CN102173632A - 一种水泥复合保塑助磨剂及使用方法 - Google Patents

一种水泥复合保塑助磨剂及使用方法 Download PDF

Info

Publication number
CN102173632A
CN102173632A CN 201110042683 CN201110042683A CN102173632A CN 102173632 A CN102173632 A CN 102173632A CN 201110042683 CN201110042683 CN 201110042683 CN 201110042683 A CN201110042683 A CN 201110042683A CN 102173632 A CN102173632 A CN 102173632A
Authority
CN
China
Prior art keywords
grinding aid
cement
grinding
admixture
concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110042683
Other languages
English (en)
Other versions
CN102173632B (zh
Inventor
蒋元海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongyuan Construction Group Co., Ltd.
Original Assignee
蒋元海
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 蒋元海 filed Critical 蒋元海
Priority to CN 201110042683 priority Critical patent/CN102173632B/zh
Publication of CN102173632A publication Critical patent/CN102173632A/zh
Application granted granted Critical
Publication of CN102173632B publication Critical patent/CN102173632B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种水泥复合保塑助磨剂及使用方法，将助磨剂与混凝土缓凝剂以一定比例复合后，再用一定比例的水稀释到一定浓度即可；采用这种水泥复合保塑助磨剂，在水泥生产的磨细作业时，既可满足助磨的目的，同时用这种水泥配制的混凝土具有很好的保塑效果，减少混凝土的经时损失，满足工程的需要，具有很好的技术经济效益和社会效益。

Description

一种水泥复合保塑助磨剂及使用方法
技术领域
本发明涉及一种水泥助磨剂及使用方法。
背景技术
现有技术中，水泥生产时为了提高强度，水泥生产中采用掺加助磨剂技术，在水泥细度、比表面积及强度提高的同时，水泥的性能也发生变化，使水泥的流动度减小，在配制混凝土时发生混凝土的流动性减小较大，特别是混凝土的坍落度损失很大(在混凝土技术上采用“经时损失”这个概念表示)；另外，一些水泥生产企业采用电厂的脱硫石膏代替二水石膏，由于其成分复杂且不稳定，也经常发生所配制的混凝土的经时损失很大，难以满足混凝土工程的施工要求，为此在混凝土搅拌时经常采用掺加混凝土缓凝剂的办法；上述二种办法是目前水泥行业和预拌混凝土行业中通常采用的技术措施。经查询，对水泥具有既助磨功能同时对所配制的混凝土具有保塑功能的复合型助磨材料，目前未见有这方面的报道。
发明内容
本发明的目的在于提供一种水泥复合保塑助磨剂及使用方法，用该保塑助磨剂生产水泥时既可以增加水泥细度及比表面积，提高水泥混合材掺量，满足强度要求；同时又可以使所配制的混凝土具有较好的流动性，减少混凝土的经时损失。
本发明的技术方案是：一种水泥复合保塑助磨剂及使用方法，将助磨剂与混凝土缓凝剂以一定比例复合后，再用水稀释到一定浓度；采用的助磨剂有：三异丙醇胺、乙二胺，掺加时只限其中一种助磨剂，采用的混凝土缓凝剂有：葡萄糖酸钠、柠檬酸，掺加时只限其中一种缓凝剂；助磨剂掺加的重量比例为50％～70％，混凝土缓凝剂的掺加的重量比例为30％～50％；上述二种材料复合后用水稀释后的浓度为40％～70％；用稀释后的水泥复合保塑助磨剂在水泥粉磨时以粉磨材料总重量的0.05％～0.3％的比例掺加，适用于硅酸盐水泥、普通硅酸盐水泥、复合硅酸盐水泥三种水泥品种。
本发明与现有技术相比具有以下优点：一种水泥复合保塑助磨剂及使用方法，采用这种水泥复合保塑助磨剂，在水泥生产的磨细作业时只要添加一种材料，既可满足助磨的目的，多掺加水泥混合材，减少水泥熟料的用量；同时用这种水泥配制的混凝土具有很好的保塑效果，减少混凝土的经时损失，满足工程的需要，一举二得，减少生产环节，具有很好的技术经济效益和社会效益。
具体实施方式
一种水泥复合保塑助磨剂及使用方法，将助磨剂与混凝土缓凝剂以一定比例复合后，再用水稀释到一定浓度；采用的助磨剂有：三异丙醇胺、乙二胺，掺加时只限其中一种助磨剂，采用的混凝土缓凝剂有：葡萄糖酸钠、柠檬酸，掺加时只限其中一种缓凝剂；助磨剂掺加的重量比例为50％～70％，混凝土缓凝剂的掺加的重量比例为30％～50％；上述二种材料复合后用水稀释后的浓度为40％～70％；用稀释后的水泥复合保塑助磨剂在水泥粉磨时以粉磨材料总重量的0.05％～0.3％的比例掺加，适用于硅酸盐水泥、普通硅酸盐水泥、复合硅酸盐水泥三种水泥品种。
实施例1.将三异丙醇胺与柠檬酸以质量比60％∶40％的比例复合，用水稀释到50％的浓度；用稀释后的水泥保塑助磨剂以粉磨时各种材料总重量的0.12％的比例掺加；水泥粉磨时硅酸盐水泥熟料∶矿渣∶石膏的重量比例为77∶18∶5，经30min粉磨，水泥的细度为1.5％，水泥的比表面积为380m2/kg，，用这种水泥配制的混凝土的经时损失为10％，完全满足混凝土施工的要求。

Claims (1)

1.一种水泥复合保塑助磨剂及使用方法，将助磨剂与混凝土缓凝剂以一定比例复合后，再用水稀释到一定浓度；采用的助磨剂有：三异丙醇胺、乙二胺，掺加时只限其中一种助磨剂，采用的混凝土缓凝剂有：葡萄糖酸钠、柠檬酸，掺加时只限其中一种缓凝剂；助磨剂掺加的重量比例为50％～70％，混凝土缓凝剂的掺加的重量比例为30％～50％；上述二种材料复合后用水稀释后的浓度为40％～70％；用稀释后的水泥复合保塑助磨剂在水泥粉磨时以粉磨材料总重量的0.05％～0.3％的比例掺加，适用于硅酸盐水泥、普通硅酸盐水泥、复合硅酸盐水泥三种水泥品种。
CN 201110042683 2011-02-16 2011-02-16 一种水泥复合保塑助磨剂的生产方法 Expired - Fee Related CN102173632B (zh)