Ventilative anti-skidding meal pad and processing method thereof
Technical field
The invention belongs to the dinnerware technical field, be specifically related to a kind of ventilative anti-skidding meal pad, and relate to the processing method of this ventilative anti-skidding meal pad.
Background technology
The technical scheme that in disclosed Chinese patent literature, is no lack of relevant meal pad, the typical meal pad of recommending as CN2680146Y, this scheme be by cotton goods, silk goods or flannelette as the some thick chinas of filling the post of by bamboo chip or wood chip of the surface recombination of base member, this patent scheme mainly plays the sensation of giving the Nature to the eater, help to adjust eater's disposition, but this meal pad does not have gas permeability, in case it is wetting, be difficult for dry, thereby easy breed bacteria, and do not have skidproof effect.
The special dinner pad structure that Granted publication CN2693131Y provides, it is that some struts and fabric one are made into plates, make strut be subjected to fabric to coat the location, and the upper and lower side surface at plates is respectively established mucigel, fabric and strut is cohered fixing, finally makes plates form stiffening sheet, and then cut (cutting) to required specification, the meal pad of this structure is not only lost flexibility, and also is difficult to ensure that promptly skid resistance is unsatisfactory with the adhesion effect of dining table.
The meal pad that Granted publication CN201256856Y introduces is to be coiled to form by the form of soft band with involute, has good technology enjoying value.Again, the meal pad that CN201542326U discloses is made of soft lower floor and bark upper strata, soft lower floor and bark upper strata are adhesively fixed, and, the meal pad that CN201612447U discloses is by bamboo mat face body and be incorporated into the barrier fabrics backsight at the bamboo mat face body back side and the decorative layer that is incorporated into bamboo mat face body front, and by the leather bound edge.There is the problem of gas permeability and skid resistance shortcoming equally in these patent schemes.
In view of above-mentioned prior art, the applicant thinks and is necessary to be improved that technical scheme described below produces under this background.
Summary of the invention
Task of the present invention is to provide a kind of both to have been had desirable gas permeability and had used in wetting back easily drying in order to avoid breed bacteria, had good skid resistance again and used and avoid the ventilative anti-skidding meal pad that moves about under user mode.
Another task of the present invention is to provide a kind of processing method of ventilative anti-skidding meal pad, this method processing step is terse, equipment requires not harsh, the industrial amplification production requirement can not only be satisfied, and comprehensive embodiment of the technique effect of described ventilative anti-skidding meal pad can be guaranteed.
For top priority of the present invention is finished in embodiment, technical scheme provided by the invention is: a kind of ventilative anti-skidding meal pad, be included under the user mode Facad structure layer of a side outward, under user mode towards the structure layer of an interior side be used for just described, the edge cover strip of position, the edge overseam of structure layer, be characterised in that: described Facad structure layer surface outward constitutes gentle suitable layer, described structure layer is by the mesh knitted layer, the sandwich structure that plain cloth braid and the middle silk articulamentum that not only is connected with the mesh knitted layer but also is connected with the plain cloth braid between mesh knitted layer and plain cloth braid constitute and be the eyelet fabric of hollow out, wherein: just described, also inserted packed layer between the structure layer.
In a specific embodiment of the present invention, described gentle suitable layer is pile loop layer, suede granulosa, suede post layer or tapetum.
In another specific embodiment of the present invention, the surface of described bottom surface structure sheaf is combined with refuses the water skid resistant course.
In another specific embodiment of the present invention, the thickness of described structure layer is 2-30mm.
In another specific embodiment of the present invention, described packed layer is a sponge.
Also have in the specific embodiment of the present invention, the mesh of described mesh knitted layer be shaped as circular port, rectangular opening or polygonal hole.
Finish another task of the present invention for embodiment, technical scheme provided by the invention is: a kind of processing method of ventilative anti-skidding meal pad may further comprise the steps:
A) raw material is selected, that selection is processed by dacron thread or polyamide composite filaments and under user mode outward surface constitute the lining of gentle suitable layer as the Facad structure layer, choose by mesh knitted layer, plain cloth braid and the middle silk articulamentum between mesh knitted layer and plain cloth braid is that constitute and the eyelet fabric of hollow out that be sandwich structure as the bottom surface structure sheaf, and choose sponge as packed layer;
B) compound, with packed layer just inserting, between the structure layer, and Facad structure layer, packed layer and the heating of structure layer is compound, and the control combined temp;
C) edge sealing is sealed the position, edge of Facad structure layer and structure layer in the mode of seam bag by edge cover strip, obtains compound blank to be coated with;
D) gluing, to wait to be coated with compound blank and introduce glue spreader, and make the glue spreader of structure layer towards glue spreader, under the state of control rubber cement temperature, the surface-coated of structure layer is refused the anti-skidding glue of water by glue spreader, the surface of structure sheaf forms and refuses the water nonskid coating overleaf, go out glue spreader, obtain ventilative anti-skidding meal pad.
More of the present invention and in specific embodiment, step B) the control combined temp described in is that combined temp is controlled to be 200-220 ℃.
In of the present invention and then specific embodiment, step D) the anti-skidding glue of water of refusing described in is SEBS type glue.
Of the present invention again more and in specific embodiment, step D) the control rubber cement temperature described in is that the rubber cement temperature is controlled to be 180-240 ℃.
Technical scheme provided by the invention softens suitable layer owing to constituting on the surface of Facad structure layer, thereby has comfortableness; Because it is that the structure layer is constituted sandwich structure by mesh knitted layer, plain cloth braid and middle articulamentum between mesh knitted layer and plain cloth braid and be the eyelet fabric of hollow out, therefore have good anti-skidding and gas permeability, avoid because of long-term moistening breed bacteria.The process steps that provides is terse, technology and equipment is required no fastidious property, and can ensure comprehensive embodiment of the aforementioned effect of ventilative anti-skidding meal pad.
Description of drawings
Fig. 1 is the example structure figure of the ventilative anti-skidding meal pad of the present invention.
The specific embodiment
For the auditor that makes Patent Office particularly the public can understand technical spirit of the present invention further; the applicant will be illustrated with the embodiment that provides below; but embodiment is not the restriction to the present invention program; all what done according to the present invention design only is form but not the variation of essence, then all should be considered as technical scheme scope of the present invention and is protected.
Embodiment 1:
Ask for an interview Fig. 1, the making of the ventilative anti-skidding meal pad of structure shown in Figure 1 may further comprise the steps:
A) raw material is selected, select to process by polyamide composite filaments and under user mode outward promptly towards on the surface and the back side all constitute the gentle suitable layer of filling the post of by tapetum 11 lining as Facad structure layer 1, the grammes per square metre of Facad structure layer 1 is 210g/m
2Selecting order number (density range) is that 18 orders and thickness are that the sponge of 2mm is as packed layer 4, choosing and adopting two-needle bar is to be connected the mesh knitted layer 21 of the plain cloth braid 22 by the top layer, bottom of terylene and being used between plain cloth braid 22 and mesh knitted layer 21 that constitute and the eyelet fabric of hollow out that is the sandwich structure form of the articulamentum 23 of plain cloth braid 22 and mesh knitted layer 21 as structure layer 2 through the material that the braiding fabrication technique obtains, the thickness of structure layer 2 is 30mm, and grammes per square metre is 2000g/m
2The notion of sandwich described here or title are released meaning and are meant that the institutional framework of structure layer 2 is three layers, be aforesaid plain cloth braid 22, mesh knitted layer 21 and middle silk articulamentum 23, the structure layer 2 of this structure can be called " sandwich air layer mesh fabric ", has air permeability and good, have excellent skid resistance again, the hole shape of the mesh of aforesaid mesh knitted layer 21 is polygonal cellular mesh;
B) compound, earlier that Facad structure layer 1 and packed layer 4 is compound, again that structure layer 2 is compound with the Facad structure layer 1 that is compounded with packed layer 4, wherein structure layer 2 fits with packed layer 4, in recombination process, the heating combined temp of compounding machine is 200 ℃, thereby just makes, structure layer 1,2 and packed layer 4 three are combined into one, a side that is packed layer 4 combines with Facad structure layer 1, and the opposite side of packed layer 4 combines with structure layer 2;
C) edge sealing, with cloth as edge cover strip 3, will be by step B) composite grey fabric after compound that obtains is by required size for example after the size cutting by 70cm * 160cm, with the sewing mode with edge cover strip 3 seams just wrapping, the edge, surrounding of structure layer 1,2, obtain waiting to be coated with the compound blank pad;
D) gluing, with step C) waiting of obtaining be coated with the compound blank pad and introduce glue spreader (also claiming gluing machine) gluing, make the glue spreader of a side of bottom surface structure sheaf 2 towards glue spreader, the rubber cement that by glue spreader with temperature is 180 ℃ is refused the anti-skidding glue of water to the surface-coated of structure layer 2, the surface of structure sheaf 2 forms and refuses the water nonskid coating overleaf, be expert at behind the glue spreader, promptly obtain ventilative anti-skidding meal pad by structure shown in Figure 1.In this step, the described water marine glue of refusing preferably uses the trade mark by the production and sales of the grand sizing material in Shanghai City, China Co., Ltd to be SEBS type glue.
Embodiment 2:
Only with steps A) in the gentle suitable layer 11 of Facad structure layer 1 change into by the suede granulosa and filling the post of, and the grammes per square metre of Facad structure layer 1 changes 300g/m into
2, change the grammes per square metre of structure layer 2 into 150g/m
2, thickness changes 2mm into; With step B) in the heating combined temp change 220 ℃ into; With step C) in size change 30cm * 30cm into; With step D) in the rubber cement temperature change 240 ℃ into, all the other are all with the description to embodiment 1.
Embodiment 3:
Only with steps A) in the gentle suitable layer 11 of Facad structure layer 1 change into by terry loop layer and filling the post of, and the grammes per square metre of Facad structure layer 1 changes 260g/m into
2, change the grammes per square metre of structure layer 2 into 1500g/m
2, thickness changes 20mm into; With step B) in the heating combined temp change 210 ℃ into; With step C) in size change 50cm * 60cm into; With step D) in the rubber cement temperature change 215 ℃ into, all the other are all with the description to embodiment 1.