CN102152407A - 一种无钴低镍预合金基干切金刚石圆锯片 - Google Patents

一种无钴低镍预合金基干切金刚石圆锯片 Download PDF

Info

Publication number
CN102152407A
CN102152407A CN2011100230438A CN201110023043A CN102152407A CN 102152407 A CN102152407 A CN 102152407A CN 2011100230438 A CN2011100230438 A CN 2011100230438A CN 201110023043 A CN201110023043 A CN 201110023043A CN 102152407 A CN102152407 A CN 102152407A
Authority
CN
China
Prior art keywords
percent
powder
alloy
nickel
cobalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100230438A
Other languages
English (en)
Inventor
张善印
朱华磊
顾骏
刘中吾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUBEI CHANGLI SUPERHARD MATERIAL CO Ltd
Original Assignee
HUBEI CHANGLI SUPERHARD MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBEI CHANGLI SUPERHARD MATERIAL CO Ltd filed Critical HUBEI CHANGLI SUPERHARD MATERIAL CO Ltd
Priority to CN2011100230438A priority Critical patent/CN102152407A/zh
Publication of CN102152407A publication Critical patent/CN102152407A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种无钴低镍预合金基干切金刚石圆锯片，属建材加工机械配件。由钢基体和刀头构成，所述刀头的结合剂组分按重量百分比为：预合金60％-70％，铜粉20％-30％，锡粉4％-8％，镍粉1％-4％，石蜡1％-2％；其中预合金的组分重量百分比为：铁粉60％，镍粉7％，铜粉27％，锡粉5.5％，铈粉0.5％。其采用预合金粉末为基础，利用预合金的独特优势，大大提高了胎体的导热，耐热效果，可以完全用于干切，解决了以往单质粉不能干切的难题，比以往的钴基，镍基结合剂降低了50％-60％的成本，锋利度提高了30％-40％，大大提高了加工效率。

Description

一种无钴低镍预合金基干切金刚石圆锯片
技术领域
本发明涉及一种用于加工石材等建筑材料的干切金刚石圆锯片，特别是涉及到预合金基金刚石圆锯片结合剂。
背景技术
金刚石圆锯片是有一个钢基体和镶嵌在基体上的刀头两部分组成，钢制基体有一个中心孔，该锯片通过所述中心孔安装在一个旋转的驱动轴上，支撑钢制基体外围的刀头，刀头里的金刚石起主要的切割作用，金刚石用于破碎，研磨被加工的材料，结合剂起保护金刚石和把持金刚石不被过早的脱落，并和金刚石同步磨损，因此结合剂的性能在整张锯片中起很的作用很重要。在现有技术中，用于制造金刚石圆锯片的结合剂大多为钴基，镍基等，并以单质粉的形式存在，一般结合剂做成的锯片在无水状态下工作，锯片会在切割点产生850度左右的高温，会造成锯片烧齿，无法正常使用，直至报废。现在市场上建筑工地相当大的一部分高空作业，要求干切，面对日益扩大的干切市场，这类结合剂对市场适应性差，使用性能达不到要求，并且成本高，缺乏市场竞争力。
发明内容
本发明所要解决的技术问题在于避免上述技术中的不足，提供一种可以有效提高胎体导热，散热，耐热并且性能优良，生产工艺简单，成本低，可以完全干切的新型金刚石圆锯片结合剂。本发明的技术方案是：一种无钴低镍预合金基干切金刚石圆锯片，由钢基体和刀头构成，所述刀头的结合剂组分按重量百分比：预合金60％---70％，铜粉20％--30％，锡粉4％---8％，镍粉1％---4％，石蜡1％---2％；其中预合金的主要组分重量百分比为：铁粉60％，镍粉7％，铜粉27％，锡粉5.5％，铈粉0.5％。
进一步优化，最优方案为，重量百分比预合金65％，铜粉26％，锡粉6％，镍粉1.5％，石蜡1.5％
本发明有如下优势，采用预合金粉末为基础，利用预合金的独特优势，大大提高了胎体的导热，耐热效果，可以完全用于干切，解决了以往单质粉不能干切的难题，比以往的钴基，镍基结合剂降低了50％---60％的成本，锋利度提高了30％---40％，大大提高了加工效率，本结合剂的烧结温度为摄氏740℃---800℃。
具体实施方式
下面结合具体的实施例来进一步说明本发明
实施例1，取预合金粉末6公斤，铜粉3公斤，镍粉0.1公斤，锡粉0.8公斤放入混料桶，混合0.5小时，加入石蜡0.1公斤，继续混合2.5小时，烧结温度为摄氏740℃---800℃。
实施例2，取预合金粉末6.5公斤，铜粉2.6公斤，镍粉0.15公斤，锡粉0.6公斤放入混料桶，混合0.5小时，加入石蜡0.15公斤，继续混合2.5小时，烧结温度为摄氏740℃---800℃。
实施例3，取预合金粉末7公斤，铜粉2公斤，镍粉0.4公斤，锡粉0.4公斤放入混料桶，混合0.5小时，加入石蜡0.2公斤，继续混合2.5小时，烧结温度为摄氏740℃---800℃。

Claims (1)

1.一种无钴低镍预合金基干切金刚石圆锯片，由钢基体和刀头构成，其特征是所述刀头的结合剂组分按重量百分比为：预合金60％---70％，铜粉20％--30％，锡粉4％---8％，镍粉1％---4％，石蜡1％---2％；其中预合金的组分重量百分比为：铁粉60％，镍粉7％，铜粉27％，锡粉5.5％，铈粉0.5％。
CN2011100230438A 2011-01-20 2011-01-20 一种无钴低镍预合金基干切金刚石圆锯片 Pending CN102152407A (zh)