CN102250442A - Multifunctional acrylonitrile-butadiene-styrene (ABS) copolymer plastic - Google Patents
Multifunctional acrylonitrile-butadiene-styrene (ABS) copolymer plastic Download PDFInfo
- Publication number
- CN102250442A CN102250442A CN201110128130XA CN201110128130A CN102250442A CN 102250442 A CN102250442 A CN 102250442A CN 201110128130X A CN201110128130X A CN 201110128130XA CN 201110128130 A CN201110128130 A CN 201110128130A CN 102250442 A CN102250442 A CN 102250442A
- Authority
- CN
- China
- Prior art keywords
- abs
- butadiene
- acrylonitrile
- zirconium nitride
- plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multifunctional acrylonitrile-butadiene-styrene (ABS) copolymer plastic. The plastic is characterized in that the plastic comprises the following raw material components by mass percent: 0.1-1% of nanometer zirconium nitride, 1-5% of compatilizer and the balance of ABS masterbatch, wherein the optimum mass percent of nanometer zirconium nitride is 0.6%. The nanometer zirconium nitride powder is characterized in that the powder can efficiently absorb visible light, reflect infrared and store energy, etc.
Description
[technical field]
The present invention relates to the engineering plastics technical field, specifically, is a kind of multi-functional ABS plastic.
[background technology]
Acrylonitrile-butadiene-styrene copolymer (Acrylonitrile-Butadiene-Styrene, be called for short ABS) is a kind of universal thermoplastic polymer, the ABS performance characteristic: good rigidly, shock strength height, heat-resisting,
Low temperature resistant, chemical proofing, physical strength and electric property are good, are easy to processing, and finish size stability and surface luster are good, and easy application, painted can also be carried out metallize, plating, welding and suitability for secondary processing such as bonding.Because the characteristic of ABS combines its three kinds of components, makes it have excellent comprehensive performances, becomes one of plastics of electric elements, household electrical appliances, computer and instrument first-selection.
The ABS engineering plastics generally are opaque, and outward appearance is shallow ivory white, nontoxic, tasteless, has tough, hard, firm characteristic concurrently, and burning is slow, and it is yellow that flame is, and black smoke is arranged, and burning back plastics soften, burn, and send special Chinese cassia tree smell, but do not have the fusion drip phenomenon.
The ABS engineering plastics have excellent comprehensive performances, have that fabulous shock strength, dimensional stability are good, an electrical property, wear resistance, chemical proof, dyeability, and forming process and mechanical workout are better.ABS resin is water-fast, inorganic salt, alkali and acids, is insoluble to most of alcohols and varsol, and is dissolved in easily in aldehyde, ketone, ester and some hydrochloric ether.
[summary of the invention]
The objective of the invention is to overcome the deficiencies in the prior art, a kind of multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic is provided.
The objective of the invention is to be achieved through the following technical solutions:
A kind of multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.1~1%
Compatilizer 1~5%
ABS master batch surplus
The mass percent of described nano boron carbide is preferably 0.6%;
Described compatilizer is an ethylene glycol;
Compared with prior art, positively effect of the present invention is:
1, nano boron carbide powder has characteristics such as purity height, particle size distribution range are little, high-specific surface area;
2, this product have high temperature resistant, anti-oxidant, intensity is high, hardness is high, thermal conductivity is good, the characteristics of good toughness are a kind of important structured materials;
3, the nano-zirconium carbide powder also has efficient absorption visible light, characteristics such as reflected infrared and energy storage.
[embodiment]
The present invention below is provided a kind of embodiment of multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic.
Embodiment 1
A kind of multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.2%
Compatilizer 1%
ABS master batch 98.8%
A kind of preparation method of multi-functional ABS plastic mixes raw material, and melt pelletization can obtain containing the multi-functional ABS plastic of nano zirconium nitride again.
Embodiment 2
A kind of multi-functional ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.4%
Compatilizer 2%
ABS master batch 97.6%
A kind of preparation method of multi-functional ABS plastic mixes raw material, and melt pelletization can obtain containing the multi-functional ABS plastic of nano zirconium nitride again.
Embodiment 3
A kind of multi-functional ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.6%
Compatilizer 3%
ABS master batch 96.4%
A kind of preparation method of multi-functional ABS plastic mixes raw material, and melt pelletization can obtain containing the multi-functional ABS plastic of nano zirconium nitride again.
Embodiment 4
A kind of multi-functional ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.8%
Compatilizer 4%
ABS master batch 95.2%
A kind of preparation method of multi-functional ABS plastic mixes raw material, and melt pelletization can obtain containing the multi-functional ABS plastic of nano zirconium nitride again.
Embodiment 5
A kind of multi-functional ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 1%
Compatilizer 5%
ABS master batch 94%
A kind of preparation method of multi-functional ABS plastic mixes raw material, and melt pelletization can obtain containing the multi-functional ABS plastic of nano zirconium nitride again.
The above only is a preferred implementation of the present invention; should be pointed out that for those skilled in the art, without departing from the inventive concept of the premise; can also make some improvements and modifications, these improvements and modifications also should be considered within the scope of protection of the present invention.
Claims (2)
1. a multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic is characterized in that, its feed composition mass percent is,
Nano zirconium nitride 0.1~1%
Compatilizer 1~5%
ABS master batch surplus.
2. a kind of multi-functional acrylonitrile-butadiene-styrene copolymer ABS plastic as claimed in claim 1 is characterized in that the mass percent of described nano boron carbide is preferably 0.6%.