CN102312547A - Composition of novel antibacterial composite floor and production method thereof - Google Patents
Composition of novel antibacterial composite floor and production method thereof Download PDFInfo
- Publication number
- CN102312547A CN102312547A CN201110064535A CN201110064535A CN102312547A CN 102312547 A CN102312547 A CN 102312547A CN 201110064535 A CN201110064535 A CN 201110064535A CN 201110064535 A CN201110064535 A CN 201110064535A CN 102312547 A CN102312547 A CN 102312547A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- carbon fibre
- epoxy resin
- production method
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to composition of a novel antibacterial composite floor. The intermediate layer is a carbon fibre layer. Epoxy resin is coated on the outer layer and used for sticking the carbon fibre layer. The production method comprises the following steps of: collecting and mixing saw powder and plant straws according to the ratio of 2.5:1, adding flexibilizer, phase solvent, adhesive and polypropylene resin according to percentage by weight, putting the mixture in a low-speed mixer, after mixing for 5 min, adding liquidity modifier, anti-paste agent, coupling agent, activating agent, paraffin, stearic acid and zinc stearate, putting the mixture in a high-speed mixer to mix, inputting the mixed raw materials in a plate producing machine, adjusting and controlling the temperature increasing process to product a plate; putting the produced plate in a cooling machine to cool and size, and preparing a novel wood-plastic composite plate; dedusting carbon fibre, coating the epoxy resin on the carbon fibre outer layer along the extension direction of the carbon fibre, sticking the wood-plastic composite plate on the carbon fibre outer layer coated with the epoxy resin, drying, and obtaining the finished product.
Description
Technical field
The present invention relates to a kind of formation and production method thereof of composite floor board, specifically relate to the formation and the production method thereof on a kind of novel antibacterial composite material floor.
Background technology
The present invention relates to a kind of formation and production method thereof of composite floor board.Existing composite floor board adopts shaving board, composite plate or solid wood plate more; Have not water-fast, not moisture resistance problem, range of application has received limitation; The crack can appear in long-term use; The situation of distortion, and there is the formaldehyde composition in shaving board in the agent of pasting that manufacturing process adds, and there is harm in human body.
Summary of the invention
Defective in view of prior art exists the objective of the invention is to provide a kind of solid wear-resisting, waterproof and dampproof, and shock resistance is with low cost, manufacture easy, environmental protection, nontoxic, the formation and the production method thereof on widely used novel antibacterial composite material floor.
Carbon fiber is a kind of new material of excellent performance, has stronger adsorption capacity, can play absorption to harmful chemical gas, decomposes the effect of peculiar smell, reaches the antibiotic effect of sterilization; Can discharge anion and far infrared rays at normal temperatures, effectively weaken the function of electromagnetic wave radiation, also play the effect of heat-preserving health-care; Also can absorb human sweat residual on cloth, moisture proof has the function of self cleaning; And has light weight, energy-conserving and environment-protective, durable characteristics.
For realizing above-mentioned purpose, the technical solution that the present invention adopted is: the formation on a kind of novel antibacterial composite material floor is that carbon fiber layer is the intermediate layer, and the outer epoxy resin of brushing is used for pasting carbon fiber layer; Production method is to collect sawdust and the mixed of plant straw powder by 2.5:1, controls the order number at the 30-40 order, adds flexibilizer 0.25% by weight percentage, phase solvent 4.5%, binding agent 3.5%; Acrylic resin 35%～45% is put into low speed mixer together and is mixed, and mixes after 5 minutes, adds mobile modifier 2.5%, antimushing agent 1%; Coupling agent 3%, activator 0.25%, paraffin 3%, stearic acid 1%; Zinc stearate 1% is put into high-speed mixer and is mixed, and mixes after 5 minutes, and mixed raw materials is input in the machine of making board; Regulate and control the process of heating, carry out making sheet, the sheet material that makes is put into the cooler cooling and shaping, process a kind of novel wood-plastic clad plate; The carbon fiber dust removal is handled, brushed epoxy resin along the carbon fiber draw direction, wood-plastic clad plate is sticked on the carbon fiber skin of brushing epoxy resin, dry, promptly make finished product at the carbon fiber skin.The acrylic resin that is adopted among the present invention is big with the affinity of sawdust and plant straw powder, and associativity is good; The sheet material texture of moulding is better, and the finished product moisture-proof corrosion resistant performance that the present invention makes is good, green non-pollution in whole manufacturing process.
In view of the present invention have solid wear-resisting, waterproof and dampproof, shock resistance, with low cost, manufacture easy, environmental protection, nontoxic, widely used characteristics have reduced the cost of production of enterprise, are a kind of new methods with promotional value.
The specific embodiment
The technical solution that the present invention adopted is: the formation on a kind of novel antibacterial composite material floor is that carbon fiber layer is the intermediate layer, and the outer epoxy resin of brushing is used for pasting carbon fiber layer; Production method is to collect sawdust and the mixed of plant straw powder by 2.5:1, controls the order number at the 30-40 order, adds flexibilizer 0.25% by weight percentage, phase solvent 4.5%, binding agent 3.5%; Acrylic resin 35%～45% is put into low speed mixer together and is mixed, and mixes after 5 minutes, adds mobile modifier 2.5%, antimushing agent 1%; Coupling agent 3%, activator 0.25%, paraffin 3%, stearic acid 1%; Zinc stearate 1% is put into high-speed mixer and is mixed, and mixes after 5 minutes, and mixed raw materials is input in the machine of making board; Regulate and control the process of heating, carry out making sheet, the sheet material that makes is put into the cooler cooling and shaping, process a kind of novel wood-plastic clad plate; The carbon fiber dust removal is handled, brushed epoxy resin along the carbon fiber draw direction, wood-plastic clad plate is sticked on the carbon fiber skin of brushing epoxy resin, dry, promptly make finished product at the carbon fiber skin.
Claims (2)
1. the formation and the production method thereof on a novel antibacterial composite material floor, production method is characterized in that collecting sawdust and the plant straw powder mixed by 2.5:1, and control order number adds flexibilizer 0.25% by weight percentage at the 30-40 order; Phase solvent 4.5%, binding agent 3.5%, acrylic resin 35%～45% is put into low speed mixer together and is mixed; Mix after 5 minutes, add mobile modifier 2.5%, antimushing agent 1%, coupling agent 3%; Activator 0.25%, paraffin 3%, stearic acid 1%, zinc stearate 1%; Put into high-speed mixer and mix, mix after 5 minutes, mixed raw materials is input in the machine of making board, regulate the process of heating of controlling; Carry out making sheet, the sheet material that makes is put into the cooler cooling and shaping, process a kind of novel wood-plastic clad plate; The carbon fiber dust removal is handled, brushed epoxy resin along the carbon fiber draw direction, wood-plastic clad plate is sticked on the carbon fiber skin of brushing epoxy resin, dry, promptly make finished product at the carbon fiber skin.
2. the formation and the production method thereof on a novel antibacterial composite material floor, its constitutive characteristic is that carbon fiber layer is the intermediate layer, the outer epoxy resin of brushing is used for pasting carbon fiber layer.