赖以生存的耕地日益减少,生态环境失调与环境质量下降的恶性循环在逐渐加剧。对于东川泥石流河砂的开发和利用一直是当地政府急需解决的问题。
东川河砂易于采选,与挖采山砂和炸山采石加工机制砂相比,不但环保、安全而且采选成本更低,是配制绿色、高强、高性能混凝土的优质材料。它的推广和应用,一方面可以为工程建设找到优质合适的替代材料,减少石灰石矿山和石英砂矿山开采带来的环境问题,另一方面还可解决由于细集料质量差而导致的混凝土开裂的问题,为建设优质耐久的大型工程奠定良好的基础。
在东川河砂应用上,由于现有技术在利用东川河砂制作混凝土时,一直没有研究出合理的技术方案,而且缺乏系统的研究证明,使得试制的混凝土存在质量隐患,容易引起质量争议,这使得东川河砂只能被限制在有限的领域内,无法通过在混凝土中的应用而得到广泛的应用推广,严重阻碍了东川河砂混凝土在建筑施工中的使用。
发明内容
本发明的目的在于解决现有技术存在的不足,提供一种强度高,耐久性能好,施工性能好、绿色环保的东川河砂混凝土。
本发明的目的是通过如下技术方案实现的。
东川河砂混凝土,采用以下方法制得:按质量百分数采用24.4%~36.2%的东川河砂、44.8%~45.8%的碎石、5.4%~16.9%的水泥、3.0%~4.8%的粉煤灰、1.0%~2.3%的矿渣、6.8%~8.3%的水、加入0.1%~0.6%的外加剂,经搅拌得到;所述东川河砂是云南省昆明市东川区及周边地区小江流域,山体表层岩石风化后被雨水冲刷形成的泥石流淤积在河道里所形成的河砂。
本发明所述东川河砂的粒径为0.16mm~5mm,细度模数2.3~3.0。所述粉煤灰为Ⅱ级及Ⅱ级以下的低品质粉煤灰。所述外加剂为聚羧酸类或萘系高效减水剂。
本发明大量利用东川河砂,环保、安全而且采选成本低。其配方合理,制作方法简单,不仅制得的东川河砂混凝土性能优良,强度高,耐久性能好,施工性能好,还为东川河沙的开发利用提供了广阔的应用空间,寻找到了一种资源丰富、绿色环保的新型混凝土原料。
下面结合实施例进一步阐述本发明的内容。
具体实施方式
本发明的东川河砂混凝土,采用以下方法制得:按质量百分数采用24.4%~36.2%的东川河砂、44.8%~45.8%的碎石、5.4%~16.9%的水泥、3.0%~4.8%的粉煤灰、1.0%~2.3%的矿渣、6.8%~8.3%的水、加入0.1%~0.6%的外加剂,搅拌得到。所述东川河砂是云南省昆明市东川区及周边地区小江流域,山体表层岩石风化后被雨水冲刷形成的泥石流淤积在河道里所形成的河砂,其粒径一般为0.16mm~5mm,细度模数2.3~3.0。碎石为公称粒径大于5mm的岩石颗粒。水泥可使用波兰特水泥或其他水泥。粉煤灰为Ⅱ级及Ⅱ级以下的低品质粉煤灰。所使用的水应满足《混凝土用水标准》JGJ63-2006。所用外加剂为聚羧酸类或萘系高效减水剂。聚羧酸类高效减水剂可用市场上可购得的三瑞vivid-500聚羧酸类超塑化剂(属高效减水剂)、以及其它一些行业内常用的减水剂。萘系高效减水剂可用市场上可购得的昆明承耀CY-BⅡ缓凝高效减水剂、建工3型JG-3缓凝高效减水剂。
实施例1
按质量百分数,取24.4%的粒径为0.16~5mm、细度模数3.0的东川河砂、45.7%的碎石、16.9%的水泥、3.4%的Ⅱ级粉煤灰、2.3%的矿渣、6.8%的水,加入0.5%的建工3型JG-3缓凝高效减水剂、搅拌45秒制备得到东川河砂混凝土。混凝土凝固后28天强度为73.2MPa, 56天电通量253C。
实施例2
按质量百分数,取29.6%的粒径为0.16~5mm、细度模数2.8的东川河砂、45.2%的碎石、11.0%的水泥、4.3%的Ⅱ级粉煤灰、1.7%的矿渣、7.9%质量的水,加入0.3%质量的昆明承耀CY-BⅡ缓凝高效减水剂,搅拌30秒,制备得到东川河砂混凝土。混凝土凝固后28天强度为38.7MPa,56天电通量652C。
实施例3
按质量百分数,取36.2%的粒径为0.16~5mm、细度模数2.3的东川河砂、45.8%的碎石、5.4%的水泥、3.0%的Ⅱ级粉煤灰、1.2%的矿渣、8.3%的水,加入0.1%的三瑞vivid-500聚羧酸类超塑化剂,搅拌35秒,制备得到东川河砂混凝土。混凝土凝固后28天强度为14.5MPa,56天电通量967C。
实施例4
按质量百分数,取35.4%的粒径为0.16~5mm、细度模数2.6的东川河砂、44.8%的碎石、5.4%的水泥、4.8%的低品质粉煤灰、1.0%的矿渣、8.0%的水,加入0.6%的昆明承耀CY-BⅡ缓凝高效减水剂,搅拌35秒,制备得到东川河砂混凝土。混凝土凝固后28天强度为20.5MPa,56天电通量521C。
本发明可广泛用于房屋建筑、桥梁、公路铺面、飞机跑道、铁路枕木、电线杆、挡土墙、护堤、涵洞、水坝、水箱、水塔、油槽、渠道、水沟、码头、防波堤、军事掩体、核能发电厂及建构物基础桩、及连续壁等构造物。
Claims (4)
1. 东川河砂混凝土,其特征在于,采用以下方法制得:按质量百分数采用24.4%~36.2%的东川河砂、44.8%~45.8%的碎石,5.4%~16.9%的水泥,3.0%~4.8%的粉煤灰,1.0%~2.3%的矿渣,6.8%~8.3%的水,加入0.1%~0.6%的外加剂,经搅拌得到;所述东川河砂是云南省昆明市东川区及周边地区小江流域,山体表层岩石风化后被雨水冲刷形成的泥石流淤积在河道里所形成的河砂。
2.根据权利要求1所述的东川河砂混凝土,其特征在于,所述东川河砂的粒径为0.16mm~5mm,细度模数2.3~3.0。
3.根据权利要求1所述的东川河砂混凝土,其特征在于,所述粉煤灰为Ⅱ级及Ⅱ级以下的低品质粉煤灰。
4.根据权利要求1所述的东川河砂混凝土,其特征在于,所述外加剂为聚羧酸类或萘系高效减水剂。