CN102211343A - Shen Nung life-prolonged compound plate and manufacturing method thereof - Google Patents
Shen Nung life-prolonged compound plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN102211343A CN102211343A CN2010101464838A CN201010146483A CN102211343A CN 102211343 A CN102211343 A CN 102211343A CN 2010101464838 A CN2010101464838 A CN 2010101464838A CN 201010146483 A CN201010146483 A CN 201010146483A CN 102211343 A CN102211343 A CN 102211343A
- Authority
- CN
- China
- Prior art keywords
- composite plate
- farming
- chip
- legendary god
- life
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a Shen Nung life-prolonged compound plate and a manufacturing method thereof. The Shen Nung life-prolonged compound plate comprises a compound plate body and an aluminum plated film layer which is covered on the external surface of the compound plate body, wherein the compound plate body is formed by bonding a Shen Nung life-prolonged Chinese herbal medicine and wood with plant straws by using biologic adhesives. By using the Shen Nung life-prolonged compound plate and manufacturing method thereof provided by the invention, the defects of the prior art that the health-care function is inferior and the cost is high are overcome, so as to realize the advantages of excellent health-care function and low cost.
Description
Technical field
The present invention relates to dalle, particularly, relate to a kind of legendary god of farming prolong life composite plate and manufacture method thereof.
Background technology
In the prior art, traditional composite plate is a replacing plate, basically all be after adding glue by wood fibre fragments such as wood chip, stalk bits, wood chip or fragment, pressing forms through heating, adopt except that small part some the adhesive of harmful volatile ingredient such as formaldehydeless grade of relative environmental protection such as polyurethane, most of adopt can release formaldehyde, the urea-formaldehyde glue or the phenol glue of volatility pernicious gas such as phenolic aldehyde.These sheet materials in use can be in the several years slow harmful substances such as release formaldehyde, phenolic aldehyde constantly, these harmful costs can be constituted the physiological function of human body and destroy by after in people's suction body.
As seen, above-mentioned conventional composite plate is a replacing plate, can save timber, reduces the destruction to natural environment; But, can not reach health-care effect.
In addition, in some environment-friendly sheets, though harmful components such as the formaldehyde that can not volatilize, the chemical adhesive that this environment-friendly sheet uses generally all needs the import from external (for example Germany), makes that the cost of this environment-friendly sheet is higher.
Summary of the invention
The objective of the invention is to, at the problems referred to above, propose a kind of legendary god of farming composite plate of prolonging life, with the advantage that realizes that health care is good and cost is low.
For achieving the above object, the technical solution used in the present invention is: a kind of legendary god of farming composite plate of prolonging life comprises the composite plate body, and pastes the aluminium plating membrane at described this external surface of composite plate; Described composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content: mother chrysanthemum: 7-11%; Argy wormwood: 7-11%; Peppermint: 5-9%; Fragrant camphor tree bits and/or leaf: 6-10%; Rhizoma atractylodis: 0.5-1.5%; The stem of noble dendrobium: 0.2-0.8%; Calamus: 1-3%; Wrinkled giant hyssop: 0.5-1.5%; The bark of official magnolia: 0.5-1.5%; Radix Glycyrrhizae: 0.5-1.5%; Lavender: 0.5-1.5%; Lemongrass: 0.5-1.5%; Rosewood bits: 0.5-1.5%; Santal: 0.1-0.3%; Glossy ganoderma: 1.0-2.0%; Cloves: 0.4-1.0%; The banksia rose: 1.0-2.0%; Radix Codonopsis: 0.5-1.5%; Sealwort: 0.9-1.5%; Cortex Periplocae: 0.5-1.5%; Pawpaw: 1-3%; The bletilla striata: 0.2-0.6%; Cassia twig: 0.5-1.5%; Oriental wormwood: 0.5-1.5%; Fennel seeds: 0.5-1.1%; The Radix Astragali: 0.5-1.5%; Ligusticum wallichii: 0.4-1.0%; Chinese prickly ash: 0.5-1.5%; Lotus leaf: 0.5-1.5%; Radix Angelicae Sinensis: 0.5-1.5%; Corydalis tuber: 0.5-1.5%; The wind-weed: 0.5-1.5%; Rheum officinale: 0.5-1.5%; Folium panacis japonici cum caule and/or palpus: 1.0-2.0%; Nutmeg: 0.5-1.0%; Rhizoma Gastrodiae: 0.5-1.5%; The root of Dahurain angelica: 0.5-1.5%; Safflower: 0.1-0.5%; Rose: 0.1-0.7%; Jasmine: 0.5-1.5%; Honeysuckle: 0.1-0.5%; The root of bidentate achyranthes: 0.5-1.5%; The bark of eucommia: 0.2-0.8%; Pseudo-ginseng: 0.5-1.5%; Husky ginger: 0.2-0.8%; Selfheal: 0.5-1.5%; The bighead atractylodes rhizome: 0.2-0.8%; Motherwort: 0.2-0.8%; The leaf of bamboo: 0.5-1.5%; The root of kudzu vine: 0.5-1.5%; Polygala root: 0.5-1.5%; Radix bupleuri: 0.5-1.5%; Windproof: 1-3%; Lucid asparagus: 0.5-1.5%; CedarLeaves: 0.5-1.5%; Monkshood: 0.5-1.5%; Glutinous rehmannia: 0.5-1.5%; Matrimony vine: 0.5-1.5%; Fructus Aurantii: 0.5-1.5%; Ginkgo leaf: 0.5-1.5%; Purple perilla: 0.5-1.5%; Mulberry leaf: 0.5-1.5%; Thyme: 0.5-1.5%; Poria cocos: 0.2-0.8%; Chinese honey locust: 0.2-0.8%; Marigold: 0.5-1.5%; Balloonflower root: 0.5-1.5%; Radix Isatidis: 0.5-1.5%; Saline cistanche: 0.2-0.8%; The fleece-flower root: 0.9-1.5%; Realgar: 0.1-0.5%; Active carbon: 1.0-3.0%; Pyroxene chip: 1.0-5.0%; Paris white or zeolite powder: 1-5%; Timber or straw or fiber: surplus.
Further, described biogum mixture comprises gelatin, modified starch, protein adhesive and frankincense.
Further, described composite plate body comprises the internal layer and the skin of order setting from inside to outside, and described internal layer and outer field density increase from inside to outside gradually; Described peppermint and lavender are entrained in described internal layer, and described glutinous rehmannia and genseng are entrained in described skin.
Further, another technical scheme that the present invention adopts is: based on the above-mentioned legendary god of farming composite plate of prolonging life, the prolong life preparation method of composite plate of the described legendary god of farming is as follows: (1) is cut into chip or thin slice with described wood chip or straw strand, press proportion relation, all the other raw material strands are cut into chip or are ground into powder, add described wood chip or straw strand to and be cut in chip or the thin slice, stir, place 1-3h; (2) in the above-mentioned raw materials mixture, add described biogum mixture, after stirring, the gained mixed material is placed on the cloth stockline, heat and pressurized treatments; (3) reach 110-150 ℃, when pressure conditions reaches 3-7Mpa, above-mentioned mixed material be pressed into the described legendary god of farming composite plate of prolonging life when temperature conditions.
Further, in step (1), further comprising the steps of: in described skin, screen described zeolite powder or Paris white with molecular sieve, and compacting.
Further, another technical scheme that the present invention adopts is: based on the above-mentioned legendary god of farming composite plate of prolonging life, the prolong life preparation method of composite plate of the described legendary god of farming is as follows: in each raw material, press proportion relation, timber or straw or fiber are pulverized skeining be cut into chip or thin slice, will be boiled into concoction except that all the other raw materials timber or straw or the fiber simultaneously; Described concoction is sprayed at described chip or thin slice, described concoction is soaked in described chip or the thin slice, and be equipped with described biogum mixture, compression moulding.
Further, another technical scheme that the present invention adopts is: based on the above-mentioned legendary god of farming composite plate of prolonging life, the prolong life preparation method of composite plate of the described legendary god of farming is as follows: in each raw material, press proportion relation, timber or straw or fiber are pressed into artificial plate; In seal cavity, will be except that all the other raw materials timber or straw or the fiber, distill or boil, utilize distillation gas or steam to fumigate described artificial plate, make described distillation gas or vapor permeates inside to artificial plate.
The legendary god of farming of the various embodiments of the present invention composite plate and preparation method thereof of prolonging life, wherein, this legendary god of farming composite plate of prolonging life comprises the composite plate body, and pastes the aluminium plating membrane at this this external surface of composite plate; This composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content: mother chrysanthemum: 7-11%; Argy wormwood: 7-11%; Peppermint: 5-9%; Fragrant camphor tree bits and/or leaf: 6-10%; Rhizoma atractylodis: 0.5-1.5%; The stem of noble dendrobium: 0.2-0.8%; Calamus: 1-3%; Wrinkled giant hyssop: 0.5-1.5%; The bark of official magnolia: 0.5-1.5%; Radix Glycyrrhizae: 0.5-1.5%; Lavender: 0.5-1.5%; Lemongrass: 0.5-1.5%; Rosewood bits: 0.5-1.5%; Santal: 0.1-0.3%; Glossy ganoderma: 1.0-2.0%; Cloves: 0.4-1.0%; The banksia rose: 1.0-2.0%; Radix Codonopsis: 0.5-1.5%; Sealwort: 0.9-1.5%; Cortex Periplocae: 0.5-1.5%; Pawpaw: 1-3%; The bletilla striata: 0.2-0.6%; Cassia twig: 0.5-1.5%; Oriental wormwood: 0.5-1.5%; Fennel seeds: 0.5-1.1%; The Radix Astragali: 0.5-1.5%; Ligusticum wallichii: 0.4-1.0%; Chinese prickly ash: 0.5-1.5%; Lotus leaf: 0.5-1.5%; Radix Angelicae Sinensis: 0.5-1.5%; Corydalis tuber: 0.5-1.5%; The wind-weed: 0.5-1.5%; Rheum officinale: 0.5-1.5%; Folium panacis japonici cum caule and/or palpus: 1.0-2.0%; Nutmeg: 0.5-1.0%; Rhizoma Gastrodiae: 0.5-1.5%; The root of Dahurain angelica: 0.5-1.5%; Safflower: 0.1-0.5%; Rose: 0.1-0.7%; Jasmine: 0.5-1.5%; Honeysuckle: 0.1-0.5%; The root of bidentate achyranthes: 0.5-1.5%; The bark of eucommia: 0.2-0.8%; Pseudo-ginseng: 0.5-1.5%; Husky ginger: 0.2-0.8%; Selfheal: 0.5-1.5%; The bighead atractylodes rhizome: 0.2-0.8%; Motherwort: 0.2-0.8%; The leaf of bamboo: 0.5-1.5%; The root of kudzu vine: 0.5-1.5%; Polygala root: 0.5-1.5%; Radix bupleuri: 0.5-1.5%; Windproof: 1-3%; Lucid asparagus: 0.5-1.5%; CedarLeaves: 0.5-1.5%; Monkshood: 0.5-1.5%; Glutinous rehmannia: 0.5-1.5%; Matrimony vine: 0.5-1.5%; Fructus Aurantii: 0.5-1.5%; Ginkgo leaf: 0.5-1.5%; Purple perilla: 0.5-1.5%; Mulberry leaf: 0.5-1.5%; Thyme: 0.5-1.5%; Poria cocos: 0.2-0.8%; Chinese honey locust: 0.2-0.8%; Marigold: 0.5-1.5%; Balloonflower root: 0.5-1.5%; Radix Isatidis: 0.5-1.5%; Saline cistanche: 0.2-0.8%; The fleece-flower root: 0.9-1.5%; Realgar: 0.1-0.5%; Active carbon: 1.0-3.0%; Pyroxene chip: 1.0-5.0%; Paris white or zeolite powder: 1-5%; Timber or straw or fiber: surplus; In this legendary god of farming composite plate of prolonging life, owing to be doped with the Chinese herbal medicine useful, can overcome the poor and defect of high cost of health care in the prior art, with the advantage that realizes that health care is good and cost is low to health.
Other features and advantages of the present invention will be set forth in the following description, and, partly from specification, become apparent, perhaps understand by implementing the present invention.Purpose of the present invention and other advantages can realize and obtain by specifically noted structure in the specification of being write, claims and accompanying drawing.
Below by drawings and Examples, technical scheme of the present invention is described in further detail.
Description of drawings
Accompanying drawing is used to provide further understanding of the present invention, and constitutes the part of specification, is used from explanation the present invention with embodiments of the invention one, is not construed as limiting the invention.In the accompanying drawings:
Fig. 1 is the prolong life structural representation of transverse sectional view of composite plate of the legendary god of farming according to the present invention;
Fig. 2 is the prolong life structural representation of longitudinal sectional view of composite plate of the legendary god of farming according to the present invention.
In conjunction with the accompanying drawings, Reference numeral is as follows in the embodiment of the invention:
The 1-skin; The 2-internal layer; The 3-aluminium plating membrane.
The specific embodiment
Below in conjunction with accompanying drawing the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein only is used for description and interpretation the present invention, and be not used in qualification the present invention.
Embodiment one
According to the embodiment of the invention, provide a kind of legendary god of farming the composite plate and preparation method thereof of prolonging life.As depicted in figs. 1 and 2, in the present embodiment, legendary god of farming's composite plate of prolonging life comprises the composite plate body, and pastes the aluminium plating membrane 3 at this external surface of composite plate.Density in the middle of the whole flaggy is lower than submarginal density, and aluminium plating membrane 3 has waterproof and dampproof effect, can also prevent that the gaseous volatilization of Chinese medicine from going out.
Wherein, the composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content:
Mother chrysanthemum: 7%;
Argy wormwood: 11%;
Peppermint: 5%;
Fragrant camphor tree bits and/or leaf: 10%;
Rhizoma atractylodis: 0.5%;
The stem of noble dendrobium: 0.8%;
Calamus: 1%;
Wrinkled giant hyssop: 1.5%;
The bark of official magnolia: 0.5%;
Radix Glycyrrhizae: 1.5%;
Lavender: 0.5%;
Lemongrass: 1.5%;
Rosewood bits: 0.5%;
Santal: 0.3%;
Glossy ganoderma: 1.0%;
Cloves: 1.0%;
The banksia rose: 1.0%;
Radix Codonopsis: 1.5%;
Sealwort: 0.9%;
Cortex Periplocae: 1.5%;
Pawpaw: 1%;
The bletilla striata: 0.6%;
Cassia twig: 0.5%;
Oriental wormwood: 1.5%;
Fennel seeds: 0.5%;
The Radix Astragali: 1.5%;
Ligusticum wallichii: 0.4%;
Chinese prickly ash: 1.5%;
Lotus leaf: 0.5%;
Radix Angelicae Sinensis: 1.5%;
Corydalis tuber: 0.5%;
The wind-weed: 1.5%;
Rheum officinale: 0.5%;
Folium panacis japonici cum caule and/or palpus: 2.0%;
Nutmeg: 0.5%;
Rhizoma Gastrodiae: 1.5%;
The root of Dahurain angelica: 0.5%;
Safflower: 0.5%;
Rose: 0.1%;
Jasmine: 1.5%;
Honeysuckle: 0.1%;
The root of bidentate achyranthes: 0.5%;
The bark of eucommia: 0.8%;
Pseudo-ginseng: 0.5%;
Husky ginger: 0.8%;
Selfheal: 0.5%;
The bighead atractylodes rhizome: 0.8%;
Motherwort: 0.2%;
The leaf of bamboo: 1.5%;
The root of kudzu vine: 0.5%;
Polygala root: 1.5%;
Radix bupleuri: 0.5%;
Windproof: 3%;
Lucid asparagus: 0.5%;
CedarLeaves: 1.5%;
Monkshood: 0.5%;
Glutinous rehmannia: 1.5%;
Matrimony vine: 0.5%;
Fructus Aurantii: 1.5%;
Ginkgo leaf: 0.5%;
Purple perilla: 1.5%;
Mulberry leaf: 0.5%;
Thyme: 1.5%;
Poria cocos: 0.2%;
Chinese honey locust: 0.8%;
Marigold: 0.5%;
Balloonflower root: 1.5%;
Radix Isatidis: 0.5%;
Saline cistanche: 0.8%;
The fleece-flower root: 0.9%;
Realgar: 0.5%;
Active carbon: 1.0%;
Pyroxene chip: 5.0%;
Paris white or zeolite powder: 5%;
Timber or straw or fiber: surplus
Further, in the present embodiment, above-mentioned biogum mixture comprises gelatin, modified starch, protein adhesive and frankincense; The composite plate body comprises internal layer 2 and the skin 1 that is provided with in proper order from inside to outside, and internal layer 2 increases from inside to outside gradually with the density of skin 1; Peppermint and lavender are entrained in internal layer 2, and glutinous rehmannia and genseng are entrained in outer 1.
Further, in the present embodiment, the prolong life preparation method of composite plate of the above-mentioned legendary god of farming is as follows:
(1) above-mentioned wood chip or straw strand are cut into chip or thin slice, press proportion relation, all the other raw material strands are cut into chip or are ground into powder, add wood chip or straw strand to and be cut in chip or the thin slice, stir, place 2h;
Further, in step (1), in outer 1, screen described zeolite powder or Paris white with molecular sieve, and compacting;
(2) in the above-mentioned raw materials mixture, add described biogum mixture, after stirring, the gained mixed material is placed on the cloth stockline, heat and pressurized treatments;
(3) reach 130 ℃, when pressure conditions reaches 5Mpa, above-mentioned mixed material be pressed into the described legendary god of farming composite plate of prolonging life when temperature conditions.
Embodiment two
Different with the foregoing description is that in the present embodiment, the composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content:
Mother chrysanthemum: 11%;
Argy wormwood: 7%;
Peppermint: 9%;
Fragrant camphor tree bits and/or leaf: 6%;
Rhizoma atractylodis: 1.5%;
The stem of noble dendrobium: 0.2%;
Calamus: 3%;
Wrinkled giant hyssop: 0.5%;
The bark of official magnolia: 1.5%;
Radix Glycyrrhizae: 0.5%;
Lavender: 1.5%;
Lemongrass: 0.5%;
Rosewood bits: 1.5%;
Santal: 0.1%;
Glossy ganoderma: 2.0%;
Cloves: 0.4%;
The banksia rose: 2.0%;
Radix Codonopsis: 0.5%;
Sealwort: 1.5%;
Cortex Periplocae: 0.5%;
Pawpaw: 3%;
The bletilla striata: 0.2%;
Cassia twig: 1.5%;
Oriental wormwood: 0.5%;
Fennel seeds: 1.1%;
The Radix Astragali: 0.5%;
Ligusticum wallichii: 1.0%;
Chinese prickly ash: 0.5%;
Lotus leaf: 1.5%;
Radix Angelicae Sinensis: 0.5%;
Corydalis tuber: 1.5%;
The wind-weed: 0.5%;
Rheum officinale: 1.5%;
Folium panacis japonici cum caule and/or palpus: 1.0%;
Nutmeg: 1.0%;
Rhizoma Gastrodiae: 0.5%;
The root of Dahurain angelica: 1.5%;
Safflower: 0.1%;
Rose: 0.7%;
Jasmine: 0.5%;
Honeysuckle: 0.5%;
The root of bidentate achyranthes: 1.5%;
The bark of eucommia: 0.2%;
Pseudo-ginseng: 1.5%;
Husky ginger: 0.2%;
Selfheal: 1.5%;
The bighead atractylodes rhizome: 0.2%;
Motherwort: 0.8%;
The leaf of bamboo: 0.5%;
The root of kudzu vine: 1.5%;
Polygala root: 0.5%;
Radix bupleuri: 1.5%;
Windproof: 1%;
Lucid asparagus: 1.5%;
CedarLeaves: 0.5%;
Monkshood: 1.5%;
Glutinous rehmannia: 0.5%;
Matrimony vine: 1.5%;
Fructus Aurantii: 0.5%;
Ginkgo leaf: 1.5%;
Purple perilla: 0.5%;
Mulberry leaf: 1.5%;
Thyme: 0.5%;
Poria cocos: 0.8%;
Chinese honey locust: 0.2%;
Marigold: 1.5%;
Balloonflower root: 0.5%;
Radix Isatidis: 1.5%;
Saline cistanche: 0.2%;
The fleece-flower root: 1.5%;
Realgar: 0.1%;
Active carbon: 3.0%;
Pyroxene chip: 1.0%;
Paris white or zeolite powder: 1%;
Timber or straw or fiber: surplus.
Further, in the present embodiment, the prolong life preparation method of composite plate of the above-mentioned legendary god of farming is as follows:
(1) above-mentioned wood chip or straw strand are cut into chip or thin slice, press proportion relation, all the other raw material strands are cut into chip or are ground into powder, add wood chip or straw strand to and be cut in chip or the thin slice, stir, place 3h;
Further, in step (1), in outer 1, screen described zeolite powder or Paris white with molecular sieve, and compacting;
(2) in the above-mentioned raw materials mixture, add described biogum mixture, after stirring, the gained mixed material is placed on the cloth stockline, heat and pressurized treatments;
(3) reach 150 ℃, when pressure conditions reaches 3Mpa, above-mentioned mixed material be pressed into the described legendary god of farming composite plate of prolonging life when temperature conditions.
Embodiment three
Different with the foregoing description is that in the present embodiment, the composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content:
Mother chrysanthemum: 9.0%;
Argy wormwood: 9.0%;
Peppermint: 7.0%;
Fragrant camphor tree bits and/or leaf: 8.0%;
Rhizoma atractylodis: 1.0%;
The stem of noble dendrobium: 0.5%;
Calamus: 2.0%;
Wrinkled giant hyssop: 1.0%;
The bark of official magnolia: 1.0%;
Radix Glycyrrhizae: 1.0%;
Lavender: 1.0%;
Lemongrass: 1.0%;
Rosewood bits: 1.0%;
Santal: 0.2%;
Glossy ganoderma: 1.5%;
Cloves: 0.7%;
The banksia rose: 1.5%;
Radix Codonopsis: 1.0%;
Sealwort: 1.2%;
Cortex Periplocae: 1.0%;
Pawpaw: 2.0%;
The bletilla striata: 0.4%;
Cassia twig: 1.0%;
Oriental wormwood: 1.0%;
Fennel seeds: 0.8%;
The Radix Astragali: 1.0%;
Ligusticum wallichii: 0.7%;
Chinese prickly ash: 1.0%;
Lotus leaf: 1.0%;
Radix Angelicae Sinensis: 1.0%;
Corydalis tuber: 1.0%;
The wind-weed: 1.0%;
Rheum officinale: 1.0%;
Folium panacis japonici cum caule and/or palpus: 1.5%;
Nutmeg: 1.0%;
Rhizoma Gastrodiae: 1.0%;
The root of Dahurain angelica: 1.0%;
Safflower: 0.3%;
Rose: 0.4%;
Jasmine: 1.0%;
Honeysuckle: 0.3%;
The root of bidentate achyranthes: 1.0%;
The bark of eucommia: 0.5%;
Pseudo-ginseng: 1.0%;
Husky ginger: 0.4%;
Selfheal: 1.0%;
The bighead atractylodes rhizome: 0.4%;
Motherwort: 0.4%;
The leaf of bamboo: 1.0%;
The root of kudzu vine: 1.0%;
Polygala root: 1.0%;
Radix bupleuri: 1.0%;
Windproof: 2.0%;
Lucid asparagus: 1.0%;
CedarLeaves: 1.0%;
Monkshood: 1.0%;
Glutinous rehmannia: 1.0%;
Matrimony vine: 1.0%;
Fructus Aurantii: 1.0%;
Ginkgo leaf: 1.0%;
Purple perilla: 1.0%;
Mulberry leaf: 1.0%;
Thyme: 1.0%;
Poria cocos: 0.5%;
Chinese honey locust: 0.5%;
Marigold: 1.0%;
Balloonflower root: 1.0%;
Radix Isatidis: 1.0%;
Saline cistanche: 0.5%;
The fleece-flower root: 1.2%;
Realgar: 0.3%;
Active carbon: 2.0%;
Pyroxene chip: 3.0%;
Paris white or zeolite powder: 3.0%;
Timber or straw or fiber: surplus.
Further, in the present embodiment, the prolong life preparation method of composite plate of the above-mentioned legendary god of farming is as follows:
(1) above-mentioned wood chip or straw strand are cut into chip or thin slice, press proportion relation, all the other raw material strands are cut into chip or are ground into powder, add wood chip or straw strand to and be cut in chip or the thin slice, stir, place 1h;
Further, in step (1), in outer 1, screen described zeolite powder or Paris white with molecular sieve, and compacting;
(2) in the above-mentioned raw materials mixture, add described biogum mixture, after stirring, the gained mixed material is placed on the cloth stockline, heat and pressurized treatments;
(3) reach 110 ℃, when pressure conditions reaches 7Mpa, above-mentioned mixed material be pressed into the described legendary god of farming composite plate of prolonging life when temperature conditions.
Embodiment four
Different with the foregoing description is, in the present embodiment, based on the above-mentioned legendary god of farming composite plate of prolonging life, the prolong life preparation method of composite plate of the legendary god of farming is as follows: in each raw material, press proportion relation, timber or straw or fiber are pulverized skeining be cut into chip or thin slice, will be boiled into concoction except that all the other raw materials timber or straw or the fiber simultaneously; Concoction is sprayed at described chip or thin slice, concoction is soaked in chip or the thin slice, and be equipped with biogum mixture, compression moulding.
Embodiment five
Different with the foregoing description is, in the present embodiment, based on the above-mentioned legendary god of farming composite plate of prolonging life, the prolong life preparation method of composite plate of the legendary god of farming is as follows: in each raw material, press proportion relation, timber or straw or fiber are pressed into artificial plate; In seal cavity, will be except that all the other raw materials timber or straw or the fiber, distill or boil, utilize distillation gas or steam to fumigate described artificial plate, make distillation gas or vapor permeates inside to artificial plate.
In the foregoing description one to embodiment five, in the legendary god of farming prolongs life composite plate, transform formulated Chinese herbal medicine adding ingredient and active carbon according to classic health secret recipe, medicinal herb components wherein in use, constantly volatilize fragrant camphor tree alcohol to the human body beneficial, menthol, alantol (being chrysol), chrysanthanone (being chrysanthenone), australene, camphor, borneol, lauro lene, saponin, flavones, beneficiating ingredients such as malic acid, these compositions not only can make the light delicate fragrance of indoor long-term maintenance, clearing and activating the channels and collaterals, clearing heat and moistening dryness, warming YANG and invigorating QI, replenishing the vital essence and removing heat, the moistening lung nourshing kidney, regulate the flow of vital energy and set upright, use the legendary god of farming to prolong life composite plate as construction wall or Furniture panel, can not only make indoor unique delicate fragrance that gives out, mosquito expelling, remove the bacterium that disappears, and the components of biomass that slowly discharges, also have dirty the exorcising evil spirits of dispelling, restore menstrual flow and invigorate blood circulation, the opposing oxidation, the special efficacy that benefit gas is prolonged life, can suppress the breeding of indoor bacteria, even kill bacteria; For example, rhizoma atractylodis can expelling wind and clearing away cold, have one's ideas straightened out; The root of Dahurain angelica can expel pathogenic wind from the body surface, dampness elimination is sensible; Cloves energy fragrance is regulated the flow of vital energy, warming middle energizer to descend adverse-rising qi.
In addition, in the foregoing description one to embodiment five, the legendary god of farming prolong life composite plate bring into play the volatilization wet goods that sends evaporate into part also have dispel dirtyly exorcise evil spirits, regulate the flow of vital energy, dry in the temperature loose tremble with fear, calm the nerves have one's ideas straightened out, the effect of multiple beneficial health such as clearing and activating the channels and collaterals clearing heat and moistening dryness, can prevent effectively that flu, pulmonary tuberculosis, bird flu etc. are by airborne epidemic disease.
In sum, the legendary god of farming of the various embodiments of the present invention composite plate and preparation method thereof of prolonging life, wherein, this legendary god of farming composite plate of prolonging life comprises the composite plate body, and pastes the aluminium plating membrane at this this external surface of composite plate; This composite plate body is bonded by the biogum mixture by the raw material of following component and weight percent content: mother chrysanthemum: 7-11%; Argy wormwood: 7-11%; Peppermint: 5-9%; Fragrant camphor tree bits and/or leaf: 6-10%; Rhizoma atractylodis: 0.5-1.5%; The stem of noble dendrobium: 0.2-0.8%; Calamus: 1-3%; Wrinkled giant hyssop: 0.5-1.5%; The bark of official magnolia: 0.5-1.5%; Radix Glycyrrhizae: 0.5-1.5%; Lavender: 0.5-1.5%; Lemongrass: 0.5-1.5%; Rosewood bits: 0.5-1.5%; Santal: 0.1-0.3%; Glossy ganoderma: 1.0-2.0%; Cloves: 0.4-1.0%; The banksia rose: 1.0-2.0%; Radix Codonopsis: 0.5-1.5%; Sealwort: 0.9-1.5%; Cortex Periplocae: 0.5-1.5%; Pawpaw: 1-3%; The bletilla striata: 0.2-0.6%; Cassia twig: 0.5-1.5%; Oriental wormwood: 0.5-1.5%; Fennel seeds: 0.5-1.1%; The Radix Astragali: 0.5-1.5%; Ligusticum wallichii: 0.4-1.0%; Chinese prickly ash: 0.5-1.5%; Lotus leaf: 0.5-1.5%; Radix Angelicae Sinensis: 0.5-1.5%; Corydalis tuber: 0.5-1.5%; The wind-weed: 0.5-1.5%; Rheum officinale: 0.5-1.5%; Folium panacis japonici cum caule and/or palpus: 1.0-2.0%; Nutmeg: 0.5-1.0%; Rhizoma Gastrodiae: 0.5-1.5%; The root of Dahurain angelica: 0.5-1.5%; Safflower: 0.1-0.5%; Rose: 0.1-0.7%; Jasmine: 0.5-1.5%; Honeysuckle: 0.1-0.5%; The root of bidentate achyranthes: 0.5-1.5%; The bark of eucommia: 0.2-0.8%; Pseudo-ginseng: 0.5-1.5%; Husky ginger: 0.2-0.8%; Selfheal: 0.5-1.5%; The bighead atractylodes rhizome: 0.2-0.8%; Motherwort: 0.2-0.8%; The leaf of bamboo: 0.5-1.5%; The root of kudzu vine: 0.5-1.5%; Polygala root: 0.5-1.5%; Radix bupleuri: 0.5-1.5%; Windproof: 1-3%; Lucid asparagus: 0.5-1.5%; CedarLeaves: 0.5-1.5%; Monkshood: 0.5-1.5%; Glutinous rehmannia: 0.5-1.5%; Matrimony vine: 0.5-1.5%; Fructus Aurantii: 0.5-1.5%; Ginkgo leaf: 0.5-1.5%; Purple perilla: 0.5-1.5%; Mulberry leaf: 0.5-1.5%; Thyme: 0.5-1.5%; Poria cocos: 0.2-0.8%; Chinese honey locust: 0.2-0.8%; Marigold: 0.5-1.5%; Balloonflower root: 0.5-1.5%; Radix Isatidis: 0.5-1.5%; Saline cistanche: 0.2-0.8%; The fleece-flower root: 0.9-1.5%; Realgar: 0.1-0.5%; Active carbon: 1.0-3.0%; Pyroxene chip: 1.0-5.0%; Paris white or zeolite powder: 1-5%; Timber or straw or fiber: surplus; In this legendary god of farming composite plate of prolonging life, owing to be doped with the Chinese herbal medicine useful, can overcome the poor and defect of high cost of health care in the prior art, with the advantage that realizes that health care is good and cost is low to health.
It should be noted that at last: the above only is the preferred embodiments of the present invention, be not limited to the present invention, although the present invention is had been described in detail with reference to previous embodiment, for a person skilled in the art, it still can be made amendment to the technical scheme that aforementioned each embodiment put down in writing, and perhaps part technical characterictic wherein is equal to replacement.Within the spirit and principles in the present invention all, any modification of being done, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (7)
1. legendary god of farming composite plate of prolonging life is characterized in that, comprises the composite plate body, and pastes the aluminium plating membrane at described this external surface of composite plate;
Described composite plate body is composed by environmental protection by the raw material of following component and weight percent content:
Mother chrysanthemum: 7-11%;
Argy wormwood: 7-11%;
Peppermint: 5-9%;
Fragrant camphor tree bits and/or leaf: 6-10%;
Rhizoma atractylodis: 0.5-1.5%;
The stem of noble dendrobium: 0.2-0.8%;
Calamus: 1-3%;
Wrinkled giant hyssop: 0.5-1.5%;
The bark of official magnolia: 0.5-1.5%;
Radix Glycyrrhizae: 0.5-1.5%;
Lavender: 0.5-1.5%;
Lemongrass: 0.5-1.5%;
Rosewood bits: 0.5-1.5%;
Santal: 0.1-0.3%;
Glossy ganoderma: 1.0-2.0%;
Cloves: 0.4-1.0%;
The banksia rose: 1.0-2.0%;
Radix Codonopsis: 0.5-1.5%;
Sealwort: 0.9-1.5%;
Cortex Periplocae: 0.5-1.5%;
Pawpaw: 1-3%;
The bletilla striata: 0.2-0.6%;
Cassia twig: 0.5-1.5%;
Oriental wormwood: 0.5-1.5%;
Fennel seeds: 0.5-1.1%;
The Radix Astragali: 0.5-1.5%;
Ligusticum wallichii: 0.4-1.0%;
Chinese prickly ash: 0.5-1.5%;
Lotus leaf: 0.5-1.5%;
Radix Angelicae Sinensis: 0.5-1.5%;
Corydalis tuber: 0.5-1.5%;
The wind-weed: 0.5-1.5%;
Rheum officinale: 0.5-1.5%;
Folium panacis japonici cum caule and/or palpus: 1.0-2.0%;
Nutmeg: 0.5-1.0%;
Rhizoma Gastrodiae: 0.5-1.5%;
The root of Dahurain angelica: 0.5-1.5%;
Safflower: 0.1-0.5%;
Rose: 0.1-0.7%;
Jasmine: 0.5-1.5%;
Honeysuckle: 0.1-0.5%;
The root of bidentate achyranthes: 0.5-1.5%;
The bark of eucommia: 0.2-0.8%;
Pseudo-ginseng: 0.5-1.5%;
Husky ginger: 0.2-0.8%;
Selfheal: 0.5-1.5%;
The bighead atractylodes rhizome: 0.2-0.8%;
Motherwort: 0.2-0.8%;
The leaf of bamboo: 0.5-1.5%;
The root of kudzu vine: 0.5-1.5%;
Polygala root: 0.5-1.5%;
Radix bupleuri: 0.5-1.5%;
Windproof: 1-3%;
Lucid asparagus: 0.5-1.5%;
CedarLeaves: 0.5-1.5%;
Monkshood: 0.5-1.5%;
Glutinous rehmannia: 0.5-1.5%;
Matrimony vine: 0.5-1.5%;
Fructus Aurantii: 0.5-1.5%;
Ginkgo leaf: 0.5-1.5%;
Purple perilla: 0.5-1.5%;
Mulberry leaf: 0.5-1.5%;
Thyme: 0.5-1.5%;
Poria cocos: 0.2-0.8%;
Chinese honey locust: 0.2-0.8%;
Marigold: 0.5-1.5%;
Balloonflower root: 0.5-1.5%;
Radix Isatidis: 0.5-1.5%;
Saline cistanche: 0.2-0.8%;
The fleece-flower root: 0.9-1.5%;
Realgar: 0.1-0.5%;
Active carbon: 1.0-3.0%;
Pyroxene chip: 1.0-5.0%;
Paris white or zeolite powder: 1-5%;
Timber or straw or fiber: surplus.
2. the legendary god of farming according to claim 1 composite plate of prolonging life is characterized in that described biogum mixture comprises gelatin, modified starch, protein adhesive and frankincense.
3. the legendary god of farming according to claim 1 and 2 composite plate of prolonging life is characterized in that, described composite plate body comprises internal layer and the skin that order from inside to outside is provided with, and described internal layer and outer field density is increase gradually from inside to outside; Described peppermint and lavender are entrained in described internal layer, and described glutinous rehmannia and genseng are entrained in described skin.
4. the legendary god of farming according to claim 3 composite plate of prolonging life is characterized in that, the prolong life preparation method of composite plate of the described legendary god of farming is as follows:
(1) described wood chip or straw strand are cut into chip or thin slice, press proportion relation, all the other raw material strands are cut into chip or are ground into powder, add described wood chip or straw strand to and be cut in chip or the thin slice, stir, place 1-3h;
(2) in the above-mentioned raw materials mixture, add described biogum mixture, after stirring, the gained mixed material is placed on the cloth stockline, heat and pressurized treatments;
(3) reach 110-150 ℃, when pressure conditions reaches 3-7Mpa, above-mentioned mixed material be pressed into the described legendary god of farming composite plate of prolonging life when temperature conditions.
5. the legendary god of farming according to claim 4 composite plate of prolonging life is characterized in that, and is in step (1), further comprising the steps of:
In described skin, screen described zeolite powder or Paris white with molecular sieve, and compacting.
6. the legendary god of farming according to claim 3 composite plate of prolonging life is characterized in that, the prolong life preparation method of composite plate of the described legendary god of farming is as follows:
In each raw material, press proportion relation, timber or straw or fiber are pulverized skeining be cut into chip or thin slice, will be boiled into concoction except that all the other raw materials timber or straw or the fiber simultaneously;
Described concoction is sprayed at described chip or thin slice, described concoction is soaked in described chip or the thin slice, and be equipped with described biogum mixture, compression moulding.
7. the legendary god of farming according to claim 3 composite plate of prolonging life is characterized in that, the prolong life preparation method of composite plate of the described legendary god of farming is as follows:
In each raw material, press proportion relation, timber or straw or fiber are pressed into artificial plate;
In seal cavity, will be except that all the other raw materials timber or straw or the fiber, distill or boil, utilize distillation gas or steam to fumigate described artificial plate, make described distillation gas or vapor permeates inside to artificial plate.