CN102199002B - Jade crystal glass ceramic - Google Patents

Jade crystal glass ceramic Download PDF

Info

Publication number
CN102199002B
CN102199002B CN 201110026125 CN201110026125A CN102199002B CN 102199002 B CN102199002 B CN 102199002B CN 201110026125 CN201110026125 CN 201110026125 CN 201110026125 A CN201110026125 A CN 201110026125A CN 102199002 B CN102199002 B CN 102199002B
Authority
CN
China
Prior art keywords
percent
crystal glass
glass ceramic
jade
product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110026125
Other languages
Chinese (zh)
Other versions
CN102199002A (en
Inventor
黄再元
黄晓冬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG SANYUAN MICROCRYSTAL GLASS TECHNOLOGY Co Ltd
Original Assignee
GUANGDONG SANYUAN MICROCRYSTAL GLASS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG SANYUAN MICROCRYSTAL GLASS TECHNOLOGY Co Ltd filed Critical GUANGDONG SANYUAN MICROCRYSTAL GLASS TECHNOLOGY Co Ltd
Priority to CN 201110026125 priority Critical patent/CN102199002B/en
Publication of CN102199002A publication Critical patent/CN102199002A/en
Application granted granted Critical
Publication of CN102199002B publication Critical patent/CN102199002B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses jade crystal glass ceramic, which is characterized by comprising the following components in percentage by weight: 62 to 68 percent of SiO2, 2 to 4 percent of Al2O3, 11 to 15 percent of B2O3, 6.5 to 8.5 percent of Na2O, 0.4 to 1 percent of K2O, 3 to 5 percent of CaO, 0.05 to 0.3 percent of BaO, 0.5 to 2 percent of ZnO, 0.01 to 0.05 percent of Fe2O3, 3 to 6 percent of F2, 0.1 to 1 percent of P2O5 and 0.1 to 0.5 percent of CeO2. The jade crystal glass ceramic has crystal clear appearance and color, is as white as jade and has the semi-transparent characteristic; and compared with the conventional milky white glass ceramic, the jade crystal glass ceramic can better attract customers, is easy to produce, is environment-friendly, and has low cost.

Description

Beautiful crystal glass pottery
Technical field
The present invention relates to the glass-ceramic field, specifically a kind of beautiful crystal glass pottery.
Background technology
Glass-ceramic has another name called for " opaque glass ", " devitrified glass ", is smelted into parent glass take quartz as main raw, processes through overmolding and crystallization, makes device shape and uses functional similarity in the product (such as cup, dish, bowl etc.) of pottery.
Conventional glass-ceramic all is oyster white or edematus, because product color is dull, is difficult to satisfy the modern consumption crowd uses function and outward appearance art to product double requirements.
Summary of the invention
The objective of the invention is to solve the problem of glass-ceramic product color dullness, a kind of beautiful crystal glass pottery is provided.
Beautiful crystal glass pottery of the present invention is characterized in that, contains by weight percentage following composition: SiO 262~68%, Al 2O 32~4%, B 2O 311~15%, Na 2O6.5~8.5%, K 2O0.4~1%, CaO3~5%, BaO0.05~0.3%, ZnO0.5~2%, Fe 2O 30.01~0.05%, F 23~6%, P 2O 60.1~1%, CeO 20.1~0.5%.
Above-mentioned beautiful crystal glass pottery, preferably made by following compositions in weight percentage: quartz sand 40~60%, aluminum oxide 1~3%, calcite 5~8%, Sodium Silicofluoride 4~7%, BORAX PENTAHYDRATE-99.9 MIN 14~21%, boric acid 4~7%, zinc oxide 0.5~2%, saltpetre 0.5~2%, primary ammonium phosphate 0.5~2%, cerium oxide 0.1~1%, useless opaque glass 5~15%.
For ease of understanding the present invention, the production method of simple declaration product of the present invention.Produce the method for beautiful crystal glass pottery with said components, comprise following production stage:
(1), component is mixed in proportion, make the melting material;
(2), the melting material is dropped into from smelting furnace top, heated by electrodes to 1380 in stove~1450 ℃ become melting liquid, are delivered to mould from the feeder system of smelting furnace and carry out moulding, and the discharge nozzle temperature remains on 1150~1250 ℃;
(3), mould in moulding process, temperature remains on 500~900 ℃;
(4), after depanning, namely enter tunnel furnace through the product of moulding and anneal, annealing time is 4~4.5 hours, annealing temperature is 250~580 ℃, makes product of the present invention.
Beautiful crystal glass pottery of the present invention, appearance luster is sparkling and crystal-clear, whitening is like beautiful, and semi-transparent characteristics are arranged, and than existing opal glass pottery, more attracts the human consumer, and produce easy, pollution is little, cost is low.
Description of drawings
Fig. 1 is the product picture that the embodiment of the invention is produced.
Embodiment
The present invention will be described in detail to reach by the following examples Comparative Examples.
Embodiment:
(1) prepares by weight percentage following component: quartz sand 50%, aluminum oxide 1.63%, calcite 6.7%, Sodium Silicofluoride 5.91%, BORAX PENTAHYDRATE-99.9 MIN 17.8%, boric acid 6.09%, zinc oxide 0.88%, saltpetre 0.84%, primary ammonium phosphate 0.81%, cerium oxide 0.34%, useless opaque glass 9.0%;
(2) component is mixed in proportion, make the melting material;
(3) the melting material is dropped into from smelting furnace top, heated by electrodes to 1400 ℃ becomes melting liquid in stove, is delivered to mould from the discharge nozzle of smelting furnace bottom and carries out moulding, and the discharge nozzle temperature remains on 1200 ℃;
(4) mould is in moulding process, and temperature remains on 700 ℃;
(5) namely enter tunnel furnace through the product of moulding after depanning and anneal, annealing time is 4 hours, and annealing temperature is 400 ℃, makes the present invention's product shown in Figure 1.
After testing, the product of making contains following composition: SiO by weight percentage 265.01%, Al 2O 33.10%, B 2O 313.40%, Na 2O7.45%, K 2O0.60%, CaO4.10%, BaO0.18%, ZnO1.0%, Fe 2O 30.01%, F 24.40%, P 2O 50.50%, CeO 20.25%.
Comparative Examples 1: different from embodiment is, in step (1), Sodium Silicofluoride is increased to 10%, and the product of making is creamy white.After testing, contained Na in the product of making 2O increases to 9.5%, contained F 2Increase to 6.6%.
Comparative Examples 2: different from embodiment is in step (1), BORAX PENTAHYDRATE-99.9 MIN to be reduced to 8%, the product slickness reduction of making, and product generation nature embrittlement in the week after making.After testing, contained B in the product of making 2O 3Be reduced to 5.8%.

Claims (2)

1. beautiful crystal glass pottery is characterized in that, contains by weight percentage following composition: SiO 262~68%, Al 2O 32~4%, B 2O 311~15%, Na 2O6.5~8.5%, K 2O0.4~1%, CaO3~5%, BaO0.05~0.3%, ZnO0.5~2%, Fe 2O 30.01~0.05%, F 23~6%, P 2O 50.1~1%, CeO 20.1~0.5%.
2. the described beautiful crystal glass pottery of claim 1 is characterized in that, is made by following compositions in weight percentage: quartz sand 40~60%, aluminum oxide 1~3%, calcite 5~8%, Sodium Silicofluoride 4~7%, BORAX PENTAHYDRATE-99.9 MIN 14~21%, boric acid 4~7%, zinc oxide 0.5~2%, saltpetre 0.5~2%, primary ammonium phosphate 0.5~2%, cerium oxide 0.1~1%, useless opaque glass 5~15%.
CN 201110026125 2011-01-22 2011-01-22 Jade crystal glass ceramic Active CN102199002B (en)