CN102241498A - Artificial jade based on red mud, and production method thereof - Google Patents
Artificial jade based on red mud, and production method thereof Download PDFInfo
- Publication number
- CN102241498A CN102241498A CN2010101821036A CN201010182103A CN102241498A CN 102241498 A CN102241498 A CN 102241498A CN 2010101821036 A CN2010101821036 A CN 2010101821036A CN 201010182103 A CN201010182103 A CN 201010182103A CN 102241498 A CN102241498 A CN 102241498A
- Authority
- CN
- China
- Prior art keywords
- oxide
- red mud
- raw material
- artificial jade
- crucible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention which belongs to the field of handicraft production concretely relates to artificial jade produced from red mud. The artificial jade is characterized in that: raw materials comprise all or parts of red mud, quartz powder, alumina or aluminum hydroxide, zinc oxide, sodium carbonate, magnesium oxide, borax, sodium silicate, calcium oxide or calcium carbonate, titanium dioxide, potassium carbonate, talc, manganese dioxide, copper oxide, and ferric oxide. The production method of the artificial jade comprises the following steps: 1, weighing; 2, fragmenting and grinding; 3, mixing and stirring; 4, melting; and 5, carving, sanding, and polishing. Artificial agate produced through the method in the invention has the advantages of exquisite and tough texture, mellow and soft brightness, and excellent mechanical property, can be used in the fields of jewelries, handicrafts and the like, and has a broad application prospect. According to the invention, red mud is used as a production raw material to produce products with high added values, so the high added value utilization of red mud which is realized creates a new approach to the integral utilization of industrial solid wastes.
Description
Technical field
The invention belongs to the artwork production field, is to utilize the industrial solid castoff that produces in the aluminum oxide production process specifically---artificial jade and manufacture method thereof that red mud is produced.
Background technology
Red mud is the industrial solid castoff that produces in the aluminum oxide production process, and one ton of aluminum oxide of general every production promptly produces about 1.0-1.3 ton red mud.Enterprise generally adopts the mode of air storage to handle red mud, and this has taken a large amount of soils on the one hand, on the other hand, and objectionable impurities meeting polluted underground water and ambient air in the red mud, thereby to the serious harm of ecotope generation.
For many years, people have adopted multiple technologies that red mud is fully utilized, as therefrom extracting useful chemical composition, being raw material production building materials etc. with the red mud, but all there is defective to a certain extent in these technology, as still can produce industrial solid castoff after extracting useful component, and when extracting useful component, generally need to add a certain amount of reactant, the amount of the waste of Chan Shenging is also more than red mud so under many circumstances; Also there are problems such as quality instability, energy consumption height in application facet in building materials.
For these reasons, active demand in the market is to new technology, the novel process of red mud comprehensive utilization.The contriver of this patent promptly is engaged in the development work of artificial jade from April, 2009, has developed multiple products such as artificial white jade, black jade, jasper, carbuncle, and excellent property has broad application prospects at jewellery and artwork field.
Summary of the invention:
The objective of the invention is to overcome the defective that conventional art exists, is that raw material production has high value-added product with the red mud---artificial jade, thus open up a new approach for the comprehensive utilization of red mud.Feature of the present invention is to be main raw material with the red mud, adds certain quantity of additive simultaneously, through artificial jade of prepared such as weighing, pulverizing, grinding, batch mixing, stirring, meltings.
Preparation method of the present invention is:
1. the raw materials for production of artificial jade and proportioning:
Red mud: 5-85%
Silica powder: 25-85%
Aluminum oxide or aluminium hydroxide: 5-15%
Zinc oxide: 5-15%
Soda ash: 5-25%
Magnesium oxide: 5-15%
Borax: 10-30%
Water glass: 10-30%
Calcium oxide or lime carbonate: 5-15%
Titanium dioxide: 1-5%
Salt of wormwood: 5-15%
Talcum powder: 0-10%
Manganse Dioxide: 0.2-15%
Cupric oxide: 0.2-15%
Ferric oxide: 0.2-15%
Above-mentioned raw materials can use simultaneously also and can partly use, according to performance requriements and the production cost decision to product.
2. the preparation technology of artificial jade is:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting.Be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 800-1650 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling.According to concrete product difference, smelting furnace can use common desk-top resistance furnace, also can use the process furnace of other type.
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, then according to the difference of concrete product chisel and carve, polish, technology such as polishing, finally obtain finished product.
Beneficial effect of the present invention:
Artificial beautiful quality exquisiteness prepared in accordance with the present invention is tough and tensile, gloss is gentle soft, and has a good mechanical performance, as higher hardness, toughness and wear resistance, high thermal resistance, erosion resistance, weathering resistance etc., can be used for fields such as jewellery, artwork, have broad application prospects.
The present invention for the production raw material production has high value-added product, has realized the high value added utilization to red mud with the red mud, for a new way has been opened up in the comprehensive utilization of industrial solid castoff.
Raw material sources of the present invention are extensive, and the additive that uses is as Chemicals common on the market, and is cheap.
Aspect preparation technology, preparation technology of the present invention is simple, and is lower to the requirement of equipment, and operators'skills is not had particular requirement yet, and the common laborer can operate.
In sum, the present invention has advantages of high practicability and application value.
Description of drawings:
Fig. 1 is preparation technology's schema of artificial jade.
Embodiment:
Embodiment 1: by shown in Figure 1, raw materials for production and proportioning are:
Red mud: 5-85%
Silica powder: 25-85%
Aluminum oxide or aluminium hydroxide: 5-15%
Zinc oxide: 5-15%
Soda ash: 5-25%
Magnesium oxide: 5-15%
Borax: 10-30%
Water glass: 10-30%
Calcium oxide or lime carbonate: 5-15%
Titanium dioxide: 1-5%
Salt of wormwood: 5-15%
Talcum powder: 0-10%
Manganse Dioxide: 0.2-8%
Preparation process and processing parameter are:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting.Be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 1080 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling.According to concrete product difference, smelting furnace can use common desk-top resistance furnace, also can use the process furnace of other type.
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, chisel and carve, polish, technology such as polishing, finally obtain finished product.
Embodiment 2: by shown in Figure 1, raw materials for production and proportioning are:
Red mud: 5-85%
Silica powder: 25-85%
Zinc oxide: 5-15%
Soda ash: 5-25%
Magnesium oxide: 5-15%
Borax: 10-30%
Water glass: 10-30%
Calcium oxide or lime carbonate: 5-15%
Titanium dioxide: 1-5%
Salt of wormwood: 5-15%
Talcum powder: 0-10%
Cupric oxide: 0.2-8%
Preparation process and processing parameter are:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting.Be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 1150 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling.According to concrete product difference, smelting furnace can use common desk-top resistance furnace, also can use the process furnace of other type.
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, chisel and carve, polish, technology such as polishing, finally obtain finished product.
Embodiment 3: by shown in Figure 1, raw materials for production and proportioning are:
Red mud: 5-85%
Silica powder: 25-85%
Aluminum oxide or aluminium hydroxide: 5-15%
Zinc oxide: 5-15%
Soda ash: 5-25%
Magnesium oxide: 5-15%
Calcium oxide or lime carbonate: 5-15%
Titanium dioxide: 1-5%
Salt of wormwood: 5-15%
Talcum powder: 0-10%
Ferric oxide: 0.2-8%
Manganse Dioxide: 0.2-8%
Preparation process and processing parameter are:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting.Be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 1250 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling.According to concrete product difference, smelting furnace can use common desk-top resistance furnace, also can use the process furnace of other type.
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, chisel and carve, polish, technology such as polishing, finally obtain finished product.
Embodiment 4: by shown in Figure 1, raw materials for production and proportioning are:
Red mud: 5-85%
Silica powder: 25-85%
Aluminum oxide or aluminium hydroxide: 5-15%
Zinc oxide: 5-15%
Soda ash: 5-25%
Borax: 10-30%
Water glass: 10-30%
Calcium oxide or lime carbonate: 5-15%
Cupric oxide: 0.2-8%
Manganse Dioxide: 0.2-8%
Preparation process and processing parameter are:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting.Be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 1380 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling.According to concrete product difference, smelting furnace can use common desk-top resistance furnace, also can use the process furnace of other type.
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, chisel and carve, polish, technology such as polishing, finally obtain finished product.
Claims (2)
1. artificial jade of the present invention is characterised in that its raw material is a red mud, silica powder, aluminum oxide or aluminium hydroxide, zinc oxide, soda ash, magnesium oxide, borax, water glass, calcium oxide or lime carbonate, titanium dioxide, salt of wormwood, talcum powder, Manganse Dioxide, cupric oxide, all or part of in the ferric oxide, its weight chemical constitution is: red mud: 5-85%, silica powder: 25-85%, aluminum oxide or aluminium hydroxide: 5-15%, zinc oxide: 5-15%, soda ash: 5-25%, magnesium oxide: 5-15%, borax: 10-30%, water glass: 10-30%, calcium oxide or lime carbonate: 5-15%, titanium dioxide: 1-5%, salt of wormwood: 5-15%, talcum powder: 0-10%, Manganse Dioxide: 0.2-15%, cupric oxide: 0.2-15%, ferric oxide: 0.2-15%.
2. the preparation method of artificial jade according to claim 1 is characterized in that it is realized by following step:
(1) various raw materials of weighing on request;
(2) with block raw material crushing, grinding;
(3) various raw materials are put into container mixing and stirring, made material composition even;
(4) pour the raw material that mixes into crucible, put into smelting furnace and carry out melting, be characterized as: raw material is put into crucible, and the smelting furnace of at room temperature packing into heats up with stove; Maximum heating temperature is 800-1650 ℃, is incubated 3 hours; Furnace cooling, fire door is closed all the time in process of cooling;
(5) after product is cooled to room temperature, from stove, take out;
(6) from crucible, take out artificial jade, then according to the difference of concrete product chisel and carve, polish, technology such as polishing, finally obtain finished product.