CN102231409A - 具有彩色图案的太阳能电池片的制备方法 - Google Patents

具有彩色图案的太阳能电池片的制备方法 Download PDF

Info

Publication number
CN102231409A
CN102231409A CN201110188795XA CN201110188795A CN102231409A CN 102231409 A CN102231409 A CN 102231409A CN 201110188795X A CN201110188795X A CN 201110188795XA CN 201110188795 A CN201110188795 A CN 201110188795A CN 102231409 A CN102231409 A CN 102231409A
Authority
CN
China
Prior art keywords
adhesive tape
silicon chip
temperature resistant
resistant adhesive
high temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110188795XA
Other languages
English (en)
Inventor
程亮
张黎明
许海军
刘鹏
姜言森
李玉花
贾河顺
徐振华
任现坤
王兆光
张春艳
崔玉杰
张丽丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Linuo Solar Power Co Ltd
Original Assignee
Linuo Solar Power Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Linuo Solar Power Co Ltd filed Critical Linuo Solar Power Co Ltd
Priority to CN201110188795XA priority Critical patent/CN102231409A/zh
Publication of CN102231409A publication Critical patent/CN102231409A/zh
Pending legal-status Critical Current

Abstract

本发明属于太阳能电池片制作技术领域，具体涉及具有彩色图案的太阳能电池片的制备方法，该种制备方法是在有钝化减反射膜的硅片上贴上具有特定镂空图案的耐高温胶带，然后再次进行减反射膜或颜色调制膜的沉积，最后将耐高温胶带去除，形成与胶带镂空图案相对应的彩色图案。本发明的可控性及可重复性好，灵活性高，能满足太阳能电池片在建筑一体化中美观的需求。

Description

具有彩色图案的太阳能电池片的制备方法
技术领域
本发明属于太阳能电池片制作技术领域，具体涉及具有彩色图案的太阳能电池片的制备方法。
背景技术
电池片的生产工序为制绒、扩散、刻蚀、镀减反膜、背电极、背场、正电极的印刷、烧结。
目前市场上，电池片的颜色主要以蓝黑色为主，封装组件之后，组件颜色比较单一。随着光伏行业的不断进步，市场对光伏产品提出了更高的要求，不但要保证效率的不断提升，对电池片的外观也提出了更苛刻的要求。目前大量光伏电站正在建设中，光伏与建筑一体化也日趋成熟，其要求电池片有各种颜色以适应美观的要求；尤其是光伏与建筑一体化对彩色电池片的需求更加迫切，对于作为建筑材料的光伏产品，人们希望能够选择自己喜欢的颜色来装扮自己的建筑，彰显建筑的个性。
发明内容
本发明的目的就是为进一步满足光伏建筑一体化的需求，而提供一种具有彩色图案的太阳能电池片的制备方法，该种制备方法是，在有钝化减反射膜的硅片上贴上具有镂空图案的耐高温胶带，然后再次进行减反射膜或颜色调制膜的沉积，最后将耐高温胶带去除，这样就可以在硅片上形成与胶带镂空图案相对应的彩色图案。本发明的可控性及可重复性好，灵活性高，能满足太阳能电池片在与建筑一体化中美观的需求。
本发明的技术方案为：具有彩色图案的太阳能电池片的制备方法，在有钝化减反射膜的硅片上贴上具有镂空图案的耐高温胶带，然后再次进行减反射膜或颜色调制膜的沉积，最后将耐高温胶带去除，在太阳能电池片上形成与胶带镂空图案相对应的彩色图案。
所述的耐高温胶带，为聚酰亚胺制成。
本发明的具体步骤为：
（1）硅片经过制绒、扩散、刻蚀边缘、磷硅玻璃去除、钝化减反射膜沉积工序之后，在硅片表面张贴具有图案的耐高温胶带，其中耐高温胶带与钝化减反射膜之间不留明显缝隙；
（2）将贴有耐高温胶带的硅片放入将反射膜或颜色调制膜沉积腔体中，进行第二次沉积；
（3）将完成二次沉积的硅片从沉积腔体中取出，冷却至室温；
（4）去除硅片表面的耐高温胶带，再用工业酒精或丙酮溶液将硅片表面残留清洗干净，再依次完成背电极、背场、正电极的印刷、烧结等步骤，得到单片片内具有彩色图案的太阳能电池片。
本发明的有益效果为：本发明是一种具有彩色图案的太阳能电池片的制备方法，通过控制二次沉积过程中减反射膜的厚度或颜色调制膜的颜色，以及耐高温胶带镂空区域的形状，使片内呈现出具有不同颜色和不同形状的彩色图案。所述的胶带是一种耐高温胶带，在沉积腔体内，不会因温度高而发生变形；易去除，不会对硅片表面产生污染。本发明的方法可控性及可重复性好，灵活性高，能满足太阳能电池片在与建筑一体化中美观的需求。
附图说明：
图1所示为本发明制备彩色太阳能电池片的结构示意图；
其中，1-耐高温胶带，2-减反射膜或颜色调制膜，3-钝化减反射膜，4-硅片。
具体实施方式：
为了更好地理解本发明，下面结合附图来详细解释本发明的实施方式。
本发明的技术方案为：具有彩色图案的太阳能电池片的制备方法，在有钝化减反射膜3的硅片4上贴上具有镂空图案的耐高温胶带1，然后再次进行减反射膜或颜色调制膜2的沉积，最后将耐高温胶带1去除，在太阳能电池片上形成与耐高温胶带1镂空图案相对应的彩色图案。
所述的耐高温胶带1，为聚酰亚胺制成。
所述的耐高温胶1带要紧贴在钝化减反射膜3上，并且在沉积腔体内，不会因温度高而发生变形。
所述的耐高温胶带1容易去除，不会对硅片4表面产生污染。。
在镀有钝化减反射膜3的硅片4表面上，通过改变耐高温胶带1镂空区域的形状，来实现在硅片4表面得到不同彩色图案的电池片。 
实施例１
硅片4在经过制绒、扩散、刻蚀边缘、磷硅玻璃去除、钝化减反射膜3沉积工序之后；在硅片4表面张贴具有镂空图案的耐高温胶带1，其中耐高温胶带1与钝化减反射膜3之间不留明显缝隙；然后将贴有耐高温胶带1的硅片4放入将反射膜或颜色调制膜2沉积腔体中，进行第二次沉积；将完成二次沉积的硅片4从沉积腔体中，取出冷却至室温；撕掉耐高温胶带1，然后再依次完成背电极、背场、正电极的印刷、烧结等步骤，变得到本发明所述的具有彩色图案的太阳能电池片。

Claims (3)

1.一种具有彩色图案的太阳能电池片的制备方法，其特征在于，在有钝化减反射膜的硅片上贴上具有镂空图案的耐高温胶带，然后再次进行减反射膜或颜色调制膜的沉积，最后将耐高温胶带去除，在太阳能电池片上形成与胶带镂空图案相对应的彩色图案。
2.根据权利要求1所述的具有彩色图案的太阳能电池片的制备方法，其特征在于，所述的耐高温胶带，为聚酰亚胺制成。
3.根据权利要求1所述的具有彩色图案的太阳能电池片的制备方法，其特征在于，具体步骤为：
（1）硅片经过制绒、扩散、刻蚀边缘、磷硅玻璃去除、钝化减反射膜沉积工序之后，在硅片表面张贴具有图案的耐高温胶带，其中耐高温胶带与钝化减反射膜之间不留明显缝隙；
（2）将贴有耐高温胶带的硅片放入将反射膜或颜色调制膜沉积腔体中，进行第二次沉积；
（3）将完成二次沉积的硅片从沉积腔体中取出，冷却至室温；
（4）去除硅片表面的耐高温胶带，再用工业酒精或丙酮溶液将硅片表面残留清洗干净，再依次完成背电极、背场、正电极的印刷、烧结等步骤，得到单片片内具有彩色图案的太阳能电池片。
CN201110188795XA 2011-07-07 2011-07-07 具有彩色图案的太阳能电池片的制备方法 Pending CN102231409A (zh)