CN102286238B - 一种金属防腐漆及其制备方法 - Google Patents

一种金属防腐漆及其制备方法 Download PDF

Info

Publication number
CN102286238B
CN102286238B CN 201110260413 CN201110260413A CN102286238B CN 102286238 B CN102286238 B CN 102286238B CN 201110260413 CN201110260413 CN 201110260413 CN 201110260413 A CN201110260413 A CN 201110260413A CN 102286238 B CN102286238 B CN 102286238B
Authority
CN
China
Prior art keywords
preparation
parts
weight
barium sulfate
resins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110260413
Other languages
English (en)
Other versions
CN102286238A (zh
Inventor
赵建立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI YIDA ELECTRONIC Co Ltd
Original Assignee
ANHUI YIDA ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI YIDA ELECTRONIC Co Ltd filed Critical ANHUI YIDA ELECTRONIC Co Ltd
Priority to CN 201110260413 priority Critical patent/CN102286238B/zh
Publication of CN102286238A publication Critical patent/CN102286238A/zh
Application granted granted Critical
Publication of CN102286238B publication Critical patent/CN102286238B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种金属防腐漆及其制备方法，其主要是将组成原料环氧树脂E20、聚酰胺树脂、纳米碳酸钙、硫酸钡、水杨酸、四甲基硅烷、醋酸丁酯、异丙醇、氯化石蜡和氯化烯烃按一定重量份混合搅拌、分散后得到成品。本发明制备的金属防腐漆漆膜附着力好、干燥快、耐热性好，环保无污染，而且本发明制备方法简单，成本低，适合大规模生产。

Description

一种金属防腐漆及其制备方法
技术领域
本发明涉及一种金属防腐漆及其制备方法，是由大分子量的聚酰胺树脂、醋酸丁酯组成，适用于沿海地区大气工业防腐。
背景技术
    近些年采用工业防腐漆来保护金属的以环氧富锌漆为最多。由于金属锌粉的密度比较大，为了不使锌粉沉降或减慢锌粉的沉降速度，需要在漆中加一定量的防沉降剂；防沉剂的加入漆的粘稠度也随之增加，在选择聚酰胺树脂时就要尽可能地选择小分子量的树脂(E44);施工时为了能满足涂刷性，要向漆中加入大量的溶剂，施工时溶剂严重危害工人的身体健康、漆在干燥过程中溶剂挥发到空气中污染环境、溶剂的使提高了施工成本；小分子量树脂固化后漆膜的脆性大，金属热胀冷缩系大在温度变化时漆膜易龟裂或脱落。
    铝镁锌合金密度小、理论发生电量大(为锌的3.6倍)、铝镁锌合金在防腐漆中的添加量仅为锌粉的50％左右就可以获得最优的涂层性能，涂层电阻高达 500KΩ.cm2以上，电极电位可长时间稳定在-0．85v(SCE)以下，一道涂层有效保护寿命在于1年。
发明内容
为了缓解现有技术的不足和缺陷，本发明目的在于提供一种金属防腐漆及其制备方法。
为了实现上述目的本发明采用如下技术方案：
金属防腐漆，其特征在于其组成原料的重量份为：环氧树脂E20 30-40份、聚酰胺树脂30-40份、纳米碳酸钙1-3份、硫酸钡8-12份、水杨酸8-12份、四甲基硅烷2-5份、醋酸丁酯8-15份、异丙醇10-15份、氯化石蜡2-5份和氯化烯烃5-10份。
所述的金属防腐漆的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份将环氧树脂E20、聚酰胺树脂、硫酸钡、纳米碳酸钙、四甲基硅烷和异丙醇混合搅拌均匀，高速分散并研磨至35um细度以下；
（2）在上述反应体系中按重量份加入水杨酸、醋酸丁酯、氯化石蜡和氯化烯烃，在700-800转/分钟转速下高速分散5-10分钟，得到成品。
本发明的有益效果：
本发明制备的金属防腐漆漆膜附着力好、干燥快、耐热性好，环保无污染，而且本发明制备方法简单，成本低，适合大规模生产。
具体实施方式
实施例1：金属防腐漆，其组成原料的重量份为：环氧树脂E20 30份、聚酰胺树脂30份、纳米碳酸钙1份、硫酸钡8份、水杨酸8份、四甲基硅烷2份、醋酸丁酯8份、异丙醇10份、氯化石蜡2份和氯化烯烃5份。
金属防腐漆的制备方法，包括以下步骤：
（1）按组成原料的重量份将环氧树脂E20、聚酰胺树脂、硫酸钡、纳米碳酸钙、四甲基硅烷和异丙醇混合搅拌均匀，高速分散并研磨至35um细度以下；
（2）在上述反应体系中按重量份加入水杨酸、醋酸丁酯、氯化石蜡和氯化烯烃，在700-800转/分钟转速下高速分散5-10分钟，得到成品。
实施例2：金属防腐漆，其组成原料的重量份为：环氧树脂E20 35份、聚酰胺树脂35份、纳米碳酸钙2份、硫酸钡10份、水杨酸10份、四甲基硅烷3份、醋酸丁酯12份、异丙醇12份、氯化石蜡4份和氯化烯烃8份。
金属防腐漆的制备方法，包括以下步骤：
（1）按组成原料的重量份将环氧树脂E20、聚酰胺树脂、硫酸钡、纳米碳酸钙、四甲基硅烷和异丙醇混合搅拌均匀，高速分散并研磨至35um细度以下；
（2）在上述反应体系中按重量份加入水杨酸、醋酸丁酯、氯化石蜡和氯化烯烃，在700-800转/分钟转速下高速分散5-10分钟，得到成品。
实施例3：金属防腐漆，其组成原料的重量份为：环氧树脂E20 40份、聚酰胺树脂40份、纳米碳酸钙3份、硫酸钡12份、水杨酸12份、四甲基硅烷5份、醋酸丁酯15份、异丙醇15份、氯化石蜡5份和氯化烯烃10份。
金属防腐漆的制备方法，包括以下步骤：
（1）按组成原料的重量份将环氧树脂E20、聚酰胺树脂、硫酸钡、纳米碳酸钙、四甲基硅烷和异丙醇混合搅拌均匀，高速分散并研磨至35um细度以下；
（2）在上述反应体系中按重量份加入水杨酸、醋酸丁酯、氯化石蜡和氯化烯烃，在700-800转/分钟转速下高速分散5-10分钟，得到成品。
实施例4：采用实施例1的金属防腐漆进行技术检测，结果如下：
1、附着力/级≤2级；2、柔韧性/级：1级；3、耐热性：200℃完好无损；4、耐碱性：15%氢氧化钠40天完好无损；5、耐酸性15%硫酸40天完好无损。

Claims (2)

1.一种金属防腐漆，其特征在于其组成原料的重量份为：环氧树脂E2030-40份、聚酰胺树脂30-40份、纳米碳酸钙1-3份、硫酸钡8-12份、水杨酸8-12份、四甲基硅烷2-5份、醋酸丁酯8-15份、异丙醇10-15份、氯化石蜡2-5份和氯化烯烃5-10份。
2.一种如权利要求1所述的金属防腐漆的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份将环氧树脂E20、聚酰胺树脂、硫酸钡、纳米碳酸钙、四甲基硅烷和异丙醇混合搅拌均匀，高速分散并研磨至35μm细度以下；
（2）在上述反应体系中按重量份加入水杨酸、醋酸丁酯、氯化石蜡和氯化烯烃，在700-800转/分钟转速下高速分散5-10分钟，得到成品。
CN 201110260413 2011-09-05 2011-09-05 一种金属防腐漆及其制备方法 Expired - Fee Related CN102286238B (zh)