CN102241941B - Water-soluble polyurethane-based quick-drying base coat with ultrahigh solid content - Google Patents
Water-soluble polyurethane-based quick-drying base coat with ultrahigh solid content Download PDFInfo
- Publication number
- CN102241941B CN102241941B CN 201110175391 CN201110175391A CN102241941B CN 102241941 B CN102241941 B CN 102241941B CN 201110175391 CN201110175391 CN 201110175391 CN 201110175391 A CN201110175391 A CN 201110175391A CN 102241941 B CN102241941 B CN 102241941B
- Authority
- CN
- China
- Prior art keywords
- water
- solid content
- titanium dioxide
- base coat
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a water-soluble polyurethane-based quick-drying base coat with an ultrahigh solid content and a production process thereof. The base coat consists of the following raw materials according to percentage by weight: 20%-40% of water-soluble polyurethane resin, 50%-65% of heavy calcium carbonate, 1%-5% of rutile type titanium dioxide, 0.4%-0.6% of thickener, 0.6%-1.0% of dispersing agent, 0.4%-0.5% of defoaming agent, 2.5%-10% of water and 0%-2% of color paste. The production process of the base coat comprises the following steps of: (1) adding the water-soluble polyurethane resin into a container; (2) adding the dispersing agent and the defoaming agent and stirring the mixture for 5 minutes; (3) adding the heavy calcium carbonate and the rutile type titanium dioxide and rapidly stirring the mixture for 20-30 minutes; (4) adding the thickener and water to adjust the viscosity and stirring the mixture for 5 minutes; and (5) adding the color paste to adjust the color for use. The base coat has the advantages of ultrahigh solid content and high drying speed, and can be applied to sealing edges of arc-shaped surfaces of medium-density fiberboards and melamine boards, as well as used as a primer instead of NC (nitrocellulose lacquer).
Description
Technical field
The present invention relates to a kind of super-high solid content quick-drying edge sealing paint and production method thereof based on aqueous polyurethane, especially a kind of waterborne edge sealing paint and production method thereof for medium density fiberboard, melamine plate arc.
Background technology
At present, edge sealing paint commonly used has solvent-borne type and water-based two big classes, and the solvent-borne type edge sealing paint contains organic solvents such as a large amount of toluene, dimethylbenzene because of it, also wasted the energy in the time of contaminate environment, is unfavorable for Sustainable development; And its solid content of common waterborne edge sealing paint is on the low side, and often less than 65%, and the evaporation rate of water is slow, so its rate of drying is slower, can not meet the actual production requirement of Furniture Factory fully.
Summary of the invention
The present invention provides a kind of super-high solid content quick-drying edge sealing paint and production method thereof based on aqueous polyurethane for medium density fiberboard, trimeric cyanamide version arc, to overcome the above-mentioned defective that prior art exists.
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane of the present invention, its solid content is about 70%, and the polishing time is less than 1h.
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane of the present invention, its prescription and weight percent are:
Waterborne polyurethane resin 20%-40%, water-ground limestone 50%-65%,
Rutile type Titanium Dioxide 1%-5%, thickening material 0.4%-0.6%,
Dispersion agent 0.6%-1%, defoamer 0.4%-0.5%
Water 2.5%-10%, mill base 0%-2%.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described waterborne polyurethane resin is aromatic waterborne polyurethane, weight contains admittedly and is that 20%-45%, size are 100 μ m-300 μ m.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described water-ground limestone is universal water-based water-ground limestone, and fineness is the 600-1500 order.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described Rutile type Titanium Dioxide is universal water-based titanium dioxide, initial size is 0.2-0.6 μ m.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described thickening material optimization polyurethane type thickening material.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described dispersion agent optimization polypropylene acid sodium-salt type dispersion agent.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: defoamer is the molecular level defoamer.
Described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its special character is: described mill base is aqueous color paste.
The production method of described super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, as follows:
(1) in container, adds waterborne polyurethane resin;
(2) add dispersion agent and defoamer then, stir 5min;
(3) add water-ground limestone and Rutile type Titanium Dioxide again, fast dispersed with stirring 20-30min;
(4) add thickening material and water at last and adjust viscosity, stir 5min;
(5) add mill base and adjust color, can use.
Embodiment
Embodiment 1
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 30%, water-ground limestone 57%,
Rutile type Titanium Dioxide 3%, thickening material 0.5%,
Dispersion agent 0.8%, defoamer 0.45%,
Water 8.25%.
Production method is according to the following steps:
(1) in container, adds waterborne polyurethane resin;
(2) add dispersion agent and defoamer then, stir 5min;
(3) add water-ground limestone and Rutile type Titanium Dioxide again, fast dispersed with stirring 20-30min;
(4) add thickening material and water at last and adjust viscosity, stir 5min, can use.
Product performance:
State in container: stir the back evenly
Non-volatile matter: 71.14%
PH value: 8.51
Package stability: no abnormal
Freeze-thaw resistance: no abnormal
Grinability: easily polishing
The polishing time: 40min.
The performance of common waterborne edge sealing paint
State in container: stir the back evenly
Non-volatile matter: 50%-65%
PH value:>7.5
Package stability: no abnormal
Freeze-thaw resistance: no abnormal
Grinability: the polishing time is longer
The polishing time: 1.5h-2h
Embodiment 2
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 40%, water-ground limestone 55%,
Rutile type Titanium Dioxide 1%, thickening material 0.4%,
Dispersion agent 0.6%, defoamer 0.5%,
Water 2.5%;
Embodiment 3
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 20%, water-ground limestone 63%,
Rutile type Titanium Dioxide 5%, thickening material 0.6%,
Dispersion agent 1%, defoamer 0.4%,
Water 10%;
Following formulation ratio also can be realized purpose of the present invention:
Waterborne polyurethane resin 33%, water-ground limestone 50%,
Rutile type Titanium Dioxide 5%, thickening material 0.5%,
Dispersion agent 1%, defoamer 0.5%,
Water 10%;
Embodiment 4
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 20%, water-ground limestone 65%,
Rutile type Titanium Dioxide 1%, thickening material 0.6%,
Dispersion agent 1%, defoamer 0.4%,
Water 10% mill base 2%
Production method is according to the following steps:
(1) in container, adds waterborne polyurethane resin;
(2) add dispersion agent and defoamer then, stir 5min;
(3) add water-ground limestone and Rutile type Titanium Dioxide again, fast dispersed with stirring 20-30min;
(4) add thickening material and water at last and adjust viscosity, stir 5min,
(5) add mill base and adjust color, can use.
Product performance:
State in container: stir the back evenly
Non-volatile matter: 73.42%
PH value: 8.16
Package stability: no abnormal
Freeze-thaw resistance: no abnormal
Grinability: easily polishing
The polishing time: 32min
Embodiment 5
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 40%, water-ground limestone 50%,
Rutile type Titanium Dioxide 5%, thickening material 0.4%,
Dispersion agent 0.6%, defoamer 0.5%,
Water 2.5% mill base 1%
Production method is according to the following steps:
(1) in container, adds waterborne polyurethane resin;
(2) add dispersion agent and defoamer then, stir 5min;
(3) add water-ground limestone and Rutile type Titanium Dioxide again, fast dispersed with stirring 20-30min;
(4) add thickening material and water at last and adjust viscosity, stir 5min;
(5) add mill base and adjust color, can use.
Can use.
Product performance:
State in container: stir the back evenly
Non-volatile matter: 68.24%
PH value: 8.93
Package stability: no abnormal
Freeze-thaw resistance: no abnormal
Grinability: easily polishing
The polishing time: 50min.
Embodiment 6
A kind of super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 40%, water-ground limestone 50%,
Rutile type Titanium Dioxide 5%, thickening material 0.4%,
Dispersion agent 0.6%, defoamer 0.5%,
Water 3.4% mill base 0.1%
Said waterborne polyurethane resin is aromatic waterborne polyurethane, and weight contains admittedly and is that 20%-45%, size are 100 μ m-300 μ m;
Said water-ground limestone is universal water-based water-ground limestone, and fineness is the 600-1500 order;
Said Rutile type Titanium Dioxide is universal water-based titanium dioxide, and initial size is 0.2-0.6 μ m, the titanium dioxide R706 of preferred Du Pont;
Said thickening material optimization polyurethane type thickening material is selected the RM-8W of DOW company for use;
Said dispersion agent optimization polypropylene acid sodium-salt type dispersion agent is selected the fast easily dispersion agent of DOW department for use;
Said defoamer preferred molecular level defoamer is selected Shenzhen Hai Chuan chemical industry for use
Preferred according to the present invention, also comprise the mill base of gross weight 0%-2%, the preferred aqueous color paste of mill base, more preferably the water-based oversubscription of Fanyu, the Guangzhou section enlightening color company limited mill base that looses;
Above-described only is preferential embodiment of the present invention.Should be pointed out that for the person of ordinary skill of the art under the situation that does not break away from the principle of the invention, can also make some improvement and modification, this also is considered as protection scope of the present invention.
Claims (1)
1. super-high solid content quick-drying edge sealing paint based on aqueous polyurethane, its prescription and weight percent are:
Waterborne polyurethane resin 30%-40%, water-ground limestone 50%-65%,
Rutile type Titanium Dioxide 1%-5%, thickening material 0.4%-0.6%,
Dispersion agent 0.6%-1%, defoamer 0.4%-0.5%
Water 2.5%-10%, mill base 0%-2%;
Described waterborne polyurethane resin is aromatic waterborne polyurethane, and weight contains admittedly and is that 20%-45%, size are 100 μ m-300 μ m;
Described water-ground limestone is universal water-based water-ground limestone, and fineness is the 600-1500 order;
Described Rutile type Titanium Dioxide is universal water-based titanium dioxide, and initial size is 0.2-0.6 μ m;
Described thickening material is the polyurethane-type thickening material;
Described dispersion agent is polyacrylic acid sodium salt type dispersion agent;
Defoamer is the molecular level defoamer;
Described mill base is aqueous color paste.