CN102294379A - 大口径高压气瓶用无缝钢管的制造方法 - Google Patents

大口径高压气瓶用无缝钢管的制造方法 Download PDF

Info

Publication number
CN102294379A
CN102294379A CN201110177148A CN201110177148A CN102294379A CN 102294379 A CN102294379 A CN 102294379A CN 201110177148 A CN201110177148 A CN 201110177148A CN 201110177148 A CN201110177148 A CN 201110177148A CN 102294379 A CN102294379 A CN 102294379A
Authority
CN
China
Prior art keywords
pipe
time
steel pipe
draw
pickling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110177148A
Other languages
English (en)
Other versions
CN102294379B (zh
Inventor
尹人洁
张涛
吕建钢
刘云涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pangang Group Chengdu Steel and Vanadium Co Ltd
Original Assignee
Pangang Group Chengdu Steel and Vanadium Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pangang Group Chengdu Steel and Vanadium Co Ltd filed Critical Pangang Group Chengdu Steel and Vanadium Co Ltd
Priority to CN 201110177148 priority Critical patent/CN102294379B/zh
Publication of CN102294379A publication Critical patent/CN102294379A/zh
Application granted granted Critical
Publication of CN102294379B publication Critical patent/CN102294379B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明为大口径高压气瓶用无缝钢管的制造方法,解决已有方法生产成本高,生产效率低,钢管的几何尺寸精度和内外表面质量不能满足大口径高压气瓶要求的问题。包括如下步骤:(1)将直径为600mm的圆铸钢坯在环形加热炉加热,(2)将加热后的圆铸造钢坯用在线机械热定心,定心也中心偏差≦5mm,经二辊斜轧穿孔穿孔得毛管,(3)将毛管送508周期式轧管机轧管,制成荒管,(4)将荒管在中频感应炉加热到780—850℃,送顶推式扩经机扩径,进行内外整体修磨,得管坯,(5)将管坯内,外表面清理、热处理、酸洗、清洗、磷化、润滑后送精密液压拔机第一次拔制,(6)将第一次拔制后的管坯清洗、磷化、润滑后送精密液压拔机第二次拔制,得成品。

Description

大口径高压气瓶用无缝钢管的制造方法
技术领域:
 本发明用直径为600mm的圆铸钢坯生产大口径高压气瓶用无缝钢管的制造方法
背景技术:
    本发明属于大口径无缝钢管制造工艺方法类。
    发明或者实用新型相关的背景技术
生产大口径无缝钢管主要有以下几种生产工艺:
⑴连轧管机组+斜轧扩径机(第一种形式)
⑵二次斜轧穿孔+均整机(第二种形式) 
⑶周期轧管+拉拔式扩管(第三种形式)
⑷轧管机组供坯+顶推式扩径机(第四种形式)
⑸∮508mm以上的周期式轧管机组(第五种形式)
第一种形式:坯料采用连铸园坯,由MPM限动芯棒连轧管机供管坯,再采用斜轧扩径机生产工艺生产该品种。该先进的工艺设备是现代生产大口径、中薄壁厚无缝钢管的最佳方法。投资大,生产成本高。目前国外意大利达尔明钢管厂、天津无缝钢管公司均采用此工艺。
第二种形式:采用钢坯经二次穿孔,均整机均匀壁厚制成钢管。该生产工艺成本低,生产的产品几何尺寸、内外表面质量均较差,也就是说该生产工艺用于生产低端产品,或用于供管坯。
第三种形式:周期轧管+拉拔式扩管。生产工艺简便,成本低,但钢管的几何精度及内外表面质量差。
第四种形式:生产成本低,产量低钢管的几何精度及内外表面质量差。
第五种形式:适合生产大、中型口径的无缝钢管以及一些大直径厚壁管等。既可使用轧制坯,也可使用钢锭与连铸坯,可批量生产,也可零星生产,生产灵活性大。 但产量低,如一套大型周期轧机年产量只有20~30万吨左右;作业率低,一般为60~80%;工具消耗量大,一般为10公斤/吨管左右; 由于周期式轧管方式在轧制过程中轧辊弹跳值大,造成壁厚与外径偏差大,不能满足现代产品标准的要求。     
上述的第一种工艺投资大,生产成本高,且生产的钢管内外表面粗糙度大于12μm。
第二至第五种工艺生产的钢管的几何精度及内外表面质量差。每支钢管的实际重量大于中间壁厚的理论重量值。
已有的生产工艺不能生产出满足要求的大口径高压气瓶钢管。
发明内容:
本发明的目的是提供一种投资省,生产成本低,生产效率高,钢管的几何精度和内外表面质量高,高品质的用直径为600mm的圆铸钢坯生产大口径高压气瓶用无缝钢管制造方法。
本发明是这样实现的:
本发明用直径为600mm圆铸钢坯生产大口径高压气瓶用无缝钢管的制造方法,包括如下步骤:
(1)将直径为600mm的圆铸钢坯在环形加热炉加热,加热时间12—14小时,出炉钢坯温度1240—1270℃,
(2)将加热后的圆铸钢坯用在线机械热定心,定心孔中心偏差≦5mm,经二辊斜轧穿孔机穿孔得毛管,毛管外径630—645mm,长度≦4.2m,
(3)将毛管送508周期式轧管机轧管,制成Φ508×20—30mm,长度:9—15m的荒管,轧辊直径大于1000mm,轧机喂入量20—25mm,轧辊侧壁开口角23度,芯棒长度4.8—5.2m,  
(4)将荒管在中频感应炉加热到780—850℃,送顶推式扩经机扩径,进行内外整体修磨,得管坯,管坯外径563—570 mm,
(5)将管坯内,外表面清理、热处理、酸洗、清洗、磷化、润滑后送精密液压拔机第一次拔制,
(6)将第一次拔制后的管坯清洗、磷化、润滑后送精密液压拔机第二次拔制,得成品。
管坯热处理加热温度为820±10℃,保温时间40—60分钟,随炉以100—150℃/h冷却至500℃再出炉空冷。
1000吨精密液压拔机的拔制速度为0.5—2.5m/min,压力为10—12Mpa,外模具Φ559mm,第一次拔制内模具Φ508—Φ522mm,第二次拔制内模具为Φ506—Φ526mm,成品钢管壁厚15—20mm,长度8.0—12.5m。
酸洗:硫酸酸液重量百分浓度在10%~20%、Fe2+浓度不大于250克/升、温度控制范围60~70℃,酸洗时间控制在60~120分钟,将钢管内外表面的氧化铁皮酸洗干净,
冲洗:酸洗后的钢管要在清水槽内多次充满水并倾倒,以倒掉管子内存的氧化铁皮和附着物为止。然后再倾倒放置在冲洗台上,用高压水自上而下逐根进行冲洗,直至管内流出清水为止,
磷化:总酸度25~40滴、游离酸度1~4滴、Zn(NO3)2为18~28克/升、H3PO4为3~7克/升、SO4 2-≤2克/升、温度60~70℃、磷化时间10~15分钟,
润滑:润滑剂浓度为1.2~2.6BN、游离碱度0~1.5Pt、温度50~65℃、皂化时间5~15分钟。
本发明是采用∮600圆连铸坯由508周期轧管机生产管坯,经顶推式扩径机扩径,1000吨精密液压拔机拔制的生产工艺,通过采用独特的制造工艺技术,生产出满足要求的高质量大口径高压气瓶钢管。
本发明生产的钢管与背景技术中第四种生产工艺生产的钢管的比较见下表:
Figure 486645DEST_PATH_IMAGE001
采用由508周期式轧管机生产荒管,荒管的外径尺寸大,顶推式扩径机扩径量小,壁厚恶化程度轻,得到较好壁厚精度的管坯,再经精密液压拔机拔制后,可得到外径和壁厚精度高,单支重量轻,整体质量优的高质量大口径高压气瓶钢管。
本发明投资省,生产工艺简单,成本低,生产效率高,产品的几何精度高,内外表面粗糙度小。本发明生产的钢管达到能满足大口径高压气瓶钢管要求的以下水平:
钢管外径559mm;钢管壁厚15~24mm;钢管长度8.0~12.5m;钢管要通过国家标准 GB/T5777-2008中L2当量的超声波探伤及全长整体测量壁厚;钢管的公差:壁厚0~+22.5%mm,外径±0.75%;要求每支钢管的实际重量必须小于或等于中间壁厚的理论重量值,钢管内外表面粗糙度Rz≤12μm。
具体实施方式:
    ⑴工艺流程:∮600圆连铸坯→坯料加热→热定心→二辊斜轧穿孔机穿孔→508周期式轧管机轧管→热锯头尾→冷却→转顶推式扩径机组扩径→内外表面整体修磨→热处理→酸洗→清洗→磷化→润滑→1000吨精密夜压拔机拔制清洗→磷化→拔机→矫直→精整→超声波探伤测壁厚→包装入库。
⑵坯料:经LF精练炉+真空脱气处理冶炼的的∮600圆连铸坯。
坯料加热:∮600mm圆连铸坯在环形炉加热时,要求圆连铸坯在炉内排列的间距为700mm,炉膛保持还原性气氛,加热不得出现阴阳面、加热不透、过热或过烧现象,加热时间12~14小时,出炉钢温1240~1270℃;
在线热定心:经环形炉加热的∮600mm圆连铸坯采用在线机械热定心,其定心孔中心偏差要求≤5mm。
二辊斜轧穿孔机穿孔:根据不同的生产规格,选择相应的穿孔顶头尺寸,毛管外径控制630~645mm,确保穿孔后毛管长度≤4.2m,要求穿孔后的毛管目视平直,全长外径大小一致。
508周期式轧机轧管:制成∮508×20~28mm的荒管,几何尺寸公差满足D±1%、S±10%,钢管任一横截面上壁厚的最大值与最小值之差应小于3.0mm。要达到此条件,必须满足轧辊直径大于1000mm;轧机喂入量20~25mm;轧辊侧壁开口角23度;芯棒长度4.8~5.2M。
⑺顶推式扩径机将508周期式轧管机生产的荒管扩制成冷拔管坯。将由508周期式轧管机提供的荒管进行检查、端面锯切、内外表面缺陷清理后,在内壁涂润滑剂,然后进行顶推扩管,经内外整体修磨后制成冷拔管坯。生产时该机组有以下五个关键点:
第一:顶推式扩径机的前台受料长度必须是大于15m;
第二:中频感应加热钢管的温度应控制在:780~850℃;
第三:推制速度:100~120mm/min;
第四:制成的冷拔管坯料外径:563~570mm;
第五:推制后的管坯需进行内外表面整体修磨,修磨量控制在1.0~1.5mm。主要清除外表面缺陷,内表面内划伤,内麻坑等缺陷。
⑻1000吨精密液压冷拔机拔制
二道次拔制变形量分配如下:
Figure 561393DEST_PATH_IMAGE002
第1道次步骤:
坯料管热处理:
热处理温度820±10℃、保温时间40~60分钟,随炉以100~150℃/h冷却至500℃再出炉空冷。
b 酸洗:
硫酸酸液浓度在10%~20%、Fe2+浓度不大于250克/升、温度控制范围50~70℃、酸洗时间60~100分钟。
c 冲洗:
酸洗后的钢管要在清水槽内多次充满水并倾倒,以倒掉管子内存的氧化铁皮和附着物为止。然后再倾倒放置在冲洗台上,用高压水自上而下逐根进行冲洗,直至管内流出清水为止。
磷化:
总酸度25~40滴、游离酸度1~4滴、Zn(NO3)2为18~28克/升、H3PO4为3~7克/升、SO4 2-≤2克/升、温度60~70℃、磷化时间10~15分钟。
e 润滑:
润滑剂浓度为1.2~2.6BN、游离碱度0~1.5Pt、温度55~65℃、皂化时间5~15分钟。
f  1000吨精密液压拔拔机制:
①拔制中心线和拔制小车中心,以保持两者一致;
②确定外模安装到位压实、定位孔与模座套端面垂直;
③内模与芯杆、螺钉装配应为过渡配合,以防止过渡松动破坏模具和拔制中的浮动;
④拔制速度控制在0.5~2.5M/min,系统压力控制在10~12Mpa。拔制初期采用低速拔制速度,拔制平稳运行后根据系统压力调整拔制速度。
第2道次步骤:重复以上第1道次c、d、e、f步骤。
精整、性能检验、探伤和全长测量壁厚、称重量、包装入库等。
本发明用Φ600圆坯连坯生产两种公称外径相同,最小壁厚不同的无缝钢管,产品技术要求和工艺参数如下:
产品技术要求:见表1:
    表1  
生产工艺
工艺流程
    ∮600圆连铸坯→坯料加热→热定心→二辊斜轧穿孔机穿孔→508周期式轧机轧管→热锯头尾→冷却→转顶推式扩径机组扩径→内外表面整体修磨→热处理→酸洗→清洗→磷化→润滑→1000吨精密夜压拔机拔制清洗→磷化→润滑→矫直→精整→超声波探伤测壁厚→包装入库。
管坯生产工艺参数:见表2
表2
顶推制工艺参数:见表3
表3
Figure 385626DEST_PATH_IMAGE005
内外表面整体修磨:修磨量控制在1.0~1.5mm。主要清除外表面缺陷,内划伤,内麻坑等缺陷。
精密冷拔工艺参数:见表4、表5、表6、表7、表8
坯料管热处理工艺:
表4
酸洗润滑:
表5
Figure 662204DEST_PATH_IMAGE007
磷化:
表6
Figure 996233DEST_PATH_IMAGE008
润滑:
表7
Figure 135091DEST_PATH_IMAGE009
精密液压拔制机工艺参数:
表8
Figure 187360DEST_PATH_IMAGE010
实物质量
坯料管几何尺寸:见表9
表9
 
推制制成的冷拔管坯几何尺寸:见表10
表10
Figure 891191DEST_PATH_IMAGE012
 
 冷拔成品钢管几何尺寸:见表11
表11
 
Figure 200950DEST_PATH_IMAGE013
试样热处理性能(纵向):见表12
表12
 
Figure 740516DEST_PATH_IMAGE014

Claims (5)

1.大口径高压气瓶用无缝钢管的制造方法,包括如下步骤:
(1)将直径为600mm的圆铸钢坯在环形加热炉加热,加热时间12—14小时,出炉钢坯温度1240—1270℃,
(2)将加热后的圆铸钢坯用在线机械热定心,定心孔中心偏差≦5mm,经二辊斜轧穿孔机穿孔得毛管,毛管外径630—645mm,长度≦4.2m,
(3)将毛管送508周期式轧管机轧管,制成Φ508×20—30mm,长度:9—15m的荒管,轧辊直径大于1000mm,轧机喂入量20—25mm,轧辊侧壁开口角23度,芯棒长度4.8—5.2m,  
(4)将荒管在中频感应炉加热到780—850℃,送顶推式扩经机扩径,进行内外整体修磨,得管坯,管坯外径563—570 mm,
(5)将管坯内,外表面清理、热处理、酸洗、清洗、磷化、润滑后送精密液压拔机第一次拔制,
(6)将第一次拔制后的管坯清洗、磷化、润滑后送精密液压拔机第二次拔制,得成品。
2.根据权利要求1所述的制造方法,其特征在于管坯热处理加热温度为820±10℃,保温时间40—60分钟,随炉以100—150℃/h冷却至500℃再出炉空冷。
3.根据权利要求1所述的制造方法,其特征在于1000吨精密液压拔机的拔制速度为0.5—2.5m/min,压力为10—12Mpa,外模具Φ559mm,第一次拔制内模具Φ508—Φ522mm,第二次拔制内模具为Φ506—Φ526mm,成品钢管壁厚15—20mm,长度8.0—12.5m。
4.根据权利要求1所述的制造方法,其特征在于酸洗:硫酸酸液重量百分浓度在10%~20%、Fe2+浓度不大于250克/升、温度控制范围60~70℃,酸洗时间控制在60~120分钟,将钢管内外表面的氧化铁皮酸洗干净,
冲洗:酸洗后的钢管要在清水槽内多次充满水并倾倒,以倒掉管子内存的氧化铁皮和附着物为止。
5.然后再倾倒放置在冲洗台上,用高压水自上而下逐根进行冲洗,直至管内流出清水为止,
磷化:总酸度25~40滴、游离酸度1~4滴、Zn(NO3)2为18~28克/升、H3PO4为3~7克/升、SO4 2-≤2克/升、温度60~70℃、磷化时间10~15分钟,
润滑:润滑剂浓度为1.2~2.6BN、游离碱度0~1.5Pt、温度50~65℃、皂化时间5~15分钟。
CN 201110177148 2011-06-28 2011-06-28 大口径高压气瓶用无缝钢管的制造方法 Active CN102294379B (zh)