CN102312275A - 铝及铝镁合金的电解抛光液 - Google Patents
铝及铝镁合金的电解抛光液 Download PDFInfo
- Publication number
- CN102312275A CN102312275A CN201110240265A CN201110240265A CN102312275A CN 102312275 A CN102312275 A CN 102312275A CN 201110240265 A CN201110240265 A CN 201110240265A CN 201110240265 A CN201110240265 A CN 201110240265A CN 102312275 A CN102312275 A CN 102312275A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- magnesium alloy
- polishing
- sodium
- electrolytic polishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
铝及铝镁合金的电解抛光液,其特征在于包括以下组分:三聚磷酸钠50-100g/L、碳酸氢钠10-50g/L、碳酸钠10-50g/L、氢氧化钠400-500g/L。本发明的抛光液对纯铝以及铝镁合金具有良好的抛光效果,全光亮且有整平效果,且污染小。溶液稳定便于调整,当抛光出来的工件光度不足时,可以添加50g/L的三聚磷酸可恢复原来的抛光性能。
Description
技术领域
本发明涉及一种金属抛光液,具体地讲是涉及一种铝及铝镁合金的碱性抛光液。
背景技术
在制作铝制标牌时,经常需要铝材表面具有镜面光亮的外表,因此需要对铝或铝合金进行抛光,机械抛光操作条件差、效率低、并且不使用比较复杂的零件,采用化学抛光和电解抛光可避免机械抛光的以上缺点,其中,碱性化学抛光是利用铝以及铝合金件在碱性溶液中的选择性自溶解作用来整平和抛光制件表面,以提高表面光洁度的方法。
发明内容
本发明所要解决的技术问题是提供一种铝及铝镁合金的碱性抛光液,抛光效果好。
为解决上述技术问题,本发明是这样实现的
铝及铝镁合金的电解抛光液,其特征在于包括以下组分:
三聚磷酸钠 50-100g/L
碳酸氢钠 10-50 g/L
碳酸钠 10-50g/L
氢氧化钠 400-500g/L。
其中氢氧化钠具有腐蚀作用;
碳酸氢钠、碳酸钠具有整平抛光效果;
三聚磷酸钠与碳酸氢钠、碳酸钠合用具有增光效果。
工艺参数是:温度90-100℃、时间1-5min。
90℃以下抛光的试件为暗色,90-100℃所抛出来的试件为全光亮,因此抛光温度为90-100℃。因为碱比酸对铝具有更强的溶解能力,因此抛光温度和时间要严格控制。
本发明有以下积极的效果:本发明的抛光液对纯铝以及铝镁合金具有良好的抛光效果,全光亮且有整平效果,且污染小。溶液稳定便于调整,当抛光出来的工件光度不足时,可以添加50g/L的三聚磷酸可恢复原来的抛光性能。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
本发明实施例采用的镁铝合金5×20×50mm3。
实施例1
铝及铝镁合金的电解抛光液,包括以下组分:三聚磷酸钠 50g/L、碳酸氢钠 20g/L、碳酸钠 30 g/L、氢氧化钠 400g/L。工艺参数是:90℃、时间1min。抛光后表面光亮且平整。
实施例2
铝及铝镁合金的电解抛光液,包括以下组分:三聚磷酸钠 80g/L、碳酸氢钠 10g/L、碳酸钠 50 g/L、氢氧化钠 500g/L。工艺参数是:100℃、时间1.5min。抛光后表面光亮且平整。
实施例3
铝及铝镁合金的电解抛光液,包括以下组分:三聚磷酸钠 100g/L、碳酸氢钠50g/L、碳酸钠 10 g/L、氢氧化钠 450g/L。工艺参数是:95℃、时间2min。抛光后表面光亮且平整。
上述具体实施方式不以任何形式限制本发明的技术方案,凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。
Claims (1)
1.铝及铝镁合金的电解抛光液,其特征在于包括以下组分:三聚磷酸钠 50-100g/L、碳酸氢钠10-50 g/L、碳酸钠 10-50g/L 、氢氧化钠 400-500g/L。