CN102240864B - 一种钛钙型结构钢焊条 - Google Patents
一种钛钙型结构钢焊条 Download PDFInfo
- Publication number
- CN102240864B CN102240864B CN 201110174519 CN201110174519A CN102240864B CN 102240864 B CN102240864 B CN 102240864B CN 201110174519 CN201110174519 CN 201110174519 CN 201110174519 A CN201110174519 A CN 201110174519A CN 102240864 B CN102240864 B CN 102240864B
- Authority
- CN
- China
- Prior art keywords
- welding
- welding rod
- mica
- type structural
- structural steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种钛钙型结构钢焊条,其特征在于它以H08A盘条作为焊芯原料,焊条药皮的配方由还原钛铁矿、硅灰石、金红石、中碳锰铁、白泥、海泡石、长石、云母、大理石、棉、回木粉、细云母组成,重量百分比为:还原钛铁矿35-42%,硅灰石6-9%,金红石12-16%,白泥4-6%,海泡石5-8%,长石7-10%,云母4-7%,大理石4-7%,中碳锰铁7-10%,回木粉1-3%,棉1-3%,细云母1-3%。优越性:本发明研制的焊条具有良好的力学性能和全位置焊接工艺性能,采用该焊条焊接低碳钢及42公斤级的低合金钢,可交直流两用,焊接时, 电弧柔和,操作轻松应手,引弧及再引弧非常容易,飞溅极少,脱渣容易、焊波成形细致、美观,特别利于焊工操作。
Description
(一)技术领域:
本发明涉及一种焊接材料及其制备技术,特别是一种钛钙型结构钢焊条。
(二)背景技术:
国民经济的发展,需要应用大量的焊接材料,每年钢产量的45%左右需要用焊材来进行连接,随着中国钢材消费量的不断增加,焊材消耗量也随着增加,现在,中国已成为世界最大的焊材生产及消耗基地。我国的基础建设每年需要使用大量的低碳钢及42公斤级的低合金钢,一方面,焊材直接影响到产品的质量、可靠性和寿命以及生产的成本、效率;另一方面,具有熟练的操作技能的焊工短缺,工资有不断增长的趋势。这就要求相配套的焊条质优价廉,同时要具有良好的可操作性,以降低对焊工的要求。
(三)发明内容:
本发明的目的在于提供一种钛钙型结构钢焊条,它能够解决现有技术存在的问题,焊条药皮具有良好的耐潮性、耐弯曲性,具有良好的全位置焊接性,特别利于焊工操作,并且大大提高了生产效率,降低了生产成本。
本发明的技术方案:一种钛钙型结构钢焊条,其特征在于它以H08A盘条作为焊芯原料,焊条药皮的配方由还原钛铁矿、硅灰石、金红石、中碳锰铁、白泥、海泡石、长石、云母、大理石、棉、回木粉、细云母组成,其中各成分的重量百分比为:还原钛铁矿35-42%,硅灰石6-9%,金红石12-16%,白泥4-6%,海泡石5-8%,长石7-10%,云母4-7%,大理石4-7%,中碳锰铁7-10%,回木粉1-3%,棉1-3%,细云母1-3%。
生产此焊条的螺旋压涂机通过改造其螺旋绞刀的形状、尺寸以及机缸的形状、直径,并配以合适的生产工艺、焊条配方,焊条生产效率、质量得到很大提高,焊条(直径3.2)台班产量由前几年的11吨提高到现在的14吨,表皮质量也有所提高。
本发明的配方分析:
焊条由焊芯和药皮组成,决定焊条性能的因素,主要在于焊条的配方设计。所述焊条一种钛钙型结构钢焊条,以H08A盘条作为焊芯原料。
硅灰石的化学成分为CaO44-50%,SiO246-54%,且S、P含量低,其结构呈纤维状、针状、长径比大,颜色光亮洁白。焊条药皮中加入适量的硅灰石,由于其含有CaO及SiO2,可提高熔敷金属的抗裂性能、塑性和韧性,改善焊接的工艺性能,两者兼顾;其结构呈纤维状、针状、长径比大,可提高药皮强度;其白度高,可替代钛白粉,提高药皮外观质量,由于其价格相对低廉,可降低焊条生产成本。
焊条药皮中加入适量的有机物,包括棉和回木粉,可改善焊条的引弧及再引弧性能。棉选用长纤维棉,可提高焊条药皮强度。回木粉可改善焊接时的气味。
配方通过大量试验,反复调整各组分含量,调节合适的药皮造渣温度、熔渣的凝固温度、熔渣的粘度,以充分利于焊接冶金的进行。通过精确调整CaO—SiO2—TiO2渣系,平衡熔渣的酸、碱度,以保证熔敷金属良好的力学性能,并兼顾焊工的可操作性。
选用适量具有一定塑性、弹性的药粉,配以适宜的水玻璃,以保证压涂的顺利进行。
本发明焊条熔敷金属化学成分检测的结果(%):
本发明的优越性:1、本发明研制的焊条具有良好的力学性能和全位置焊接工艺性能,采用该焊条焊接低碳钢及42公斤级的低合金钢,可交直流两用,焊接时, 电弧柔和,操作轻松应手,引弧及再引弧非常容易,飞溅极少,脱渣容易、焊波成形细致、美观,特别利于焊工操作;2、焊条药皮具有良好的耐潮性、耐弯曲性;3、熔敷金属具有良好的抗裂性能及良好的塑性和韧性;4、同时,采用了焊条原材料,并改造了螺旋压涂机其螺旋绞刀的形状、尺寸以及机缸的形状、直径,并配以合适的生产工艺,大大提高了生产效率,降低了生产成本,熔敷金属具有良好的抗裂性能及良好的塑性和韧性;5、生产的焊条质优价廉,同时具有良好的可操作性,降低了对焊工的要求,可更好的满足我国大量基础建设的需要。
(四)具体实施方式:
实施例1:一种钛钙型结构钢焊条,以H08A盘条作为焊芯原料,采用改进的设备、生产工艺进行制造,焊条药皮的配方由还原钛铁矿、硅灰石、金红石、中碳锰铁、白泥、海泡石、长石、云母、大理石、棉、回木粉、细云母组成。
所述焊条药皮的配方各成分的重量百分比为还原钛铁矿 38%,硅灰石 8%,金红石13%,白泥 5%,海泡石 6%,长石 8%,云母6%,大理石 5%,中碳锰铁7%,回木粉1%,棉2%,细云母1%。
焊条熔敷金属成分检测,其重量百分比为:碳0.072%、锰0.42%、硅0.18%、硫0.012%、磷0.018%,余量为铁。
所述焊条主要适用于低碳钢及42公斤级的低合金钢的焊接,具有良好的力学性能和全位置焊接工艺性能,力学性能完全满足使用要求,熔敷金属具有良好的抗裂性能及良好的塑性和韧性。焊条药皮具有良好的耐潮性、耐弯曲性。生产的焊条质优价廉,同时具有良好的可操作性,焊工操作轻松应手。
实施例2:一种钛钙型结构钢焊条,以H08A盘条作为焊芯原料,采用改进的设备、生产工艺进行制造,焊条药皮的配方由还原钛铁矿、硅灰石、金红石、中碳锰铁、白泥、海泡石、长石、云母、大理石、棉、回木粉、细云母组成。
所述焊条药皮的配方各成分的重量百分比为还原钛铁矿35%,硅灰石6%,金红石15%,白泥 6%,海泡石5%,长石7%,云母 7%,大理石 6%,中碳锰铁8%,回木粉2%,棉1%,细云母2%。
焊条熔敷金属成分检测,其重量百分比为:碳0.067%、锰0.46%、硅0.20%、硫0.010%、磷0.020%,余量为铁。
所述焊条主要适用于低碳钢及42公斤级的低合金钢的焊接,具有良好的力学性能和全位置焊接工艺性能,力学性能完全满足使用要求,熔敷金属具有良好的抗裂性能及良好的塑性和韧性。焊条药皮具有良好的耐潮性、耐弯曲性。
Claims (3)
1.一种钛钙型结构钢焊条,其特征在于它以H08A盘条作为焊芯原料,焊条药皮的配方由还原钛铁矿、硅灰石、金红石、中碳锰铁、白泥、海泡石、长石、云母、大理石、棉、回木粉、细云母组成,其中各成分的重量百分比为:还原钛铁矿35-42%,硅灰石6-9%,金红石12-16%,白泥4-6%,海泡石5-8%,长石7-10%,云母4-7%,大理石4-7%,中碳锰铁7-10%,回木粉1-3%,棉1-3%,细云母1-3%。
2.根据权利要求1所述一种钛钙型结构钢焊条,其特征在于所述焊条药皮的配方各成分的重量百分比为还原钛铁矿 38%,硅灰石 8%,金红石13%,白泥 5%,海泡石 6%,长石 8%,云母 6%,大理石5%,中碳锰铁7%,回木粉1%,棉2%,细云母1%。
3.根据权利要求1所述一种钛钙型结构钢焊条,其特征在于所述焊条药皮的配方各成分的重量百分比为还原钛铁矿35%,硅灰石 6%,金红石15%,白泥 6%,海泡石5%,长石7%,云母 7%,大理石 6%,中碳锰铁8%,回木粉2%,棉1%,细云母2%。