CN102206413A - 具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法 - Google Patents

具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法 Download PDF

Info

Publication number
CN102206413A
CN102206413A CN 201110137074 CN201110137074A CN102206413A CN 102206413 A CN102206413 A CN 102206413A CN 201110137074 CN201110137074 CN 201110137074 CN 201110137074 A CN201110137074 A CN 201110137074A CN 102206413 A CN102206413 A CN 102206413A
Authority
CN
China
Prior art keywords
composite material
conduction
electro
plastic
magnetic screen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110137074
Other languages
English (en)
Other versions
CN102206413B (zh
Inventor
曾斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN SHUNDE DISTRICT GAOYI NEW PLASTIC Co Ltd
Original Assignee
FOSHAN SHUNDE DISTRICT GAOYI NEW PLASTIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN SHUNDE DISTRICT GAOYI NEW PLASTIC Co Ltd filed Critical FOSHAN SHUNDE DISTRICT GAOYI NEW PLASTIC Co Ltd
Priority to CN 201110137074 priority Critical patent/CN102206413B/zh
Publication of CN102206413A publication Critical patent/CN102206413A/zh
Application granted granted Critical
Publication of CN102206413B publication Critical patent/CN102206413B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种具有导电和电磁屏蔽功能的塑料基复合材料，其是由以下质量份的原料组成：40-80份的塑料基体、1-10份的表面改性的高效导电剂、10-40份的偏铁酸亚铁、5-10份的相容剂、0.5-1份的抗氧剂。本发明的产品，具有良好的导电性能、电磁屏蔽性能和力学性能，可以广泛用于电子消费品、远程监控/通讯、军事、野外/室内供电领域。

Description

具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法
技术领域
本发明涉及一种具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法。
背景技术
随着电子工业的发展,各种家电、办公电器、仪器设备等电子产品得到广泛的普及和应用,给人们带来便利的同时也释放出大量的电磁辐射,危害着人们的健康。
为此，人们不断寻找具有较好电磁屏蔽性能的复合材料，以塑料为基体的具有导电与电磁屏蔽功能的复合材料由于具有较小的密度，较低的成本逐渐受到社会的关注，人们寻求各种方法对塑料进行改性，如向塑料基体中添加导电金属粉末、导电云母粉等等来获得相应功能的复合材料，然而，由于导电粒子与塑料基体的相容性、导电粒子的分散性、以及加工条件等等问题，最后得到的复合材料的屏蔽性能、力学性能等往往不佳。
发明内容
本发明的目的是提供一种具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法。
本发明所采取的技术方案是：
一种具有导电和电磁屏蔽功能的塑料基复合材料，其是由以下质量份的原料组成：40-80份的塑料基体、1-10份的表面改性的高效导电剂、10-40份的偏铁酸亚铁、5-10份的相容剂、0.5-1份的抗氧剂。
所述的塑料基体为PA6、PA66、PC、ABS、PS中的一种。
所述的相容剂为POE-g-MAH、SEBS-g-MAH、SMA中的一种。
所述的抗氧剂为1010、1135、168中的至少一种。
一种具有导电和电磁屏蔽功能的塑料基复合材料的制备方法，包括以下步骤：
1）将塑料基体、相容剂、偏铁酸亚铁混合均匀；
2）将步骤1）所得到的物料与表面改性的高效导电剂、抗氧剂混合均匀；
3）将步骤2）得到的物料在挤出机中挤出。
本发明的有益效果是：本发明的产品，具有良好的导电性能、电磁屏蔽性能和力学性能，可以广泛用于电子消费品、远程监控/通讯、军事、野外/室内供电领域。
具体实施方式
一种具有导电和电磁屏蔽功能的塑料基复合材料的制备方法，包括以下步骤：
1）将塑料基体、相容剂、偏铁酸亚铁置于混合机中混合2-3分钟；
2）将步骤1）所得到的物料与表面改性的高效导电剂、抗氧剂置于混合机中混合2-3分钟；
3）将步骤2）得到的物料在同向双螺杆挤出机中挤出，挤出机的螺杆长径比为1:30-40。
用以下实施例的配方进行制备时，实施例1-6中，挤出机的温度为200-250℃，实施例7中，挤出机的温度为150-200℃，实施例8中，挤出机的温度为250-300℃。
SEBS-g-MAH的型号为FG1901、SMA型号为AT300、POE-g-MAH为自制（通过原位熔融接枝法制备，制备技术为本领域的公知技术），最后测得MAH的接枝率为2.5%。
下面结合具体实施例对本发明的配方做进一步的说明：
实施例1：
具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表1：
表1：具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PA6 45
偏铁酸亚铁 40
表面改性的高效导电剂 10
POE-g-MAH 5
抗氧剂1010 0.5
实施例2：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表2：
表2：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PA6 55
偏铁酸亚铁 30
表面改性的高效导电剂 10
POE-g-MAH 5
抗氧剂1010 0.5
实施例3：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表3：
表3：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PA6 50
偏铁酸亚铁 40
表面改性的高效导电剂 5
POE-g-MAH 5
抗氧剂1010 0.5
实施例4：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表4：
表4：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PA6 55
偏铁酸亚铁 35
表面改性的高效导电剂 5
POE-g-MAH 5
抗氧剂168 0.5
实施例5：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表5：
表5：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PA6 58
偏铁酸亚铁 35
表面改性的高效导电剂 2
POE-g-MAH 5
抗氧剂1010 0.5
实施例6：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表6：
表6：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
ABS 80
偏铁酸亚铁 40
表面改性的高效导电剂 10
SEBS-g-MAH 10
抗氧剂168 0.9
实施例7：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表7：
表7：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PS 40
偏铁酸亚铁 10
表面改性的高效导电剂 1
SEBS-g-MAH 6
抗氧剂1010 0.6
实施例8：
一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成如下表8：
表8：一种具有导电和电磁屏蔽功能的塑料基复合材料的配方组成
原料 质量份
PC 60
偏铁酸亚铁 20
表面改性的高效导电剂 8
SMA 8
抗氧剂1135 0.7
本发明中，表面改性的高效导电剂是通过以下方法制得的：将石墨烯（型号：GS-1）与占石墨烯质量1%的钛酸酯偶联剂置于高速混合机中混合2-3分钟即可。
由实施例1-5制备的复合材料的性能如下表9：
表9：本发明制备的具有导电和电磁屏蔽功能的塑料基复合材料的性能
性能 单位 实施例1 实施例2 实施例3 实施例4 实施例5
拉伸强度 Mpa 70 65 68 67 64
弯曲模量 Mpa 4200 4160 3730 3540 3250
简支梁缺口冲击 KJ/m2 6.5 7.3 7.8 8.3 8.8
表面电阻 Ω ＜102 ＜102 ＜102 ＜102 ＜102
电磁屏蔽效率 dB 60～90 60～90 60～90 60～90 60～90
本发明的产品，具有良好的导电性能、电磁屏蔽性能和力学性能，同时，该复合材料具有耐用、比重轻、可成型复杂结构的产品等特点，可以广泛用于电子消费品、远程监控/通讯、军事、野外/室内供电领域。完全符合国家建设资源节约型、环境友好型社会的战略部署。

Claims (5)

1.一种具有导电和电磁屏蔽功能的塑料基复合材料，其特征在于：其是由以下质量份的原料组成：40-80份的塑料基体、1-10份的表面改性的高效导电剂、10-40份的偏铁酸亚铁、5-10份的相容剂、0.5-1份的抗氧剂。
2.根据权利要求1所述的一种具有导电和电磁屏蔽功能的塑料基复合材料，其特征在于：所述的塑料基体为PA6、PA66、PC、ABS、PS中的一种。
3.根据权利要求1所述的一种具有导电和电磁屏蔽功能的塑料基复合材料，其特征在于：所述的相容剂为POE-g-MAH、SEBS-g-MAH、SMA中的一种。
4.根据权利要求1所述的一种具有导电和电磁屏蔽功能的塑料基复合材料，其特征在于：所述的抗氧剂为1010、1135、168中的至少一种。
5.权利要求1所述的一种具有导电和电磁屏蔽功能的塑料基复合材料的制备方法，其特征在于：包括以下步骤：
1）将塑料基体、相容剂、偏铁酸亚铁混合均匀；
2）将步骤1）所得到的物料与表面改性的高效导电剂、抗氧剂混合均匀；
3）将步骤2）得到的物料在挤出机中挤出。
CN 201110137074 2011-05-25 2011-05-25 具有导电和电磁屏蔽功能的塑料基复合材料及其制备方法 Expired - Fee Related CN102206413B (zh)