CN102180640A - 一种保温专用的粘接材料及其使用方法 - Google Patents

一种保温专用的粘接材料及其使用方法 Download PDF

Info

Publication number
CN102180640A
CN102180640A CN 201110072324 CN201110072324A CN102180640A CN 102180640 A CN102180640 A CN 102180640A CN 201110072324 CN201110072324 CN 201110072324 CN 201110072324 A CN201110072324 A CN 201110072324A CN 102180640 A CN102180640 A CN 102180640A
Authority
CN
China
Prior art keywords
water
parts
special
adhesives
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110072324
Other languages
English (en)
Other versions
CN102180640B (zh
Inventor
朱光皓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Lianjie Biotechnology Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110072324 priority Critical patent/CN102180640B/zh
Publication of CN102180640A publication Critical patent/CN102180640A/zh
Application granted granted Critical
Publication of CN102180640B publication Critical patent/CN102180640B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种保温专用的粘接材料及其使用方法，通过采用钠水玻璃与膏状甲基硅醇钾钠对生淀粉进一步改性，通过长时间的试验证明其粘结效果更佳，导热性更低，防水效果更好，适用于作为防火保温材料的粘结剂。

Description

一种保温专用的粘接材料及其使用方法
技术领域
本发明涉及建筑保温和工业保温领域，尤其涉及一种保温专用的粘接材料及其使用方法。
背景技术
目前市场普遍应用有机保温材料（如聚苯乙烯泡沫板，发泡聚氨酯）主要来源于石油，虽然具有较低的吸水率和导热性能，但易燃不防火，且价格昂贵。南方建筑常用的以水泥为粘结剂的无机保温隔热材料（如泡沫水泥材料，水泥基珍珠岩材料，水泥基聚苯颗粒腻子），吸水率和导热系数较高，节能效果不好。其它无机材料（如泡沫玻璃，漂珠）生产的保温板制作工艺复杂，吸水，强度低，脆性大，施工难度大，造价高，很难满足市场需要。
因此，现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足，本发明的目的在于提供一种保温专用的粘接材料及其使用方法，旨在解决现有有机保温材料防火性能差、无机粘结剂合成的保温材料防水、保温性能差及脆性大等问题。
本发明的技术方案如下：
一种保温专用的粘接材料，其中，所述保温专用的粘接材料由膏状甲基硅醇钾钠、生淀粉、钠水玻璃、水组成；其中各组分的重量份为，膏状甲基硅醇钾钠0.5～1.5份、生淀粉4～8份、钠水玻璃6～12份、水2～6份。
一种上述的保温专用的粘接材料的使用方法，其中，包括以下步骤：
S100、按比例将膏状甲基硅醇钾钠、生淀粉、钠水玻璃、水进行机械混合，制成粘稠状物料待用；
S200、将粘稠状物料加水加热，在100~120℃熬5~30分钟成糊状。
所述保温专用的粘接材料的使用方法，其中，在S200步骤中，加水的量为粘稠状物料重量的7～13倍。
有益效果：本发明所提供的保温专用的粘接材料的粘结效果佳、导热性低、防水效果好、防火性能超群，适用于作为防火保温材料的粘结剂，而且综合成本造价低。
具体实施方式
本发明提供一种保温专用的粘接材料及其制备方法，为使本发明的目的、技术方案及效果更加清楚、明确，以下对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
在水泥发明之前，我国大部分古建筑均采用糯米粉或米粉（生淀粉）煮熟与石灰相混制成粘结材料砌墙，历经数千年仍保留完好，本发明采用钠水玻璃与膏状甲基硅醇钾钠对生淀粉进一步改性，通过长时间的试验证明其粘结效果更佳，导热性更低，防水效果更好，适用于作为防火保温材料的粘结剂。
将膏状甲基硅醇钾钠0.5～1.5份、生淀粉4～8份、钠水玻璃6～12份、水2～6份（重量份数）经机械混合，制成粘稠状，使用时，在粘稠状物料中加入粘稠状物料重量的7～13倍的水，加热100~120℃熬5~30分钟成糊状粘结其它无机物料或物件，经脱水固化后粘结效果极好。生淀粉和钠水玻璃相混经加热处理后粘结强度高，遇明火不燃烧，烟气少，有良好的阻燃性，并有一定韧性，膏状甲基硅醇钾钠吸附于物料粒子表面经脱水处理后有极好而稳定的疏水性能，可使型材不吸水吸潮。本发明用作无机物料粘结，有韧性、防火性能超群。
本发明所提供的保温材料采用的物料来源广泛，价格低廉，制作工艺简单，样品粘结强度检验结果为2.5MPa，综合成本造价约为4元/kg。通过采用钠水玻璃与膏状甲基硅醇钾钠对生淀粉进一步改性，通过长时间的试验证明其粘结效果更佳，导热性更低，防水效果更好，适用于作为防火保温材料的粘结剂。
更具体的，可按照下表准备原料（重量份），按照下述方法进行制备，得到膏状的成品。
实例一
膏状甲基硅醇钾钠0.5份、生淀粉8份、钠水玻璃6份、水6份经机械混合，制成粘稠状，使用时，在粘稠状物料中加入粘稠状物料重量的7倍的水，加热100℃熬30分钟成糊状粘结其它无机物料或物件，经脱水固化后粘结效果良好。
实例二
膏状甲基硅醇钾钠1.5份、生淀粉4份、钠水玻璃12份、水3份经机械混合，制成粘稠状，使用时，在粘稠状物料中加入粘稠状物料重量的13倍的水，加热120℃熬5分钟成糊状粘结其它无机物料或物件，经脱水固化后粘结效果良好。
实例三
膏状甲基硅醇钾钠1份、生淀粉6份、钠水玻璃10份、水3份经机械混合，制成粘稠状，使用时，在粘稠状物料中加入粘稠状物料重量的10倍的水，加热110℃熬15分钟成糊状粘结其它无机物料或物件，经脱水固化后粘结效果良好。
实例四
膏状甲基硅醇钾钠0.8份、生淀粉7份、钠水玻璃9份、水4份经机械混合，制成粘稠状，使用时，在粘稠状物料中加入粘稠状物料重量的12倍的水，加热100℃熬30分钟成糊状粘结其它无机物料或物件，经脱水固化后粘结效果良好。
应当理解的是，本发明的应用不限于上述的举例，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，所有这些改进和变换都应属于本发明所附权利要求的保护范围。

Claims (3)

1.一种保温专用的粘接材料，其特征在于，所述保温专用的粘接材料由膏状甲基硅醇钾钠、生淀粉、钠水玻璃、水组成；
其中各组分的重量份为，膏状甲基硅醇钾钠0.5～1.5份、生淀粉4～8份、钠水玻璃6～12份、水2～6份。
2.一种如权利要求1所述的保温专用的粘接材料的使用方法，其特征在于，包括以下步骤：
S100、按比例将膏状甲基硅醇钾钠、生淀粉、钠水玻璃、水进行机械混合，制成粘稠状物料待用；
S200、将粘稠状物料加水加热，在100~120℃熬5~30分钟成糊状。
3.根据权利要求2所述的保温专用的粘接材料的使用方法，其特征在于，步骤S200中加水的量为粘稠状物料重量的7～13倍。
CN 201110072324 2011-03-24 2011-03-24 一种保温专用的粘接材料 Expired - Fee Related CN102180640B (zh)