CN102310301A - 药芯焊丝 - Google Patents
药芯焊丝 Download PDFInfo
- Publication number
- CN102310301A CN102310301A CN 201110246329 CN201110246329A CN102310301A CN 102310301 A CN102310301 A CN 102310301A CN 201110246329 CN201110246329 CN 201110246329 CN 201110246329 A CN201110246329 A CN 201110246329A CN 102310301 A CN102310301 A CN 102310301A
- Authority
- CN
- China
- Prior art keywords
- percent
- flux
- cored wire
- welding
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种药芯焊丝,按照质量百分比,组分为:金红石38~42%,石英4.2~4.8%,镁砂2.8~3.5%,氟化物3.5~4.2%,镍粉11~14%,钛铁5~5.4%,硅铁5.9~6.4%,金属锰8~11%,钼粉4~5%,铁粉5.9~6.5%,合金元素1.1~1.2%,稀有金属5~5.3%。该药芯焊丝在焊接过程中,熔滴为细小颗粒过渡,飞溅小,稳定性好,可实现全方位焊接,熔渣覆盖均匀,脱渣容易,可用于焊接行业的各个领域。
Description
技术领域
本发明涉及一种金属药芯焊丝。
背景技术
药芯焊丝是一种新型的焊接材料,具有高效益、低成本、高质量等各方面的优势,它继承了焊条成分可调,又克服了焊条不能连续、自动焊接的缺点,还具效率高、焊缝成形光顺美观等一系列优点。药芯焊丝与实芯焊丝相比具有下列特点:生产效率高、成分调节灵活、节能低污染。如在造船行业,药芯焊丝已取代手工焊条和实心焊丝,成为消耗最大的焊接材料,并且凭借其焊接具有的高强度、高韧性、抗裂、抗气孔的优异性能,已经成为造船、大型桥梁、海洋平台等建造最重要的焊材。
目前,市场中出现的药芯焊丝,由于药粉成份及比例调配不理想,在焊接过程中熔滴过渡性差,飞溅,稳定性不好,熔渣覆盖不均匀,不易脱渣等问题。
发明内容
本发明所要解决的技术问题是:提供一种焊接过程中熔滴为细小颗粒过渡,飞溅小,稳定性好,可实现全方位焊接,熔渣覆盖均匀,脱渣容易的药芯焊丝。
为解决上述技术问题,本发明采用的技术方案为:一种药芯焊丝,按照质量百分比,组分为:金红石38~42%,石英4.2~4.8%,镁砂2.8~3.5%,氟化物3.5~4.2%,镍粉11~14%,钛铁5~5.4%,硅铁5.9~6.4%,金属锰8~11%,钼粉4~5%,铁粉5.9~6.5%,合金元素1.1~1.2%,稀有金属5~5.3%。
其中,合金元素为钛,铝,铬任意比混合组成。
所述稀有金属选自钛、锆、铪、钒、铌、钽、钼、钨中的一种或两种以上的组合。
所述氟化物为氟化钾。
本发明的有益效果为:本发明药芯焊丝在焊接过程中,熔滴为细小颗粒过渡,飞溅小,稳定性好,可实现全方位焊接,熔渣覆盖均匀,脱渣容易。
具体实施方式
实施例1
金红石40g,石英4.5g,镁砂3g,氟化钾4g,镍粉12g,钛铁5g,硅铁6g,金属锰10g,钼粉4g,铁粉6.5g,合金元素1.2g,钛5.3g。
实施例2
金红石38g,石英4.8g,镁砂3.5g,氟化钾3.9g,镍粉12g,钛铁5.4g,硅铁6g,金属锰9g,钼粉4.5g,铁粉5.9g,合金元素1.2g,钼和钨5.2g。
利用该药芯焊丝的熔敷金属化学成份C≤0.05%,Mn≤1.25%,Si≤0.46,P≤0.012%,S≤0.01%;焊缝机械性能:屈服强度≥470Mpa,抗拉强度≥560 Mpa,伸长率≥28%,冲击值≥128J。
Claims (3)
1.一种药芯焊丝,其特征在于,按照质量百分比,组分为:金红石38~42%,石英4.2~4.8%,镁砂2.8~3.5%,氟化物3.5~4.2%,镍粉11~14%,钛铁5~5.4%,硅铁5.9~6.4%,金属锰8~11%,钼粉4~5%,铁粉5.9~6.5%,合金元素1.1~1.2%,稀有金属5~5.3%;
其中,合金元素为钛,铝,铬任意比混合组成。
2.根据权利要求1所述药芯焊丝,其特征在于,所述稀有金属选自钛、锆、铪、钒、铌、钽、钼、钨中的一种或两种以上的组合。
3.根据权利要求1所述药芯焊丝,其特征在于,所述氟化物为氟化钾。