CN102211896A - Baking-free brick and preparation method thereof - Google Patents
Baking-free brick and preparation method thereof Download PDFInfo
- Publication number
- CN102211896A CN102211896A CN2010101424972A CN201010142497A CN102211896A CN 102211896 A CN102211896 A CN 102211896A CN 2010101424972 A CN2010101424972 A CN 2010101424972A CN 201010142497 A CN201010142497 A CN 201010142497A CN 102211896 A CN102211896 A CN 102211896A
- Authority
- CN
- China
- Prior art keywords
- brick
- burning brick
- baking
- burning
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a baking-free brick and a preparation method thereof. The baking-free brick is prepared by the process steps of burdening mixing, stirring, brick-making, maintaining and the like and comprises the following main raw materials by weight percent: 75% of furnace slag, 5% of gangue, 10% of coal ash and 10% of cement. The prepared baking-free brick can be a solid brick or hollow brick, the weight of each solid brick is 2.5kg. The invention also provides a preparation method of the baking-free brick. According to the invention, the problems that soil resources are excessively wasted in China and the emission of wastes is over big are solved, thereby reducing the production cost of an enterprise and improving the benefits of the enterprise; through constant-temperature aerial fog maintenance, the instability of the product quality due to over-big natural air temperature difference can be avoided so that the qualified rate of the product is improved and simultaneously, a building wall body has small possibility of cracking, deforming and shrinking; and the baking-free brick is environmentally-friendly, has no pollution, no irradiation and no harmfulness on human body, and the benefit of consumer can be protected.
Description
Technical field
The present invention relates to building material field, a kind of specifically non-burning brick and preparation method thereof.
Technical background
At present, because the clay brick manufacturing processed causes certain pollution to environment, and the land resources to China also causes sizable waste, country takes to limit the manufacturing measure of clay brick, and general non-burning brick main raw material is a river sand, river sand also belongs to natural resources, excessively can cause the ecotope overbalance equally if gather, and with river sand is that the body of wall of the buildings of the produced non-burning brick construction of main raw material shrinks easily, cracking, distortion etc., make that some buildings occurs now " building seam seam " etc. and allow the helpless situation of people, and the viscosity of river sand itself is good inadequately, in the process of making, need to use a large amount of cement to increase viscosity, so just make that production cost improves greatly, reduced the performance of enterprises, the too much use owing to cement simultaneously also damages environment.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art; slag to a large amount of industrial production dischargings is recycled; provide a kind of non-burning brick and preparation method thereof; solved the waste of China's land resources; discharging wastes is excessive; and the production cost of enterprise is too high; benefit is low; building masonry wall ftractures easily; distortion; shrink; problems such as not enough environmental protection; make the present situation of environmental pollution obtain certain control, natural resources also obtains corresponding protection simultaneously, makes the production cost of enterprise reduce simultaneously; increased the benefit of enterprise; adopt the aerosol spray maintenance of temperature control room, thermostatic control can be avoided the excessive unstable that causes quality product of nature temperature difference, and the water smoke spray evenly helps the raising of the product percentage of A-class goods.
The invention is characterized in: a kind of non-burning brick and preparation method thereof, described non-burning brick main raw material is a slag, coal drystone, and cement and flyash, its preparation process is as follows:
(1) batching, mixing: mix by a certain percentage by above-mentioned non-burning brick main raw material;
(2) stir: said mixture is put into stirrer evenly stir, make that raw material is done, wet appropriateness;
(3) brickmaking: the non-burning brick raw material after the stirring is inserted in the brick press and is produced, and obtains non-burning brick work in-process;
(4) maintenance: with temperature control room aerosol spraying process non-burning brick work in-process are maintained, and temperature control room thermostat temperature is between positive and negative 2 degree;
(5) check: non-burning brick the testing after will maintaining;
(6) final inspection: the storehouse always checks in.
The percentage of described non-burning brick each main raw material is:
Slag 75%, coal drystone 5%, flyash 10%, cement 10%, non-burning brick after making can be solid brick, also can be hollow brick, every of solid brick is about 2.5KG.
Advantage of the present invention:
One: solved the excess waste of China's land resources, discharging wastes is excessive, can not get reclaiming timely, makes serious environmental pollution problem day by day be under control and improve,
Its two, reduced the production cost of enterprise, improved the performance of enterprises,
Its three since adopt slag be main raw material make non-burning brick, make that building masonry wall is not easy to crack, distortion, shrink, and environmental protection,
Its four: because slag needs before discharging through about 1700 degrees centigrade high temperature roasting refining; so objectionable impuritiess such as the harmful chemical element in the raw material etc. all can disappear thereupon; so just make produced non-burning brick pollution-free, radiationless; harmless, also make human consumer's interests obtain protection.
Embodiment
Preferred embodiment:
Produce 64000000 non-burning brickly soon, need 120,000 tons of raw materials altogether, wherein slag accounts for 90,000 tons, coal drystone and accounts for 0.6 ten thousand tons, flyash and account for 1.2 ten thousand tons, and cement accounts for 1.2 ten thousand tons.
The step of preparation is as follows:
(1) batching, mixing: by above-mentioned non-burning brick main raw material mixed;
(2) stir: said mixture is put into stirrer evenly stir, make that raw material is done, wet appropriateness;
(3) brickmaking: the non-burning brick raw material after the stirring is inserted in the brick press and is produced, and obtains non-burning brick work in-process;
(4) maintenance: with temperature control room aerosol spraying process non-burning brick work in-process are maintained, and temperature control room thermostat temperature is between positive and negative 2 degree;
(5) check: non-burning brick the testing after will maintaining;
(6) final inspection: the storehouse always checks in.
Final acquisition is solid non-burning brick, every fast about 2.5KG.
It should be noted that at last: above embodiment only in order to the explanation the present invention and and unrestricted technical scheme described in the invention; Therefore, although this specification sheets has been described in detail the present invention with reference to each above-mentioned embodiment,, those of ordinary skill in the art should be appreciated that still and can make amendment or be equal to replacement the present invention; And all do not break away from the technical scheme and the improvement thereof of the spirit and scope of the present invention, and it all should be encompassed in the claim scope of the present invention.
Claims (3)
- One kind non-burning brick, it is characterized in that: described non-burning brick main raw material is a slag, coal drystone, cement, flyash, each component proportions of described main raw material is: slag 75%, coal drystone 5%, flyash 10%, cement 10%.
- 2. non-burning brick preparation method is characterized in that: comprise as claimed in claim 1 a kind of non-burning brickly, preparation process is as follows:(1) batching, mixing: mix by a certain percentage by above-mentioned non-burning brick main raw material;(2) stir: said mixture is put into stirrer evenly stir, make that raw material is done, wet appropriateness;(3) brickmaking: the non-burning brick raw material after the stirring is inserted in the brick press and is produced, and obtains non-burning brick work in-process;(4) maintenance: with temperature control room aerosol spraying process non-burning brick work in-process are maintained, and temperature control room thermostat temperature be positive and negative 2 spend between,(5) check: non-burning brick the testing after will maintaining;(6) final inspection: the storehouse always checks in.
- 3. a kind of non-burning brick preparation method according to claim 2 is characterized in that: non-burning brick after making, can be solid brick, and also can be hollow brick, every of solid brick is about 2.5KG.