CN102295903B - 快速预固化白乳胶生产方法 - Google Patents

快速预固化白乳胶生产方法 Download PDF

Info

Publication number
CN102295903B
CN102295903B CN201110175259A CN201110175259A CN102295903B CN 102295903 B CN102295903 B CN 102295903B CN 201110175259 A CN201110175259 A CN 201110175259A CN 201110175259 A CN201110175259 A CN 201110175259A CN 102295903 B CN102295903 B CN 102295903B
Authority
CN
China
Prior art keywords
parts
weight
add
temperature
cooled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201110175259A
Other languages
English (en)
Other versions
CN102295903A (zh
Inventor
于红卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongxiang Beite Technology Co ltd
Original Assignee
Zhejiang A&F University ZAFU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang A&F University ZAFU filed Critical Zhejiang A&F University ZAFU
Priority to CN201110175259A priority Critical patent/CN102295903B/zh
Publication of CN102295903A publication Critical patent/CN102295903A/zh
Application granted granted Critical
Publication of CN102295903B publication Critical patent/CN102295903B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种快速预固化白乳胶生产方法，先进行基料的制备，用2000重量份(下同)水、120份PVA17-88、36份甲醛和22份尿素在一定温度与pH值的条件下，反应生成聚乙烯醇缩甲醛与脲醛树脂作基料，再加入10份作乳化剂的OP-10，在4-5h内滴加完600份VAc并同时按每隔0.5h加2份地分次加完10份浓度为10％的过硫酸铵水溶液，升温至88-90℃，保温反应1h，降温至70℃，加入125份邻苯二甲酸二丁酯、50份淀粉和75份甲醇，搅拌、反应，再加2、3份小苏打和5份改性壳聚糖金属配合物防霉剂，搅拌、冷却至45℃出料便制成了本快速预固化白乳胶。用本方法制得的胶在25℃环境中4h即预固化，且抗霉杀菌性能优越。

Description

快速预固化白乳胶生产方法
技术领域
本发明涉及一种胶粘剂生产方法，具体是用作竹木制品、纸制品胶粘剂的白乳胶的改性白乳胶生产方法。
背景技术
白乳胶是用于粘接木竹制品或纸制品的通用胶粘剂，在使用过程中，其一些性能欠理想，因此，对该胶的改性研究成果不断出现，如CN1249323“特种水基乳白胶”，是在乳白胶原有基础上添加了特种添加剂，使原来只能粘接竹木制品、纸制品和皮革制品等吸水性材料的乳白胶改性为可用于吸水性材料与非吸水性材料如金属、玻璃、橡胶、石材的粘接。CN1445323“白乳胶的生产方法”，是在普通白乳胶基础上添加苯乙烯与丙烯酸共聚乳液以提高胶体耐水性和粘接力，加入乙二醇以防冻，加氢氧化铝以阻燃等。现在通用的白乳胶，及一些已公开的专利资料所报道的改性白乳胶的预固化速度与防霉性欠理想，尚未发现有关白乳胶预固化快和防霉性强的改性白乳胶生产方法的报道。
发明内容
本发明要解决的技术问题是提供一种防霉性好、快速预固化的白乳胶生产方法。
解决该技术问题采用如下技术方案：本快速预固化白乳胶生产方法按如下步骤进行：
(1)基料的制备：将下列原料按重量份投入反应釜中：加入2000份水后升温至40℃，再加120份聚乙烯醇即PVA17-88，再升温至90℃，保温至少1h至全溶解，用酸调pH为2，加入36份浓度为37％的甲醛，搅拌，反应至溶液产生有白色絮状物，用碱调pH值为7.0-7.5，加入22份尿素并降温至80℃，生成聚乙烯醇缩甲醛与脲醛树脂，作为基料；
(2)快速预固化白乳胶的制取：在步骤(1)基料降温至80℃时，再依次加入下列重量份的原料，加入10份作为乳化剂的烷基酚聚氧乙烯醚即OP-10、搅拌、首次加入2份浓度为10％的过硫酸铵水溶液，温度控制在80±2℃时用滴加方式加入醋酸乙烯酯即VAc共600份，开始按160L/h的流量滴加，待开始回流，滴加流量减为120L/h，滴加时间共4-5h，这期间每隔0.5h，加2份过硫酸铵水溶液，醋酸乙烯酯滴完则共10份过硫酸铵也全加完，升温88-90℃，保温反应1h，降温至70℃，加入125份邻苯二甲酸二丁酯、50份淀粉和75份甲醇，保温反应30min，降温至60℃，加2-3份小苏打和5份改性壳聚糖金属配合物防霉剂，搅拌，冷却至45℃出料即成。
本发明的有益效果是添加了甲醇后预固化速度明显加快，在25℃时4h即预固化，壳聚糖本身具有杀菌功能，还能螯合具有杀菌功能的金属离子，添加改性壳聚糖金属配合物后，胶的杀菌防霉性很强。
具体实施方式
本发明下面结合实施例予以详述。因本发明公开的各原料的配比值均按重量份计算，因此在实验室试制用克或毫克计算，中试用斤或公斤计算，大规模生产用吨计算，各取所需。又因各原料的配比值均为单值，不是区间值，因此只用一个实施例来说明，该实施例也就是最佳实施例。
实施例：本快速预固化白乳胶生产方法按如下步骤进行：
(1)基料的制备：将下列原料按重量份投入反应釜中：加入2000份水后升温至40℃，再加120份聚乙烯醇即PVA17-88，再升温至90℃，保温至少1h至全溶解，用酸调pH为2，加入36份浓度为37％的甲醛，搅拌，反应至溶液产生有白色絮状物，用碱调pH值为7.0-7.5，加入22份尿素并降温至80℃，生成聚乙烯醇缩甲醛与脲醛树脂，作为基料；
(2)快速预固化白乳胶的制取：在步骤(1)基料降温至80℃时，再依次加入下列重量份的原料，加入10份作为乳化剂的烷基酚聚氧乙烯醚即OP-10、搅拌、首次加入2份浓度为10％的过硫酸铵水溶液，温度控制在80±2℃时用滴加方式加入醋酸乙烯酯即VAc共600份，开始按160L/h的流量滴加，待VAc开始回流，滴加流量减为120L/h，滴加时间共4-5h，这期间每隔0.5h，加2份过硫酸铵水溶液，醋酸乙烯酯滴完则共10份过硫酸铵也全加完，升温88-90℃，保温反应1h，降温至70℃，加入125份邻苯二甲酸二丁酯、50份淀粉和75份甲醇，保温反应30min，降温至60℃，加2-3份小苏打和5份改性壳聚糖金属配合物防霉剂，搅拌，冷却至45℃出料即成。
上述反应中的各原料均可市售获得，其中的改性壳聚糖金属配合物防霉剂可从浙江农林大学工程学院实验厂购得。各原料除注明纯度和浓度的以外，其余均为工业级。
壳聚糖本身具有杀菌功能，其分子结构中有丰富的羟基和氨基等活性基因，既能螯合一些具有杀菌性的金属离子，又能与木竹材上的相关基因牢固结合，使本改性白乳胶的抑菌、刹菌防霉性强。
甲醇的沸点低，仅为64.7℃，挥发快，添加甲醇有利本改性白乳胶的快速预固化。
制成的本胶，粘度5-20Pa·S/25℃，固体含量29％-30％，粒度1-2μm，pH4-6，储存期3-6个月。

Claims (1)

1.一种快速预固化白乳胶生产方法，其特征是按如下步骤进行：
(1)基料的制备：将下列原料按重量份投入反应釜中：加入2000份水后升温至40℃，再加120份聚乙烯醇PVA17-88，再升温至90℃，保温至少1h至全溶解，用酸调pH为2，加入36份浓度为37％的甲醛，搅拌，反应至溶液产生有白色絮状物，用碱调pH值为7.0-7.5，加入22份尿素并降温至80℃，生成聚乙烯醇缩甲醛与脲醛树脂，作为基料；
(2)快速预固化白乳胶的制取：在步骤(1)基料降温至80℃时，再依次加入下列重量份的原料，加入10份作为乳化剂的烷基酚聚氧乙烯醚OP一10、搅拌、首次加入2份浓度为10％的过硫酸铵水溶液，温度控制在80±2℃时用滴加方式加入醋酸乙烯酯VAc共600份，开始按160L/h的流量滴加，待VAc开始回流，滴加流量减为120L/h，滴加时间共4-5h，这期间每隔0.5h，加2份过硫酸铵水溶液，醋酸乙烯酯滴完则共10份过硫酸铵水溶液也全加完，升温至88-90℃，保温反应1h，降温至70℃，加入125份邻苯二甲酸二丁酯、50份淀粉和75份甲醇，保温反应30min，降温至60℃，加2-3份小苏打和5份改性壳聚糖金属配合物防霉剂，搅拌，冷却至45℃出料即成。
CN201110175259A 2011-06-24 2011-06-24 快速预固化白乳胶生产方法 Expired - Fee Related CN102295903B (zh)