CN102269522B - 一种电炉炉底的砌筑工艺 - Google Patents

一种电炉炉底的砌筑工艺 Download PDF

Info

Publication number
CN102269522B
CN102269522B CN 201110177058 CN201110177058A CN102269522B CN 102269522 B CN102269522 B CN 102269522B CN 201110177058 CN201110177058 CN 201110177058 CN 201110177058 A CN201110177058 A CN 201110177058A CN 102269522 B CN102269522 B CN 102269522B
Authority
CN
China
Prior art keywords
layer
furnace
brick
magnesia
heat insulating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110177058
Other languages
English (en)
Other versions
CN102269522A (zh
Inventor
周剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Iron and Steel Co Ltd
Original Assignee
Nanjing Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Iron and Steel Co Ltd filed Critical Nanjing Iron and Steel Co Ltd
Priority to CN 201110177058 priority Critical patent/CN102269522B/zh
Publication of CN102269522A publication Critical patent/CN102269522A/zh
Application granted granted Critical
Publication of CN102269522B publication Critical patent/CN102269522B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及冶金领域的砌筑工艺,是一种电炉炉底的砌筑工艺,检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层胶;在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米材料反射绝热板作为保温材料层,每层纳米材料反射绝热板厚度为5mm,纳米材料反射绝热板要贴平,贴实,贴齐,且无空穴,两层纳米材料反射绝热板的接缝要错开;在保温材料层上方由下至上平砌两层镁砖,用细镁砂填封砖缝,每层镁砖厚度为76mm;在镁砖上方砌一层镁碳砖,厚度为150mm,并用细镁砂填封砖缝;在镁碳砖上方铺垫炉底打结料,厚度为650mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。本发明保证碳氧反应可控,增大了熔池,提高电弧炉炉底的保温效果。

Description

一种电炉炉底的砌筑工艺
技术领域
本发明涉及冶金领域的砌筑工艺,具体的说是一种电炉炉底的砌筑工艺。
背景技术
由于成本的压力,国内电炉普遍都在提高铁水热装比和供氧强度。这一举措确实达到了缩短冶炼周期、降低综合能耗和降低生产成本的目的,然而也带来了一系列问题。首先是随着铁水热装比和供氧强度的增加,熔池内碳氧反应的激烈程度也随之变大,钢液面上涨,炉门跑钢现象增多,不仅增加了钢铁料消耗,也增大了冶炼顺行的难度;其次,碳氧反应多是从炉底开始,其反应的激烈程度变大也造成了电弧炉炉底工作层的侵蚀速度的增加,为安全生产带来威胁。再则,碳氧反应的激烈和炉底工作层变薄使得电弧炉下炉壳温度升高,变性加剧,降低炉壳使用寿命。因此,需要重新设计电炉炉底来满足电炉提高铁水热装比和供氧强度的要求。
发明内容
本发明所要解决的技术问题是,针对以上现有技术存在的缺点,提出一种电炉炉底的砌筑工艺,保证碳氧反应可控,增大了熔池,提高电弧炉炉底的保温效果。
本发明解决以上技术问题的技术方案是:
一种电炉炉底的砌筑工艺,按以下步骤进行:
⑴检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层丙烯酸丁酯胶水;
⑵在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米级二氧化硅或纳米级三氧化二铝作为保温材料层,每层纳米材料反射绝热板厚度为5±0.5 mm,纳米材料反射绝热板要贴平,贴实,贴齐,且无空穴,两层纳米材料反射绝热板的接缝要错开;
⑶在保温材料层上方由下至上平砌两层镁砖,并用细镁砂填封砖缝,每层镁砖厚度为76±1mm;
⑷在镁砖上方砌一层镁碳砖,厚度为150±1mm,并用细镁砂填封砖缝;
⑸在镁碳砖上方铺垫炉底打结料,厚度为650±10mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。
本发明进一步限定的技术方案是:
前述的电炉炉底的砌筑工艺,步骤⑶中,位于下方的第一层镁砖沿出钢座砖边向炉门方向砌筑,第一层镁砖周边与炉墙处留200±5mm的缝,位于上方的第二层镁砖与第一层镁砖的砌筑方向顺时针旋转45度,第二层镁砖周边比第一层第二层镁砖向中心收100±5mm。
前述的电炉炉底的砌筑工艺,步骤⑷中,镁碳砖与位于上方的第二层镁砖的砌筑方向顺时针旋转45度。
本发明的有益效果是:本发明的电炉炉底的砌筑工艺在不改变炉壳现状的前提下,炉底工作层厚度增加了100mm左右,保证工作层使用安全。本发明的电炉炉底的砌筑工艺可使电炉容积深度增加,增大了熔池,保证碳氧反应可控,而且提高电弧炉炉底的保温效果。本发明炉壳实验中测温表明,电弧炉炉壳温度由300℃以上降低到230℃以下,经统计,吨钢电弧炉冶炼电耗可降低0.5kWh/t。
具体实施方式
实施例1
一种电炉炉底的砌筑工艺,按以下步骤进行:
⑴检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层丙烯酸丁酯胶水;
⑵在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米级二氧化硅或纳米级三氧化二铝作为保温材料层,每层纳米材料反射绝热板厚度为4.5 mm,纳米材料反射绝热板要贴平,贴实,贴齐,且无空穴,两层纳米材料反射绝热板的接缝要错开;
⑶在保温材料层上方由下至上平砌两层镁砖,并用细镁砂填封砖缝,每层镁砖厚度为75mm;位于下方的第一层镁砖沿出钢座砖边向炉门方向砌筑,第一层镁砖周边与炉墙处留195mm的缝,位于上方的第二层镁砖与第一层镁砖的砌筑方向顺时针旋转45度,第二层镁砖周边比第一层第二层镁砖向中心收95mm;
⑷在镁砖上方砌一层镁碳砖,厚度为149mm,并用细镁砂填封砖缝;镁碳砖与位于上方的第二层镁砖的砌筑方向顺时针旋转45度;
⑸在镁碳砖上方铺垫炉底打结料,厚度为640mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。
实施例2
一种电炉炉底的砌筑工艺,按以下步骤进行:
⑴检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层丙烯酸丁酯胶水;
⑵在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米级二氧化硅或纳米级三氧化二铝作为保温材料层,每层纳米材料反射绝热板厚度为5 mm,纳米材料反射绝热板要贴平,贴实,贴齐,且无空穴,两层纳米材料反射绝热板的接缝要错开;
⑶在保温材料层上方由下至上平砌两层镁砖,并用细镁砂填封砖缝,每层镁砖厚度为76mm;位于下方的第一层镁砖沿出钢座砖边向炉门方向砌筑,第一层镁砖周边与炉墙处留200mm的缝,位于上方的第二层镁砖与第一层镁砖的砌筑方向顺时针旋转45度,第二层镁砖周边比第一层第二层镁砖向中心收100mm;
⑷在镁砖上方砌一层镁碳砖,厚度为150mm,并用细镁砂填封砖缝;镁碳砖与位于上方的第二层镁砖的砌筑方向顺时针旋转45度;
⑸在镁碳砖上方铺垫炉底打结料,厚度为6500mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。
实施例3
一种电炉炉底的砌筑工艺,按以下步骤进行:
⑴检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层丙烯酸丁酯胶水;
⑵在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米级二氧化硅或纳米级三氧化二铝作为保温材料层,每层纳米材料反射绝热板厚度为5.5 mm,纳米材料反射绝热板要贴平,贴实,贴齐,且无空穴,两层纳米材料反射绝热板的接缝要错开;
⑶在保温材料层上方由下至上平砌两层镁砖,并用细镁砂填封砖缝,每层镁砖厚度为77mm;位于下方的第一层镁砖沿出钢座砖边向炉门方向砌筑,第一层镁砖周边与炉墙处留205mm的缝,位于上方的第二层镁砖与第一层镁砖的砌筑方向顺时针旋转45度,第二层镁砖周边比第一层第二层镁砖向中心收105mm;
⑷在镁砖上方砌一层镁碳砖,厚度为151mm,并用细镁砂填封砖缝;镁碳砖与位于上方的第二层镁砖的砌筑方向顺时针旋转45度;
⑸在镁碳砖上方铺垫炉底打结料,厚度为660mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。

Claims (1)

1.一种电炉炉底的砌筑工艺,其特征在于:按以下步骤进行:
⑴检查炉底炉壳圆度,确定炉壳无明显变形,清理炉壳内粘渣和积灰,保证透气孔畅通,均匀抹上一层丙烯酸丁酯胶水;
⑵在炉底与炉壁相接处,向炉底方向在炉底上逐层粘贴两层纳米级二氧化硅或纳米级三氧化二铝作为保温材料层,每层纳米级二氧化硅或纳米级三氧化二铝保温材料层厚度为5±0.5 mm,纳米级二氧化硅或纳米级三氧化二铝保温材料层要贴平,贴实,贴齐,且无空穴,两层纳米级二氧化硅或纳米级三氧化二铝保温材料层的接缝要错开;
⑶在保温材料层上方由下至上平砌两层镁砖,并用细镁砂填封砖缝,每层镁砖厚度为76±1mm;
⑷在镁砖上方砌一层镁碳砖,厚度为150±1mm,并用细镁砂填封砖缝;
⑸在镁碳砖上方铺垫炉底打结料,厚度为650±10mm,使用打夯机捣打炉底打结料,保证表面牢固,使炉底呈锅底形。
CN 201110177058 2011-06-28 2011-06-28 一种电炉炉底的砌筑工艺 Active CN102269522B (zh)