CN102219976A - 一种高黏度沥青改性剂、改性沥青、沥青混合料 - Google Patents

一种高黏度沥青改性剂、改性沥青、沥青混合料 Download PDF

Info

Publication number
CN102219976A
CN102219976A CN2010101525719A CN201010152571A CN102219976A CN 102219976 A CN102219976 A CN 102219976A CN 2010101525719 A CN2010101525719 A CN 2010101525719A CN 201010152571 A CN201010152571 A CN 201010152571A CN 102219976 A CN102219976 A CN 102219976A
Authority
CN
China
Prior art keywords
high viscosity
asphalt
asphalt modifier
viscosity asphalt
styrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010101525719A
Other languages
English (en)
Inventor
何唯平
唐小亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Oceanpower New Material Technology Co Ltd
Original Assignee
Shenzhen Oceanpower Industrial Co Ltd
Shenzhen Oceanpower Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Oceanpower Industrial Co Ltd, Shenzhen Oceanpower Engineering Technology Co Ltd filed Critical Shenzhen Oceanpower Industrial Co Ltd
Priority to CN2010101525719A priority Critical patent/CN102219976A/zh
Publication of CN102219976A publication Critical patent/CN102219976A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高黏度改性剂的配方及其应用。按重量份组成为：热塑性弹性体3-10份；热塑性树脂2-10份；橡胶类聚合物2-10份；硫化剂0.05-0.3份；碳类物质0.05-0.3份，优选松香树脂、苯乙烯-丁二烯-苯乙烯共聚物、丁苯橡胶、硫磺和炭黑。本发明的高黏度沥青改性剂生产工艺简单，可以用来制备黑色高粘沥青，用来铺筑黑色排水路面以及黑色透水路面，降低了城市噪音污染，提高了路面摩擦系数，有效防止产生水膜，提高了雨天行车的安全性；本发明的高粘沥青改性剂，所需要材料来源广泛、生产工艺简单，适应性广泛。

Description

一种高黏度沥青改性剂、改性沥青、沥青混合料
技术领域
本发明涉及一种用于工程领域的建筑材料，特别涉及的是一种工程用的沥青改性剂，本发明还涉及一种沥青和沥青混合料。
背景技术
随着交通事业的不断发展进步，以汽车为主的交通工具数量不断的激增，这就从客观上要求公路建设的进度和质量，其中公路的质量建设尤为重要，一方面要保证修建的公路能够长久使用，比如能够降低噪音、透水、透气等；另一方面能够为汽车的安全运行提供保障，比如提高刹车时的摩擦系数、缩短刹车距离等等。而衡量公路质量的重要标准之一就是路面的空隙率，国家有关空隙率的标准为18-25％。
目前一般的密集配沥青混凝土路面的空隙率仅为3-6％，而空隙率的高低主要取决于铺路用的沥青胶结料，所以这就对铺路用沥青胶结料的性能提出了更高要求。
为了解决上述技术问题，本发明提供了一种新的技术方案。
发明内容
本发明为了解决现有的沥青混凝土路面的空隙率低的技术问题，而提供一种能够提高沥青混凝土路面空隙率的高黏度沥青改性剂。
本发明还提供了一种高黏度改性沥青和高黏度沥青混合料。
为解决上述技术问题，本发明主要采取以下技术方案：
一种高黏度沥青改性剂，按重量份组成为：热塑性弹性体3-10份；热塑性树脂2-10份；橡胶类聚合物2-10份；硫化剂0.05-0.3份；碳类物质0.05-0.3份。
进一步的，所述热塑性弹体为乙烯基芳香单体与含有至少两个未饱和烯烃的脂肪族单体聚合形成的嵌段共聚物。
更进一步的，所述热塑性弹体为苯乙烯-丁二烯-苯乙烯共聚物或苯乙烯-异戊二烯-苯乙烯共聚物。
进一步的，所述橡胶类聚合物为天然橡胶或丁苯橡胶；所述热塑性树脂为松香树脂。
进一步的，所述硫化剂为硫磺或硫化物；所述碳类物质为高目数炭黑，能够有效的防止老化。
一种高黏度改性沥青，由重交沥青和前面任一所述的高黏度沥青改性剂按照重量比为84∶16的比例制备而成。
一种高黏度沥青混合料，由集料和前面所述的高黏度改性沥青混合制备而成，所述高黏度改性沥青为混合料总重量的3～6％。
本发明提供的沥青改性剂、改性沥青以及沥青混合料具有较高的黏度，能够增加胶结料与集料的粘结力，防止表面集料在车轮荷载作用下飞散；同时，大大提高了路面的空隙率，采用本发明提供的技术方案制备的路面结构增加了沥青胶结料与日光和空气接触的机会；在本发明的技术方案中增加了高目数炭黑，有效的防止了由此产生的老化。
具体实施方式
下面结合实施例，进一步详细阐述本发明的技术方案。
实施例1：将苯乙烯-丁二烯-苯乙烯共聚物、丁苯橡胶、松香、硫磺和炭黑按照4∶2∶8∶0.15∶0.1的比例进行称量，然后将四种物质放入高速混合料机中进行充分混合，四种物质充分混合均匀后将物料加入到双螺杆挤出机中进行加热挤出，挤出的条形改性剂在进行冷却和吹干以后，送入到切粒机中进行切粒，所切好的颗粒就是高粘沥青改性剂。
实施例2：将实施例1中制备的高黏度沥青改性剂根据实际工程的需要加入到重交沥青中，重交沥青和高黏度沥青改性剂的混合比例为84∶16，进而制备成需要的高黏度改性沥青，含有高黏度沥青改性剂的高黏度改性沥青的各项性能指标都满足了国家的相关标准，具体如表1所示。
表1
实施例3：在混合料的生产过程中，将实施例2中制备的高黏度改性沥青投入到拌和楼当中，与集料一起拌和，其中高黏度改性沥青占混合料总重量的5％，进而制备出高黏度沥青混合料，用于公路建设等。制备的高黏度沥青混合料的各项性能指标如表2所示。
表2
  检测项目   单位   检测数据   国家相关标准
  油石比   ％   4.5   实测
  稳定度   KN   4.5   ＞3.5
  流值   0.1mm   29   20-40
  空隙率   ％   21   18-25
  析漏实验质量损失   ％   0.25   ＜0.3
  飞散实验质量损失   ％   13   ＜20
  动稳定度   ％   7850   ＞3000
  冻融劈裂强度比   ％   91   ＞80
从以上实验数据可以看出，利用此高黏度沥青改性剂所制备的高粘沥青和高粘沥青混合料在各个方面的性能表象的都十分优异，完全达到国家对于高黏度沥青和高黏度沥青混合料的相关技术标准。

Claims (9)

1.一种高黏度沥青改性剂，按重量份组成为：热塑性弹性体3-10份；热塑性树脂2-10份；橡胶类聚合物2-10份；硫化剂0.05-0.3份；碳类物质0.05-0.3份。
2.根据权利要求1所述的高黏度沥青改性剂，其特征在于：所述热塑性弹体为乙烯基芳香单体与含有至少两个未饱和烯烃的脂肪族单体聚合形成的嵌段共聚物。
3.根据权利要求2所述的高黏度沥青改性剂，其特征在于：所述热塑性弹体为苯乙烯-丁二烯-苯乙烯共聚物或苯乙烯-异戊二烯-苯乙烯共聚物。
4.根据权利要求1所述的高黏度沥青改性剂，其特征在于：所述橡胶类聚合物为天然橡胶或丁苯橡胶。
5.根据权利要求1所述的高黏度沥青改性剂，其特征在于：所述热塑性树脂为松香树脂。
6.根据权利要求1所述的高黏度沥青改性剂，其特征在于：所述硫化剂为硫磺或硫化物。
7.根据权利要求1所述的高黏度沥青改性剂，其特征在于：所述碳类物质为高目数炭黑。
8.一种高黏度改性沥青，其特征在于，由重交沥青和权利要求1至7任一所述的高黏度沥青改性剂按照重量比为84∶16的比例制备而成。
9.一种高黏度沥青混合料，其特征在于，由集料和权利要求8所述的高黏度改性沥青混合制备而成，所述高黏度改性沥青为混合料总重量的3～6％。
CN2010101525719A 2010-04-16 2010-04-16 一种高黏度沥青改性剂、改性沥青、沥青混合料 Pending CN102219976A (zh)