CN102180046B - Foaming printing method - Google Patents
Foaming printing method Download PDFInfo
- Publication number
- CN102180046B CN102180046B CN201010573013.XA CN201010573013A CN102180046B CN 102180046 B CN102180046 B CN 102180046B CN 201010573013 A CN201010573013 A CN 201010573013A CN 102180046 B CN102180046 B CN 102180046B
- Authority
- CN
- China
- Prior art keywords
- foaming
- resin
- fabric
- coated
- foamed resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A foam printing method using polyurethane resin is provided to reduce manufacturing costs while improving quality of foamed fabric through stable foam of the fabric regardless of kinds of the fabric. A foam printing method using polyurethane resin includes the following steps: preparing a print board by selecting fabric and a design; applying the polyurethane resin to prevent foam resin and the fabric from being separated each other while preventing leakage of the foam resin to the fabric(S2); attaching the print board on the polyurethane resin; forming a foamed layer by applying the foam resin(S3); applying color ink resin on a second polyurethane resin(S5); drying the resin for 1 - 12 hours at a room temperature(S6); and foaming the resin through compulsory thermo-compression in 120-160[deg.]C for 2 - 8 seconds.
Description
Technical field
The present invention relates to a kind of foaming printing method that uses polyurethane resin, more specifically, the present invention relates to a kind of improved foaming printing method, wherein, no matter what type fabric is can both be expressed as desirable user design to have 3-D effect, and the product of the high-quality of production cost reduction can be provided simultaneously.
Background technology
Conventionally,, in the time using serigraphy to form pattern, on the surface of fabric, use the various designs of Color Expression.Such design is expressed with the variety of way of character, figure, picture or real pictures, but is confined to plane expression always.
Therefore, recently developed and used the method for expressing various designs on the surface of fabric with three dimensional constitution.As representative example, there is following method: foamed resin is attached on fabric, then makes the foamed resin foaming of adhering to by heating, thereby three-D grain is provided.
In this example, paper, OPP, PVC etc. are as fabric.On this fabric face being of close texture, be coated on again in design to be expressed manual foamed resin by operator.Then, after the coating again that completes foamed resin, for example, in order to suppress the variation (shrinking) of fabric, make foamed resin in low temperature (below 100 ℃) foaming, realize three-D grain simultaneously.
Summary of the invention
According in the foaming printing method of conventional art, foamed resin is coated on fabric by operator is manual again.Therefore, the expression of design is difference along with the difference of operator's qualification, therefore causes the quality discrepancy of fabric finished product.
In addition,, in a lot of situations, operator can not the desirable design of accurate expression, and design may be plotted to outside desirable region in foamed resin is coated on to the process on fabric again.Given this,, after foamed resin foaming, be difficult to realize desirable design.Therefore, can not keep continuously on the whole homogeneous quality.
As mentioned above, be coated with foamed resin again on fabric time, the fabric that need to be of close texture, for example paper, OPP or PVC, thus cause expressing limited.On the other hand, on having the fabric of loose quality, common Woven fabric etc. make foamed resin be formed as can foaming layer time, can between fabric quality, flowing down in liquid foamed resin, thereby can not using.
Herein, on fabric, foamed resin is formed as can foaming layer after, fabric foams by low-temp foaming roller.But, for preventing that fabric is damaged, the temperature of roller does not reach the high temperature to being enough to make foamed resin foaming, and this has hindered the even foaming of foamed resin and foaming completely.Therefore, the problem of existence is, is difficult to provide the foaming that can in fact use fabric, because can not give full expression to desirable three-D grain.
Therefore, complete the problems referred to above that the present invention occurs to solve prior art, the invention provides the foaming printing method that uses polyurethane resin, wherein, irrelevant with the kind of fabric, just can obtain the foaming fabric of high-quality by uniform and stable foaming, and can reduce production costs.
According to an aspect of the present invention, provide a kind of foaming printing method that uses polyurethane resin, described method comprises: preparation process S1, for selecting to treat fabric and the design to be expressed of foaming printing and preparing printed panel; The first polyurethane resin application step S2, for being coated on described polyurethane resin on the fabric of whole preparation or part is expressed in the design of fabric, to prevent that foamed resin from flowing out and preventing that described foamed resin from separating with described fabric; Foamed resin application step S3, for described printed panel being closely attached to the described polyurethane resin being coated on described fabric, and be coated with described foamed resin thereon according to described design to be expressed can foaming layer to form; The second polyurethane resin application step S4, for being suppressed and making described foamed resin described polyurethane resin to be coated on again on the described foamed resin being coated with and to cover described foamed resin in the mode of even height foaming with the irregular foaming that makes described foamed resin; Painted step S5, for by resin-coated colored ink on the described polyurethane resin of the second layer with express shades of colour; Drying steps S6, for being coated on the described polyurethane resin on described fabric, described foamed resin and described colored ink resin drying; With foaming step S7, for dry workpiece is forced to hot pressing, make described foamed resin foam and expand, to realize three-D grain simultaneously.
In the present invention, regardless of the type (loose quality or fine and closely woven quality) of fabric, by using foamed resin just can express desirable design.In addition,, owing to can maintaining the high-foaminess of homogeneous, therefore can realize accurate expression and significantly improve 3-D effect.This has improved the quality of foaming fabric, thereby has strengthened international competitiveness.In addition, can reduce the production cost of foaming fabric, respond actively turn of the market simultaneously.
Accompanying drawing explanation
That carries out in conjunction with the drawings the following specifically describes, and above and other object of the present invention, feature and advantage will become clearer, in figure:
Fig. 1 describes according to the process chart of the foaming printing method of the use polyurethane resin of technology of the present invention;
Fig. 2 A～2D has shown according to the photo of the foaming printed fabric of technology of the present invention, wherein, Fig. 2 A shows dermatine, and Fig. 2 B shows natural leather, Fig. 2 C shows individual layer mesh (mono-mesh) fabric, and Fig. 2 D shows interlayer mesh (sandwich-mesh) fabric; With
Fig. 3 is the photo that shows the footwear of being made up of the foaming printed fabric that obtaining by technology of the present invention.
The specific embodiment
Foaming printing method according to the preferred embodiment of the present invention is described below with reference to accompanying drawings.
Fig. 1 describes according to the process chart of the foaming printing method of the use polyurethane resin of technology of the present invention; Fig. 2 A～2D shown according to the photo of the foaming printed fabric of technology of the present invention, and wherein, Fig. 2 A shows dermatine, and Fig. 2 B shows natural leather, and Fig. 2 C shows individual layer mesh fabric, and Fig. 2 D shows interlayer mesh fabric; Fig. 3 is the photo that shows the footwear of being made up of the foaming printed fabric that obtaining by technology of the present invention.
In the foaming printing method of use polyurethane resin according to the present invention, there is the foaming printing of three-D grain by preparation process S1, the first polyurethane resin application step S2, foamed resin application step S3, the second polyurethane resin application step S4, painted step S5, drying steps S6 and foaming step S7.
In preparation process S1, select to treat the fabric of foaming printing and design to be expressed, and prepare printed panel.In the present invention, the kind of fabric is not limited, as long as described fabric can reality use in industrial circle, for example clothing, footwear etc.
For example, the operable fabric that not only has such as leather (natural leather or dermatine) etc. to be of close texture, also has the loose fabrics of quality such as common Woven fabric, interlayer mesh fabric, individual layer mesh fabric.
In the first polyurethane resin application step S2, polyurethane resin is coated on whole fabric or the design of fabric to express part upper, to prevent that foamed resin from flowing out by fabric quality and preventing that described foamed resin from separating with fabric.
In foamed resin application step S3, printed panel close attachment, in the polyurethane resin being coated on fabric, is then coated with to foamed resin thereon to form foaming layer according to design to be expressed.
In the second polyurethane resin application step S4, on foamed resin, be coated with again polyurethane resin.The polyurethane resin being coated with is protected foamed resin in the mode that can make the inhomogeneous foaming of foamed resin in its foaming process be suppressed.This has suppressed the loss of foamed resin, and makes foaming layer to foam with uniform height.
In painted step S5, by resin-coated colored ink on the second urethane resin layer with express shades of colour.
In drying steps S6, by resin-coated to polyurethane resin to be foamed, foamed resin and colored ink on fabric after, by fabric in room temperature (approximately 20 ℃～35 ℃) dry 1 hour～12 hours.
In foaming step S7, be that the hot press of 120 ℃～160 ℃ carries out the pressure hot pressing of 2 seconds～8 seconds to dry workpiece by temperature.Therefore, foamed resin is foamed and expand, thereby three-D grain is provided.
In foamed resin application step S3, foamed resin can be coated with repeatedly according to design to be expressed, thus make can foaming layer alterable height.For example, the coating number of times of foamed resin (number of plies of coating) can change according to region or pattern in a design, thereby changes the final foaming height in foaming step S7.As a result, can express more three-D grain.
In foaming step S7, when in the time that the surface of the hot pressing die contacting with described foamed resin is applied by coating materials such as teflons (Teflon), treat the surface of foaming and carry out gloss finish.Otherwise in the time that coating processing is not carried out on the surface of hot pressing die, surface to be foamed is carried out tarnish and is processed.Therefore, by selecting these processing can show different expression.
Embodiment
Embodiment 1
According to design to be expressed, polyurethane resin is coated on to the surface of dermatine, makes the printed panel close attachment of layout in the fabric face that has been coated with polyurethane resin, being then coated with foamed resin can foaming layer to form.
Form can foaming layer after, polyurethane resin is applied to again can foaming layer, then coating is thereon for the blue ink resin of Color Expression.Subsequently drying at room temperature workpiece 8 hours.
To be dried workpiece and put into hot press, by forcing hot pressing to be foamed for 6 seconds at 140 ℃, thereby realize the foaming printing shown in Fig. 2 A.The workpiece of gained has shown highly homogeneous foamed state on the whole.
Embodiment 2
According to design to be expressed, polyurethane resin is coated on to the surface of natural leather, makes the printed panel close attachment of layout in the fabric face that has been coated with polyurethane resin, being then coated with foamed resin can foaming layer to form.
Form can foaming layer after, polyurethane resin is applied to again can foaming layer, then coating is thereon for the pink ink resin of Color Expression.Subsequently drying at room temperature workpiece 6 hours.
To be dried workpiece and put into hot press, by forcing hot pressing to be foamed for 8 seconds at 120 ℃, thereby realize the foaming printing shown in Fig. 2 B.The workpiece of gained has shown highly homogeneous foamed state on the whole.
Embodiment 3
According to design to be expressed, polyurethane resin is coated on to the surface of individual layer mesh fabric, makes the printed panel close attachment of layout in the fabric face that has been coated with polyurethane resin, being then coated with foamed resin can foaming layer to form.
Form can foaming layer after, polyurethane resin is applied to again can foaming layer, then coating is thereon for the blue ink resin of Color Expression.Subsequently drying at room temperature workpiece 5 hours.
To be dried workpiece and put into hot press, by forcing hot pressing to be foamed for 5 seconds at 150 ℃, thereby realize the foaming printing shown in Fig. 2 C.The workpiece of gained has shown highly homogeneous foamed state on the whole.
Embodiment 4
According to design to be expressed, polyurethane resin is coated on to the surface of interlayer mesh fabric, makes the printed panel close attachment of layout in the fabric face that has been coated with polyurethane resin, being then coated with foamed resin can foaming layer to form.
Form can foaming layer after, polyurethane resin is applied to again can foaming layer, then coating is thereon for the pearl ash color ink resin of Color Expression.Subsequently drying at room temperature workpiece 12 hours.
To be dried workpiece and put into hot press, by forcing hot pressing to be foamed for 7 seconds at 130 ℃, thereby realize the foaming printing shown in Fig. 2 D.The workpiece of gained has shown highly homogeneous foamed state on the whole.
In above-mentioned the present invention, in the time of coating foamed resin, the total height including polyurethane resin, foamed resin and colored ink resin is 0.1mm.But, in the time workpiece being dried and foam by pressure hot pressing subsequently, it is even foaming on the whole.The height of foaming part is 0.4mm～0.8mm after measured, and this is highly enough to show three-D grain.
The foaming printed fabric obtaining as mentioned above can be used as the upper of a shoe of footwear, as shown in Figure 3.Contrast with the another kind of situation of simple expression plane design on fabric face, above-mentioned foaming printed fabric demonstrates the 3-D effect of height.And its Color Expression is not worse than another kind of situation.Therefore, described fabric has advantages of other industrial circles that can be applied to fully beyond footwear.
Although illustrative embodiments of the present invention is described for purpose of explanation, but one skilled in the art will recognize that and can carry out various modifications, interpolation and replacement and can not deviate from as scope of the present invention disclosed in the accompanying claims and essence.
Claims (3)
1. use a foaming printing method for polyurethane resin, described foaming printing method comprises:
Preparation process S1, this step is used for selecting the fabric of pending foaming printing and design to be expressed, and prepares printed panel;
The first polyurethane resin application step S2, this step is for being coated on the described fabric of selection described polyurethane resin to prevent that foamed resin from flowing out and preventing that described foamed resin from separating with described fabric;
Foamed resin application step S3, this step is for being closely attached to by described printed panel the described polyurethane resin being coated on described fabric, and be coated with described foamed resin thereon according to described design to be expressed can foaming layer to form;
The second polyurethane resin application step S4, this step is for to make the irregular foaming of described foamed resin be suppressed and make described foamed resin described polyurethane resin to be coated on again on the described foamed resin being coated with and to cover described foamed resin in the mode of even height foaming;
Painted step S5, this step for by resin-coated colored ink on the described polyurethane resin of the second layer with express shades of colour;
Drying steps S6, this step is for being coated on the described polyurethane resin on described fabric, described foamed resin and described colored ink resin drying at room temperature 1 hour～12 hours; With
Foaming step S7, this step is used for making described foamed resin foam and expand, and realizes thus three-D grain,
Wherein, in described foaming step S7, by carry out the pressure hot pressing of 2 seconds～8 seconds the temperature of 120 ℃～160 ℃, to the processing of foaming of dry workpiece, to realize described three-D grain.
2. foaming printing method as claimed in claim 1, wherein, in described foamed resin application step S3, is coated with described foamed resin according to described design to be expressed repeatedly, thereby changes described height that can foaming layer.
3. foaming printing method as claimed in claim 1, wherein, in described foaming step S7, when in the time that the surface of the hot pressing die contacting with described foamed resin is coated or not coated, treats the surface of foaming and carries out gloss finish or matt processing.